• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.3
• /
• pp.33-41
• /
• 1991

Cermic has been widely used because of its excellent esthetics and strength. The recently introduced castable ceramic system is regarded as the more esthetic and biocompatible restorative material. The purpose of this study was to compare the shear bond strength of Dicer & G-Cera porcelain laminate veneer according to the type of cement and surface treatment and to observe the surface of bonding failure with SEM. Total forty disks(3.5mm $diam.\times2.0mm$ thickness) were prepared. Forty extracted human maxillary central incisor teeth were stored in saline solution. Ten teeth were bonded to Dicer specimen with Dicer ZPC cement and ten teeth were bonded with Dicer resin cement. Ten silicoated G-Cera specimen and ten non-silicoated G-Cera specimen were bonded to teeth with G-Cera resin cement. Bonded units were mounted in a plastic tube with hard stone and stored in a humidor at $37^{\circ}C$ for 24 hours. Shear bond strength was measured by Instron Universal Testing Machine (Model 1125) and all the specimen were observed with SEM(JEOL, JSM-T2000)and modes of failure were recorded. The obtained results were as follows: 1. The mean shear bond strength of Dicer bonded with Dicer resin cement was 11.62 MPa and that bonded with Dicor ZPC cement was 0.88 MPa : Shear bond strength of Dicer bonded with Dicer resin cement was significantly increased(P<0.05). 2. The mean shear bond strength of silicoated G-Cera was 13.10 MPa and that of non silicoated G-Cera was 10.93 MPa : Shear bond strength of silicoated G-Cera was not significantly increased (P>0.05). 3. Shear bond strength of Dicer and G-Cera porcelain laminate veneer was not significantly different (P>0.05). 4. In observation of bond failure with SEM, Dicer bonded with Dicer ZPC cement exhibited adhesive failure. Dicer bonded with Dicer resin cement and silicoated and non silicoated G-Cera exhibited cohesive failure.

• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.2
• /
• pp.79-100
• /
• 1989

The Purpose of this study was to investigate material differences in stress transmission among various artificial teeth and denture base materials. For this study, a two-dimensional finite element model and a two-dimensional photoelastic model of a mandible with complete denture were made. A resin tooth and a porcelain tooth were used as artificial teeth, and a resin base, a metal lined base, and a soft-liner lined base were used as denture bases. An occlusal load was applied and principal stresses generated in the supporting tissues were compared. To test the impact stress transmission, strain gauge attached to the denture base specimens made of the different materials were made in thick and thin groups. Voltage outputs from hitting the specimen with a steel ball were compared. The results were as follows : 1. In FEM, increasing the mucosal thickness reduced the maximum principal stresses in the supporting tissues, but altering the tooth materials and the base materials induced no difference in the stresses. 2. In photoelastic model study, no difference in fringe order among the specimens were observed, but the thick mucosa group and the soft-liner lined group revealed a more uniform distribution of the load. 3. In strain measuring, the impact force transmission was highest in the soft-liner lined group, and was the lowest in the metal lined group(p<0.01). 4. In the thin group using the resin base, the porcelain tooth showed higher impact stress transmission than the resin tooth(p<0.01), but no difference was observed between them in the thick group. In the soft-liner lined group, the porcelain tooth showed higher impact stress transmission than the resin tooth(p<0.01), but no difference was observed between them in the metal lined group. 5. The thick group showed lower impact stress transmission than the thin group(p<0.01).

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.2
• /
• pp.129-145
• /
• 1991

The purpose of this study was to analyze the stresses and displacements of various esthetic restorations and abutment teeth. The finite element models of central incisor were divided into four groups according to the types of restoration. Three load cases were applied; 1) 45 degrees on the incisal edge, 2) horizontal force on the labial surface, and 3) 26 degrees diagonally on the lingual surface. Material property, geometry, and load conditions of each model were inputed to the two dimensional finite element program and stresses and displacements were analyzed. Results were as follows; 1. In the cases of porcelain fused gold ann and porcelain laminate venner, stresses were equally distributed in supporting abutment tooth. 2. The metal coping of porcelain fused gold u and collarless porcelain fused gold crown functioned as a good stress distributor. 3. When the horizontal load applied, the highest tensile and compressive stresses were seen in the cervical margin of restoration and the dentin of the abutment tooth. 4. The highest displacement of restoration was seen when load was applied at an mee of 26 degrees diagonally in lingual surface of tooth in centric occlusion. 5. The influence of loading direction on the stresses and displacements in the restoration was greater than that of various design. 6. The possibility of fracture was highest in porcelain jacket crown.

• The Journal of Korean Academy of Prosthodontics
• /
• v.25 no.1
• /
• pp.161-179
• /
• 1987

To study the mechanical behaviors of the margins of porcelain-fused-to-metal crown on the posterior teeth, 5 types of margins on the lower first molar were chosen, and then the finite element models were constructed. 50kg forces were applied to the porcelain on the axial wall supported by the metal vertically. The displacements and stresses of the porcelain-fused-to-metal crown were analyzed to investigate the influence of the type of margins. The results were as follows; 1. High tensile stresses were exhibited on the porcelain of the portion of the coronal line angle insufficient metallic support. 2. In case metal coping had a good supporting form to vertical force, uniform compressive stresses were exhibited on their supporting form. 3. Tensile stresses in the inframetallic margin on the series of the shoulder with a bevel margins were decreased in the bevel portion. 4. Principal stresses on the metal of the chamfer marginal portion were decreased comparing with the series of the shoulder margins. 5. The noticeable compressive stress gradients were exhibited between axial cement layer and metal on the series of the shoulder margins. 6. The principal stresses on the marginal cement layer were higher than that of the occlusal surface and axial wall.

• The Journal of Advanced Prosthodontics
• /
• v.3 no.4
• /
• pp.186-189
• /
• 2011

PURPOSE. Porcelain fused to metal (PFM) crowns provide the best treatment option for teeth that have a large or defective restoration. More than 20% of teeth with PFM crowns or bridges require non-surgical root canal treatment (NSRCT). This may be due to the effect of restorative procedures and the possible leakage of bacteria and or their by-products, which leads to the demise of the tooth pulp. Thus, this study was planned to compare the ability of the restorative materials to seal perforated PFM specimens. MATERIALS AND METHODS. The study evaluates the ability of amalgam, composite or compomer restorative materials to close perforated PFM specimen's in-vitro. Ninety PFM specimens were constructed using Ni-Cr alloys and feldspathic porcelain, and then they were divided into 3 groups: amalgam (A), composite + Exite adhesive bond (B) and compomer + Syntac adhesive bond (C). All the PFM samples were embedded in an acrylic block to provide complete sealing of the hole from the bottom side. After the aging period, each group was further divided into 3 equal subgroups according to the thermocycling period (one week for 70 cycles, one month for 300 cycles and three months for 900 cycles). Each subgroup was put into containers containing dye (Pelikan INK), one maintained at $5^{\circ}C$ and the other at $55^{\circ}C$, each cycle for 30 sec time. The data obtained was analyzed by SPSS, 2006 using one way ANOVA test and student t-test and significant difference level at (P<.01). RESULTS. The depth of dye penetration was measured at the interfaces of PFM and filling materials using Co-ordinate Vernier Microscope. The lowest levels of the dye penetration for the three groups, as well as subgroups were during the first week. The values of dye leakage had significantly increased by time intervals in subgroups A and C. CONCLUSION. It was seen that amalgam showed higher leakage than composite while compomer showed the lowest level of leakage.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.28 no.2
• /
• pp.191-200
• /
• 2012

The patients' demand for treatment of unesthetic anterior teeth is steadily growing. Accordingly, several treatment options such as porcelain laminate veneers(PLV) have been proposed to restore the esthetic appearance of the dentition. Porcelain laminate veneers are considered minimally invasive, but they also require removal of sound enamel. One critical step in the porcelain laminate veneer technique is the achievement of sufficient ceramic thickness, and several different strategies for tooth preparation can be found in the literature. This clinical report describes a step-by-step protocols for preparation of these restorations used with the silicone index from diagnostic wax-up and the acrylic resin mock-up. Conservative use of porcelain laminate veneers provided satisfactory esthetic outcomes and preserved sound tooth structure.

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.23 no.2
• /
• pp.70-76
• /
• 2014

After extraction of tooth, alveolar ridge resorption is inevitable in most cases. Clinicians confront with horizontal and vertical resorption of alveolar bone. Without massive amount of bone and soft tissue graft, dental implant will be placed apically to gain stability. In those cases, not only white esthetic part, but also pink esthetic part should be restored with pink porcelain. The margin of prosthesis should be located apically to reproduce natural look with adjacent teeth. However, when the margin is located apically, it is always hard to remove remaining cement, thus complications may arise. In this report, a novel design of implant prosthesis is introduced to solve those issues. The novel design is consisted of zirconia framework with pink porcelain and separate crowns on top of the framework. It eliminates the possibility of cement remnants by bringing the crown margin coronally. Pink esthetic part is incorporated in abutment part instead of crown part and the screw hole is covered with separate crowns.

• Journal of Technologic Dentistry
• /
• v.2 no.1
• /
• pp.35-38
• /
• 1980

이 기술은 레진(acrylic resin) 또는 의과용 도재(dental porcelain)에 의한 치아 색깔의 전장부위를 갖고 있는 금속구치 block(metal posterior tooth block)의 개조에 대한 기술의 일면이다. 이 기술은 모든 가철식 보철물(removable dental restoration)에 적용할 수 있으며 특히 자연치열(natural dentition) 대합치에 가철식 국부의치(removable partial denture)를 갖고 있는 만성 이갈음 환자(chronic bruxing patient)에 적용할 수 있다.

• Journal of Technologic Dentistry
• /
• v.26 no.1
• /
• pp.115-128
• /
• 2004

In this study, optical and mechanical properties were investigated with 4 kinds of commercial dental enamels. As a result of EDS analysis $SiO_2,\;Na_{2}O,\;Al_{2}O_3\;and\;K_{2}O$ were the main components of commercial dental enamels. In case of H specimen, content of $SiO_2\;and\;K_2O$ were more than that of another specimens. Starting powder and fired specimens were glass ceramics which were consist of amorphous phase and leucite (crystalline) phase. Crystallization did not occurred during firing process, since the XRD peak intensity was similar between starting powder and fired specimens. As a result of differential thermal analysis, $T_g$ and crystalline temperature was varied with composition in the range of $548\sim576^{\circ}C$ and $735\sim780^{\circ}C$ respectively. 0.5mm thickness dental enamel specimens showed sufficient translucent properties. However, transmittance and reflectance were lower than 5% result from scattering due to the refractive index difference between glass and crystalline phase. 3 point bending strength was in the range of 73.9$\sim$101.8MPa which was similar or slightly higher than enamel of natural teeth and Vickers hardness was higher than enamel of natural teeth more than 100.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.5
• /
• pp.587-598
• /
• 2005

Statement of problem: Ceramic restorations should be made of porcelain layers of different opacity, shade, and thickness in order to provide a natural appearance. Lithium disilicate glass-ceramic system has superior color reproducibility, because it uses the ceramic ingot which is similar to teeth shade and uses the staining technique and layering technique. However, staining technique has a fault of discoloration. Also, porcelain is divided core and dentin layer, it is not enough to study about the influence of porcelain layer thickness and shade on the shade of ceramic restorations. Purpose: The purpose of this study was to evaluate the influence of porcelain layer thickness and color on the final shade of ceramic restorations. Materials and method: The CIE $L^*a^*b^*$(CIELAB) values of 72 assembled specimens, each consisting of 3 discs (enamel porcelain 0.2 mm/dentin porcelain -1.2, 0.9, 0.7, 0.5 or 0.3 mm/ceramic core -0.3, 0.5, 0.7, 0.9 or 1.2 mm, diameter is 1.0 mm) were evaluated with a spectrophotometer (Model Chromaview 300, Spectron Tech Co, Korea) for the shade A1, A2, A3 and A4. Distilled water (refractive index: 1.7) was used to attain optical contact between the layers. White, white gray, and white brown backgrounds were used to assess the influence of the background on the final shade. And the mean color difference value$({\Delta}E)$ was calculated. Results and conclusion: The results obtained from this study were as follows. 1. There was a significant correlation between the thickness ratio of the ceramic core/dentin porcelain system and $L^*,\;a^*\;and\;b^*$ values when the total thickness of specimen combination was smaller than 1.4 mm(P<0.05). 2. The specimen which the ceramic core thickness was more than 0.7 mm had the best masking effect against background colors. 3. The mean color difference value$({\Delta}E)$ is smaller than 2 $({\Delta}E<2)$ when the ceramic core thickness was larger than 0.7 mm and the total thickness of specimen was more than 1.4 mm.