• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.309-312
• /
• 2005

Admixture compounds for shortening setting time and accelerating early strength development of EVA polymer powder-modified mortars were made by mixing various quick setting agents. As a result, the quick setting agents contribute to strength development of the mortars in the early curing age of 168h or less. In the viewpoint of early strength development of EVA polymer powder-modified mortars, an quick setting agent content of 20$\%$ is recommended. Early strength of EVA polymer powder-modified mortars expresses the excellent strength with 5$\%$, 10$\%$ of rates of polymer mixing. The rate of polymer mixing was able to be adjusted and flexural strength which is a predeterminded initial strength was also able to satisfy 3MPa(s).

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1227-1228
• /
• 2006

The electrochemical properties of novel metal powders were investigated for the electrode materias of polymer electrolyte memebrane electrolysis. Two types of Pt black and $IrO_2$ powder electrodes were hot-pressed on the polymer electrolyte membrane to form membrane electrode assembly. The galvanodynamic polarization methode was used to characterize the electrochemical properties of both electrodes. From the experimental results, we concluded that the $IrO_2$ powder electrode exhibits better electrochemical performance than Pt black as cathode material for the electrolysis.

• 콘크리트학회논문집
• /
• 제14권5호
• /
• pp.660-667
• /
• 2002

본 연구에서는 에틸렌 초산 비닐 (EVA) 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 응결시간, 수밀성, 염화물이온 침투에 대한 저항성, 동결음해 저항성 및 내약품성에 미치는 분말소포제 첨가율 및 폴리머-시멘트비의 영향에 대하여 검토하였다. 그 결과, 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 공기량은 분말소포제 첨가율 및 폴리머-시멘트비의 증가에 따라 감소하는 경향을 보였다. 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 응결시간은 분말소포제 첨가율에 관계없이 폴리머-시멘트비의 증가에 따라 길게 되는 경향을 보였다. 또한 재유화형 분말수지를 혼입한 초속경폴리머 시멘트 모르타르의 수밀성 및 염화물이온 침투깊이는 분말소포제 첨가율에 관계없이 폴리머-시멘트비의 증가에 따라 감소하는 경향을 보였다. 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 동결융해 저항성 및 내약품성의 개선은 재유화형 분말수지의 혼입에 의해 시멘트 수화룰과 골재간의 접착성이 개선되기 때문이라 판단된다.

• 콘크리트학회논문집
• /
• 제17권5호
• /
• pp.703-708
• /
• 2005

본 연구에서는 에틸렌 초산 비닐 (EVA) 재유화형 분말수지를 혼입한 고유동 폴리머 시멘트 모르타르의 응결 시간 수밀성, 염화물이온 침투에 대한 저항성, 동결융해 저항성 및 중성화 깊이에 미치는 분말소포제 첨가율 및 폴리머-시멘트비의 영향에 대하여 검토하였다. 그 결과, 재유화형 분말수지를 혼입한 고유동 폴리머 시멘트 모르타르의 응결 시간은 분말소포제 첨가율에 관계없이 폴리머-시멘트비의 증가에 따라 지연되는 경향을 보였다. 또한 재유화형 분말수지를 혼입한 고유동 폴리머 시멘트 모르타르의 수밀성, 염화물 이온 침투 깊이 및 중성화 깊이는 분말소포제 첨가율에 관계없이 폴리머-시멘트비의 증가에 따라 감소하는 경향을 보였다. 재유화형 분말수지를 혼입한 고유동 폴리머 시멘트 모르타르의 동결융해 저항성의 개선은 재유화형 분말수지의 혼입에 의해 시멘트 수화물과 골재간의 접착성이 개선되기 때문이라 판단된다.

• 콘크리트학회논문집
• /
• 제16권5호
• /
• pp.651-657
• /
• 2004

본 연구에서는 재유화형 분말수지 혼입 고유동 폴리머 시멘트 모르타르의 공기량, 응결시간, 건조수축 및 강도특성에 미치는 분말소포제 첨가율 및 수축저감제 첨가량의 영향에 대하여 검토하였다. 그 결과, 재유화형 분말수지 혼입 고유동 폴리머시멘트 모르타르의 공기량은 분말소포제 첨가율 및 폴리머-시멘트비의 증가에 따라 감소하는 경향을 보였다. 재유화형 분말수지 혼입 고유동 폴리머 시멘트 모르타르의 응결시간은 분말소포제 첨가율에 관계없이 폴리머-시멘트비의 증가에 따라 늦어지는 경향을 보였다. 재유화형 분말수지 혼입 고유동 폴리머 시멘트 모르타르의 건조수축은 분말소포제 첨가율에 관계없이 폴리머-시멘트비 및 분말 수축저감제 첨가율의 증가에 따라 감소하는 경향을 보였다. 또한 분말소포제 첨가율 및 수축저감제 첨가율에 관계없이 재유화형 분말수지 혼입 고유동 폴리머 시멘트 모르타르의 휭 및 인장강도는 폴리머-시멘트비의 증가에 따라 증가하는 경향을 보였으나, 압축강도는 감소하는 경향을 보였다.

• 공업화학
• /
• 제16권3호
• /
• pp.317-322
• /
• 2005

오늘날 대규모 건설사업에 따른 골재의 고갈과 환경보호 측면에서 폐콘크리트 골재의 재활용이 절실히 요구되고 있다. 본 연구에서는 페콘크리트의 분쇄공정에서 발생되는 페콘크리트 미분말을 폴리머 모르타르의 충전재 대용으로 재활용하고자 하였다. 폴리머 모르타르의 공시체는 폴리머 결합재의 첨가율을 9~15 wt%, 실리카 미분말 충전재 대용의 폐콘크리트 미분말 치환율을 0~20 wt%, 0.1~0.3 mm 잔골재(21~24 wt%)와 0.7~1.2 mm 잔골재(44~47 wt%)의 첨가율을 65~71 wt% 범위로 다양하게 변화시켜 제조하였다. 폴리머 모르타르의 물성을 평가하기 위하여 압축 및 휨강도, 흡수율, 내열수성, 내산성, 세공분포특성, 전자현미경에 의한 미세조직 관찰시험을 행하였다. 시험결과, 폴리머 모르타르의 물성은 폴리머 결합재의 첨가율 증가에 따라 현저히 증가되었으나 페콘크리트 미분말의 치환율 증가에 따라서는 크게 저하되었다.

• 한국도로학회논문집
• /
• 제20권2호
• /
• pp.19-25
• /
• 2018

PURPOSES : This purpose of this study is to analyze the effect to autogenous shrinkage of the top-layer material of a two-lift concrete pavement mixing both silica fume and polymer powder. METHODS : The bottom-layer of a two-lift concrete pavement was paved with original portland cement (OPC) with a 20~23 cm thickness. Additionally, the top-layer which is directly exposed to the environment and vehicles was paved with a high-performance concrete (HPC) with a 7~10 cm thickness. These types of pavements can achieve a long service life by reducing joint damage and increasing the abrasion and scaling resistance. In order to integrate the different bottom and top layer materials, autogenous shrinkage tests were performed in this study according to the mixing ratio of silica fume and polymer powder, which are the admixture of the top-layer material. RESULTS : Autogenous shrinkage decreased when polymer powder was used in the mix. Contrary to this, autogenous shrinkage tended to rise with increasing silica fume content. However, the effects were not significant when small amounts of polymer powder were used (3% and 11%). CONCLUSIONS : The durability and compressive strength increase when silica fume is used in the mix. The flexural strength considerably increases and autogenous shrinkage of concrete decreases when polymer powder is used in the mix. As seen from above, the proper use of these materials improves not only durability, but also autogenous shrinkage, leading to better shrinkage crack control in the concrete.

• 한국분말재료학회지
• /
• 제12권4호
• /
• pp.249-254
• /
• 2005

Titanium dioxide was prepared by Polymer Complex Solution Method(PCSM) according to the mole ratio of Titanium (IV) isopropoxide(TTIP)/solvent and polymer(Poly Ethylene Glycol). Polymer electrolytes were usually made by dispersing preproduced ceramic nanoparticles in a polymer matrix. Using this method, pure and nano-sized $TiO_2$ powder was synthesized through a simple procedure and polymer entrapment route. At the optimum amount of the polymer, the titanium ions are dispersed in solution and a homogeneous polymeric network is formed. The maximum intensity of anatase phase of $TiO_2$ was achieved by calcining at $500^{\circ}C$ for 2h. The synthesized $TiO_2$ powders were nano-sized and the average size was about 50nm. Anatase/Rutile ratio of the synthesized $TiO_2$ was 70%/30%.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.300-303
• /
• 2004

In this study, the mixing contents of ceramic powder and of shrinkage-reducing agent (SRA) influencing on the strength properties of MMA-modified polymer paste were examined. Regardless of SRA content, the flexural. the compressive and the adhesive strengths of the MMA-modified polymer paste tended to increase as the mixing content of ceramic powder increased. On the other hand, those strengths of the polymer paste tended to decrease as the mixing content of SRA increased without regard to the paste content. Furthermore. the adhesive strength of MMA-modified polymer paste in a wet condition decreased about $30-40\%$ of that in an air-dry condition without regard to the mixing content of ceramic powder and SRA.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.533-536
• /
• 2005

Drying shrinkage and strength of the redispersible SBR and PAE powder-modified mortars were experimentally investigated. Results of the study that the drying shrinkage rapidly increased until 7 days of age and it was then saturated to the value of about $1\~2\times10^{4}$ after 14 days. It turned out that the polymer-cement ratio exerted more influence on the drying shrinkage than the content of powder shrinkage-reducing agent did. Flexural (compressive) strength of the mortar increased (decreased) as the polymer-cement ratio increased and it was 7$\~$11 (23$\~$39) MPa at 7 days of age. The average (maximum) increasing (decreasing) rate turned out to be about 10 (30) $\%$. As in the drying shrinkage case, the polymer-cement ratio exerted more influence on both flexural and compressive strengths than the content of powder shrinkage agent did.