• Elastomers and Composites
• /
• v.34 no.2
• /
• pp.128-134
• /
• 1999

Steel tire cords were coated via RF plasma polymerization of acetylene and butadiene gas in order to enhance adhesion to rubber compounds. Adhesion of tire cords was measured by TCAT and T-test as a function of type of gas, plasma powder, treatment time, gas pressure and Ar gas etching. Some samples were subjected to aging study in distilled water at $80^{\circ}C$ for a period of 7 days. After testing, tire cords were analysed by SEM to elucidate the adhesion mechanism. The highest adhesion values were obtained at 20W, 2min and 25mtorr for acetylene plasma polymerization, and l0W, 4min, 25mtorr for butadiene plasma polymerization. However, Ar plasma etching did not affect adhesion, while the adhesion of tire cords increased rather than decreased, contrary to expectations. It was not possible to elucidate failure mode by SEM, owing to the rough surface of the tire and the thin plasma polymer coating layer.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.3.1-3.1
• /
• 2009

Normal sintering process of producing porous ceramics is not to sinter perfectly, i.e., stop sintering in middle-process. Our porous ceramic materials are a product of complete sintering. For example if one want to make a porous carborundum, raw carborundum powder is sintered at either lower temperatures than normal sintering temperature or shorter sintering periods than normal sintering time to obtain incompletely sintered materials, i.e., porous carborundum. This implies normally sintered porous ceramic materials can mot be used in high vacuum conditions due to dust coming out from uncompleted sintering. We could produce completely sintered porous ceramic materials. For example, we can produce porous carborundum material by using carborundum particles bonded by glassy material. The properties of this material are similar to carborundum. We could make quasi-zero thermal expansion porous material by using carborundum and particles of negative thermal expansion materials bonded by the glassy material. We apply to sinter them also by microwave to sinter quickly. We also use HIP process to introduce closed pores. We could sinter them in large size to produce $2.5m{\times}2.5m$ ceramic plate to use as a precision plate for flat display industries. This flat ceramic plate is the world largest artificial ceramic plate. Precision plates are basic importance to any advanced electronic industries. The produced precision plate has lower density, lower thermal expansivity, higher or similar damping properties added extra properties such as vacuum vise, air sliding capacity. These plates are highly recommended to use in flat display industries. We could produce also cylindrical porous ceramics materials, which can applied to precision roller for polymer film precision motion for also electronic industries.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.275-275
• /
• 2007

Two sorts of electrode composed of Sulpur/CNT/PVDF and Silver/CNT/PVDF were prepared by in situ chemical method and their electrochemical performance were evaluated by using cyclic voltammetry, impedance measurement and constant-current charge/discharge cycling technique. Also, composite electrodes were characterized by FE-SEM and BET. Raw materials such as CNT/Silver and CNT/Sulfur were mixed in ethanol, dried. These mixed materials were heated at 900 and $320^{\circ}C$ for 2hr, respectively in order to enhance contact among CNT electrodes. Electric double layer capacitor cells were fabricated using these mixed powder with polymer of PVDF. For the charging and discharging characteristics measured at scan rate of 1 mA/s, Supercapacitor of Sulphur-CNT-PVDF electrode showed a better performance than that of Ag-CNT-PVDF, which seems to be related with lower contact resistance of Sulphur-CNT-PVDF electrode.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.324-327
• /
• 2005

An electrophoretic display using $TiO_2$ particles is the most promising candidate because it offers various advantages such as ink-on-paper appearance, good contrast ratio, wide viewing angle, image stability in the off-state and extremely low power consumption. The core technology of electrophoretic display is the dispersion controlling of $TiO_2$ nano particles in nonaqueous solution. To prepare an ink for electronic paper using electrophoretic properties of $TiO_2$ nano particles, cyclohexane with low dielectric constant and transparency, polyethylene for producing polymer coating layer which reduces apparent gravity of $TiO_2$, and $TiO_2$ powders were mixed together by planetary-mill. The zeta-potential value of $TiO_2$ particles in cyclohexane was measured about -40mV, but was measured over -110mV by dispersant attached to polyethylene-coated $TiO_2$ surface. Prepared electronic ink was filled in cross patterned micro-wall with $200{\mu}m$ in width and $40{\mu}m$ in height on ITO glass designed by photolithography. The response time of electronic paper evaluated by mobility of $TiO_2$ particle between micro-walls was measured 0.067sec, but the drift velocity from reflectance wave form during reverse from of electronic ink was measured 0.07cm/sec.

• Korean Journal of Materials Research
• /
• v.11 no.2
• /
• pp.137-145
• /
• 2001

A new process, gelcasting in aqueous medium, to fabricate complex-shaped ceramic core has investigated. The ceramic slurry, mixture of fused silica powder and additives such as zircon and cordierite, was electrosterically stabilizes. The slip was prepared by ball milling of polydispered ceramic suspension with monomer, dimer and dispersant. The rheological behavior of slip was evaluated by viscosity measurement. It was found that the high solid loading of polydispersed ceramic slip, which has low viscosity of 50vol%, is possible to obtained. The viscosity of the slip was significantly dependent upon the amount of polymer dispersant and the formulation of monomer and dimer. The green bodies were fabricated through casting and gelation at room temperature followed by drying at $25^{\circ}C$ for 48hrs under relative humidity of 80~85%. Crack-free green body was successfully fabricated through the above process.

• Journal of the Korean Society of Radiology
• /
• v.12 no.1
• /
• pp.9-16
• /
• 2018

Hangover after drinking is different from person to person symptoms and degree, but usually thirst, fatigue, headache, general boredom, gastrointestinal disorder, vomiting, diarrhea, deficiency of vitamin appears. This hanging phenomenon is caused by the action of precursors such as ethyl acetate and acetaldehyde, which are the by products of fermentation contained in alcohol and alcohol accumulated in hepatocytes and body. In order to solve the hangover phenomenon, the same Origin as polysaccharide Polydeoxyribonucleotide, which is a nucleic acid-sugar-phosphate complex, which is a semen or testicular extract in salmon extract, and a water soluble salmon extract powder having the same structure and lower price than Polydeoxyribonucleotide And D-Glucuronic acid and N-Acetyl glucosamine. It has excellent biocompatibility, viscoelasticity and moisturizing power. It has effect on reduction of body water loss and skin moisture content in hangover phenomenon. It is antioxidant and skin moisturizing effect Hyaluronic acid was irradiated with gamma rays, and the composition was prepared by using the salmon extract powder and the main raw material. The ethanol degradation, the acetaldehyde reduction amount, the blood acetaldehyde concentration and the acetic acid concentration were measured to evaluate the alcoholysis effect, Skin moisture evaporation rate To examine the evaluation unit water content of the skin was improved determine whether the antioxidant and provide skin moisturizing effect. The addition of ethanol extracts of salmon extracts showed a decrease of 5 to 7 times compared with no addition, and a decrease of 3 to 5 times of acetaldehyde. In addition, the change of acetaldehyde concentration and acetic acid concentration in blood showed a rapid decrease compared to the no - added control group. In addition, when the raw material of hyaluronic acid was used, skin moisture content was high and skin moisture evaporation amount was decreased. Therefore, hyaluronic acid, which is a polysaccharide polymer, has excellent viscoelasticity and moisturizing ability, It is considered to provide antioxidant and skin moisturizing effect. Therefore, it can be said that the composition containing salmon extract powder and hyaluronic acid as a main ingredient is effective for the hangover phenomenon which occurs after drinking.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2005.09a
• /
• pp.201-212
• /
• 2005

[ $Epoxy/BaTiO_3$ ] composite embedded capacitor films (ECFs) were newly designed fur high dielectric constant and low tolerance (less than ${\pm}15\%$) embedded capacitor fabrication for organic substrates. In terms of material formulation, ECFs are composed of specially formulated epoxy resin and latent curing agent, and in terms of coating process, a comma roll coating method is used for uniform film thickness in large area. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ composite ECF is measured with MIM capacitor at 100 kHz using LCR meter. Dielectric constant of $BaTiO_3$ ECF is bigger than that of $SrTiO_3$ ECF, and it is due to difference of permittivity of $BaTiO_3\;and\;SrTiO_3$ particles. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ ECF in high frequency range $(0.5\~10GHz)$ is measured using cavity resonance method. In order to estimate dielectric constant, the reflection coefficient is measured with a network analyzer. Dielectric constant is calculated by observing the frequencies of the resonant cavity modes. About both powders, calculated dielectric constants in this frequency range are about 3/4 of the dielectric constants at 1 MHz. This difference is due to the decrease of the dielectric constant of epoxy matrix. For $BaTiO_3$ ECF, there is the dielectric relaxation at $5\~9GHz$. It is due to changing of polarization mode of $BaTiO_3$ powder. In the case of $SrTiO_3$ ECF, there is no relaxation up to 10GHz. Alternative material for embedded capacitor fabrication is $epoxy/BaTiO_3$ composite embedded capacitor paste (ECP). It uses similar materials formulation like ECF and a screen printing method for film coating. The screen printing method has the advantage of forming capacitor partially in desired part. But the screen printing makes surface irregularity during mask peel-off, Surface flatness is significantly improved by adding some additives and by applying pressure during curing. As a result, dielectric layer with improved thickness uniformity is successfully demonstrated. Using $epoxy/BaTiO_3$ composite ECP, dielectric constant of 63 and specific capacitance of 5.1nF/cm2 were achieved.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.1
• /
• pp.888-894
• /
• 2015

Inorganic composite particles have excellent physical and chemical characteristics and have been applied in various industries. Recently, many studies have examined the optical properties, such as light scattering, refraction, transmission characteristics, by coating organic-inorganic materials on a substrate, such as mica. Mica is widely applied as a pigment, plastics, painted products, and ceramics because of its high chemical stability, durability and non-toxicity. Magnesium oxide has a range of properties, such as high light transmittance, corrosion resistance and non-toxicity, and it is used as an optical material and polymer additives. To use the optical properties of mica and magnesium oxide, mica was coated with magnesium hydroxide by a dissolution and recrystallization process. In this study, the optimal conditions for the haze value of the particles were found by adjusting the amount of precursors and pH. Magnesium hydroxide layers were formed on the surfaces of mica and converted to MgO after calcination at $400^{\circ}C$ for 4 h. The results showed that the value of MgO-coated mica haze can be controlled easily by the amount of the magnesium hydroxide and pH. The optical properties of the inorganic composite powder were analyzed using a hazemeter and the highest haze value was 85.92 % at pH 9. The physicochemical properties of the synthesized composite was analyzed by SEM, XRD, EDS, and PSA.

• Journal of Pharmaceutical Investigation
• /
• v.32 no.3
• /
• pp.185-190
• /
• 2002

To improve the solubility of poorly water-soluble drug and to develop a sustained release tablets, the need for the technique, the formation of solid dispersion with polymeric materials that can potentially enhance the dissolution rate and extent of drug absorption was considered in this study. The 1:1, 1:4, and 1:5 solid dispersions were prepared by spray drying method using PVP K30, ethanol and methylene chloride. The dissolution test was carried out at in phosphate buffer solution at $37^{\circ}C$ in 100 rpm. Solid dispersed drugs were examined using differential scanning calorimetry and scanning electron microscopy, wherein it was found that felodipine is amorphous in the PVP K30 solid dispersion. Felodifine SR tablets were prepared by direct compressing the powder mixture composed of solid dispersed felodipine, lactose, Eudragit and magnesium stearate using a single punch press. In order to develop a sustained-release preparation containing solid dispersed felodipine, a comparative dissolution study was done using commercially existing product as control. The dissolution rate of intact felodipine, solid dispersed felodipine and its physical mixture, respectively, were compared by the dissolution rates for 30 minutes. The dissolution rates of felodipine for 30 minutes from 1:1, 1:4, 1:5 PVP K30 solid dispersion were 70%, 78% and 90%. However, dissolution rate offelodipine from the physical mixture was 5% of drug for 30 minutes. Our developed product Felodipine SR Tablet showed dissolution of 17%, 50% and 89% for 1, 4, and 7 hours. This designed oral delivery system is easy to manufacture, and drug releases behavior is highly reproducible and offers advantages over the existing commercial product. The dissolution rate of felodipine was significantly enhanced, following the formation of solid dispersion. The solid dispersion technique with water-soluble polymer could be used to develop a solid dispersed felodipine SR tablet.

• YAKHAK HOEJI
• /
• v.41 no.3
• /
• pp.305-311
• /
• 1997

Sustained release-microspheres and immediate release-pellets were prepared to develop a controlled release multiparticulate system containing both water soluble and insoluble dr ug. Pseudoephedrin.HCl (EPD) and terfenadine (TRF) were used as model drugs, respectively. Sustained release-EPD microspheres were prepared by solvent evaporation method using Eudragit RL or RS as a matrix combined with pH-insensitive film coating. Smaller EPD microspheres were obtained when smaller amount of Eudragit as a matrix material or larger amount of magnesium stearate as a dispersing agent was used. However the obtained microspheres did not show syfficient sustained release characteristics. About 97% of EPD was released after 1 hr irrespective of matrix material used. Subsequent coating of the microspheres with pH-insensitive polymer such as Eudragit RS or ethylcelulose (EC) resulted good sustained in 37.5, 73.3 and 92.0% release of encapsulated EPD in distilled water after 1, 3 abd 7 hr, respectively. It corresponds to mean dissolution time (MDT) of 2.3 hr, which is much larger than that of un-coated EPD microspheres (0.0048 hr). Immediate release TRF pellets were prepared by spherically agglomerated crystallization using Eudragit E as an inert matrix and methylene chloride as a liquid binder. Using Eudragit E alone as a matrix resulted in satisfactory physical properties of the pellets such as sphericity, surface texture and flowability, but led to slower release of TRF from pellets than un-modified TRF powder (MDT of 1.70 vs 1.43 hr in pH 1.2 dissolution medium). Introducing propylene glycol or sodium lauryl sulfate as an emulsifier brought about faster release of TRF from pellets (MDT of 1.14 and 0.95 hr, respectively). In conclusion, microencapsulation by solvent evaporation combined with film coating and spherically agglomerated crystallization were successfully utilized to prepare controlled release multiparticulate system composed of sustained release EPD-microspheres and immediate release TRF pellets.