• Bulletin of the Korean Chemical Society
• /
• v.18 no.12
• /
• pp.1269-1273
• /
• 1997

The system which employs iron, palladium, molecular oxygen and hydrogen as a model mono-oxygenase, has been investigated to develop a new method for selective cyclohexane oxidation uner mild conditions. This system provides much higher yield and selectivity for the formation of cyclohexanol and cyclohexanone compared to that of the existing industrial method. When the catalytic system, FeCl2-Pd/alumina, was employed, the oxidation system required acetone as a solvent to be efficient and acidifying the solvent by a little addition of acetic acid or HCl made the system more efficient. The Pd catalyst was recyclable without a significant deactivation but the recycling of ferrous chloride showed the decrease in the activity. On the other hand, the heterogeneous catalytic system, Pd/Fe2O3 could be recovered easily and reused after drying treatment.

• Applied Chemistry for Engineering
• /
• v.26 no.5
• /
• pp.575-580
• /
• 2015

Pd/C catalysts were prepared by various preparation methods such as ion exchange, impregnation and polyol method and also characterized by nitrogen adsorption-desorption isothermal, XRD, FE-TEM and CO-chemisorption. The activities of these catalysts were tested in the hydrogenation of cyclohexene to cyclohexane. Catalytic activities of Pd/C catalysts were found to be effected by the chosen preparation methods. Pd dispersions of each Pd/C catalysts prepared by ion exchange, impregnation and polyol method were 17.55, 13.82% and 1.35%, respectively, confirmed by CO-chemisorption analysis. These were also in good agreement with the FE-TEM results. The Pd/C catalyst prepared by ion exchange method exhibits good performance with the cyclohexene conversion rate of 71% for 15 min. These results indicate that Pd/C catalyst having higher dispersion and lower particle size is in favor of hydrogenation cyclohexene and also Pd dispersion increases with the increment of catalytic activity.

• Journal of Magnetics
• /
• v.17 no.2
• /
• pp.86-95
• /
• 2012

This study investigated the effects of adding a third alloying element, Ni, to create $Fe_{70-x}Pd_{30}Ni_x$ (x = 2, 4, 6, 8 at.% Ni) ferromagnetic shape memory alloys (FSMAs). The Ni replaced a portion of the Fe. The $Fe_{70-x}Pd_{30}Ni_x$ alloys were homogenized through hot and cold forging to gain a ~38% reduction in thickness, next they were solution-treated (ST) with annealing recrystallization at $1100^{\circ}C$ for 8 h and quenched in ice brine, and then aged at $500^{\circ}C$ for 100 h. Investigation of the microstructures and magnetostriction indicated that the greater Ni amount in the $Fe_{70-x}Pd_{30}Ni_x$ alloys reduced saturation magnetostriction at room temperature (RT). It was also observed that it was more difficult to generate annealed recrystallization. However, with greater Ni addition into the $Fe_{70-x}Pd_{30}Ni_x$ (x = 6, 8 at.% Ni) alloys, the $L1_0+L1_m$ twin phase decomposition into stoichiometric $L1_0+L1_m+{\alpha}_{bct}$ structures was suppressed after the $500^{\circ}C$/100 h aging treatment. The result was that the $Fe_{70-x}Pd_{30}Ni_x$ (x = 6, 8 at.% Ni) alloys maintained a high magnetostriction and magnetostrictive susceptibility (${\Delta}{\lambda}{_\parallel}{^s}/{\Delta}H$) after the alloys were aged at $500^{\circ}C$ for 100 h. This magnetic property of the $Fe_{70-x}Pd_{30}Ni_x$ (x = 6, 8 at.% Ni) alloys make it suitable for application in a high temperature (T > $500^{\circ}C$) and high frequency environments.

• Journal of the Korean Magnetics Society
• /
• v.19 no.5
• /
• pp.165-170
• /
• 2009

It is well-known that a meta-stable fcc bulk Fe has an antiferromagnetic (AFM) ground state and could be synthesized by growing Fe on a proper fcc metal substrate. In this study magnetism of Fe monolayers on nonmagnetic fcc transition metal (Cu, Rh, Pd, and Ag) (001) surfaces has been investigated using the all-electron full-potential linearized augmented plane wave method. The Fe monolayers on Rh(001) and Pd(001) surfaces were calculated to be stabilized in an AFM state, whereas the Fe monlayers on Cu(001) and Ag(001) surfaces are stabilized in a ferromagnetic (FM) state. Noting that Cu and Ag have the smallest and largest lattice constants and the fcc bulk Fe with a larger lattice constant is getting stabilized in a ferromagnetic state, it is unexpectable and interesting. The calculated magnetic moments of the Fe atoms on Cu, Rh, Pd, and Ag(001) surfaces are 2.811, 2.945, 2.987, and 2.990 $_{{\mu}B}$ in FM states and 2.624, 2.879, 2.922, and 3.001 $_{{\mu}B}$ in AFM states.

• Journal of the Korean Magnetics Society
• /
• v.22 no.1
• /
• pp.1-5
• /
• 2012

We investigate the exchange bias effect in $[Pd/Co]_5$ superlattice structures which are representative system of the perpendicular magnetic anisotropy. We fabricate Si/$[Pd/Co]_5$/FeMn structures, and study the exchange bias variations by measuring hysteresis loop variations with thickness of FeMn layer. In order to optimize the perpendicular magnetic anisotropy, we fix the thickness of Pd with 1.1 nm and investigate the dependence of the perpendicular magnetic anisotropy on the ferromagnetic Co layer thickness. As results, we find that the biggest coercivity in 0.3 nm of Co layer without FeMn layer. The biggest exchange bias field is found for 0.3 nm of Co layer when we change the Co thickness with fixed FeMn thickness. When we vary thickness of FeMn layer, the biggest coercivity is found for 5 nm of FeMn layer. No exchange bias is observed when the FeMn layer is thinner than 3 nm, and the exchange bias field increases with FeMn layer thickness continuously up to 15 nm.

• Journal of the Korean Magnetics Society
• /
• v.14 no.4
• /
• pp.127-130
• /
• 2004

Magnetic properties and thermal stability by exchange biased perpendicular magnetic anisotropy in (Pd/Co)$_{N}$FeMn multilayer deposited by do magnetron sputtering system are investigated. We measured the perpendicular magnetization curves of (Pd(0.8nm)/Co(0.8nm)$_{5}$FeMn multilayer as function of FeMn thickness and annealing temperature. As FeMn thickness increases from 0 to 21nm, the perpendicular exchange bias(Hex) obtained 127 Oe at FeMn thickness 15nm. As the annealing temperature increases to 24$0^{\circ}C$, the E$_{ex}$ increased from 115 Oe to 190 Oe and disappeared exchange biased perpendicular magnetic anisotropy effect at 33$0^{\circ}C$.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1992.10a
• /
• pp.84-85
• /
• 1992

• Journal of the Korean Magnetics Society
• /
• v.18 no.3
• /
• pp.98-102
• /
• 2008

Dependence of the exchange bias and coercivity as surface magnetic anisotropy and ferromagnet materials for $[Pd/Co]_N$ and $[Pd/Co,(CoFe)]_N$/FeMn multilayers with perpendicular magnetic anisotropy were investigated. The coercivity was proportionally increased to 670 Oe by increasing stack number N in Ta(2.1 nm)/[Pd(3.1/N)/$Co(1.2/N)]_N$/Ta(2.1) multilayers with perpendicular magnetic anisotropy. Also, the coercivity in exchange biased multilayer was tend to increased by increasing stack number N. But coercivity of each materials have been in order of Co (600 Oe), $Co_5Fe_5$ (520 Oe) and $Co_8Fe_2$ (320 Oe) as function of the ferromagnet materials. The other side, exchange force of each materials is 300 Oe when the reiteration layer number N is 3. In over number of reiteration layer 3, they maintained coercivity between 200 Oe and 300 Oe.

• Clean Technology
• /
• v.18 no.1
• /
• pp.89-94
• /
• 2012

In this study, we investigated the activity of Pd and Pt supported on acidic Fe-ZSM5 supports for selective catalytic oxidation of ammonia ($NH_3$-SCO). Among the catalysts, Pt/Fe-ZSM5 catalyst exhibited superior $NH_3$-SCO activity to Pd/Fe-ZSM5 catalyst. We also tested Pt/Fe-ZSM5 catalysts with different Fe loading using ion-exchange method to prepare Fe-ZSM5 supports, which resulted in the increased catalytic performance with smaller Fe content: $NH_3$ was oxidized completely at low temperature ($250^{\circ}C$). The physicochemical properties of Fe-ZSM5 were investigated to figure out the relationship between the characteristics of the catalysts and the catalytic activity on $NH_3$-SCO by Inductively coupled plasma-atomic emissions spectrometer (ICP-AES), $N_2$ sorption, X-ray diffraction (XRD), temperature programmed desorption of $NH_3$ ($NH_3$-TPD) technique.

• Journal of the Korean Magnetics Society
• /
• v.14 no.5
• /
• pp.192-195
• /
• 2004

Magnetic properties by exchange biased perpendicular magnetic anisotropy in [Pd(0.8 nm)/Co(0.8 nm)]$_{5}$/FeMn(15 nm) multilayers deposited by dc magnetron sputtering system are investigated. As inserted Pd layer of interface between [Pd/Co] multilayer and FeMn film, the Hex of perpendicular anisotropy was improved from 127 Oe to 145 Oe. But result of an experiment by thermal stability, the Hex of the case that an inserted layer was inserted in decreased from low 20$0^{\circ}C$ in about 5$0^{\circ}C$ more if not inserted. If Ta was a buffer layer, the experiment results along material of buffer layer, the H$_{ex}$ obtained the largest 127 Oe. And if Pd was a buffer layer, H$_{ex}$ obtained the largest 169 Oe. Also, the Hc in buffer layer of Ta and Pd obtained the largest 203 Oe and 453 Oe, respectively.