• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.296-299
• /
• 2004

The effects of polymer-cement ratio, antifoamer content and shrinkage-reducing agent content on the setting time and drying shrinkage of high-fluidity polymer-modified mortars using redispersible polymer powder are examined. As a result, the setting time of the high-fluidity polymer-modified mortars using redispersible polymer powder tend to delayed with increasing polymer-cement ratio, regardless of the antifoamer conten,. Irrespective of the antifoamer content, the drying shrinkage of the high-fluidity polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and shrinkage-reducing agent content.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.328-331
• /
• 2004

Recently, the study for practical construction application of recycled aggregate concrete is actively being proceeded, on the purpose of technical development for recycling on the construction waste concrete occurred at the time of destruction of building construction by the rapid increase of building wastes and exhaustion of natural aggregates. This study is performed to develop the permeable polymer concrete using recycled coarse aggregate and blast furnace slag for application of structures needed permeability. At 7 days of curing, compressive strength, flexural strength, water permeability and flexural load are in the ragge of $18\~20MPa,\;6\~7MPa,\;4.6\times10^{-2}\~6.9\times10^{-2}cm/s$ and $20\~25kN$, respectively. It is concluded that the recycled aggregate can be used in the permeable polymer concretes.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2002.10a
• /
• pp.149-152
• /
• 2002

This study is performed to evaluate the properties of ECO-permeable polymer concrete with blast furnace slag powder and stone dust. The unit weight is in the range of $1,821kg/m^3{\sim}1,955kg/m^3$, the unit weights of those concrete are decreased $15%{\sim}20.8%$ than that of the normal cement concrete. The highest strength is achieved by ECO-permeable polymer concrete filled blast furnace slag powder 50% and stone dust 50%, it is increased 36% by compressive strength, 119% by tensile strength and 217% by bending strength than that of the normal cement concrete, respectively. The coefficient of permeability is in the range of $5.6{\times}10^{-2}cm/s{\sim}8.1{\times}10^{-2}cm/s$, and it is largely dependent upon the mix design.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.125-128
• /
• 2005

Recently new materials, such as fiber reinforced polymer(FRP) and other composite materials are being applied in reinforcing plate or plate or prestressing cables of concrete structures. Although these new materials themselves show the excellent durability and high strength, the bond behaviour between concrete surface and FRP is not well recognized. Therefore, this paper propose a evaluation method for effective bond length between fiber reinforced polymer(FRP) and concrete. To develop the evaluation method, this paper presents a review of current evaluation methods for effective bond length. These methods are compared by single face test, expose merits and demerits. And based on them, new evaluation method was developed. Finally, the new method was compared with existing methods to verify a adequateness for evaluation of effective bond length.

• Advances in concrete construction
• /
• v.8 no.4
• /
• pp.247-255
• /
• 2019

Several reinforced concrete structures that get deteriorated by rebar corrosion are retrofitted using Carbon Fiber Reinforced Polymer (CFRP). When rebar comes in direct contact with CFRP, rebar may corrode, as iron is more active than carbon. Progression of corrosion of rebar in strengthened RC structures has been carried out when rebar comes in direct contact with CFRP. The experimentation is carried out in two phases. In phase I, corrosion of bare steel bar is monitored by making its contact with CFRP. In phase II, concrete specimens with surface bonded CFRP were casted and subjected to the realistic exposure conditions keeping direct contact between rebar and CFRP. Progression of corrosion has been monitored by various parameters: Half-cell potential, Tafel extrapolation and Linear Polarisation Resistance. On termination of exposure, to find residual bond stress between rebar and concrete, pull-out test was performed. Rebar in contact with CFRP has shown substantially higher corrosion. The level of corrosion will be more with more area of contact.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10b
• /
• pp.1139-1144
• /
• 2000

Recent advance in material technology has accelerated the development of high strength concrete using lightweight artificial aggregates. The lightweight concrete has many advantages that the reduction of dead lads and the increase in load capacity can ofter. In this study, lightweight polymer concrete using unsaturated polyester resin and lightweight aggregate were prepared and tested for testing the physical and the mechanical properties. The compressive strengths of lightweight polymer concretes with specific gravities from 1.32 to 1.78 were compressive strength of 250 to 470 $kgf/cm^2$ and flexural strengths were measured to be in the range of a third to a quarter of compressive strength

• Computers and Concrete
• /
• v.19 no.2
• /
• pp.127-131
• /
• 2017

This paper presents a generalized formulation for optimizing the design of concrete beam reinforced with glass fiber reinforced polymer bar. The optimization method is formulated to find the design variables leading to the minimum weight of concrete beam with constraints imposed based on ACI code provisions. A simple genetic algorithm is utilized to solve the optimization task. The weights of concrete and glass fiber reinforced polymer bar are included in the formulation of the objective function. The ultimate limit states and the serviceability limit states are included in formulation of constraints. The results of illustrated example demonstrate the efficiency of the proposed method to reduce the weight of beam as well as to satisfy the above requirement. The application of the optimization based on the most economical design concept have led to significant savings in the amount of the component materials to be used in comparison to classical design solutions.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1991.10a
• /
• pp.93-98
• /
• 1991

Polymer-Impregnated Concrete(PIC) can be considered composite material of concrete and polymer and has superior properties compared to conventional cement concrete, such as strength, stiffness, toughness, durability, water-proofing, chemical resistance. However, so far, the usage of PIC has been limited to repairing materials and non-structural applications, due to the lack of the design criteria and the analytical model to determine structural behavior. The objective of this study is to define the stress-strain response and strength characteristics of PIC in uniaxial and various biaxial compressive loading. On the bases of experimental results, general stress-strain relation, biaxial failure envelope and strength evaluation formular of PIC made with normal aggregate and methylmethacrylate(MMA) are proposed.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.45 no.7
• /
• pp.11-19
• /
• 2003

In this study, unsaturated polyester resin, artificial lightweight coarse aggregate, artificial lightweight fine aggregate, heavy calcium carbonate and steel fiber were used to produce a steel fiber-reinforced lightweight polymer concrete with which mechanical properties were examined. Results of this experimental study showed that the flexural strength of unnotched steel fiber-reinforced lightweight polymer concrete increased from 8.61 to 13.96 MPa when mixing ratio of fiber content increased from 0 to 1.5%. Stress intensity factors($K_{IC}$) increased with increasing fiber content ratio while it did not increase with increasing notch ratio. Energy release rate ($G_{IC}$) turned out to depend upon the notch size, and it increased with increasing steel fiber content.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2002.10a
• /
• pp.157-160
• /
• 2002

This study was developed high-quality a large size precast channel structure using polymer concrete to improve quality of the product as well as to enhance construction quality. Practical precast channel structure design and manufacture procedure for the high polymer concrete were described in this paper. Precast PC represent the fastest growing segment of the polymer concrete industry. The fast curing, high strength, and low impermeability permit thin section and rapid reuse of moulds. Precast channel structure will carry out structural experiment and analysis.