• The Journal of Korea Robotics Society
• /
• v.11 no.3
• /
• pp.140-145
• /
• 2016

In this paper, we fabricate arrayed-type flexible capacitive touch sensor using liquid metal (LM) droplets (4 mm spatial resolution). Poly-4-vinylphenol (PVP) layer is used as a dielectric layer on the electrode patterned Polyethylene naphthalate (PEN) film. Bonding tests between hydroxyl group (-OH) on the PVP film and polydimethylsiloxane (PDMS) are conducted in a various $O_2$ plasma treatment conditions. Through the tests, we can confirm that non-$O_2$ plasma treated PVP layer and $O_2$ plasma treated PDMS can make a chemical bond. To measure dynamic range of the device, one-cell experiments are conducted and we confirmed that the fabricated device has a large dynamic range (~60 pF).

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2003.02a
• /
• pp.146-148
• /
• 2003

SrZrO$_3$ resistive oxide barriers on Ag sheathed Bi2223 monocore tapes were prepared by the sol-gel and dip coating method to reduce AC coupling loss. The performance of the dip-coated SrZrO$_3$ thin films was evaluated in terms of bond strength and surface microstructure by varying the amount of PVP (polyvinylpyrrolidone) binder. Although bond strength and coating thickness increased as the PVP content rose, surface microcracking was more severe for the specimen containing higher content of PVP binder. It suggests that coating thickness and microcracking of the SrZrO$_3$ films on Bi2223 tapes was governed primarily by the amount of PVP binder.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.312-314
• /
• 2009

We have fabricated pentacene based organic thin film transistors (OTFTs) with formulated poly[4-vinylphenol] (PVP) gate dielectrics. The gate dielectrics is composed of PVP, poly[melamine-coformaldehyde] (PMF) and photo-initiator [1-phenyl-2-hydroxy-2-methylpropane-1-one, Darocur1173]. By adding small amount (1 %) of photo-initiator, the cross-linking temperature is lowered to $115^{\circ}C$, which is lower than general thermal curing reaction temperature of cross-linked PVP (> $180^{\circ}C$). The hysteresis and the leakage current of the OTFTs are also decreased by adding the PMF and the photoinitiator in PVP gate dielectrics.

• Proceedings of the PSK Conference
• /
• 2003.10b
• /
• pp.231.1-231.1
• /
• 2003

Mucoadhesive microsphere was prepared by interpo]ymer complexation of po]y(acrylic acid) (PAA) with po]y(vinyl pyrrolidone) (PVP) using solvent diffusion method. The loading efficiency of acetaminophen into the microsphere was 91.3 ${\pm}$ 6.5%. The release rate of acetaminophen from the PAA/PVP complex microspheres was slower than that from PVP microspheres at pH 2.0 and 6.8. The dissolution of microspheres made of the complex was significantly slower than those made of PVP due to H-bond between PVP and PAA. As a result, the release rate of acetaminophen from the complex microspheres was slower than that from PVP microspheres.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.1
• /
• pp.27-31
• /
• 2007

The cpapcitors with MIM(metal-insulator-metal) structures using PVP gate insulation films were prepared for the application of flexible organic thin film transistors (OTFT). The co-polymer organic insulation films were synthesized by using PVP(poly-4-vinylphenol) as a solute and PGMEA(propylene glycol monomethyl ether acetate) as a solvent. The cross-linked PVP insulation films were also prepared by addition of poly(melamine-co-formaldehyde) as thermal hardener. The leakage current of the cross- linked PVP films was found to be about 1.3 nA on Al/PES(polyethersulfone) substrate, whereas, on ITO/ glass substrate was about 27.5 nA indicating improvement of the leakage current at Al/PES substrates. Also, the capacitances of all prepared samples on ITO/glass and Al/PES substrates w ere ranged from 1.0 to $1.2nF/cm^2$, showing very similar result with the calculated capacitance values.

• Korean Journal of Optics and Photonics
• /
• v.24 no.5
• /
• pp.251-255
• /
• 2013

In this paper, the characteristics of a humidity sensor implemented by Mach Zehnder Interferometer (MZI) in a Planar Lightwave Circuit (PLC) have been designed and demonstrated. The humidity outside is detected with polyvinylpyrrolidone (PVP) coated on the etched arm of the MZI. The length of the etched arm is 10 mm and the PVP was coated by dip-coating into the etched region. As the refractive index of the PVP changes with the surrounding humidity, the PVP-coated humidity sensor presented changes in the interferogram depending on RH (Relative Humidity) around the PLC. The measured results show that the proposed humidity sensor works successfully in the range of 30% to 80% of RH.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.221-221
• /
• 2012

Small-molecule organic photovoltaic cells have recently attracted growing attention due to their potential for the low-cost fabrication of flexible and lightweight solar modules. The PVP/Ag nanoparticles were synthesized by the reaction of poly vinylpyrrolidone (PVP) and silver nitrate at $150^{\circ}C$. In the reaction, the size of the nanoparticles was controlled by relative mole fractions between PVP and Ag. The PVP/Ag nanoparticles with various sizes were then spin coated on the patterned ITO glass prior to the deposition of the PEDOT:PSS hole transport layer. The scattering of the incident light caused by these incorporated nanoparticles resulted in an increase in the path length of the light through the active layer and hence the enhancement of the light absorption. This scattering effect increased as the size of the nanoparticles increased, but it was offset by the decrease in total transmittance caused by the non-transparent nanoparticles. As a result, the maximum power conversion efficiency, 0.96% which was the value enhanced by 14% compared to the cell without incorporation of nanoparticles, was obtained when the mole fraction of PVP:Ag was 24:1 and the size of the nanoparticles was 20~40 nm.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.5
• /
• pp.1587-1592
• /
• 2011

The aim of the present study was to improve the solubility and bioavailability of a poorly water-soluble drug in human body, using a solid dispersion technique (hot melt extrusion). The solid dispersion was prepared by cooling the hot melt of the drug in the carrier (Vitamin E TPGS and PVP). The dissolution rate of formulation 1 from a novel formulation prepared by solid dispersion technique was equal to release of formulation 6 (40% of eprosartan mesylate is in contrast to teveten$^{(R)}$) within 60 min (Table 1). The oral bioavailability of new eprosartan mesylate tablet having vitamin E TPGS and PVP K29 was tested on rats and dogs. Of the absorption enhancer and polymer tested, vitamin E TPGS and PVP K29, resulted in the greatest increases of AUC in animals (about 2.5-fold increase in rat and dog). When eprosartan mesylate was mixed with the absorption enhancer and polymer in a ratio of 2.94:2:1, vitamin E TPGS and PVP K29 improved eprosartan mesylate bioavailability significantly compared with the conventional immediate release (IR) tablet Teveten$^{(R)}$ (formulation 7). These results show that solid dispersion using vitamin E TPGS and PVP K29 is a promising approach for developing eprosartan mesylate drug products.

• Proceedings of the IEEK Conference
• /
• 2004.06b
• /
• pp.375-378
• /
• 2004

In this paper, we fabricated pantacene TFTs using PVP copolymer and cross-linked PVP as gate insulator on glass and plastic (PET) substrate. Depending on the density of PVP and poly (melamine-co-formaldehyde) the performance has been changed. We obtained the best performance with the mobility of 0.12cm2/V sec and the on/off current ratio of $1.19{\times}10^6$ for the case of $10wt\%$ PVP copolymer mixed with $5wt\%$ poly(melamine-co-formaldehyde). Additionally using OTFTs with the above PVP gate insulator, we fabricated the integrated circuit including inverter which produced the gain of 5.56 on the glass substrate and gain of 9.7 on the plastic (PET) substrate. And the threshold voltage was respectively +8V and +14v$ldots$

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.1
• /
• pp.30-34
• /
• 2007

[ $TiO_2/PVP$ ] nanofibers were electrospun by varying the collector grounding design to improve the axial alignment of fibers. The collectors are composed of two pieces of conductive substrates separated by a gap f3r the uniaxial alignment of fibers (X design). The collectors consisting of two sets of substrates placed by $90^{\circ}$ (XY design) equipped with a timer are also prepared for biaxial alignment of fibers. Both collectors show that the charged nanofibers are stretched to span across the gap between the electrodes. Experimental results reveal that the latter collector is more effective on the directionality of electrospun $TiO_2/PVP$ nanofibers due to the dissipation of accumulated electric charge between the collectors.