• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.4
• /
• pp.367-372
• /
• 2010

A power plant's heat exchangers work under poor conditions, such as high temperature, high pressure, corrosion, mechanical stress and vibration. Especially, partial joint-weld of heat exchanger's header to stub-tube is the place where incomplete penetration flaws can easily occur. But, it is hard to evaluate the safety of the structure by conventional nondestructive testing techniques. So it is necessary to test integrity of the weld inside and to develop testing technique and equipment that can detect the flaws at the weld point in order to enhance reliability of the test result. In this study, we developed a suitable automated ultrasonic testing system that can inspect the partial joint-weld of header to stub-tube of power plant. Finally, we showed the efficiency of the automated ultrasonic-testing-system from the application.

• Journal of Korean Society of Steel Construction
• /
• v.12 no.3 s.46
• /
• pp.231-238
• /
• 2000

There was extreme improvement in the processing result of weld toe, but there is possibility that the fatigue failure occurs from the weld root part where the fatigue strength became low relatively. This study did the fatigue test at the cross rib specimens which implemented a partial penetration weld to improve the fatigue strength of the weld root part. As a result of the fatigue test of the partial penetration weld and the fillet weld specimens, almost the same fatigue strength appeared. Because the fatigue failure began from toe, there was not a reinforcement effect in the weld root part by the partial penetration weld. So, it examined fatigue strength at the partial penetration welding specimens which processed toe to stop the fatigue failure of toe part. As a result, there was big fatigue strength improvement from the partial penetration weld than the fillet weld. Therefore, if fatigue crack occurrence can be restrained from toe, it thinks that the fatigue strength of the root part can improve by the partial penetration weld, after all, it thinks that the overall fatigue life can improve.

• Journal of Mechanical Science and Technology
• /
• v.16 no.9
• /
• pp.1033-1039
• /
• 2002

Partial penetration welding joint refers to the groove weld that applies to the one side welding which does not use steel backing and to both side welding without back gouging, that is, the partial penetration welding joint leaves an unwelded portion at the root of the welding area. In this study, we analyzed the residual stress and fracture on the thick metal plates that introduced the partial penetration welding method. According to the above-mentioned welding method, we could draw a conclusion that longitudinal stress and traverse stress occurred around the welding area are so minimal and do not affect any influence. We also performed the fracture behavior evaluation on the partial penetration multi pass welding with 25.4 mm thick plate by using the J-integral, which finally led us the conclusion that the partial penetration multi-pass welding method is more applicable and effective in handling the root face with less than 6.35 mm.

• Proceedings of the KWS Conference
• /
• 1991.11a
• /
• pp.123-125
• /
• 1991

• Journal of Welding and Joining
• /
• v.20 no.3
• /
• pp.122-128
• /
• 2002

The laser welding in the automotive industries has been used widely for the butt joint of blank sheets rather than the lap joint of automotive body panels. But as a substitute far the spot welding of automotive body panels, the so called three dimensional laser welding will be important far the body panel engineers. Specially the laser welding of body panels with a smooth weld line is applied increasingly, for example, to the side panels. So far, some criteria of the laser weld quality was suggested by in-house regulations or national standards from experiences and/or rule of thumbs. In the manufacturing places, a go or no-go criterion is adopted because of the simplicity or a lack of rational criteria. It is true specially for the selection of the process parameters, which gives the basic causes for the good quality of laser welds. In this study, the effects of joint combination, gap and welding speed on the lap joint $CO_2$ laser welding of two mild steel sheets with different thicknesses are obtained through a $2{\times}3{\times}7$ factorial experiment. The results of the weld quality are statistically analysed using analysis of variance (ANOVA) and compared between two characteristic zones, which are separated by the type of sectional shapes and the level of input energy per volume. The thickness combinations are 0.8mm/1.2mm, 1.2mm/0.8mm of mild steel sheets. The welding speed covers from the deep penetration to the partial penetration. The gap size has three levels of no-gap, 0.16m, and 0.26mm. The bead width, penetration depth and input energy per volume are measured and used as the weld quality criteria.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.11
• /
• pp.1813-1819
• /
• 2001

Partial penetration welding Joint defines that groove welds without steel backing, welded from on side, and groove weeds welded from both sides but without back gouging, that is. it has an unwelded portion at the root of the weld. In this study we analysed fur residual stress and displacement distribution on partial penetration welding condition of thick plate metal. For 25.4mm thick plate, theoretical residual stress and displacement analysis by finite element method using ABAQUS was carried out and compared with the experimental result using hole-drilling method. In results of the condition of partial penetration, it appeared that longitudinal stress at welding area was a little difference and transverse stress did not have any effect by partial penetration multi-pass welding. From a point of welding distortion in partial penetration multi-pass welding, it seemed to be better to control root face smaller than 6.35mm.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.2
• /
• pp.300-307
• /
• 2002

Partial penetration welding joint is defined as groove welds welded from one side, without steel backing or groove welds welded from both sides but without back gouging. So it has an unwelded portion at the root of the weld. Study of partial penetration weldment fracture behavior includes residual stress analysis and fracture analysis. The J-integral loses its path independency in residual stress field. Therefore, it is necessary to introduce a new J-integral, J, which is defined including the effect of plastic deformation and thermal strain. In this study, theoretical formulation and program were developed for the evaluation of J-integral for the crack tip located in the weldment. Evaluations of fracture behavior were performed for partial penetration multi-pass weldment of 25.4mm thick plate by J-integral. From a point of fracture in partial penetration multi-pass welding, it seemed to be better to control root face smaller than 6.35mm.

• Journal of Welding and Joining
• /
• v.27 no.2
• /
• pp.63-68
• /
• 2009

Microminiature heat exchanger has been applied to the gas turbine in order to increase energy efficiency. During the production of microminiature heat exchanger, however, it is very difficult to weld tube to tubesheet. In this study, therefore, welding process of resistance ring projection was used, and weld tensile tests were performed. Sound weld joint was obtained as a result of applying resistance ring projection welding to microminiature heat exchanger to tubesheet. Cold weld occurred at under 1600A. Even though tensile strength was increased with increasing current, splash occurred and tensile strength decreased at 2000A due to the excessive current. Therefore it was determine that the optimal current is 1900A. As result of tensile tests based on ASME code for tube to tubesheet weldment, rupture position was weldment due to Fs(Fractured section) of nugget, which was smaller than tube thickness (t), and it was proven as a partial strength welding because of the average joint efficiency fr = 0.90.

• Journal of Welding and Joining
• /
• v.19 no.6
• /
• pp.636-642
• /
• 2001

Partial penetration welding joint defines the groove welds that applies the one side welding which does not use steel backing and both side welding without back gouging, that is, the partial penetration welding joint leaves an unwelded portion at the root of the welding area. In this study, we analyzed the residual stress and fracture on the thick metal plates that introduced the partial penetration welding method. As results of using above mentioned welding method, we could draw a conclusion that longitudinal stress and traverse stress occurred around the welding area was so minimal and did not affect any influence. We also performed the fracture behavior evaluation on the partial penetration multi-pass welding with 25.4mm thick plate by using theJ-integral, which finally led us the conclusion that the partial penetration multi -pass welding method is more applicable and effective in handling the root face with less than 6.35mm.

• Journal of the Society of Naval Architects of Korea
• /
• v.33 no.3
• /
• pp.1-7
• /
• 1996

The stress concentration factor gives the significant effect the fatigue strength of welded joints. The model used herein is the type of the load carrying fillet welded cruciform joint with full or partial penetration. In order to obtain the stress concentration factor at the weld toe of fillet joint, the reasonable element size of the toe part is investigated and the stress analysis for the series models by FEM under tensile load is performed. On the basis of the calculation results, the estimated formulae for the stress concentration factor(Kt) at weld toe part of the fillet welded joint, which the effect of toe radius, flank angle and other parameters are taken into account, is derived.