• Rapid Communication in Photoscience
• /
• v.2 no.1
• /
• pp.1-8
• /
• 2013

Transparent $TiO_2$ films in various thicknesses were prepared by sol-gel and MOCVD method, respectively, and their photocatalytic activities in decomposing gaseous 2-propanol were evaluated. The surfaces and grain structures of the prepared films were characterized by FESEM, XRD, and AFM. It was found that the photocatalytic activities of $TiO_2$ films were greatly dependent on the film thickness and surface roughness: The photocatalytic activity increases with the increase of film thickness, while it decreases with the increase of surface roughness. We have proposed that these phenomena originate from the transfer of photogenerated electron and hole pairs from the bulk to the surface of $TiO_2$ film. Several experimental evidences supporting this mechanism have also been provided.

• Journal of Korean Society for Atmospheric Environment
• /
• v.16 no.4
• /
• pp.389-398
• /
• 2000

Photocatalytic removal of benzene from air was examined using titanium dioxide photocatalyst films prepared on soda lime glass(50$\times$50$\times$2 mm) by spin coating and chemical vapor deposition. For the measurement of photocatalytic reactivity titanium dioxide coated glass was placed into a batch reactor and concentration of benzene in the reactor was set to abuot 100 ppm, and then illuminated with UV. It was found that catalytic reactivity of titanium dioxide films increased with the increase of titanium dioxide film thickness and then level off beyond a certain film thickness. UV absorption by the films showed the similar trend. The formation of stoichiometric amount of carbon dioxide was confirmed by measurement of carbon dioxide concentration in the reactor. In general spin coated films revealed better photocatalytic reactivity than chemically deposited one within the experimental ranges covered in this study. Morphology and crystal structure of prepared films were investigated by XRD and SEM and they showed significant difference between spin coated films and CVD films. Highest quantum efficiency of prepared titanium dioxide photocatalyst was close to 50%.

• Journal of Surface Science and Engineering
• /
• v.53 no.4
• /
• pp.153-159
• /
• 2020

Photocatalytic decomposition of polyethylene film with TiO₂ nanotube powders (NTs) was investigated under UV irradiation at ambient conditions. TiO₂ NTs composed of individual nanotubes are prepared by rapid breakdown anodization technique. A comparative study on the photocatalytic decomposition of polyethylene-TiO₂ composite films prepared using TiO₂ nanoparticles (NPs) or TiO₂ NTs (NTs), respectively, was conducted under UV irradiation. Polyethylene film incorporated with TiO₂ NTs showed 26 wt% weight loss after 200 h under UV irradiation about two times faster decomposition rate than TiO₂ NPs which is attributed to large surface area of TiO₂ NTs.

• Journal of Korean Vacuum Science & Technology
• /
• v.6 no.1
• /
• pp.40-42
• /
• 2002

TiO$_2$/Fe$_2$O$_3$composite thin films were prepared on common glass substrates by sol-gel processing and dip-drawing method. The effect of Fe$_2$O$_3$content on the photocatalytic and hydrophilic properties of composite films was studied. The results indicate that the photocatalytic activities of composite TiO$_2$films are superior to that of pure TiO$_2$film, and the film containing 0.5% Fe$_2$O$_3$has the best photocatalytic activity. The hydrophilicity is difference with variant Fe$_2$O$_3$content, the films containing 0.05% ~0.1% Fe$_2$O$_3$have the best hydrophilicity and their contact angles are 0。.

• Environmental Engineering Research
• /
• v.13 no.1
• /
• pp.28-32
• /
• 2008

The photocatalytic treatment of water contaminated with 2,4,6-trinitrotoluene (TNT) was explored in bench-scale experiments in batch mode using a Pyrex tube coated with a thin film of $TiO_2$ located inside a photoreactor. The reactor was aerated by purging it with compressed air before initiating the photocatalytic reaction. The rate of TNT degradation approximated first-order kinetics. The reaction rate constant decreased as the TNT concentration increased from 25 to 100 mg/L, while the first-order kinetics could be modeled using a Langmuir adsorption isotherm. The addition of the organic reductants methanol and EDTA significantly enhanced the rate of TNT degradation, with optimum results in the presence of 20% methanol by volume. EDTA increased the rate of TNT removal by enhancing the role of the reductants.

• Bulletin of the Korean Chemical Society
• /
• v.22 no.11
• /
• pp.1183-1191
• /
• 2001

The metallorganic chemical vapor deposition (MOCVD) method has been used to prepare TiO2 thin films for the degradation of hazardous organic compounds, such as 2-chlorophenol (2-CP). The effect of supporting materials and metal doping on the photocatalytic activity of TiO2 thin films also has been studied. TiO2 thin films were coated onto various supporting materials, including stainless steel cloth(SS), quartz glass tube (QGT), and silica gel (SG). Transition metals, such as Pd(II), Pt(IV), Nd(III) and Fe(III), were doped onto TiO2 thin film. The results indicate that Nd(Ⅲ) doping improves the photodegradation of 2-CP. Among all supporting materials studied, SS(37 ${\mu}m)$ appears to be the best support. An optimal amount of doping material at 1.0 percent (w/w) of TiO2-substrate thin film gives the best photodegration of 2-CP.

• Journal of the Korean GEO-environmental Society
• /
• v.11 no.1
• /
• pp.5-11
• /
• 2010

The objective of this study is to evaluate the effect of operational parameters such as rotation speed and vibrating milling time for the fabrication of photocatalytic $TiO_2$ thin film using aerosol deposition methods. $TiO_2$ powders produced in the range of 1,000-3,000 rpm of rotation speed of centrifugal separator are ineffective on the fabrication of $TiO_2$ thin film by aerosol deposition due to the problem of nozzle powder jam. $TiO_2$ powders controlled by vibrating milling had about 420 nm of average diameter after 2 hr of vibrating milling time. The result of XRD analysis indicated that $TiO_2$ powders had a anatase phase. Vibrating milling methods was considered to be an effective pre-treatment process for $TiO_2$ powder control. Consequently $TiO_2$ photocatalytic thin film with dispersion of anatase crystallites controled by vibrating milling was successfully fabricated by aerosol deposition. The permeation flux of $TiO_2$ photocatalytic thin film with the immobilized $TiO_2$ powder was higher than that of suspended $TiO_2$ powder. Therefore, $TiO_2$ photocatalytic thin film promises to be one of the effective methods for enhancing filtration performance for the treatment of organic pollutants.

• Korean Journal of Materials Research
• /
• v.31 no.1
• /
• pp.8-15
• /
• 2021

Transparent, photocatalytic, and self-cleaning TiO2 thin film is developed by TiO2 sol-gel coating on glass and polycarbonate (PC) substrates. Acetyl acetone (AcAc) suppresses the precipitation of TiO2 by forming a yellowish (complex) transparent sol-gel. XPS analysis confirms the presence of Ti2p and O1s in the thin films on glass and PC substrates. The TiO2-sol is prepared by stabilizing titanium (IV) isopropoxide (TTIP) with diethylamine and methyl alcohol. The addition of AcAcsilane coupling solution to the TiO2-sol instantaneously turns to yellowish color owing to the complexing of titanium with AcAc. The AcAc solution substantially improves the photocatalytic property of the TiO2 coating layer in MB solutions. The coated TiO2 film exhibits super hydrophilicity without and with light irradiation. The TiO2 thin film stabilized by adding 8.7 wt% AcAc shows the highest photo-degradation for methylene blue (MB) solution under UV light irradiation. Also, the optimum photocatalytic activity is obtained for the 8.7 wt% AcAc-stabilized TiO2 coating layer calcined at 450 ℃. The thin-films on glass exhibit fast self-cleaning from oleic acid contamination within 45 min of UV-light irradiation. The appropriate curing time at 140 ℃ improves the anti-fogging and thermal stability of the TiO2 film coated on PC substrate. The watermark-free PC substrate is particularly beneficial to combat fogging problems of transparent substrates.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.11
• /
• pp.3991-3995
• /
• 2011

$TiO_2-SiO_2-In_2O_3$ nanocomposite thin film was deposited on the glass substrates using a dip coating technique. The morphology, surface composition, surface hydroxyl groups, photocatalytic activity and hydrophilic properties of the thin film were investigated by AFM, XPS, methyl orange decoloring rate and water contact angle measurements. The hydroxyl content for $TiO_2$, $TiO_2-SiO_2$ and $TiO_2-SiO_2-In_2O_3$ nanocomposite films was calculated to be 11.6, 17.1 and 20.7%, respectively. $TiO_2-SiO_2-In_2O_3$ film turned superhydrophilic after 180-min irradiation with respect to pure $TiO_2$ and $TiO_2-SiO_2$ thin films. The photocatalytic decomposition of methyl orange for $TiO_2$, $TiO_2-SiO_2$ and $TiO_2-SiO_2-In_2O_3$ thin films was measured as 38.19, 58.71 and 68.02%, respectively. The results indicated that $SiO_2$ and $In_2O_3$ had a significant effect on the hydrophilic, photocatalytic and self-cleaning properties of $TiO_2$ thin film.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.461-468
• /
• 2005

Transparent TiO$_{2}$ sols were prepared by hydrothermal synthesis to heat Ti precursor solutions, from Ti hydroxides obtained with neutralizing aqueous TiOCl$_{2}$ solutions having various concentrations of NaCI by aqueous NaOH solution, in the autoclave at 120$^{\circ}C$ The photocatalytic abilities of glass beads coated with the sol for gaseous benzene were evaluated. As a result, it was found that due to the increase of brookite phase in TiO$_{2}$ by controlling the concentration of Na ion the optical absorption of TiO$_{2}$ increases toward long wavelength but that in the area of short wavelength becomes relatively low and consequently the photocatalytic performance of TiO$_{2}$ thin film for benzene gas rather decreases, compared to that of composite film of anatase and brookite phases. These results suggest that in order for coated TiO$_{2}$ thin film to have high dissociation performance for benzene gas it is effective to form anatase and brookite phases compositely in TiO$_{2}$.