• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.22-29
• /
• 2001

Plasma-sprayed coatings were prepared using by spray-dried Cr$_2$O$_3$ powder with and without MoO$_3$ addition. A reciprocal type tribe-tester was employed to examine friction and wear behavior of the specimens at room temperature. The worn surfaces of plasma spray coated specimens were observed by SEM. The results showed that friction coefficient of the MoO$_3$-added coatings were lower than those without MoO3 addition. However pure Cr$_2$O$_3$ coating showed the lowest wear loss at the self-mated test. The larger protecting layers were observed at the worn surface of plasma spray coated specimens with MoO$_3$ addition.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.11a
• /
• pp.96-102
• /
• 2001

plasma-sprayed Cr$_2$O$_3$-based coatings containing MoO$_3$ were studied to gain a better understanding of the influence of MoO$_3$ composition in the coatings on their tribological behaviour. A reciprocal type tribo-tester was employed to examine friction and wear behavior of the specimens at high temperature(450。C). The physical characteristics of worn surfaces were investigated by scanning electron microscopy and chemical composition of the coating surfaces was analyzed using a X-ray photoelectron spectrometer. The results showed that friction coefficient of the MoO$_3$-added coatings were lower than those without MoO$_3$ addition. The larger protecting layers were observed at the worn surface of plasma spray coated specimens with MoO$_3$ addition. XPS analysis of the protecting layer indicated that MoO$_3$ composition was dominantly formed at the surface. MoO$_3$ composition in the protecting layer appears to be more favorable in reducing the friction.

• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.160-167
• /
• 2011

Plasma sprayed ceramic coatings inherently contain pores and usually also cracks. Post-treatment of the plasma sprayed coatings is a way to close the connected pores and cracks. In this study, post-sealing treatment in plasma sprayed $Al_2O_3$ coatings was employed to overcome the reduction of coating properties. $Al_2O_3$ plasma thermal spray coating was made on aluminum alloys plate, $CrO_3$ post coating and heat treatment at $550^{\circ}C$ was carried out in order for final $Cr_2O_3$ to be saturated through phase transformation. Chromia sealing began at the fine defect in coated microstructure, while larger pores were permeated later. The increase in concentration and treatment frequency of sealing solution resulted in the decrease of porosity of coating layer, while cracks occurred partially after the third treatment. After twice treatment of 10M $CrO_3$ solution, microhardness and breakdown voltage of $Al_2O_3$ coatings were found to increase by ${\fallingdotseq}$ 50% and ${\fallingdotseq}$ 390% respectively than without post-treatment.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.17-24
• /
• 1998

Plasma-sprayed coatings were obtained by spray-dried $Cr_2O_3$ powder with and without Mo addition. A reciprocal type tribo-tester was employed to examine friction and wear behavior of the specimens at room temperature. The composition and the worn surface of coated specimens were observed by XRD and SEM. The results showed that friction Coefficient of the Mo added specimens were lower than one of $Cr_2O_3$ specimen. But $Cr_2O_3$ specimen had a lower wear loss. Protecting layer were observed at the worn surface of coated specimens with Mo addition.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.2
• /
• pp.91-98
• /
• 1994

For the plasma sprayed as well as the EB-PVD thermal barrier coatings, the fracture paths within the oxidation products developed at the interface between the partially stabilized zirconia ceramic coating and NiCoCrAlY bond coat during cyclic thermal oxidation has been investigated. It was observed that the fracture in the oxidation products primarily took place within the oxide such as $Ni_{1-x}Co_3(Al_,Cr)_2O_4$ or at the interface between the oxide and $Al_2O_3$. It was found that Al2O3 developed first, followed by the Ni/Co/Cr rich oxides such as ,,$Ni_{1-x}Co_x(Al_,Cr)_2O_4$ $Cr_2O_3$and NiO at the interface between the ceramic coating and the bond coat in a cyclic high temperature environment. It was therfore concluded that the formation of the oxide containing Ni, Cr and Co was a life-limiting event for thermal barrier coatings during cyclic thermal oxidation.

• Journal of the Korean Ceramic Society
• /
• v.39 no.1
• /
• pp.79-85
• /
• 2002

Plasma-sprayed Cr$_2$O$_3$-based coatings containing MoO$_3$were studied to gain a better understanding of the influence of MoO$_3$composition in the coatings on their tribological behaviour. A reciprocal type tribo-tester was employed to examine friction and wear behavior of the specimens at room temperature. The physical characteristics of worn surfaces were investigated by scanning electron microscopy and chemical composition of the coating surfaces was analyzed using a X-ray photoelectron spectrometer. The results showed that friction coefficient of the MoO$_3$-added coatings were lower than those without MoO$_3$addition. However pure Cr$_2$O$_3$coating showed the lowest wear loss at the self-mated test. The larger protecting layers were observed at the worn surface of plasma spray coated specimens with MoO$_3$addition. XPS analysis of the protecting layer indicated that MoO$_3$composition was dominantly formed at the surface. MoO$_3$composition in the protecting layer appears to be more favorable in reducing the friction.

• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.184-192
• /
• 1999

Various compositions of$ Cr_2$$O_3$/Mo composite powders were fabricated using spray-drying method and plasma-spray coatings of these powders were prepared to understand their tribological properties. Experiments were conducted using a reciprocal type tribo-tester at room temperature under dry sliding condition. The worn surface of coated specimens were observed using SEM (Scanning Electron Microscopy) and chemical compositions were analyzed using XRD (X-ray Diffractometry) and XPS (X-ray Photoelectron Spectroscopy). The results showed that friction coefficient of the Mo added specimens were lower than that of $Cr_2$$O_3$specimen. However $Cr_2$$O_3$specimen showed the lowest wear loss. Wear protecting layer were observed at the worn surface of coated specimens with Mo addition. From the XPS analysis, the mixed phases of $Cr_2$$O_3$ $CrO_3$and $MoO_3$were founded in the wear protecting layer.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.73-80
• /
• 1999

The effect of alloy compositions of the bond coating on the plasma sprayed-thermal barrier coatings was investigated. The performance of the coating composed of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ and Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$was evaluated by isothermal and thermal cyclic test in an ambient atmosphere at 115$0^{\circ}C$. The failure of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coatings was occurred at the bond coating/ceramic coating interface while Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coating was failed at the substrate/bond coating interface after thermal cyclic test. The lifetime of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coatings was longer than Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coating. The oxidation rate of the NiCrAl bond coating examined by TGA was lower than CoNiCrAlY bond coatings. In summary, these results suggest that Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$system as thermal barrier coating be not suitable considering the durability of the coating layer for high temperature oxidation and thermal stress.

• Journal of Powder Materials
• /
• v.6 no.3
• /
• pp.224-230
• /
• 1999

Oxide powders of $Cr_2O_3 \;and\;Cr_2O_3+3{\%}TiO_2$ were prepared by spray drying, plasma densification and fused+crushed processes. The oxide coating layers were made by plasma spray and characterized by microstructure, hardness, adhesion strength and relative density. The optimum spray distance for the high quality coatings by spraying dried powders was found to be 9cm. A small amount addition of $TiO_2\;in\;Cr_2O_3$ powder significantly improved coating characteristics by lowering the melting point of powders. The hardness and relative density of coating layers of the plasma densified powders were comparable to fused and crushed powders, however, the adhesion strength was much higher in the former case.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.32-32
• /
• 1999