PZT(40/60) and PZT(60/40) powders, prepared by the sol-gel method, were mixed with an organic vehicle and the PZT(40/60)/PZT(60/40) heterolayered thick films were fabricated by the screen-printing method on $Pt/Al_2O_3$ substrates. The structural properties such as DTA, X-ray diffraction and microstructure, were examined as a function of the applied pressure. In the DTA analysis, the formation of the polycrystalline perovskite phase was observed at around $880^{\circ}C$. The average thickness of the PZT heterolayered thick films which were coated five times was approximately $95-100{\mu}m$.

• The Journal of the Acoustical Society of Korea
• /
• v.17 no.2
• /
• pp.56-62
• /
• 1998

전기-기계변환효율이 좋은 PZT를 송신용으로, 대역특성이 우수한 PVDF를 수신용 으로한 PZT/PVDF 복합구조 수중초음파 트랜스듀서를 제안하고, 외부는 PZT, 내부는 PVDF로 된 동심원형의 트랜스듀서를 설계·제작하여, 그 특성을 이론적, 실험적으로 파악 하였다. 삽입손실과 임펄스 응답파형에 대한 등가회로해석 및 측정결과로부터 제안한 트랜 스듀서의 특성, 특히, 대역폭이 종래의 PZT 단일소자에 의한 트랜스듀서보다 향상될 수 있 음을 알았다.

• Journal of the Korean Ceramic Society
• /
• v.25 no.1
• /
• pp.54-58
• /
• 1988

In order to depress PbO vaporization during calcination and improve sinterability in low temperature, a method for preparing homogeous Lead-Zirconate-Titanate (PZT) powder from aqueous salt solution by precipitation is described. In this method, single phae PZT fine powders are formed at above 500$^{\circ}C$. PZT-ceramics using these powders have high sinterability, and good sintering characteristics relatively low temp. (-high apparent density, low porosity, low water adsorption etc.)

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.05a
• /
• pp.13-16
• /
• 1994

The porous PZT was prepared from a mixture of PZT and polyvinylalcohol (PVA ) powders by BURPS( Burnedout Plastic Sphere) technique. The dielectric and piezoelectric properties of piezoceramic/polymer composites dependent on the PVA wt. % were evaluated. The density of PZT/polymer 3-3 composites were decreased almost linearly with increasing the PVA wt. %.

• Proceedings of the Acoustical Society of Korea Conference
• /
• 1997.06a
• /
• pp.64-67
• /
• 1997

PZT 및 PVDF의 장점을 이용한 송.수신 일체의 PZT/PVDF 복합구조 초음파 트랜스듀서를 제안하고, 그 특성을 분포정수형 등가회로를 이용하여 해석하였다. 특히 수신부의 PVDF를 다층으로 하여 송.수신 특성을 상당히 개선할 수 있음을 확인하였다.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.168-172
• /
• 1988

In order to prevent the PbO vaporization during calcination and to produce the powder of good sinterability, a coprecipitation method for preparing homogeneous Lead-Zirconate-Titanate (PZT) powder from aqueous salt solution is described. In this method, the PZT-ceramics show low calcining and sintering temperature, and they have good sintering and electronic properties.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.11a
• /
• pp.389-390
• /
• 2010

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1986-1988
• /
• 1999

Ferroelectric lead zirconate titanate(PZT) thin films were prepared on various bottom electrodes by rf magnetron sputtering methode. The structural phase and surface morphology of the PZT thin films were largely affected by the bottom electrodes. P-E curves of PZT thin films deposited on Pt. $RuO_2$ and Ru/$RuO_2$ bottom electrode showed typical P-E hysteresis loop. The measure values of $P_r,\;E_c$ of the Ru/PZT/Ru/$RuO_2$ capacitor were $16.9{\mu}C/Cm^2$, 140kV/ cm, respectively. The Ru/PZT/Ru/$RuO_2$ capacitors were fatigue free uP to nearly $10^9$ switching cycle but Pt/PZT/Pt capacitor showed 34% degradation uP to $10^9$ switching cycle.

• Journal of Ocean Engineering and Technology
• /
• v.29 no.1
• /
• pp.94-99
• /
• 2015

Lead zirconate titanate (PZT) thick films with thicknesses of ㎛ were fabricated on silicon substrates using an aerosol deposition method. A PZT powder solution was prepared using a sol-gel process. The average diameters (d50) obtained were 1.67, 1.98, and 2.40μm when the pyrolysis temperatures were 300℃, 350℃, and 450℃ respectively. The as-deposited film had a uniform microstructure without any cracks or pores. The as-deposited films on silicon were annealed at a temperature of 700℃. The 20-㎛-thick PZT film showed good adherence between the PZT film and substrate, with no tearing observed in the conventional solid phase process. This was probably because the presence of pores produced from organic residue during annealing relieved the residual stresses in the deposited film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.7
• /
• pp.667-672
• /
• 2006

Ferroelectric $Pb(Zr_{0.52}Ti_{0.48})O_3$ (PZT(52/48)) thick films were fabricated by the screen-Printing method on the alumina substrates, and $PbTiO_3$ (PT) Precursor solution, which prepared by sol-gel method, was spin-coated on the PZT(52/48) thick films to obtain a densification. Its structural and electrical properties of the PZT(52/48) thick films with the treatment of PT precursor solution coating were investigated. The particle size of the thick films was increased with increasing the number of coatings and the thickness of the PZT-6 (6: number of coatings) films was about $60{\mu}m$. The relative dielectric constant increased and the dielectric loss decreased with increasing the number of PT sol coatings. The relative dielectric constant and dielectric loss of the PZT-6 thick film were 475 and 2 %, respectively. The remanent polarization, coercive field and breakdown strength of the PZT-6 film were $32.6{\mu}C/cm^2$, 15 kV/cm and 60 kV/cm, respectively.