• 보존과학회지
• /
• 제36권4호
• /
• pp.296-305
• /
• 2020

Konbaung Dynasty was the last unified dynasty that ruled Myanmar from 18^th to 19^th century. During this time Buddhist art flourished in Myanmar due to the interest of the rulers toward their traditional culture. Metal decorative artifacts in the 18^th century are classified into structures and Buddha statues. They are further subdivided into gilt-bronze and bronze objects, depending on their material component. Three-dimensional gilt-bronze decorative artifacts were cast with a brass alloy of Cu-Zn-Sn-Pb and their surfaces were gilded with extremely thin gold leaves (less than 1 ㎛ in thickness). The gilded layer approximately comprised 10 wt% silver in addition to the main element, gold. The lack of Hg in the gilded layer, indicated that the amalgam gilding technique was not applied. The analysis results indicated that the lacquered gilding technique was applied to the objects. Bronze decorative artifacts without gilding were cast with materials containing Cu-Sn-Pb. The bronze pavilions and bronze Buddha staues were crafted using the same alloy of high-tin bronze, which approximately contained 20 wt% Sn. No heat treatment was applied to reduce the brittleness of the objects after they were cast with a large amount of Sn. The most significant difference between the gilt-bronze and bronze decorative artifacts lie in their elemental compositions. The gilt-bronze decorative artifacts with their gilded surface were manufactured using brass containing zinc, while the unplated bronze decorative artifacts were composed of bronze containing tin. Artifacts of the same type and size are classified differently depending on the materials utilized in the surface treatment such as gilding.

• Journal of Welding and Joining
• /
• 제25권3호
• /
• pp.57-63
• /
• 2007

Electrochemical migration characteristics of Pb-free solder alloys are quantitatively correlated with corrosion characteristics in harsh environment conditions. In-situ water drop test and corrosion resistance test for Sn-3.0Ag-0.5Cu solder alloys were carried out in NaBr and NaF solutions to obtain the electrochemical migration lifetime and pitting potential, respectively. Sn-3.0Ag-0.5Cu solder alloy shows similar ionization and electrochemical migration behavior with pure Sn because of Ag and Cu do not migrate due to the formation of resistant intermetallic compounds inside solder itself. Electrochemical migration lifetime in NaBr is longer than in NaF, which seems to be closely related to higher pitting potential in NaBr than NaF solution. Therefore, it was revealed that electrochemical migration lifetime of Sn-3.0Ag-0.5Cu solder alloys showed good correlation to the corrosion resistance, and also the initial ionization step at anode side is believed to be the rate-determining step during electrochemical migration of Pb-free solders in these environments.

• 보존과학회지
• /
• 제25권4호
• /
• pp.411-420
• /
• 2009

경북 안동 옥동유적에서 출토된 청동유물 14점 중 청동시(靑銅匙) 5점을 대상으로 하여 ICP, 미세조직, TIMS 등의 과학적 분석을 실시하였다. 분석 결과 청동시(靑銅匙)는 Cu- Sn 합금으로 Cu 75%이내, Sn 21~23%로 방짜유기에 해당되며, Pb, Fe, Zn 등이 미량성분으로 첨가되었다. 특히 납(Pb)은 0.04%의 미량으로 존재하는 것으로 보아 제련시 원광석에 포함된 불순물로 보인다. 청동시(靑銅匙)의 미세구조를 볼 때 청동시(靑銅匙)의 모양으로 골을 판 거푸집을 써서 주조한 다음 $586^{\circ}C$ 근방에서 가공하여 급랭한 것으로 추정된다. 열이온화질량분석(TIMS) 측정을 시행하여, 한국, 중국, 일본 납광석의 산지별 데이터 베이스에 대조해 봤을 때 청동시(靑銅匙)의 원료산지는 중국 남부의 납동위원소비와 유사함을 알 수 있다.

• 보존과학회지
• /
• 제36권3호
• /
• pp.178-186
• /
• 2020

동록(銅綠)은 고문헌에 기록되어 있는 전통적인 인공안료 중 하나이다. 고문헌에 기록되어 있는 제법에 따르면, 동록은 동(銅)을 초(醋)를 이용해 부식시키고 생성된 녹을 긁어모아 제조한다. 삼국시대 이후 청동, 황동 등의 동합금을 이용한 다양한 동기(銅器)가 사용되었으며, 채색문화재의 안료분석 연구를 통해 녹색안료에서 구리뿐만 아니라 주석, 아연, 납 등의 검출이 확인되었다. 이와 같은 자료를 바탕으로 구리 및 청동, 황동 등의 구리합금으로 5종의 동록안료를 제조하고 특성 규명을 위한 분석을 수행한 결과, 제조된 동록안료는 청록색을 나타내며, 제조에 사용된 동판의 종류에 따라 색상, 입자형태, 흡유량 등 물성에 차이를 보였다. 또한, 동록안료의 주요 구성원소는 Cu, Sn, Zn, Pb 등으로, 각 원소의 함유 비율은 사용된 동판의 합금 종류에 영향을 받는 것을 알 수 있었다. 동록안료를 구성하는 주요 구성광물은 동판의 종류에 상관없이 호가나이트[hoganite, Cu(CH₃COO)₂·H₂O]로 확인되었다. 촉진내후성 시험을 통해 안정성을 평가한 결과, 동록안료는 전체적으로 빠르게 색변화가 나타나 안정성이 낮은 것으로 보이며, 특히 납 성분을 함유한 경우에는 더 빠르게 색변화가 나타나 상대적으로 취약한 모습을 보였다.

• 보존과학회지
• /
• 제37권6호
• /
• pp.767-777
• /
• 2021

본 연구는 전라남도 고흥과 담양지역에서 출토된 청동거울의 금속학적 분석으로 제작방법을 확인하고자 하였다. 연구한 대상 유물은 담양 제월리 고분에서 출토된 청동거울 2점, 고흥 봉룡리에서 발견된 청동거울 1점으로 총 3점이다. 분석 결과 X선을 이용한 조사에서 육안으로 관찰되지 않던 균열과 부식으로 인해 발생된 결실부와 주조제작으로 인해 형성된 기공을 확인할 수 있었다. 청동거울의 주성분은 Cu-Sn-Pb이며 Cu 73~79 wt%, Sn 17~21 wt%, Pb 3~4 wt%로 2 wt% 이상의 Pb이 포함되어 있어 청동거울에 필요한 주조성 및 기계적 성질을 조절하기 위한 것으로 확인된다. 또한 미세조직 관찰 결과 주조한 상태에서 추가적인 열처리가 이루어지지 않은 α상과 α+δ공석상의 조직으로 비교적 이른 시기에 제작된 삼국시대 청동거울로 추정할 수 있다.

• 보존과학회지
• /
• 제10권1호
• /
• pp.31-37
• /
• 2001

부여 능산리절터 제3건물지(공방)의 북측 공방터에서 수습된 청동덩어리 시료 4개에 대한 금속학적 조사를 실시하였다. 시료 단면의 미세조직은 SEM을 이용하여 관찰하였고, 시료의 정성 및 정량분석은 EDS를 이용하였다. 분석 결과는 다음과 같다. 절터 제3건 물지 내의 북측공방터에서 수습된 청동덩어리 시료 1과 시료 2는 동제련 과정에서 형성된 동피(matte)를 제련하여 만든 조동(粗銅)로 추정되고, 시료 3은 구리 제련 과정에서 만든 정동(精銅)에 주석만을 첨가하여 합금했을 가능성이 있는 Cu-Sn계 청동덩어리이고, 시료 4는 정동에 주석과 납을 함께 첨가하여 합금했을 가능성이 있는 Cu-Sn-Pb계의 청동덩어리였다. 이 제3건물지(공방)에서는 동광석을 제련하여 동피를 만들거나, 외부에서 반입된 동피를 녹여 조동을 만들고, 이것들을 다시 정련하여 정동을 만든 다음에, 주석과 납을 첨가시켜 조성이 다른 여러 가지 청동제품을 만든 것으로 추정된다.

• Journal of Welding and Joining
• /
• 제23권6호
• /
• pp.93-98
• /
• 2005

The purpose of this study is to investigate the characteristics of pb-free $Zn-(3\~6)\%Al-(1\~6)\%Cu$ solder alloys for ultra high temperature(>573K) which applied to air craft, space satellite, automotive, oil, gas well exploration and data logging of geo-thermal wells. Melting range, solderability, electric resistivity, microstructure and mechanical properties were examined with solder alloys casted in Ar gas atmosphere. $Zn-4\%Al-(1\~3)\%Cu,\;Zn-5\%Al-(2\~4)\%Cu\;and\;Zn-6\%Al-(3\~5)\%Cu$ alloys satisfied the optimum melting range of 643 to 673k for ultra high temperature solder. A melting temperature increased with increasing Cu content, but decreased with increasing Al content. The spreadability was improved with increasing hi content. But the content of Cu had no effect on the spreadability. The electric resistivity was lowered with increasing Al and decreasing Cu content. In all Zn-Al-Cu solder alloys, primary dendritic $\varepsilon$ phase(Zn-Cu), dendritic $\eta$ phase(Zn-Cu-Al), $\alpha(Al-Zn)-\eta$ eutectic and eutectoid phase were observed. The addition of Al increased the volume fraction of eutectic and eutectoid phase and it decreased f phases. Also, the addition of Cu increased slightly the volume fraction of e, the eutectic and eutectoid phases. With increasing total content of Al and Cu, a hardness and a tensile strength were linearly increased, but anelongation was linearly decreased.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 일렉트렛트 및 응용기술
• /
• pp.47-52
• /
• 2002

A processing method is developed for preparing sol-gel derived $Pb(Zr_{1-x}Ti_x)O_3$ (x=0.5) thin films on Pt-Ir($Pt_{80}Ir_{20}$)-alloy substrates. The as-deposited layer was dried on a plate in air at $70^{\circ}C$. And then it was baked at $1500^{\circ}C$, annealed at $450^{\circ}C$ and finally annealed for crystallization at various temperatures ranging from $580^{\circ}C$ to $700^{\circ}C$ for 1hour in a tube furnace. The thickness of the annealed film with three layers was $0.3{\mu}m$. Crystalline properties and surface morphology were examined using X-ray diffractometer (XRD). Electrical properties of the films such as dielectric constant, C-V, leakage current density were measured under different annealing temperature. The PZT thin film which was crystallized at $600^{\circ}C$ for 60minutes showed the best structural and electrical dielectric constant is 577. C-V measurement show that $700^{\circ}C$ sample has window memory volt of 2.5V and good capacitance for bias volts. Leakage current density of every sample show $10^{-8}A/cm^2$ r below and breakdown voltage(Vb) is that 25volts.

• 한국재료학회지
• /
• 제13권10호
• /
• pp.640-644
• /
• 2003

NiCr thin films were fabricated by rf magnetron sputtering for applying to both the top electrode and absorption layer on Pb(Zr, Ti)O$_3$(PZT) thin films for infrared sensors. The rms roughness and resistivity of NiCr films prepared with Ni power of 80 W and Cr power of 50 W showed the most stable oxidation resistance after annealing at $600^{\circ}C$ for 5 min in oxygen ambient. The rms roughness and resistivity of NiCr films annealed at $V^{\circ}C$ in oxygen ambient were about 2$0\AA$ and $70 \mu$Ω-cm, respectively. As-deposited Ni/PZT/Pt and NiCr (Ni 80 W, Cr 50 W)/PZT/Pt structures showed well saturated hysteresis loops. However, in case of the samples annealed at $500^{\circ}C$ in oxygen ambient, only NiCr/PZT/Pt showed saturated loops having a remanent polarization of 20$\mu$C/$\textrm{cm}^2$. Ultra-thin NiCr films showed a possibility as a top electrode for infrared sensors.

• 보존과학회지
• /
• 제1권1호
• /
• pp.60-79
• /
• 1992

In relation to the scientific conservation treatment of ancient gilt bronze, the gold film coated on the bronze excavated from Hwangnam Great Tomb of Old Silla Kingdom(A. D. 5C) was studied in the view of coating technology and metallurgy of bronze. The uniform and dense gold film containing $2.44\sim12.40%$ of Hg with the thickness of $5.99\sim12.97{\mu}m$ was found to be coated on the bronze objects by amalgam coating method. On silver objects, the film with the thickness of $19.96{\mu}m$ was coated also continously and uniformly with gold by the same method. The bronze objects was fabricated by forging technique and contained almost $4.7\sim11.5%$ of Pb. Its microstructure was $\alpha-phase$ solid solution including Pb segregation in the matrix. The amount of $0.4\sim2.0%$ Zn was added in the bronze for the purpose of easy fabricating of Cu alloy. Based on the data studied, the gold film on bronze sample was reproduced by amalgam coating method and compared with the ancient gold film.