• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.226-231
• /
• 2002

The present study discusses the results of the controlled precipitation of HgTe nanocrystals in a PbTe semiconductor matrix and demonstrates its effectiveness in producing well-organized and crystallographically aligned semiconductor nanocrystals. Following the similar procedure used in metallic alloys, the semiconductor alloys are treated at 600$^{\circ}C$ for 48 hours, quenched and aged up to 500 hours at 300$^{\circ}C$ and 450$^{\circ}C$ to induce homogeneous nucleation and growth of HgTe nanocrystalline precipitates. Examination of the resulting precipitates using transmission electron microscopy (TEM) and high resolution TEM (HRTEM) reveals that the coherent HgTe precipitates form as thin discs along the {100} habit planes making a crystallographic relation of {100}$\sub$HgTe///{100}$\sub$PbTe/ and [100]$\sub$HgTe///[100]$\sub$PbTe/. It is also found that the nato-disc undergoes a gradual thickening and a faceting under isothermal aging up to 500 hours without any noticeable coarsening. These results, combined with the extreme dimension of the precipitates (4 nm in length and sub-nanometer in thickness) and the simplicity of the formation process, leads to the conclusion that controlled precipitation is an effective method for the preparation of the desirable quantum-dot nanostructures.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.251-255
• /
• 2001

SrTeO$_3$는 312$^{\circ}C$~485$^{\circ}C$의 제한된 온도범위에서 강유전성이 나타난다고 보고된 바 있다. 본 연구에서는 (Sr$_{1-x}$Pb$_{x}$)TeO$_3$(x=0~0.15) 고용체의 상형성 거동, 미세구조, 유전특성 등을 조사하였다. $700^{\circ}C$에서 하소하였을 때 질소 기체 분위기에서는 SrTeO$_3$상이 합성되었지만 공기 중에서는 더욱 산화된 상인 SrTeO$_4$상이 주된 상으로 존재하였다. (Sr$_{1-x}$Pb$_{x}$)TeO$_3$세라믹스에서 Pb 치환량이 0.15 몰까지 증가함에 따라 최적 소결온도가 80$0^{\circ}C$에서 $650^{\circ}C$로 감소하였고, 입자 크기는 증가하였으며, 유전상수가 13에서 25로 증가하였다. 또한, Pb 치환량이 0.05 이상일 때 강유전상이 안정한 온도 영역이 상온까지 확장되었다.

• Journal of the Korean Ceramic Society
• /
• v.33 no.5
• /
• pp.507-513
• /
• 1996

Nonlinear optical properties of TeO2-PbO-GeO2 glasses were investigated and their correlation with struc-tural modification was investigated. Third-order nonlinear susceptibility $\chi$, ranged between 5.0$\times$10-13 esu and 10.7$\times$10-13 esu which are approximately 20-40 times larger than that of silica glass. The glass with a composition of 85(80TeO2-20PbO)-15GeO2(mol%) seemed to provide an optimum compromise between $\chi$and the stability against crystallization. Analyses of the Raman spectra suggested that these glasses are mainly composed of [TeO4] tbp, [TeO3]tp and [GeO4] tetrahedral structural units. It was concluded that the positive contribution of Pb2+ with high polarizability to $\chi$ in TeO2-PbO glasses overwhelmed the negative influence due to the structural modification of [TeO4]tbplongrightarrow[TeO3]tp. On the other hand addition of GeO2 in TeO2-PbO-GeO2 glasses resulted in the decrease of $\chi$ values. This behavior was attributed to the formation of [GeO4] polyhedra at the expense of [TeOn] polyhedra and Pb2+ ions which normally sowed a higher contribu-tion to $\chi$ than [GeO4] polyhedra.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.03a
• /
• pp.11-11
• /
• 2010

In order to design for nano structured materials with enhanced thermoelectric properties, the alloys in the pseudo-binary $Bi_2Te_3$-PbTe system were investigated for their micro structure and thermal properties. For this synthesis the liquid alloys were cooled by water quenching method. The micro structure images were taken by using electron probe micro analyzer (EPMA). Dendritic and lamellar structures were clearly observed with the variation in the composition ratio between $Bi_2Te_3$ and PbTe. It was confirmed that a metastable compounds is $PbBi_2Te_4$ in the The $Bi_2Te_3$-PbTe system. The change in the composition increasing $Bi_2Te_3$ ratio causes to change structure from dendritic to lamellar. Seebeck coefficient of alloys 5 which the mixture rate of $Bi_2Te_3$ is 83% was measured as the highest value. In contrast, the others decreased by increasing $Bi_2Te_3$. n-type characteristics was observed at all condition except alloy 6 which $Bi_2Te_3$ ration is 91%. The power factors of all samples were calculated with Seebeck coefficient and resistivity. Also the thermal conductivity was measured by using laser flash analyzer (LFA). In this work, the microstructures and thermal properties have been measured as a function of ratio of $Bi_2Te_3$ in the $Bi_2Te_3$-PbTe system.

• Korean Journal of Materials Research
• /
• v.5 no.2
• /
• pp.251-258
• /
• 1995

In an effort to increase the thermoelectric figure of merit by reducing the thermal conductivity, the unidirectionally solidified n-type (Bi, Pb)-Te based alloys which form a $Bi_{2}Te_{3}-PbBi_{4}Te_{7}$eutectic lamellar structure were investigated with the microstructural control at various solidification conditions. PbBi_{4}Te_{7}$ lamellae were grown on cleavage plane(0001) of $Bi_{2}Te_{3}$ and the interlamellar spacing decreased from 10.4 $\mu \textrm{m}$to 3.2$\mu \textrm{m}$ with growth velocity variation from 1.4 \times 10^{-4}$cm/sec to $8.3 \times 10^{-4}$cm/sec. Seebeck coefficient was constant, $\mid$$\alpha$$\mid$=29 $\mu$ V/K regardless of growth direction, growth velocity and temperature gradient. Electrical conductivity showed a tendency to decrease slightly with growth velocity and it parallel to growth direction was about three times as large as perpendicular direction. The figures of merit were varied differently from Seebeck coefficients and electrical conductivities depending on the growth direction, growth velocity and temperature gradients. They showed the relative increase in case of perpendicular direction compared with parallel to growth direction. It is believed to be due to the reduction of the thermal conductivity according to decrease of the interlamellar spacing.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.4
• /
• pp.1-5
• /
• 2000

Properties of AC applied hot pressed ($Pb_{1-x}Sn_{x}$) Te thermoelectrics were investigated. Mechanical alloying process used to produce alloyed powder to reduce the inhomogeneity and to avoid vaporization of constituents. It showed an increase in the mechanical alloying time with increasing of Sn contents in ($Pb_{1-x}Sn_{x}$)Te. ($Pb_{1-x}Sn_{x}$)Te were sintered at 873 to 923K for 1-4 minutes, under 150 kgf/$\textrm{cm}^2$ by AC applied hot pressng method. The short sintering time of AC applied hot pressing process could reduce the vaporization of Te. The density of ($Pb_{1-x}Sn_{x}$) Te was more dependent on the sintering temperature than the sintering time. The p-n transition was observed at x=0.1 but only p type conduction behavior was observed at more than 20 mol% of Sn compositions. The maximum value of Seebeck coefficient is 250 $\mu$V/K for x=0.2 at 500K. As the amount of Sn increases, the peak value of Seebeck coefficient drops and shifts to higher temperature and the peak value of electrical conductivity decreased with increasing temperature.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.6
• /
• pp.502-507
• /
• 2010

In order to design nano structured materials with enhanced thermoelectric properties, the alloys in the pseudo-binary $Bi_2Te_3$-PbTe system are investigated for their micro structure properties. For this synthesis, the liquid alloys are cooled by the water quenching method. Micro structure images are obtained by using an electron probe micro analyzer(EPMA). Dendritic and lamellar structures are clearly observed with the variation in the composition ratio between $Bi_2Te_3$ and PbTe. The increase in the $Bi_2Te_3$ composition ratio causes to change of the structure from dendritic to lamellar. The Seebeck coefficient of sample 5, in which the mixture rate of $Bi_2Te_3$ is 83%, is measured as the highest value. In contrast, the others decrease with the increase of the $Bi_2Te_3$ composition ratio. Meanwhile, p-type characteristics are observed in sample 6, at 91%-$Bi_2Te_3$ mixture rate. The power factors of the all samples are calculated with the Seebeck coefficient and resistivity.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.438-445
• /
• 2001

600 W의 마이크로파 출력 하에서 PbO, V$_2$O$_{5}$, TeO$_2$ 및 V$_2$O$_{5}$-PbO-TeO$_2$성분들의 마이크로파 발열 특성을 조사하였다. V$_2$O$_{5}$ 성분의 높은 마이크로파 흡수능에 기인하여 V$_2$O$_{5}$-PbO-TeO$_2$유리상 시편들은 마이크로파를 흡수하여 주어진 온도까지 직접 가열되었다. XRD, OM, SEM 및 고전압 발생 측정기를 통하여 재래식 열 및 마이크로파 공정에서 열처리된 시편들의 결정화 및 전기 전도도의 특성을 비교 조사하였다. PbV$_2$O$_{6}$ 및 Pb$_4$V$_2$O$_{9}$ 결정상들이 마이크로파 열처리된 시편에서는 존재하였다. 그러나, 재래식 열처리된 시편들에서는 존재하지 않는다는 것을 확인하였고, 재래식 열처리된 시편들에 비하여 마이크로파 열처리된 시편들의 전기 전도도 값이 상대적으로 높았다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.263-263
• /
• 2009

The microtstructures and properties of alloys in the pseudo-binary $Bi_2Te_3-PbTe$ system were investigated as a first step towards the design of nanostructured materials with enhanced thermoelectric properties. The liquid alloys were cooled by water quenching method. Dendritic and lamellar structures were observed clearly by using environmental scanning electron microscope(eSEM) and electron probe micro analyzer(EPMA) take into account composition ratio between $Bi_2Te_3$ and PbTe. The compound $Pb_2Bi_6Te_{11}$ precipitated as a metastable phase under all conditions. The structure of those samples changed from dendritic to lamellar by increasing $Bi_2Te_3$ ratio of composition.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.145-145
• /
• 2000