• Proceedings of the Korean Fiber Society Conference
• /
• 1996.10a
• /
• pp.117-123
• /
• 1996

Cabon fiber of general purpose was prepared from coal tar pitch modified with 10% benzoquinine(BQ) at 380C for 3 hours. Such a modified pitch raised the softening of the pitch from 85C to 271C at the yield of 40%. The modified pitch was spun smoothly at a rate of 480m/min into a fiber of 20um diameter. The fiber was stabilized stepwise at 236C (5C/min) and 312C (1C/min) for 3 hours each. Both carbonized and graphitized fibers exhibited tensile strength of 570MPa which appears large enough as a precursor for active carbon fiber. The activated carbon fiber prepared exhibited relatively high surface area of 2062m2/g at 76% burn-off and rather narrow distribution pore size of 20A.

• Journal of the Korean Ceramic Society
• /
• v.43 no.7 s.290
• /
• pp.439-444
• /
• 2006

Artificial graphite generally manufactured by carbonization sintering of shape-body of kneaded mixture using granular cokes as filler and pitch as binder, going through pitch impregnation process if necessary and finally applying graphitization heat treatment. Graphite materials are used for core internal structural components of the High-Temperature Gas-cooled Reactors (HTGR) because of their excellent heat resistibility and resistance of crack progress. The HTGR has a core consisting of an array of stacked graphite fuel blocks are machined from IG-110, a high-strength, fine-grained isotropic graphite. In this study, crack stabilization and micro-structures were measured by bend strength and fracture toughness of isotropic graphite grade IG-110. It is important to the reactor designer as they may govern the life of the graphite components and hence the life of the reactor. It was resulted crack propagation, bend strength, compressive strength and micro-structures of IG-110 graphite by scanning electron microscope and universal test machine.

• Carbon letters
• /
• v.3 no.2
• /
• pp.80-84
• /
• 2002

The surface treatment of C-type isotropic pitch-based carbon fiber was carried out by anodic oxidation in 5 wt% $NH_4NO_3$ electrolyte. The changes of fiber surface and carbon fiber/ABS resin composites were characterized by SEM, XPS and mechanical properties test. The oxygen functional groups on the surface, such as hydroxyl (-C-OH), carboxyl (-COOH) groups etc., increased after oxidation. Tensile strength, flexural strength and modulus of carbon fiber/ABS composites were also enhanced. However, the impact strength decreased with the improvement of the surface adhesion between CF and matrix.

• Journal of Power System Engineering
• /
• v.21 no.1
• /
• pp.5-10
• /
• 2017

Pitch drive system in wind turbine is composed by the planetary gear system to satisfied its required performance such as long life and light weight for gear train. When the planetary gear system can reduce its volume and weight, the power consumption of the wind turbine can be reduced. In this study, the planetary gear system of the pitch drive system in medium-sized wind turbine is obtained for weight reduction by shape optimization method. And the planetary gear system is verified for their strength by the structural analysis.

• Textile Coloration and Finishing
• /
• v.30 no.4
• /
• pp.313-320
• /
• 2018

As carbon fiber reinforced composites(CFRP) are widely used in aerospace, automobile, marine, and sports goods applications, they have been studied extensively by various researchers. However, CFRP have been pointed out because of machining problems such as delamination and burr phenomenons. Especially, hole machining process, drilling, has non-smooth features on inlet and outlet surfaces of drilled hole. This kind of machining problem can be controlled to some extent by using high modulus pitch-CF, which has considerable effects on fracture behavior of composite compared with only PAN CF composite. Therefore, PAN and pitch hybridized CF composites were prepared having high strength and modulus. The results demonstrate that the hybrid CFRP specimens with pitch CF offer the good potential to enhance modulus as well as strength properties. Dynamic mechanical, flexural, and impact properties were measured and analyzed. Morphological surface of the composites were also observed by IFS-28, canon after hole machining.

• Proceedings of the KOSOMBE Conference
• /
• v.1995 no.05
• /
• pp.23-26
• /
• 1995

The objectives of the present study are 1)to find the effect of the diameter of transpedicular screws on their fixational strength in pedicles under static pull-out loading, 2)to determine the biomechanical correlation between the pedicle diameter and the screw diameter, and 3)to find the effects of other factors in the screw design, such as materials, screw pitch, thread height and shape on their fixational strength. Biomechanical tests (Test I) were performed to evaluate the effect of the screw diameter on pull-out strength by using 60 porcine pedicls and six groups of custom-made pedicle screws with different diameters (the major and the minor diameter of the screws used in the testing varied from 4mm upto 9mm and from 3mm upto 8mm, respectively) while all other factors (materials, screw pitch, thread height and shape etc.) were fixed. In Test II, by using 61 porcine pedicles, the relationship between the ratio of the pedicle diameter and the screw diameter(=aspect ratio) of the custum-made screw and the pull-out strength of the screw was investigated. Test III was performed with 94 porcine pedicles and 8 different types of the commercial screws from 6 major productors in order to determine the effect of the screw diameter, pitch and the thread shape on the pull-out strength of the screw, respectively. The results of Test I showed that the axial pull-out resistance of the screw could be increased prportionaly to the screw diameter(P<0.05). But this increase in the pull-out resistance did not found when the screws of 4mm or 9mm in the diameter were employed. It was found from the results of Test II that the screws had its maximum pull-out resistant force when the aspect ratio ranging 40 - 69% (P<0.05). based on the results for the major diameter against the minor diameter of screw, the maximal pull-out resistance was found at 60-65% (P<0.05). According to these biomechanical testing results, it seems that the screw with a moderately large pitch is more desirable and the buttress-shaped screw can provide stronger fixation than the V-shape one can, if other designal factor and conditions were fixed.

• Korean Chemical Engineering Research
• /
• v.54 no.6
• /
• pp.830-837
• /
• 2016

In order to improve the compressive strength of graphite foams (GFms), mesophase pitch (MP) was stabilized in air atmosphere and then fluorinated at different conditions. The Fluorine/Carbon (F/C) in surface-chemical contents of fluorinated MP has range of 23.75%~61.48% according to the different fluorine partial pressure. The compressive strengths of GFms prepared from fluorinated MP were increased in proportion to the apparent densities. The compressive strength of the GFm produced from MP with 35.93% of F/C (%) showed maximum value in $2.93{\pm}0.06MPa$, which was increased up to 27.95% than that of the GFm prepared from un-fluorinated MP. This result was attributed that the interface bonding between of MPs due to fluorine functional groups with high surface energy helped to improve compressive strength of the GFm.

• Korean Chemical Engineering Research
• /
• v.54 no.2
• /
• pp.268-273
• /
• 2016

To improve mechanical strength of carbon foams, the carbon black (CB) added carbon foams were fabricated by impregnating different contents of carbon black (CB) and mesophase pitch using polyvinyl alcohol (PVA) solution into polyurethane foam and being followed by heat treatment. The cell wall-thicknesses of carbon foams were controlled by adding amounts of CB, and it was confirmed that the compressive strength of carbon foams was increased as increasing cell wall-thickness. The compressive strength had the highest value of $0.22{\pm}0.05MPa$ with the highest bulk density of $0.44g/cm^3$ when adding 5 wt% CB in carbon foam. However, the thermal conductivity was decreased by adding CB in carbon foam. The results indicated that the thermal conductivities of carbon foams were reduced by increased interlayer spacing ($d_{002}$) with the addition of CB in carbon foams.

• Journal of Biomedical Engineering Research
• /
• v.39 no.3
• /
• pp.134-139
• /
• 2018

One of the most common problems with pedicle screw system is pullout of the screw. This study was performed to evaluate the pullout strength and driving torque of newly designed pedicle screws. The design of three type screws were standard pedicle screw, which had single lead threaded and single pitched design (Type A), single pitched and dual lead threaded pedicle screw (Type B), dual pitched and dual lead threaded pedicle screw (Type C), respectively. The tests were performed in accordance with the ASTM standards using polyurethane (PU) foam blocks. There was no significant difference in pullout strength among three types of screw. Type B and Type C exhibited higher insertion torque and removal torque than Type A, respectively (p<0.05). Pedicle screws newly developed with dual pitched and dual lead threaded design showed higher driving torque without decrease in pullout strength compared to the standard pedicle screw and could be inserted more rapidly with the same number of revolutions.

• Nuclear Engineering and Technology
• /
• v.56 no.6
• /
• pp.2367-2374
• /
• 2024

In this paper, based on the need for high-strength connections between all-tungsten-oriented plasma materials and thermal sinking materials of copper and its alloys in nuclear fusion devices, a study on the effect of tungsten surface laser micro structuring on the interfacial bonding properties of W/Cu joints was carried out. In the experiment, the connectors were prepared by vacuum fusion infiltration technology, and the effects of microgroove structure on the mechanical and thermal conductivity of W/Cu connectors were investigated under different parameters (including microgroove pitch, microgroove depth, and microgroove taper). The maximum shear strength is 126.0 MPa when the pitch is 0.15 mm and the depth is 34 ㎛. In addition, the negative taper structure, i.e., the width of the entrance of the microstructure is smaller than the width of the interior of the microstructure, is also investigated. The shear tests show that there is an approximately linear relationship between the shear strength of W/Cu and taper. Compared with the positive taper, the shear strength of the samples with the same morphological density and depth of the tungsten surface is significantly higher.