• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10b
• /
• pp.1211-1214
• /
• 2000

The purpose of this paper was to study of blast furnace slag cement of high early strength and replacement ordinary portland cement. we prepared the specimens of cement and concrete with various mixing proportions of elementary materials. For example, clinker, gypsum(1~10%), fineness $4, 000~6, 000cm^2/g$ of blast furnace slag(30~50%), limestone etc. As a result of this study, fineness $(4, 000cm^2/g)$ blast furnace slag was of used replacement ordinary portland cement and fineness $(6, 000cm^2/g)$ blast furnace slag was of used blast furnace slag cement of high early strength.

• Journal of the Korean Ceramic Society
• /
• v.44 no.9
• /
• pp.477-482
• /
• 2007

The effect of the mixing ratio of compounds in a slag-OPC-Gypsum system on the physical properties of Slag cement is investigated in this study. $Na_2SO_4$ was used as an alkali activator. Blast furnace slag cement was prepared from a mixture of blast furnace slag, ordinary Portland cement and anhydride gypsum. The fluidity and the compressive strength according to the ratio of each mixture were analyzed in statistical analyses in order to discover the parameters influencing the fluidity and compressive strength. The results showed that the hydration of blast furnace slag took place with the addition of $Na_2SO_4$ and that column-crystalline ettringite was created as the main hydration product of the blast furnace slag. In addition, it was found that the compressive strength of blast furnace slag cement tends to increase when the ordinary Portland cement content is higher up to three days. However, it is known that the compressive strength tends to increase as the blast furnace slag content becomes higher with increases in the level of OPC after 28 days. As a result of this analysis, it is believed that the ordinary Portland cement content influences the initial compressive strength of blast furnace slag cement, and that in later days this is highly influenced by the slag content.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.40 no.5
• /
• pp.59-67
• /
• 1998

The object of this study is to investigate the strength characteristics and the freeze-thaw resistance of high strength concrete incorporating fine blast furnace slag. Major experimental variables were the water/cement ratio, maximum size of coarse aggregate, and cement types such as ordinary portland and slag cement. The results were as follows ; The workability of fresh concrete incorporating fine blast furnace slag was better than that of OPC(ordinary Portland cement) in terms of slump. The freeze-thaw resistance showed better than that of OPC, keeping more than 90% of relative modules of elasticity after 506 cycles and showing only a hair crack at surface without serious damage. Thus, the fine blast furnace slag might be recycled at concrete to make high strength concrete at fields.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.89-94
• /
• 2003

In this research, the physical properties of self compacting concrete using ground granulated blast furnace slag and fly ash as a part of cement were investigated. Concrete using ground granulated blast furnace slag and fly ash was prepared with various ground granulated blast furnace slag(30-50 volume %) and fly ash(10-20 volume %) replacement for cement. The effect of each of the materals, which have effects on self compacting concrete made by the basic mix proportion used granulated blast furnace slag and fly ash after hardening, has been checked. The workability, flowing characteristics, resistance of segregation of materals, air content, and compressive strength of concrete using ground granulated blast furnace slag and fly ash were tested and the results were compared with those of ordinary portland cement concrete. In the experiment, we acquired satisfactory results at the point of flowing characteristics and strengths of concrete using ground granulated blast furnace and slag fly ash within the replacement ratio of 65%

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.193-196
• /
• 2003

In this paper, the experimental investigation for the setting properties of cement paste, the consistency and strength properties of mortar with steel furnace slag dust was performed and compared with those of cement paste and mortar with ground granulated blast furnace slag. When steel furnace slag dust was replaced with normal portland cement, setting time and flow value indicated to good results like as mortar with ground granulated blast furnace slag. However, mortar with steel furnace slag dust expressed to appreciably strength devaluation according to containing ratio, and did not indicate the pozzolanic reaction like as ground granulated blast furnace slag.

• Journal of the Korea Concrete Institute
• /
• v.27 no.1
• /
• pp.3-9
• /
• 2015

In this study, hydration properties of ordinary Portland cement were examined, shown from a limestone and blast furnace slag alone or their mixture up to 10% as a minor mineral additives. As of setting time, it was identified that final setting became faster as the amount of limestone mixture increased, which showed limestone accelerated early hydration faster than blast furnace slag. This is because limestone did accelerate the hydration of alite. At the age of 3 days, limestone 5%-blast furnace slag 5% mixture had the highest compressive strength of mortar. It is because hydration acceleration of alite by limestone, and $Ca(OH)_2$ that was additionally formed by hydration acceleration of alite reacted with blast furnace slag, and as a result, additionally created C-S-H hydrate. Regarding the hydration properties by the age of 7 and 28 days, limestone 3%-blast furnace slag 7% of composited mixture showed the largest compressive strength, and in comparison with the 3 days in curing age. This period is when hydration reaction of blast furnace slag is active and the amount of hydrate depends on the amount of blast furnace slag mixture more than that of the limestone mixture. And in order to vitalize hydration reaction of blast furnace slag the amount of $Ca(OH)_2$ created has to increase, and thus, a small amount of limestone is necessary that can accelerate the hydration of alite. Therefore, after the age of 7 days, the fact that there were a large amount of blast furnace slag mixture and small amount of limestone mixture was effective to the strength development of ordinary Portland cement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.44-47
• /
• 2003

High flowing concrete has not spread whole in the normal concrete structure, because it requires special quality control technique. Recently owing to the lack of natural resources and reinforcement of environmental standard, the construction cost of cement is rapidly increased. Also ready mixed concrete industry has gone through various economical difficulty as the manufacture cost of concrete is increased. So, the purpose of this study is to evaluate the qualities of middle fluidity concrete using the fly-ash and portland blast-furnace slag cement in order to decrease the amount of cement and resolve the problem of the quality control of high flowing concrete and the manufacture cost. The results of this study show that it reduces the amount of addition of superplasticizer and develope properties of concrete to the use the fly-ash and portland blast-furnace slag cement.

• Journal of the Korean Ceramic Society
• /
• v.36 no.2
• /
• pp.130-135
• /
• 1999

The enhanced slag fineness and the batch water of low water-to-cement ratio(W/C) were employed in order to improve the early strength of blast-furnace slag blended cement at low temperature. A grinding aid was used to grind the blast-furnace slag into the fineness of 6,280$\textrm{cm}^2$/g (Blaine), and this fine slag was then homogeneously mixed with the ordinary Portland cement to produce the blast-furnace slag blended cement containing 40% slag by weight composition. On the other hand, the batch water could be reduced from W/C=0.50 (KS L 5105) to W/C=0.33 through a commercial, naphthalene type superplasticizer. Through the method mentioned above, the early strength of the blast-furnace slag blended cement at low temperature could be enhanced even somewhat higher than the Portland cement strength. And the microsturcture of the cement was studied by both the pore structure analysis and the A.C. impedance measurement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.124-128
• /
• 1997

In order tohave a betterunderstanding of thefavorable effect ofground granulated blast-furnace slag and fly ash, slump loss, temperature risingand compressive strength of concrete were investigated into diffrent conditions. When slag was mixed with ordinary portland cement as30%, slump loss gotto some 18% at 60min, maximum temperatureto some $43^{\cire}C$ at 180min, compressive strength similar to that of ordinary portland concrete at 28 days. Therefore it wasnoted thatslump loss andmaximum teaperaturerising of concrete were very reduced according to ground granulated blast-furnace slag and fly ash mixed with ordinary portland cement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.579-584
• /
• 2002

In this research, the physical properties of self compacting concrete using ground granulated blast furnace slag as a part of cement were investigated. Concrete using ground granulated blast furnace slag was prepared with various ground granulated blast furnace slag replacement(20~80 volume %) for cement and the quantities of coarse aggregate in concrete were 50%, 55% and 60% of ratio of absolute volume of coarse aggregate. The workability, flowing characteristics, air content and compressive strength of concrete using ground granulated blast furnace slag were tested and the results were compared with those of ordinary portland cement concrete. In the experiment, we acquired satisfactory results at the point of flowing characteristics and strengths of concrete using ground granulated blast furnace slag within tile replacement ratio of 50% and the optimum quantity of coarse aggregate in concrete was found to be 50%~55% of ratio of absolute volume of coarse aggregate.