• Smart Structures and Systems
• /
• v.17 no.4
• /
• pp.593-610
• /
• 2016

In this study, an innovative and smart glass fiber-reinforced polymer (GFRP) hybrid bar was developed for stronger durability of concrete structures. As comparing with the conventional GFRP bar, the smart GFRP Hybrid bar can promise to enhance the modulus of elasticity so that it makes the cracking reduced than the case when the conventional GFRP bar is used. Besides, the GFRP Hybrid bar can effectively resist the corrosion of conventional steel bar by the GFRP outer surface on the steel bar. In order to verify the bond performance of the GFRP hybrid bar for structural reinforcement, uniaxial pull-out test was conducted. The variables were the bar diameter and the number of strands and pitch of the fiber ribs. Tensile tests showed a excellent increase in the modulus of elasticity, 152.1 GPa, as compared to that of the pure GFRP bar (50 GPa). The stress-strain curve was bi-linear, so that the ductile performance could be obtained. For the bond test, the entire GFRP hybrid bar test specimens failed in concrete splitting due to higher shear strength resulting in concrete crushing as a function of bar deformation. Investigation revealed that an increase in the number of strands of fiber ribs enhanced the bond strength, and the pitch guaranteed the bond strength of 19.1 mm diameter hybrid bar with 15.9 mm diameter of core section of deformed steel the ACI 440 1R-15 equation is regarded as more suitable for predicting the bond strength of GFRP hybrid bars, whereas the CSA S806-12 prediction is considered too conservative and is largely influenced by the bar diameter. For further study, various geometrical and material properties such as concrete cover, cross-sectional ratio, and surface treatment should be considered.

• Carbon letters
• /
• v.1 no.3_4
• /
• pp.158-164
• /
• 2001

It is well known that the fabrication process of carbon/carbon composites is very complex. Above all, the carbonization process have major effect on the morphology development of carbon matrix. Carbon/carbon composites of 4-directional fiber preform were fabricated using the coal tar based pitch as a matrix precursor in this study. According to carbonization pressure of 1 bar, 100 bar, 600 bar, and 900 bar, morphological changes of cokes and matrix of composites were discussed. As the carbonization pressure increased to 600 bar, the flow pattern morphology of bulk mesophse was well developed. On the contrary, mosaic pattern morphology was found in case of 900 bar of carbonization pressure. It is confirmed that the carbonization pressure have profound effect on the degree of graphitization and crystal size of carbon matrix. Even in the highly densified carbon/carbon composites, large voids were still found in the matrix pocket region.

• Carbon letters
• /
• v.6 no.1
• /
• pp.6-14
• /
• 2005

The study of mechanical properties and fracture behaviour of carbon/carbon composites is significant to its application and development. These are dependent on microstructure and properties of reinforcing fibers and matrix, fiber/matrix interface and porosity/cracks present in the composites. In the present studies high-density carbon/carbon composites have been prepared using PAN and various pitch based carbon fibers as reinforcements and pitch as matrix with repeated densification cycles using high-pressure impregnation and carbonization technique. Scanning electron microscopy has been used to study the fracture behaviour of the highly dense composites and correlated with structure of the composites. The geometry of reinforcement and presence of unfilled voids/cracks was found to influence the path of crack propagation and thereby the strength of composites. The type of stresses (tensile or compressive) accumulated also plays an important role in fracture of composites.

• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.6_3
• /
• pp.1333-1339
• /
• 2023

To produce activated carbon fibers, the process is carried out through either physical activation method or chemical activation method. In this study, we present the results regarding the characteristics of activated carbon fibers manufactured under various conditions through the quantitative control of steam. The yield after activation indicates a decreasing trend with the increase in steam quantity and activation time. Additionally, specific surface area characteristics exhibit variations based on activation time and steam flow rate. The SEM analysis results reveal that higher steam flow rates lead to the presence of both mesopores and macropores on the surface of activated carbon fibers (ACF).

• Magazine of the Korea Concrete Institute
• /
• v.5 no.4
• /
• pp.145-155
• /
• 1993

The results of an experimental study on the manufacture and the mechanical properties of fiber reinforced fly ash$\cdot$lime$\cdot$gypsum composites are presented in this paper. 'The composites using fly ash, lime, and gypsum were prepared with various fibers (PAN-derived and Pitch-derived carbon fiber, alkali-resistance glass fiber) and a small amount of polymer emulsion-styrene butadiene rubber latex (SBR). As the test results show, the manufacturing process technology of fly ash$\cdot$lime$\cdot$gypsum composites was developed and its optimum mix proportions were successfully proposed. And the flexural strength and toughness of fiber reinforced fly ash$\cdot$lime $\cdot$gypsum composites were increased remarkably by fiber contents, but the compressive strength of the composites were influenced by the kinds fiber more than by the fiber contents. Also, the addition of a polymer emulsion to the composites decreased the bulk specific gravity, but the compressive and flexural strength, and the toughness of the composites were not influenced by it, but were considerably improved by increasing fiber contents.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.4
• /
• pp.165-171
• /
• 2002

The study on the adsorption, the surface properties and the antibacterial effects of the metal-treated pitch based activated carbon fibers was carried out. From the adsorption studies on the series of metal-treated activated carbon fiber, the specific surface areas of the metal treated activated carbon fiber obtained from BET equation were in the range of 113.2~1574 $m^2$/g for the Ag-ACFs. And that of Cu treated ACF are distributed to 688.2-887.8 $\m^2$/g. And, the specific surface areas of the Ni-treated pitch based ACFs were in the range of 692.6~895.2 $\m^2$/g. From the ${\alpha}_s$- method, 0.06~1.1 cm^3/g of the micropore volumes were obtained from Ag-ACFs. And, 0.1~0.2 cm^3/ and 0.2~0.6 cm^3/g of the micropore volumes were obtained from Cu and Ni-ACFs, respectively. And, from the SEM morphology results, it was observed that the surface of activated carbon fiber are partially blocked and coated by metal after the treatment. Finally, from the antibacterial effects of metal-treated activated carbon fiber against E. coli, the areas of antibacterial effect become larger with the increase in mole ratio of metal treated. And, from the antibacterial effects using Shake flask method against E. coli, the percentage of the effects was 92.5~100 % and the antibacterial effect was increased with the increase in mole concentration of metal treated.

• Korean Journal of Materials Research
• /
• v.4 no.7
• /
• pp.733-740
• /
• 1994

Oxidized-PAN fiber reinforced composite(OFRP), carbon fiber reinforced composite(CFRP), aramid fiber reinforced composite(AFRP), and glass fiber reinforced composite(GFRP) were fabricated with phenolic resin matrix by hot press molding. We tested the friction coefficient and wear rate varying with fiber weight fraction and observed the effect of fibers according to characteristics of individual reinforcement. When the amount of aramid fiber was 45wt%, average friction coefficient was maximum value of 0.353~0.383, where as, when the amount of pitch based carbon fiber was 45wt%, average friction coefficient was the lowest value of 0.164~0.190. The wear rate of AFRP and CFRP was low, but that of GFRP and OFRP increases drastically in the case of increasing of fiber weight fraction. Wear diagram of OFRP was unstable, but that of CFRP and AFRP was a bit stable. Through very unstable diagram of GFRP, we found that friction stability of GFRP was the lowest.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.2
• /
• pp.154-165
• /
• 2020

To assign the functionality of the regenerated fiber from waste MDF(wMDF) made of pitch pine, we examined the dyeing characteristics of natural dyes, sappan wood as a polychromatic natural red series, monochromatic gardenia as a yellow series, and indigo blue series. For nonemordanting dye, the colors of regenerated fiber dyed by sappan wood and gardenia were reddish yellow (YR) and yellow (Y) series, respectively, and dyeing conditions were appropriate a 30 ~ 50 g/L of dyeing materials at 60 ℃ for 60minutes of dyeing time. We obtained regenerated woody dyed fibers (Re-WDF), YR to the red (R) series by premordanting with Al and Cu mordant for sappan wood and the purplish red (RP) series by Fe premordanting. In the case of gardenia, only Y series colors were developed in nonemordanting dye or all three mordants. Indigo dye produced Re-WDF with greenish yellow (GY) tone at 1%, green (G) tone at 3%, and blue (B) tone at 5% concentration or more. Re-WDF with indigo showed the best light fastness followed by sappan wood and gardenia. In particular, the light fastness of Re-WDF with gardenia was very poor. The light fastness was somewhat improved by premordanting(Fe>Cu>Al) both sappan wood and gardenia dyes.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.1
• /
• pp.46-53
• /
• 2008

Ultrasonic C-scan technique is one of very popular techniques being used for detection of flaws in polymer matrix composite(PMC). However, the application of this technique is very limited for evaluation of defects in PMC fabricated by the automated fiber placement process. The purpose of this study is to develop a novel ultrasonic hybrid system based on nondestructive and non-contact ultrasonic techniques for evaluation of delamination in carbon/epoxy and carbon/PPS composite laminates. It was shown that the newly developed ultrasonic hybrid system based on dual air-coupled pitch-catch technique with ultrasonic scattering reflection concept could provide excellent image with higher resolution of delamination in PMC compared with the conventional pitch-catch method. It is expected that this ultrasonic hybrid technique can be applied for on-line inspection of flaws in PMC during the fabrication process.

• Applied Chemistry for Engineering
• /
• v.26 no.5
• /
• pp.598-603
• /
• 2015

In this study, electrochemical properties of pitch-based activated carbon fibers (ACFs) were investigated by different heat-treatment temperature of the pitch-based ACFs in order to improve the specific capacitance of electric double-layer capacitor (EDLC). The ACFs were prepared by different heat-treatment temperatures of 1050 and $1450^{\circ}C$, after activation with 4 M KOH at $800^{\circ}C$ using stabilized pitch fiber. The specific surface area of prepared ACFs increased from $828m^2/g$ to $987m^2/g$, also the micropore and mesopore volumes of prepared ACFs were increased. These results because pore was produced by desorbing oxygen and hydrogen elements within the ACFs, and pore size was increased by contraction ACFs by heat-treatment process. Because of the porous properties, the specific capacitance was increased from 73 F/g to 119 F/g using cyclic voltammetry with 1 M $H_2SO_4$ at scan rates of 5 mV/s.