Abstract
The enhanced slag fineness and the batch water of low water-to-cement ratio(W/C) were employed in order to improve the early strength of blast-furnace slag blended cement at low temperature. A grinding aid was used to grind the blast-furnace slag into the fineness of 6,280$\textrm{cm}^2$/g (Blaine), and this fine slag was then homogeneously mixed with the ordinary Portland cement to produce the blast-furnace slag blended cement containing 40% slag by weight composition. On the other hand, the batch water could be reduced from W/C=0.50 (KS L 5105) to W/C=0.33 through a commercial, naphthalene type superplasticizer. Through the method mentioned above, the early strength of the blast-furnace slag blended cement at low temperature could be enhanced even somewhat higher than the Portland cement strength. And the microsturcture of the cement was studied by both the pore structure analysis and the A.C. impedance measurement.
고로슬래그 시멘트의 저온 조기 강도를 증진키 위하여 고로슬래그의 분말도를 높이고 낮은 물:시멘트 비(W/C)의 혼합수량을 사용하였다. 분쇄조제를 사용하여 6,280$\textrm{cm}^2$/g(Blaine)로 미분쇄한 고로슬래그를 일반 포틀랜드 시멘트와 혼합하여 고로슬래그 40%의 고로슬래그 시멘트를 만들었다. 그리고 시판의 naphthalene계 고성능감수제를 사용하여 혼합수량을 W/C=0.50(KS L 5105)에서 W/C=0.33으로 저하시킬 수 있었다. 상술한 방법을 통하여 고로슬래그 시멘트의 저온 조기 강도를 포트랜드 시멘트 강도보다 오히려 더 높게 향상시킬 수 있었으며, 기공구조 및 임피던스 분석의 방법으로 본 시멘트의 미세구조를 조사하였다.