• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.51-55
• /
• 2011

In this paper, the optimized doping condition of crystalline silicon solar cells with 156 ${\times}$ 156 mm2 area was studied. To optimize the drive-in condition in the doping process, the other conditions except drive-in temperature and time were fixed. After etching 7 ${\mu}m$ of the surface to form the pyramidal structure, the silicon nitride deposited by the PECVD had 75~80 nm thickness and 2 to 2.1 for a refractive index. The silver and aluminium electrodes for front and back sheet, respectively, were formed by screen-printing method, followed by firing in $400-425-450-550-850^{\circ}C$ five-zone temperature conditions to make the ohmic contact. Drive-in temperature was changed in range of $828^{\circ}C$ to $860^{\circ}C$ and time was from 3 min to 40 min. The sheet resistance of wafer was fixed to avoid its effect on solar cell. The solar cell fabricated with various conditions showed the similar conversion efficiency of 17.4%. This experimental result showed the drive-in temperatures and times little influence on solar cell characteristics.

• Korean Journal of Materials Research
• /
• v.28 no.11
• /
• pp.680-684
• /
• 2018

We investigate the effect of light intensity and wavelength of a solar cell device using photoconductive atomic force microscopy(PC-AFM). A $POCl_3$ diffusion doping process is used to produce a p-n junction solar cell device based on a polySi wafer, and the electrical properties of prepared solar cells are measured using a solar cell simulator system. The measured open circuit voltage($V_{oc}$) is 0.59 V and the short circuit current($I_{sc}$) is 48.5 mA. Moreover, the values of the fill factors and efficiencies of the devices are 0.7 and approximately 13.6 %, respectively. In addition, PC-AFM, a recent notable method for nano-scale characterization of photovoltaic elements, is used for direct measurements of photoelectric characteristics in limited areas instead of large areas. The effects of changes in the intensity and wavelength of light shining on the element on the photoelectric characteristics are observed. Results obtained through PC-AFM are compared with the electric/optical characteristics data obtained through a solar simulator. The voltage($V_{PC-AFM}$) at which the current is 0 A in the I-V characteristic curves increases sharply up to $18W/m^2$, peaking and slowly falling as light intensity increases. Here, $V_{PC-AFM}$ at $18W/m^2$ is 0.29 V, which corresponds to 59 % of the average $V_{oc}$ value, as measured with the solar simulator. Furthermore, while the light wavelength increases from 300 nm to 1,100 nm, the external quantum efficiency(EQE) and results from PC-AFM show similar trends at the macro scale but reveal different results in several sections, indicating the need for detailed analysis and improvement in the future.

• Korean Journal of Materials Research
• /
• v.25 no.9
• /
• pp.487-491
• /
• 2015

In photovoltaic power generation where minority carrier generation via light absorption is competing against minority carrier recombination, the substrate thickness and material quality are interdependent, and appropriate combination of the two variables is important in obtaining the maximum output power generation. Medici, a two-dimensional semiconductor device simulation tool, is used to investigate the interdependency in relation to the maximum power output in front-lit Si solar cells. Qualitatively, the results indicate that a high quality substrate must be thick and that a low quality substrate must be thin in order to achieve the maximum power generation in the respective materials. The dividing point is $70{\mu}m/5{\times}10^{-6}sec$. That is, for materials with a minority carrier recombination lifetime longer than $5{\times}10^{-6}sec$, the substrate must be thicker than $70{\mu}m$, while for materials with a lifetime shorter than $5{\times}10^{-6}sec$, the substrate must be thinner than $70{\mu}m$. In substrate fabrication, the thinner the wafer, the lower the cost of material, but the higher the cost of wafer fabrication. Thus, the optimum thickness/lifetime combinations are defined in this study along with the substrate cost considerations as part of the factors to be considered in material selection.

• 한국태양에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.383-387
• /
• 2009

Multi-crystalline silicon surface etching without grain-boundary delineation is a challenging task for the fabrication of high efficiency solar cell. The use of sodium hydroxide - sodium hypochlorite (NaOH40% + NaOCl 12%) solution for texturing multi-crystalline silicon wafer surface in solar cell fabrication line is reported in this article. in light current-voltage results, the cells etched in NaOH 40% + NaOCl 12% = 1:2 exhibited higher short circuit current and open circuit voltage than those of the cells etched in NaOH 40% + NaOCl 12% = 1:1 solution. we have obtained 15.19% conversion efficiency in large area(156cm2) multi-Si solar cells etched in NaOH 40% + NaOCl 12% = 1:1 solution.

• Journal of Advanced Navigation Technology
• /
• v.14 no.3
• /
• pp.426-431
• /
• 2010

68% of the manufacturing costs of solar cell wafer can be attributed to the slurry. The recycling of slurries is mandatory for reducing the costs of manufacturing wafering production, and the disposal of industrial waste, as well as for cutting down pollution levels. Slurries are currently being recycled using the centrifuge(decanter) method. However, this method is less than optimal as it does not completely remove the fine particles, leading to low quality. Also, be cause of the incomplete separation from the oil, it causes the impurities in the dried slurries. This study aims to develope a new recycling technology that overcomes the flaws of the centrifuge by utilizing chemicals. It will provide a total solution to the crucial process of recycling slurries in the making of solar cell wafer, by increasing the efficiency and renewable rate.

• Ceramist
• /
• v.21 no.2
• /
• pp.75-82
• /
• 2018

In the photovoltaics (PV) industry, there were many efforts to reduce the cost of production with high efficiency. The single most important cost factor in silicon technology is the wafer, accounting presently for ~35% of the module cost. it was already shown that the solar cell efficiency can be maintained up to the thickness range of $40-60{\mu}m$. The direct production of ultra-thin silicon wafer is very attractive and numerous different techniques, such as electrochemical process, ion implantation, and epitaxial growth, have been proposed and developed in many academic and industrial laboratories.

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.743-746
• /
• 2003

We have successfully used hydrophobic direct-wafer bonding, along with H-induced layer splitting of Ge, to transfer 700nm think, single-crystal Ge films to Si substrates. Optical and electrical properties have been also observed on these samples. Triple-junction solar cell structures gown on these Ge/Si heterostructure templates show comparable photoluminescence intensity and minority carrier lifetime to a control structure grown on bulk Ge. When heavily doped p$^{+}$Ge/p$^{+}$Si wafer bonded heterostructures were bonded, ohmic interfacial properties with less than 0.3Ω$\textrm{cm}^2$ specific resistance were observed indicating low loss thermal emission and tunneling processes over and through the potential barrier. Current-voltage (I-V) characteristics in p$^{+}$Ge/pSi structures show rectifying properties for room temperature bonded structures. After annealing at 40$0^{\circ}C$, the potential barrier was reduced and the barrier height no longer blocks current flow under bias. From these observations, interfacial atomic bonding structures of hydrophobically wafer bonded Ge/Si heterostructures are suggested.ested.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.39.1-39.1
• /
• 2010

이종접합태양전지는 단결정 실리콘 기판 표면에 고품질 비정질 실리콘층을 적층함으로써 전기의 근원인 전하의 재결합 손실을 줄여 높은 개방전압을 얻을 수 있다는 특징이 있다. 초박형 태양전지는 기존 태양전지보다 뛰어난 광전변환 특성(Photovoltaic characteristic)을 가지고 두께가 얇아 제품 형상 시 자유도가 높아진다. 본 논문에서는 n-type Bare wafer($160{\sim}180{\mu}m$)를 이용하여 $50{\mu}m$의 웨이퍼를 제작하였다. a-Si:H(p)_a-Si:H(i)_c-Si(n)의 광흡수층 구조를 성막하여 cell을 제작하였다. 그 결과 Voc(Open Circuit Voltage)가 0.666, Jsc(Short-Circuit Current)가 34.77, FF(Fill Factor) 69.413, Efficency 16.07%를 달성했다.

• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.649-653
• /
• 2010

In this paper, double texturization of multi crystalline silicon solar cells was studied with laser and reactive ion etching (RIE). In the case of multi crystalline silicon wafers, chemical etching has problems in producing a uniform surface texture. Thus various etching methods such as laser and dry texturization have been studied for multi crystalline silicon wafers. In this study, laser texturization with an Nd:$YVO_4$ green laser was performed first to get the proper hole spacing and $300{\mu}m$ was found to be the most proper value. Laser texturization on crystalline silicon wafers was followed by damage removal in acid solution and RIE to achieve double texturization. This study showed that double texturization on multi crystalline silicon wafers with laser firing and RIE resulted in lower reflectance, higher quantum yield and better efficiency than that process without RIE. However, RIE formed sharp structures on the silicon wafer surfaces, which resulted in 0.8% decrease of fill factor at solar cell characterization. While chemical etching makes it difficult to obtain a uniform surface texture for multi crystalline silicon solar cells, the process of double texturization with laser and RIE yields a uniform surface structure, diminished reflectance, and improved efficiency. This finding lays the foundation for the study of low-cost, high efficiency multi crystalline silicon solar cells.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.36 no.3
• /
• pp.233-240
• /
• 2023

p-type Tunnel Oxide Passivating Contacts (TOPCon) solar cell is fabricated with a poly-Si/SiO_x structure. It simultaneously achieves surface passivation and enhances the carriers' selective collection, which is a promising technology for conventional solar cells. The quality of passivation is depended on the quality of the tunnel oxide layer at the interface with the c-Si wafer, which is affected by the bond of SiO formed during the subsequent annealing process. The highest cell efficiency reported to date for the laboratory scale has increased to 26.1%, fabricated by the Institute for Solar Energy Research. The cells used a p-type float zone silicon with an interdigitated back contact (IBC) structure that fabricates poly-Si and SiO_x layer achieves the highest implied open-circuit voltage (iV_oc) is 750 mV, and the highest level of edge passivation is 40%. This review presents an overview of p-type TOPCon technologies, including the ultra-thin silicon oxide layer (SiO_x) and poly-silicon layer (poly-Si), as well as the advancement of the SiO_x and poly-Si layers. Subsequently, the limitations of improving efficiency are discussed in detail. Consequently, it is expected to provide a basis for the simplification of industrial mass production.