• Journal of environmental and Sanitary engineering
• /
• v.20 no.4 s.58
• /
• pp.51-58
• /
• 2005

Photocatalytic degradation using $TiO_2$ Particles suspended in a reactor was experimentally performed to degrade the formaldehyde of indoor pollutants. Exponential increase of degradation appears to prove light availability due to the scattering of W light by particles themselves. Comparative removal studies of formaldehyde were done in both cases of dipping and spraying immobilized techniques of $TiO_2$ Particles suspended in solution. Experiments were performed under several different experimental conditions such as initial concentration of formaldehyde, UV intensity and concentration of photocatalysts. Optimal conditions to degrade formaldehyde were obtained under the conditions of $30\;mg/cm^2$ concentration of catalyst and UV intensity of 30 Watt at the distance of 30 cm using immobilized technique by dipping coating.

• Journal of Korean Society of Water and Wastewater
• /
• v.18 no.3
• /
• pp.307-311
• /
• 2004

The objective of this work is to evaluate the hypothesis that a good technique for supplying oxygen to the saturated zone in the presence of light nonaqueous phase liquid (LNAPL) pool contamination at the water table is to pass air through the unsaturated zone above the pool. This hypothesis was evaluated in experimental studies performed using a bench-scale, sand-tank reactor, Steady-state abiotic experiments in the sand-tank reactor with air flowing through the reactor headspace demonstrated that oxygen supply through the water table interface into the saturated zone was enhanced when an LNAPL (dodecane) pool was present at the water table. These experimental results confirmed the hypothesis that an LNAPL pool can serve as a high concentration oxygen source to the oxygen-limited area beneath the pool and, as a result, enhance the in situ biodegradation rate.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.5
• /
• pp.196-203
• /
• 2007

We have studied a method for the preparation of hybrid $carbon/TiO_2$ complexes involving pitch coating, pitch binding and the penetration of titanium n-butoxide(TNB) solution with porous carbon. The photocatalysts were investigated with surface textural properties and SEM morphology, structural crystallinity and elemental identification between porous carbon and $TiO_2$, and dye decomposition performance. For the all $carbon/TiO_2$ complexes prepared by some kinds of different methods, the excellent photocatalytic effect for dye degradation should be attributed to the both effects between photo-decomposition of the supported $TiO_2$ and adsorptivity of the porous carbons.

• Elastomers and Composites
• /
• v.51 no.1
• /
• pp.31-37
• /
• 2016

In this study, we studied the photocatalytic functionality such as deodorant, antibacterial, antistatic of polyester fabrics treated with visible-light responsive photocatalyst. According to UV/visible spectrometry result, the UV-visible peak of visible-light responsive photocatalyst was found to be red shift at 420 nm sensitive in the visible light region. Also, the deodorizing and antimicrobial performance were shown to be retained more than 99% both before washing and even after 25 times washing. According to washing durability of polyester fabrics treated with visible-light responsive photocatalyst, the reduction effects for gas such as ammonia, trimethylamine, formaldehyde and toluene after 25 times washing appeared to be retained as much as before washing. At both before washing and after 25 times washing, antistatic property showed frictional voltage of approximately 250V.

• Carbon letters
• /
• v.9 no.2
• /
• pp.131-136
• /
• 2008

In order to investigate the effect of doping C, N, B and F elements on $TiO_2$ for reducing the band gap, the heat treatment of $TiO_2$ was carried out with tetraethylammonium tetrafluoroborate. Through XRD and XPS analysis, the C, N, B and F doped anatase $TiO_2$ was confirmed. According to the increase of temperature during treatment, the particle size was increased due to aggregation of $TiO_2$ with elements (B, C, N and F). To investigate the capacity of photocatalyst for degradation of dye under solar light, the degradation of acridine orange and methylene blue was conducted. The degradation of dyes was carried out successfully under solar light indicating the effect of doping elements (B, C, N and F) on $TiO_2$ for reducing the band gap effectively.

• Korean Journal of Environmental Agriculture
• /
• v.23 no.2
• /
• pp.85-91
• /
• 2004

The objective of this study is to determine the optimum conditions of operational parameters using factorial design for phenol degradation in photocatalytic oxidation reactors. Factorial design is widely used to select the dominant factors and their ranges in experiments involving several factors where it is necessary to study the effect of factors on a response. The effects of initial concentration of phenol, intensity of UV light and surface area of catalyst on phenol degradation were investigated. Two levels were considered in this study so that the experiment was a $2^3$ factorial design with three replicates. The experimental results show that an increase in initial concentration of phenol from 5 to 50 mg/L intensity of UV light from 5,000 to $20,000\;{\mu}W/cm^2$, and surface area of catalyst from 740 to $2,105\;cm^2$ enhanced the phenol degradation rate by an average of 1.86, 1.79, and 2.10 mg/L hr, respectively. Interaction effects do not appear to be as large on the phenol degradation rate as the main effects of single factors. The optimum working condition for photocatalytic oxidation reactors, despite the higher three factors the better removal rate, is the highest surface area or catalyst.

• Membrane Journal
• /
• v.21 no.1
• /
• pp.46-54
• /
• 2011

In this study, combined effect of airflow rate, $TiO_2$ concentration, solution pH and $Ca^{+2}$ addition on HA (humic acid) fouling in submerged, photocatalytic hollow-fiber microfiltraiton was investigated systematically. Results showed that UV irradiation alone without $TiO_2$ nanoparticles could reduce HA fouling by 40% higher than the fouling obtained without UV irradiation. Compared to the HA fouling without UV irradiation and $TiO_2$ nanoparticles, the HA fouling reduction was about 25% higher only after the addition of $TiO_2$ nanoparticles. Both adsorptive and hydrophilic properties of $TiO_2$ nanoparticles for the HA can be involved in mitigating membrane fouling. It was also found that the aeration itself had lowest effect on fouling mitigation while the HA fouling was affected significantly by solution pH. Transient behavior of zeta potential at different solution pHs suggested that electrostatic interactions between HA and $TiO_2$ nanoparticles should improve photocatalytic efficiency on HA fouling. $TiO_2$ concentration was observed to be more important factor than airflow rate to reduce HA fouling, implying that surface reactivity on $TiO_2$ naoparticles should be important fouling mitigation mechanisms in submerged, photocatalyic microfiltraiton. This was further supported by investigating the effect of $Ca^{+2}$ addition on fouling mitigation. At higher pH (= 10), addition of $Ca^{+2}$ can play an important role in bridging between HA and $TiO_2$ nanoparticles and increasing surface reactivity on nanoparticles, thereby reducing membrane fouling.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.41-46
• /
• 2014

The property improvement of polycarbonate coated with a multilayer film composed of an inorganic $SiO_2$ film and a photocatalytic $TiO_2$ film was studied. The $SiO_2$ film as a binder had an excellent light transmission characteristic. After the treatment with atmospheric pressure plasma, the surface of $SiO_2$ film showed the hydrophilicity, which increased the film coating uniformity with a $TiO_2$-containing aqueous solution. When $TiO_2$ film was over 200 nm thick, the absorption effect of UV rays in the range of 180~400 nm suppressed the yellowing phenomena of polycarbonate substrate. The inorganic film improved the heat resistance of polycarbonate substrates. $TiO_2$ film in the outmost under the exposure of UV rays promotes the catalytic oxidation characteristics and yields the capability to the decomposition of organic contaminants, and also increases the self-cleaning properties due to the increase of hydrophilicity. Structural stability of the polycarbonate substrate coated with inorganic $TiO_2$ and $SiO_2$ film was shown. The role of $SiO_2$ film between $TiO_2$ and polycarbonate substrate suppressed the peeling of $TiO_2$ film by inhibiting the photocatalytic oxidation effect of $TiO_2$ film on the polycarbonate substrate.

• Analytical Science and Technology
• /
• v.20 no.4
• /
• pp.279-288
• /
• 2007

We have studied a method for the preparation of $ACF/TiO_2$ composites involving the penetrationof titanium n-butoxide (TNB) solution into activated carbon fiber. It was focused on the characterization of $TiO_2$ formed in prorous carbon was which increased with surface functional groups by hydrochloric acid treatment. The conversion of TNB to $TiO_2$ for the acid treatment effect must be important for the preparationof $ACF/TiO_2$ composites. From the characterization of surface properties, both the BET surface area and the total pore volume decreased as the distribution of $TiO_2$ on the activated carbon fiber surfaces after acid treatments.The changes in XRD pattern showed the typical anatase type on $ACF/TiO_2$ composite for the sample named FT, FT1 and FT2 treated with 0.05, 0.1 and 0.5 M, respectively. However, XRD patern of FT3 treated with 0.5M showed mixed amatase-rutile structure. According to the results of SEM micrographs, the titanium complexe particles were irregularly distributed around carbon. And some large clusters were found when an amount of acid treatment increased. The EDX results of $ACF/TiO_2$ composites showed the presence of C, O and P with strong Ti peaks. Finally, the excellent photocatalytic activity of the $ACF/TiO_2$ composites between relative concentration($c/c_o$) of MB (methylene blue) and UV irradiation time could be attributed to the both effects between photocatalysis of the formation of titania complexes and adsorptivity of the activated carbon fiber.

• Journal of the Korean Institute of Gas
• /
• v.10 no.2 s.31
• /
• pp.1-6
• /
• 2006

In this study we proposed on effect of the photodecomcomposition of coated nanofiber by $Pd/TiO_2$ for the removal of formaldehyde gas as indoor air pollutant. The photocatalytic reactor was setup in the inside of rectangular box (volume 2 l), UV lamp and the coating nanofiber with $Pd/TiO_2$. This study investigated the reaction rate and the adsorption constant of Langmuir-Heinshelwood, conversion of formaldehyde gas on temperature ($40^{\circ}C{\sim}80^{\circ}C$), effect of conversion (%) under different concentration, and effect of conversion (%) with humidity level on added $SO_2$ gas. As results, the rate constant (k) and adsorption constant (ft) were 114.94ppmv/min, $0.0036ppmv^{-1}$, respectively. and the conversion (%) of formaldehyde gas on temperature ($40^{\circ}C{\sim}80^{\circ}C$) was decreased to about 24%, compare with the first conversion (%). In conversion effect of increasing humidity levels, the presence of sulfur dioxide further decreased than without sulfur dioxide. the decreasing reason of conversion with presence sulfur dioxide judged as a cause of interference factor on the decrease of contact chance with photocatalysts.