PbS, CuS and (Pb,Cu)S thin films were chemically deposited on glass from alkaline baths containing lead acetate, copper chloride, thiourea and triethanolamine. The deposition, optical, resistivity and thermal electric properties of these films were studied. PbS thin films showed a hexagonal structure and CuS thin films showed amorphous. The crystalline of (Pb,Cu)S thin films was obtained by heat treatment at 200$\^{C}$ and the deposition ratio of Pb to Cu showed 7:3. The energy gap of PbS, CuS and (Pb,Cu)S thin films were 1.7, 2.1 and 2.4 eV, respectively. Sheet resistance of PbS thin films was less affected on thermal annealing, but hose of (Pb,Cu)S and CuS thin films were more reduced about 3 orders of magnitude. All of those thin films indicated p type semiconductor in temperature ranging 30$\^{C}$ to 150$\^{C}$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.13-16
• /
• 2000

(PbS)$_{1-x}$ -(CuS)$_{x}$ thin films(x=0, 0.5, 1) were grown on glass substrates by using a chemical bath deposition method. The molecular ratio of Pb to Cu for the PbS-CuS thin films(x=0.5) was measured about 7:3 by using EDX and XRF. The resistivity of non-annealed (PbS)$_{1-x}$ -(CuS)$_{x}$ thin films was about 10 $\Omega$ . cm. However, after annealing, the resistivity of PbS showed a little change, while PbS-CuS and CuS significantly decreased in the range of 0.002 to 0.005$\Omega$.cm. PbS was p-type and CuS was n-type.-type.

• 보존과학회지
• /
• 제32권3호
• /
• pp.313-320
• /
• 2016

청동으로 주조된 공예품의 금속 조직학적 연구를 통해 그 내부에 관찰되는 불순물을 추측하고, 그 물질의 특성을 파악하여 향후 제련 및 과거 청동 주물 제조 방법 및 재료 연구의 기초데이터를 제공하는 것을 목적으로 한다. 분석에는 SEM-EDS, XRD, 광학현미경을 이용하였다. 분석 결과, 3점의 시료는 ${\alpha}$상, ${\delta}$상, Pb, 불순물 입자인 $Cu_2S$의 4개의 상으로 이루어져 있으며, $Cu_2S$입자는 황동광을 제련하였을 때 생기는 제련 중간 발생물로 추측된다. 이 입자는 Pb와 인접하여 주로 관찰되며, ${\delta}$상 내부에서 관찰되는 경우도 있었다. $Cu_2S$의 입자 특성을 파악하기 위하여 1) 고려경 파편 및 2) $Cu_2S$와 Pb을 1273 K에서 녹여 $10^{\circ}C/min$의 속도로 냉각시켰다. 두 가지 실험으로 공통적으로 검은색 연기가 발생하였으며, 이 연기를 분석한 결과 PbS이었다. $Cu_2S$와 Pb을 반응 시킨 실험에서는 $Cu_2S+Pb{\rightarrow}PbS{\uparrow}+2Cu$의 반응식을 얻었다.

• Transactions on Electrical and Electronic Materials
• /
• 제15권4호
• /
• pp.217-220
• /
• 2014

We studied the plating properties of Sn-Pb solder according to the shape of the Cu wire's cross-section for photovoltaic ribbon. The thickness of the Sn-Pb layer largely decreased to 29% on a curved Cu surface, compared to a flat Cu surface. This phenomenon is caused by the geometrical decrease in the contact angle of the liquid Sn-Pb solder and an increase in the surface energy of the solid/vapor on the curved Cu surface. We suggest a new ribbon's design where the Cu wire's cross-section is a semi-ellipse. These semi-ellipse ribbons can decrease the use of Sn-Pb solder to 64% and increase the photovoltaic efficiency, by reducing the contact area between the ribbon and cell, to 84%. We also see an improvement of reflectivity in the curved surface.

• 대한환경공학회지
• /
• 제30권4호
• /
• pp.446-452
• /
• 2008

중금속 제거를 위한 조류 Spirulina platensis의 생물흡착 특성에 관해 연구하기 위하여, 조류 균체와 Ca-alginate를 이용하여 조류를 고정화한 고정체에 대하여 각각 회분식반응기에서 Pb와 Cu의 제거 실험을 하였다. Spirulina platensis 균체에 의한 Pb와 Cu의 생물흡착은 20분 이내에 흡착평형에 도달하였다. Pb와 Cu의 흡착량은 초기 농도가 증가하거나 용액의 pH가 높아짐에 따라 증가하여, pH 4.5$\sim$5.0에서 최적 조건을 나타내었다. Pb 혹은 Cu의 농도가 200 mg/L일 때, Spirulina platensis의 단위 무게당 흡착된 Pb와 Cu의 최대 흡착량은 각각 86.43과 57.02 mg/g이었으며, 이는 같은 조건에서 활성탄보다 1.94와 1.48배 높은 값이다. Spirulina platensis 균체에 의한 Pb와 Cu의 흡착특성은 Freundlich와 Langmuir 흡착등온식에 의해 잘 해석되었으며, Langmuir 흡착등온식에 의해 구한 흡착제 단위 무게당 흡착되는 Pb 혹은 Cu의 최대 흡착량($q_{max}$)은 각각 95.24와 62.50 mg/g이었다. Sp. platensis 균체에 대한 FT-IR 분석결과 여러 가지의 기능기들을 확인하였고, 이러한 기능기들이 수용액상에서 금속 이온과 반응할 수 있다. 조류 Spirulina platensis를 Ca-alginate를 이용하여 고정화한 고정체에 의한 Pb와 Cu의 생물흡착의 경우, 40분 정도에 흡착평형에 도달하여 균체에 의한 경우에 비하여 약간의 확산제한이 관찰되었다.

• 대한전기학회논문지
• /
• 제43권5호
• /
• pp.795-801
• /
• 1994

The BiPbSrCaCuO superconductor was fabricated by diffusion of The dual layer composed of SrS12TCaS11TCuS12TOS1xT in upper layer and BiS12TPbSI0.3TCuS12TOS1yT in lower layer, and varified growh-mechanism of BiPbSrCaCuO superconducting phase. And, we produced optimum conditions of spread volume and each stage of sintering time were upper layer:Lower layer=1:0.2, 1:0.4, 1:0.6 and 24hr., 120hr., 210hr. From the result, the optimum conditions are spread volume(Upper layer:Lower layer=1:0.6), sintering time(210hrs.) at 820$^{\circ}C$.The BiPbSrCaCuO superconductor, fabricated optimum condition, showed zero resistance at critical temperature of 70k.

• 한국초전도ㆍ저온공학회논문지
• /
• 제20권3호
• /
• pp.1-4
• /
• 2018

The effect of sulfate substitution on the formation of (Pb,S)-1201 type phase was investigated. Polycrystalline samples with nominal compositions of $(Pb_{0.5}B_{0.5-x}S_x)(Sr_{2-y}La_y)CuO_z$, (x = 0 - 0.5, y = 0.7 - 1.0) and $(Pb_{0.5}S_{0.5})(Sr_{2-y}La_y)CuO_z$ (y = 0.5 - 1.0) were prepared by using a solid-state reaction method. The samples were characterized by powder X-ray diffraction (XRD) and resistivity measurements. XRD data revealed that almost-single (Pb,S)-1201 phase samples could be obtained for x = 0.5 and y = 0.9-1.0, judging from the similar results of the XRD patterns between the (Pb,S)-1201 and (Pb,B)-1201 phases. Each of the samples has a crystal structure with tetragonal symmetry. The sample with x = 0.5 and y = 0.9 is found to show an onset of resistivity dropping at over 23 K and zero resistivity at 12 K.

• 대한화학회지
• /
• 제31권2호
• /
• pp.162-167
• /
• 1987

Monohydrogen arsenate를 전위차법으로 직접 정량하기 위하여 네가지 성분인 $Ag_2S$-PbS-$PbHAsO_4-Cu_2S$와 세가지 성분인 $Ag_2S$-PbS-$PbHAsO_4$로 된 전극이 제조되어 평가되었다. $Ag_2S$:PbS:$PbHAsO_4:Cu_2S$의 성분비(몰비)가 2.0:0.5:1.0:0.25인 전극이 전위차 감응, 안정도, 감응 속도와 재현성이 우수하였다. 0.1F $NH_4A_C-NH_4OH$ 완중용액 중의 일정한 이온 강도와 pH 8.50으로 조정된 $10^{-1}$~$10^{-4}M\;HA_SO_4^{2-}$ 농도 범위에서 실험하였고, $CN^-,\;I^-,\;S^{-2}$ 와 $Cl^-$등이 방해하였다.

• 보존과학회지
• /
• 제33권3호
• /
• pp.167-179
• /
• 2017

서산 비경도 출수 상평통보를 대상으로 혐기성 수중 매장환경에서 형성되는 부식화합물 성분과 이에 따른 혐기성 부식 원인을 추정하였다. 미세조직 관찰, 원소 mapping, 층위별 주성분 분석, 부식화합물 동정을 실시하였다. 그 결과 표면의 고착물은 침상형 육면체형 팔면체형으로 분류되며, 그에 따른 분석 결과 Cu, Pb, S 등의 원소가 검출되었다. 원소 mapping에서는 최외곽에 Cu-S로 이루어진 뚜렷한 층이 확인되었다. 층위별 주성분은 Cu, S, Pb 등이 검출되었고, Zn은 검출되지 않았다. 부식화합물은 $PbCO_3$(고착물), $Cu_{1.96}S$(소지금속)이 나타났다. 따라서 서산 비경도 출수 상평통보의 혐기성 부식 특성은 탈아연, 황화동, 납화합물 세 가지로 요약할 수 있다.

• KSBB Journal
• /
• 제11권2호
• /
• pp.173-180
• /
• 1996

S. CereVlSWe를 이용하여 Pb 이온의 흡착 능력을 조사하였다. 살아있는 S. CereVlSWe 및 멸균된 S. cereVlswe 보다 건조분쇄 된 S. cerevisiae가 Pb 흡착 능력이 가장 좋았다. 통일의 중금속 농도에서 중금 속 단위 흡착량은 미생물 농도가 높아짐에 감소하였다. 살아있는 S. cereVlsiae의 흡착 능력 순서는 Pb > >Cu> Cd = Co>Cr > Zn = Ni순이었다. 중금속 흡 착에서 0.1 M NaOH로 24시간 전처리하여 흡착량을 1.5배 증가시킬 수 있었다. 0.1 M HCl 및 0.1 M $H_2S_O4$ 로 Pb이온을 효과적으로 탈착시킬 수 있었다. Pb 이온의 흡착평형은 Freundlich 흡착등온식과 Langmuir 흡착등온식으로 설명할 수 있었다.