• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2005년도 제25회 추계학술대회논문집
• /
• pp.22-25
• /
• 2005

열용량분석기(TGA)를 사용하여 고온에서의 탄소/페놀릭 복합재료의 열분해를 연구하였다. 온도상승 속도는 5, 10, 15, 30 그리고 $50^{\circ}C/min$ 이었으며 온도 상승속도가 증가할수록 최대 열분해 반응의 온도도 상승하였다. 열분해반응에서 얻어진 자료를 근간으로 물리-수학적인 모델을 제시하였으며 모델의 실효성을 판단하기 위하여 고체 추진기관 노즐의 연소시험을 통하여 내부 온도 분포 및 밀도 분포 자료를 해석 모델과 비교하였다. 향후 연구를 통하여 이러한 열분해 인자는 고체 추진기관의 열 및 구조 해석의 입력 자료로 활용이 될 것이다.

• 한국전기전자재료학회논문지
• /
• 제13권12호
• /
• pp.1058-1062
• /
• 2000

We investigated resistive superconducting fault current limites (SFCLs) fabricated using YBCO thin films on 2-inch diameter sapphire substrates. Nearly identical SFCL units were prepared and tested. The units were connected in series and parallel to increase the current and voltage ratings. A serial connection of the units showed significantly unbalanced power dissipation between the units. This imbalance was removed by introducing a shunt resistor to the firstly quenched unit. Parallel connection of the units increased the current rating. An SFCL module of 4 units in parallel, each of which has minimum quench current rating. An SFCL module of 4 units in parallel, each of which has minimum quench current 25 A$\_$peak/, was produced and successfully tested at a 220 V$\_$rms/circuit. From the resistance increase, we estimated that the film temperature increased to 200 K in 5 msec, and 300 K in 120 msec. Successive quenches revealed that this system is stable without degradation in the current limiting capability under such thermal shocks as quenches at 220 V$\_$rms/.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.38-42
• /
• 2002

HAZ(Heat Affected Zone of weldm ents) properties were investigated for a high nitrogen austenitic stainless steel with a chemical composition of Fe-0.02C-0.15Si-6.00Mn-10.0Ni-23.0Cr-2.00Mo-0.48N-0.14V. Thermal cycle of HAZ was simulated by the thermal cycle simulator (Gleeble 1500). The heat treatment was applied to the Charpy test size sample without notch under various peak temperatures and/or the holding times condition. V-notch Charpy test was performed at the temperature range of 273~77 K. Metallographic examination also was carried out by using optical microscopy, scanning electron microscopy and transmission electron microscopy. The simulated specimens revealed a slight embrittlement compared with the base materials. The impact toughness of the specimens deteriorated with the decreasing test temperature. The results from Charpy V-notch test, however, showed that significant degradation of absorbed energy caused by brittle fracture was not observed for the specimen tested in the test temperature range.

• Journal of the Korean Wood Science and Technology
• /
• 제34권5호
• /
• pp.59-66
• /
• 2006

The thermal properties of wood flour, Hwangto, and maleated polyethylene (MAPE) reinforced HDPE composites were investigated in this study. The thermal behavior of reinforced wood polymer composites was characterized by means of thermogravimetric (TGA) and differential scanning calorimetric (DSC) analyses. Hwangto and MAPE were used as an inorganic filler and a coupling agent, respectively. According to TGA analysis, the increase of wood flour level increased the thermal degradation of composites in the early stage, but decreased in the late stage. On the other hand, Hwangto reinforced composites showed the higher thermal stability than virgin HDPE, from the determination of differential peak temperature ($DT_p$). Decomposition temperature of wood flour and/or Hwangto reinforced composites increased with increase of heating rate. From DSC analysis, melting temperature of reinforced composites little bit increased with the addition of wood flour or Hwangto. As the loading of wood flour or Hwangto to HDPE increased, overall enthalpy decreased. It showed that wood flour and Hwangto absorbed more heat energy for melting the reinforced composites. Hwangto reinforced composites required more heat energy than wood flour reinforced composites and virgin HDPE. Coupling agent gave no significant effect on the thermal properties of composites. Thermal analyses indicate that composites with Hwangto are more thermally stable than those without Hwangto.

• Archives of Pharmacal Research
• /
• 제28권1호
• /
• pp.68-72
• /
• 2005

Pseudolaric acid B is a major compound found in the bark of Pseudolarix kaempferi Gordon. In our study, pseudolaric acid B inhibited growth of human melanoma cells, A375-S2 in a time and dose-dependent manner. A375-S2 cells treated with pseudolaric acid B showed typical characteristics of apoptosis including morphologic changes, DNA fragmentation, sub-diploid peak in flow cytometry, cleavage of poly-ADP ribose polymerase (PARP) and degradation of inhibitor of caspase-activated DNase (ICAD). P53 protein expression was upregulated while cells were arrested at the $G_2/M$ phase of the cell cycle. There was a decrease in the expression of anti-apoptotic Bcl-2 and Bcl-xL proteins, whereas pro-apoptotic Bax was increased. The two classical caspase substrates, PARP and ICAD, were both decreased in a time-dependent manner, indicating the activation of downstream caspases.

• 한국세라믹학회지
• /
• 제44권8호
• /
• pp.407-411
• /
• 2007

A 3-cell stacked anode-supported solid oxide fuel cell was designed and fabricated to achieve a complete gas seal and the facile stacking of components. The stack was assembled with a unit cell with $10{\times}10cm^2$ area, and each cell was interconnected by a stainless steel 430 separator using a proprietary sealant sheet. The stack performance was examined at various gas flow rates of $H_2+3.5vol%\;H_2O$, and air at a fixed temperature of $800^{\circ}C$. No gas leakage was found from the sealing between cells and inter-connects within a measurement system in this research during a prolonged time of 500 h in operation. The test resulted in an open circuit voltage of 3.12 V, a peak power of 149 W, and a power density of $0.61W/cm^2$, while the long term durability of the power showed 19.1% degradation during the prolonged time of 500 h when tested at $800^{\circ}C$.

• 전자공학회논문지 IE
• /
• 제49권2호
• /
• pp.9-17
• /
• 2012

음성 인식 시스템의 용용에서 실제 문제점의 하나는 음성신호의 왜곡에 의한 인식성능의 저하이다. 음성신호의 왜곡에 가장 중요한 원인은 부가적인 잡음이다. 이 논문은 잡음에 강인한 음성인식을 위하여, 스펙트럼 피크 향상 기법과 효과적인 잡음 차감 기법에 기초한 스펙트럼 보상 방법을 기술한다. 제안한 방법은 음성 스펙트럼의 포먼트 구조를 향상시키고 스펙트럼 기울기를 보상하면서도 광 대역폭 스펙트럼 요소는 그대로 유지한다. 백색 가우스 잡음, 자동차 잡음, 음성 잡음 또는 지하철 잡음에 의해 왜곡된 음성을 이용한 인식실험을 수행한 결과, 새로운 방법은 스펙트럼 보상을 하지 않은 경우에 비해, 높은 SNR(Signal to Noise Ratio) 환경에서는 평균 오인식율을 약간 줄였으며, 낮은 SNR(10 dB) 환경에서는 평균 오인식율을 1/2로 크게 줄였다.

• 대한방사선기술학회지:방사선기술과학
• /
• 제25권1호
• /
• pp.77-81
• /
• 2002

The purpose of this study is to examine quantitatively the relationship between visual image quality and degradation In spatial resolution for a gamma camera by the increase in distance from collimator. The relationship between the portion(p) of images identified the difference of image quality and the difference(${\Delta}FWHM$) in FWHM between paired images was showed in a sigmoid curve. Using Dendy's method, minimum level to be correctly identified the difference of Image duality on three out of four occasion(p=0.75) was corresponded to 0.4 mm in ${\Delta}FWHM$. Using fuzzy theory, the level to be identified the difference of image quality was examined under various conditions. The truth-value of fuzzy sets-degraded or slightly degraded and not-degraded in image quality between palled Images-was gained the peak at 0.5 mm of ${\Delta}FWHM$. It was founded that changes of $0.4{\sim}0.5\;mm$ in FWHM-corresponding about 2 cm distance from collimator could be sufficiently identified in the difference of image quality.

• 신재생에너지
• /
• 제3권3호
• /
• pp.5-13
• /
• 2007

Stacks of solid oxide fuel cell with 1kW max power performance were designed on planar type employing anode-supported cells and metallic interconnects. The stacks composed of 3-cells, 8-cells, and 16-cells were fabricated and tested in serials by using anode-supported cells purchased from Indec, and sealants/interconnects prepared at RIST. In the performance test of the final 16-cells stack, OCV was recorded to be 16.7V. The peak power and the power density showed 1 kW, $0.77W/cm^2$ at $820^{\circ}C$, respectively. In addition, the long-term degradation rate of the power exhibited 2.25 % during 500h at $750^{\circ}C$.

• 한국전자파학회:학술대회논문집
• /
• 한국전자파학회 2003년도 종합학술발표회 논문집 Vol.13 No.1
• /
• pp.8-12
• /
• 2003

To protect digital communications and broadcasting that are expected to be increasingly used at frequencies above 1GHz, there is a need to determine permissible disturbance limits for frequency bands above 1GHz according to indicates that better correlates with interference level in digital systems. The quality of digital communications is expressed in terms of bit error rate(BER) or throughput. In this regard, it has been reported that degradation of BER or throughput can be estimated from the amplitude probability distribution (APD) of disturbance amplitude. Therefore, if the APD can simply be measured with a high accuracy, APD will be an optimal index for the assessment of interference in digital communications. In this paper, we show that a measurement method using statistic model of APD has compatibility about performance reduction estimation of WLAN. And through approach of this inspection, we propose numeral models about interference effects of peak value and time rate of spurious.