• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.76-80
• /
• 2007

Three nano-sized Fe-N particle samples synthesized by Chemical Vapor Condensation (CVC) were analyzed using $M\"{o}ssbauer$ spectroscopy, XRD and BET. The synthesized nanoparticles consisted of ${\epsilon}-Fe_{2.12}N,\;{\gamma}'-Fe_4N,\;{\alpha}-Fe\;and\;{\gamma}-Fe.\;{\gamma}'-Fe_4N$ was mainly formed at the low decomposition temperature. With increasing decomposition temperature, the phase was changed to ${\gamma}-Fe$ via ${\epsilon}-Fe_{2.12}N$. For synthesizing Fe-N phases, this study implies that the low decomposition temperature is better than high temperature during Chemical Vapor Condensation.

• Journal of the Korean Ceramic Society
• /
• v.21 no.3
• /
• pp.278-282
• /
• 1984

Barium titanate powder was made by firing the complex hydroxide which had been synthesized with chemical wet process by the medium of $H_2O_2$. This experiment was done as following A mixed solution of $BaCl_2$, $TiCl_4$ and $H_2O_2$ with 1:1:10 mol ratio was prepared. Ammonium hydroxide was added into the mixed solution. In the range of pH 8-10 $BaTiO_3$ complex hydroxide was obtained and treated at room temperature 11$0^{\circ}C$, 20$0^{\circ}C$, 40$0^{\circ}C$ and $600^{\circ}C$. The results obtaiined from this experiment were as follows. At room temperature $BaTiO_3$ complex hydroxide was amorphous. Above 10$0^{\circ}C$ crystalline $BaTiO_3$ was obtained and particle size of $BaTiO_3$ was increased with elevated temperature. So the particle size of BaTiO3 could be controlled by the firing temperature. After treating $BaTiO_3$ complex hydroxide at 10$0^{\circ}C$ the average particle size of $BaTiO_3$ was 0.22$\mu\textrm{m}$.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.28 no.9
• /
• pp.1101-1109
• /
• 2004

Experimental measurements of flame structure and soot characteristics were performed fur ethene inverse diffusion flames (IDF). IDF has been considered as the excellent flow field to study the incipient soot because soot particle do not experience the oxidation process. In this study, LIF image clarified the reaction zone of IDF with OH signal and PAH distribution. laser light scattering technique also identified the being of soot particle. To address the degree of soot maturing, C/H ratio and morphology of soot sample were investigated. From these measurements, the effect of flow residence time and temperature on soot inception could be suggested, and more details on soot characteristic in the IDF was determined according to fuel dilution and flame condition. The fuel dilution results in a decrease of temperature and enhancement of residence time, but the critical dilution mole fraction is existed for temperature not to effect on soot growth. Also, the soot inception evolved on the specific temperature and its morphology are independent of the fuel dilution ratio of fuel.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.1 no.1
• /
• pp.49-54
• /
• 2000

The effect of Particle size of coating Powder and coating temperature on the Properties of coating layer was studied by calorizing(or aluminizing). The surface properties of coating layer were fully characterized, using SEM and EDXS. Coating powders were separated according to the particle size by 3 steps and the coating temperature was varied from $950^{\circ}C$ to $980^{\circ}C$. Calorizing with pack cementation method carried under Ar atmosphere for 5 hrs. Results show that the thickness and Al content of coating layer increased as the size of coating powder decreased and coating temperature increased. And pores formed on the coating layer reduced and homogeneity of coating layer increased with smaller particle size of coating powder.

• Journal of Environmental Health Sciences
• /
• v.22 no.4
• /
• pp.1-9
• /
• 1996

Experiments have been made to test the practical feasibility of using calcined manganese ore to desulfurize hot reducing gas. In this study, the effects of particle size of sorbents, temperature of sulfidation, flow rate and sorbent characteristics on the $H_2S$ removal efficiency of calcined manganese ore were investigated. Experimental results showed that the removal efficiency of $H_2S$ was optimum when the temperature was about 800$\circ$C and that the smaller particle size the higher the $H_2S$ removal efficiency. When the temperature was above 800$\circ$C, the reactivity of sorbent has lowered because agglomeration of sorbent increased intraparticle transport resistance, and this phenomenon was confirmed by SEM photographs. As the temperature increases, capacity for the $H_2S$ removal was increased but the equilibrium concentration of $H_2S$ was not affective.

• Journal of the Korean Society of Safety
• /
• v.15 no.3
• /
• pp.83-87
• /
• 2000

Combustion characteristics of immobilized benzene and toluene in sands were studied. Experiments were performed by burning benzene and toluene immobilized on sands(particle size 0.1~0.5mm) to measure combustion rate and combustion temperature. The longer time from ignition to extinguishment was resulted from the larger particle size exhibited the higher mass burning rate. Of aromatic compounds tested the relative magnitude of facilitation of combustion was benzene and toluene. Combustion temperature of benzene and toluene without regard to the types of benzene and toluene was not increased with smaller sand. However, with larger sands, combustion temperature of benzene and toluene were increased by 50~$100^{\circ}C$ and the highest combustion temperature was obtained with larger sands.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.3
• /
• pp.501-508
• /
• 1987

Experimental studies of particle (TiO$\_$2/) deposition from the laminar hot gas particle flow (about 1565K) onto the cold wall surface (about 1215K-1530K) were carried out by the 'real time' laser light reflectivity method (LLRM) and the photographs of scanning electron microscope(SEM). The LLRM was used for the measurement of thermophoretic deposition rates of small particles (d$\_$p/<3.mu.m), and the photographs of SEM were used for determining what factors control the collection of particles having diameters ranging from 0.2 to 30 microns. Two phenomena are primarily responsible for transport of the particles across the laminar boundary layers and deposition: (1) particle thermophoresis (i.e. particles migration down a temperature gradient), and (2) particle inertial impaction, the former effect being especially larger factor of the particle deposition in its size over the range of 0.2 to 1 microns. And also, this study indicates that thermophoresis can be important for particles as large as 15 microns. Beyond d$\_$p/=16.mu.m, this effect diminishes and the inertial impaction is taken into account as a dominant mechanism of particle deposition. The results of present experiments found to be in close agreement with existing theories.

• Journal of Powder Materials
• /
• v.11 no.3
• /
• pp.202-209
• /
• 2004

In this study, nano-sized powder of Ni-ferrite was fabricated by spray pyrolysis process using the Fe-Ni complex waste acid solution generated during the shadow mask processing. The average particle size of the produced powder was below 100 nm. The effects of the reaction temperature, the inlet speed of solution and the air pressure on the properties of powder were studied. As the reaction temperature increased from 80$0^{\circ}C$ to 110$0^{\circ}C$, the average particle size of the powder increased from 40 nm to 100 nm, the fraction of the Ni-ferrite phase was also on the rise, and the surface area of the powder was greatly reduced. As the inlet speed of solution increased from 2 cc/min. to 10 cc/min., the average particle size of the powder greatly increased, and the fraction of the Ni-ferrite phase was on the rise. As the inlet speed of solution increased to 100 cc/min., the average particle size of the powder decreased slightly and the distribution of the particle size appeared more irregular. Along with the increase of the inlet speed of solution more than 10 cc/min., the fraction of the Ni-ferrite phase was decreased. As the air pressure increased up to 1 $kg/cm^2, the average particle size of the powder and the fraction of the Ni-ferrite phase was almost constant. In case of 3 $kg/cm^2 air pressure, the average particle size of the powder and the fraction of the Ni-ferrite phase remarkably decreased.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.575-576
• /
• 2012

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07a
• /
• pp.814-816
• /
• 2005

In this paper, we describe how specially developed polymer capped, nano-particle silver inks can be used to print circuitry for applications like displays, RFID antennas and "disposable electronics". The requirements of printing on temperature sensitive flexible substrates (such as polymer films and papers) that require low temperature curing is also discussed.