• JSTS:Journal of Semiconductor Technology and Science
• /
• v.1 no.4
• /
• pp.202-208
• /
• 2001

In Recent results suggested that doping $Ta_2O_5$ with a small amount of $TiO_2$ using standard ceramic processing techniques can increase the dielectric constant of $Ta_2O_5$ significantly. In this paper, this concept is studied using RTCVD (Rapid Thermal Chemical Vapor Deposition). Ti-doped $Ta_2O_5$ films are deposited using $TaC_{12}H_{30}O_5N$, $C_8H_{24}N_4Ti$, and $O_2$ on both Si and $NH_3$-nitrided Si substrates. An $NH_3$-based interface layer at the Si surface is used to prevent interfacial oxidation during the CVD process and post deposition annealing is performed in $H_2/O_2$ ambient to improve film quality and reduce leakage current. A sputtered TiN layer is used as a diffusion barrier between the Al gate electrode and the $TaTi_xO_y$ dielectric. XPS analyses confirm the formation of a ($Ta_2O_5)_{1-x}(TiO_2)_x$ composite oxide. A high quality $TaTi_xO_y$ gate stack with EOT (Equivalent Oxide Thickness) of $7{\AA}$ and leakage current $Jg=O.5A/textrm{cm}^2$ @ Vg=-1.0V has been achieved. We have also succeeded in forming a $TaTi_x/O_y$ composite oxide by rapid thermal oxidation of the as-deposited CVD TaTi films. The electrical properties and Jg-EOT characteristics of these composite oxides are remarkably similar to that of RTCVD $Ta_2O_5, suggesting that the dielectric constant of $Ta_2O_5$ is not affected by the addition of $TiO_2$.

• The Korean Journal of Physiology and Pharmacology
• /
• v.19 no.2
• /
• pp.167-175
• /
• 2015

A retinal prosthesis is being developed for the restoration of vision in patients with retinitis pigmentosa (RP) and age-related macular degeneration (AMD). Determining optimal electrical stimulation parameters for the prosthesis is one of the most important elements for the development of a viable retinal prosthesis. Here, we investigated the effects of different charge-balanced biphasic pulses with regard to their effectiveness in evoking retinal ganglion cell (RGC) responses. Retinal degeneration (rd1) mice were used (n=17). From the ex-vivo retinal preparation, retinal patches were placed ganglion cell layer down onto an $8{\times}8$ multielectrode array (MEA) and RGC responses were recorded while applying electrical stimuli. For asymmetric pulses, 1st phase of the pulse is the same with symmetric pulse but the amplitude of 2nd phase of the pulse is less than $10{\mu}A$ and charge balanced condition is satisfied by lengthening the duration of the pulse. For intensities (or duration) modulation, duration (or amplitude) of the pulse was fixed to $500{\mu}s$($30{\mu}A$), changing the intensities (or duration) from 2 to $60{\mu}A$(60 to $1000{\mu}s$). RGCs were classified as response-positive when PSTH showed multiple (3~4) peaks within 400 ms post stimulus and the number of spikes was at least 30% more than that for the immediate pre-stimulus 400 ms period. RGC responses were well modulated both with anodic and cathodic phase-1st biphasic pulses. Cathodic phase-1st pulses produced significantly better modulation of RGC activity than anodic phase-1st pulses regardless of symmetry of the pulse.

• Applied Chemistry for Engineering
• /
• v.26 no.6
• /
• pp.640-647
• /
• 2015

As the need for next-generation flexible electronics grows, novel materials and technologies that can replace conventional indium tin oxide (ITO) for transparent electrodes have been of great interest. Among them, a conducting polymer, especially poly(3,4-ethylenedioxythiophene) : poly(styrene sulfonate) (PEDOT : PSS) is one of the most promising candidates because it is mechanically flexible, inexpensive, and capable of being processed in solution. Currently, there are a lot of research efforts on enhancing its electrical conductivity to the level of ITO or metal electrodes through chemical and/or physical processing. In this review article, we present various additives and pre-/post-deposition processing methods for improving the electrical conductivity of PEDOT : PSS. Some of representative reports are also introduced, which demonstrated the use of conductivity-enhanced PEDOT : PSS as transparent electrodes in electronics and energy conversion.

• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.23-27
• /
• 2008

We have investigated the effect of annealing on the structural and optical properties of polycrystalline Ga doped ZnO (GZO) films grown on glass substrates by RF-magnetron sputter at room temperature. The structural and optical properties of as-grown GZO films were characterized and then samples were annealed at $400{\sim}600^{\circ}C$ in $N_2$ ambient for 30, 60 minutes, respectively. The field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD) were used to measure the grain size and the crystalline quality of the films. We found that the crystalline quality was improved and the grain size tends to be increased. The optical properties of GZO thin films were analyzed by UV-VIS-NIR spectrophotometers. It is found that optical properties of thin films are increased by annealing and can be used for transparent electrode application. We believe that the appropriate post-growth heat treatment could be contributed to the improvement of GZO-based devices.

• Journal of the Korean Vacuum Society
• /
• v.22 no.2
• /
• pp.98-104
• /
• 2013

$VO_2$ is an attractive thermochromic material, in which its electrical and optical properties can be switched by the structural phase-transition about $68^{\circ}C$. Recently, graphene is also a rising material which is researched as a transparent electrode because of its superior electrical and optical characteristics. In this respect, we try to fabricate the hybridized films using $VO_2$ and graphene on transparent sapphire substrate and then we investigate a structure and characterize an optical property for the samples as a function of temperature. According to the result of IR-transmittance analysis of $VO_2$ films as a function of temperature, the graphene-supported sapphire substrates are better about 10% than the bare sapphire substrates. The mean phase transition temperatures are also decreased as the number of graphene-layers increased and the hysteresis of phase transitions are narrowed.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1170-1175
• /
• 1998

PZT films without lower electrode were deposited on the highly doped Si(100) substrate with MgO buffer layer (Mgo/si) by RF magnetron sputtering method followed by the rapid thermal annealing at $650^{\circ}C$ . We investigated the dependences of the crystalline and electrical properties on the MgO thickness and the RTA post annealing. The PZT films on bare Si (without MgO) showed pyrochlore crystal structure while those on MgO(50 )/Si substrates showed the typical perovskite crystal structures. From SEM and AES analysis, the thickness of PZT films was about 7000 showing relatively smooth interface. The depth profiles indicated that atomic species were distributed homogeneously in the PZT/MgO/Si substrate. The dielectric constant($\varepsilon_{r}$ ) and remanent polarization(2Pr) were about 300 and $14\mu$C/$\textrm{cm}^2$;, respectively. The leakage current was about $3.2\mu$/A$\textrm{cm}^2$.

• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.162-165
• /
• 2007

We investigated the effects of the capping layer materials on the crystallization of the amorphous top-CoFeB (t-CoFeB) electrode and the magnetoresistance properties of the magnetic tunnel junctions (MTJs). When the hcp(002)-textured Ru capping layer was used, the amorphous t-CoFeB was crystallized to bcc-CoFe(110). The CoFe(110)/Ru(002) texture relation can be minimized the lattice mismatch down to 5.6%. However, when the fine polycrystalline but almost amorphous TiAl or amorphous ZrAl were used, the amorphous t-CoFeB was crystallized to bcc-CoFe(002). When the amorphous capping materials were used, the evolution of the t-CoFeB texture was affected mainly by the MgO(001) texture. Consequently, the M ratios of the annealed MTJ capped with the ZrAl and TiAl (72.7 and 71.8%) are relatively higher than that of the MTJ with Ru capping layer (46.7%). In conclusions, the texture evolution of the amorphous t-CoFeB during the post deposition annealing could be controlled by the crystallinity of the adjacent capping layer and in turn, it affects the TMR ratio of MTJs.

• Applied Chemistry for Engineering
• /
• v.7 no.6
• /
• pp.1078-1086
• /
• 1996

The peroxo-polytungstic acid was formed by the direct reaction of tungsten powder with the hydrogen peroxide solution. Peroxo-polytungstic powder were prepared by rotary evaporator using the fabricated on to ITO coated glass as substrate by dip-coating method using $2g/10mL(W-IPA/H_2O)$ sol solution. A substrate was dipped into the sol solution and after a meniscus had settled, the substrate was withdrawn at a constant rate of the 3mm/sec. Thicker layer could be built up by repeated dipping/post-treatment 15 times cycles. The layers dried at the temperature of $65{\sim}70^{\circ}C$ during the withdrawn process, and then tungsten oxides thin film was formed by final heating treatment at the temperature of $230{\sim}240^{\circ}C$ for 30min. A linear rotation between the thickness of thin film and the number of dipping/post-treatment cycles for tungsten oxides thin films made by dip-coating was found. The thickness of thin film had $60{\AA}$ after one dipping. From the patterns of XRD, the structure of tungsten oxides thin film identified as amorphous one and from the photographs of SEM, the defects and the moderate cracks were observed on the tungsten oxides thin film, but the homogeneous surface of thin films were mostly appeared. The electrochemical characteristic of the $ITO/WO_3$ thin film electrode were confirmed by the cyclic voltammetry and the cathodic Tafel polaization method. The coloring bleaching processes were clearly repeated up to several hundreds cycles by multiple cyclic voltammetry, but the dissolved phenomenon of thin film revealed in $H_2SO_4$ solution was observed due to the decrease of the current densities. The diffusion coefficient was calculated from irreversible Randles-Sevick equation from the data obtained by the cyclic voltammetry with various scan rates.