• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.354-360
• /
• 2005

Polyvinyl alcohol (PVA) hydrogels were prepared by the irradiation and heating. Irradiation and heating processes were carried out to improve the heat resistance of PVA hydrogels at high temperature. The physical properties such as gel content, degree of swelling and gel strength for the synthesized hydrogels were examined. The structure variations were investigated using the following techniques: differential scanning calorimetry (DSC) and X-ray diffraction (XRD). Gel content and gel strength of the hydrogels were higher when the two steps of irradiation followed by heat treatment were used rather than only with the irradiation. The hydrogels prepared by the irradiation and the two steps had good heat resistance at high temperature.

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.270-278
• /
• 2001

Hydrogels for wound dressing were manufactured using poly(vinylalcohol)(PVA) and poly(N-vinylpyrrolidone)(PVP). The hydrogels were obtained by exposing to $^{60}$ Co${\gamma}$-rays after freezing and thawing of aqueous solutions of PVA and PVP to improve mechanical strength. Mechanical properties such as gelation, water absorptivity and gel strength were examined after repeating the \"freezing and thawing\" of PVA/PVP hydrogels, and then irradiating them at 40 kGy. The PVA/PVP ratio was in the range of 30:70 ~ 100:0, and the solid concentration of PVA/PVP was 20 wt%. The gelation and strength of hydrogels were much higher when \"freezing and thawing\" and the irradiation process were used than when only the irradiation process was utilized. In addition, the mechanical properties of PVA/PVP hydrogels after repetition of \"freezing and thawing\" are discussed. thawing\" are discussed.ssed.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.728-735
• /
• 2001

In this study, hydrogels from mixtures of chitosan/poly(vinyl alcohol) (PVA) and chitosan/poly(N-vinylpyrrolidone) (PVP) were prepared by ${\gamma}$-ray irradiation, and the mechanical properties such as gelation, water absorptivity and gel strength were examined to evaluate the applicability of these for wound dressing. The PVA : chitosan and PVP : chitosan ratio were in the range of 97:3 ~ 90:10, and the solid concentration of PVA/chitosan and PVP/chitosan solution were 15 wt%. Gamma irradiation with doses of 25, 35, 50, 60 and 70 kGy, was exposed to mixtures of PVA/chitosan and PVP/chitosan to evaluate the effect of irradiation dose. Gel content and gel strength increased as chitosan concentrations in PVA/chitosan and PVP/chitosan decreased, and as irradiation dose increased. Swelling degree increased as chitosan concentrations in PVP/chitosan and PVA/chitosan increased, and as irradiation dose decreased.

• Clean Technology
• /
• v.20 no.3
• /
• pp.251-255
• /
• 2014

PVA gel beads were made by immobilization of thenoyltrifluoroacetone (HTTA) and trioctylphoshineoxide (TOPO) with poly vinyl alcohol (PVA). The prepared PVA gel beads were used for the removal of $Cu^{2+}$ from aqueous solution. The removal characteristics of $Cu^{2+}$ by PVA gel beads was found to follow the pseudo-second-order kinetic equation. The maximum removal capacity calculated from Langmuir isotherm equation was 9.59 mg/g. The optimal pH was in the range of 3.5~6. Even when the PVA gel beads were reused 5 times, the leakage of extractant and the damage of PVA gel beads was not observed.

• Polymer(Korea)
• /
• v.26 no.6
• /
• pp.792-802
• /
• 2002

In this study, hydrogels from mixtures of poly (vinyl alcohol) (PVA)/poly(N-vinylpyrrolidone) (PVP)/glycerin/chitosan were prepared by γ-ray irradiation and the mechanical properties such as gelation, water absorptivity, and gel strength were examined to evaluate the applicability of these for wound dressing. Then PVA:PVP was weight ratio of 6 : 4, the concentration of chitosan was 0.3 wt%, the concentration of glycerin was in the range of 0∼5 wt%t. The solid concentration of PVA/PVP/glycerin/chitosan solution was 15 wt%. Gamma irradiation doses of 25, 35, 50, and 60 kGy were exposed to a mixture of PVA/PVP/glycerin/chitosan to evaluate the effect of irradiation dose. Gel content and gel strength increased as glycerin concentration in PVA/PVP/glycerin/chitosan decreased, and as irradiation dose increased. Swelling degree increased as glycerin concentration in PVA/PVP/glycerin/chitosan increased, and as irradiation dose decreased. The glycerin in PVA/PVP/glycerini/chitosan hydrogel prevented the transformation of shape. These hydrogel dressings had better curing effect than vaseline gauge.

• Polymer(Korea)
• /
• v.32 no.6
• /
• pp.587-592
• /
• 2008

High molecular weight poly(vinyl alcohol) (PVA) hydrogel to be expected as a candidate material for the wound-dressing was successfully prepared by electron beam (EB) irradiation. To produce PVA hydrogels with various gel fractions, degrees of swelling in water, gel strengths, and elongations, two different number-average degrees of polymerization [($P_n$)s] of PVA were adapted such as 1700 and 4000, and the PVA solution concentration and irradiation dose of EB were controlled to range of 5 $\sim$ 20% and 30 $\sim$ 100 kGy, respectively. The gel fraction and strength of PV A hydrogel were increased with increasing molecular weight of PVA, solution concentration, and irradiation dose of EB. On the contrary, the degree of swelling and elongation of PVA hydrogel were decreased. The thermal property and crystallinity related to degree of crosslinking of PVA hydrogel were examined by the analyses of differential scanning calorimetry and X-ray diffraction.

• Applied Microscopy
• /
• v.31 no.2
• /
• pp.117-128
• /
• 2001

DMF is not a good solvent for PVA. There is no solvent-PVA interaction such as H-bonding. DMF/PVA makes a UCST system. DMF/PVA makes a gel through crystallization-induced gelation. X-ray, thermal analysis, and other experimental proofs are presented. The gelation rate was faster at low temperature. Small addition of PEG increased the rate of gelation, but urea decreased the rate. SEM showed the phase demixing process very clearly. In the early stage of gelation, only phase demixing was occurring at a low rate. Hence, no holes appear in the early stage photographs. As demixing proceeded further, the holes began to appear and the sizes became bigger. DMF phase remains many holes after vaporization and PVA phase constitute the matrix phase.

• Composites Research
• /
• v.35 no.2
• /
• pp.98-105
• /
• 2022

In this study, polyvinyl alcohol (PVA)/graphene oxide (GO)/iron oxide (Fe₃O₄) magnetic microgels were prepared using a microfluidic approach and the dye adsorption capacity of the microgels was confirmed. The adsorption capacity (q_e) of the gels was evaluated by varying the dye concentration, pH, and contact time with the microgels. The dyes used in this work were methylene blue (MB), crystal violet (CV), and malachite green (MG), and microgels showed the highest adsorption capacity (191.1 mg/g) in methylene blue. The microgels exhibited the highest adsorption capacity in the dye aqueous solution at pH 10 due to the presence of atomic nitrogen ions (N⁺) on the dye molecules. The adsorption isotherm studies revealed that the Langmuir isotherm is the best fit isotherm model for the dye adsorption on the microgels, indicative of monolayer adsorption. The kinetic analysis exhibited that the pseudo-second order model fits better than the pseudo-first order model, confirming that the adsorption process is chemisorption. In addition, the magnetic microgels showed good reusability and recovery efficiency. It was confirmed that the adsorption capacity of the gels maintains more than 70% of the initial capacity after 5 times of cycle experiments.

• Membrane Journal
• /
• v.22 no.3
• /
• pp.208-215
• /
• 2012

Gel polymer electrolyte membranes were prepared from blends of polyvinyl alcohol (PVA) and poly (acrylic acid) (PAA), by solution-cast technique. The PAA content in the blend varied from 30 to 80 wt%. With the gel polymer electrolyte membranes, Zn air batteries were fabricated. The gel polymer electrolyte membranes were characterized by means of stress-strain test, impedance test. The Zn air batteries were tested by current interrupt method and galvanostatic discharge method. The tensile strength and tensile modulus decreased with increasing PAA content in the gel polymer electrolyte membrane. On the other hand, the ionic conductivity increased with increasing PAA content. The effect of ionic conductivity trend of the gel polymer electrolyte membrane in the Zn air battery was confirmed through current interrupt method and galvanostatic discharge method experiments. The battery with higher PAA content gel polymer electrolyte membrane showed lower IR drop and higher discharge capacity.

• Proceedings of the Korean Fiber Society Conference
• /
• 2002.04a
• /
• pp.215-218
• /
• 2002

Poly(vinyl alcohol)(PVA)는 1924년 W. O. Herrmann과 W. Haehnel이 Poly(vinyl esters)를 caustic soda 용액에서 비누화하여 합성한 뒤 많은 연구 및 사용되어지고 있는 고분자이다. 환경친화적이고, 인체에 무해하여 인공관절, 콘택트 렌즈 등에 이용이 되고 있다. 특히 구조가 선형적이고 zig-zag구조를 가지기 때문에 고강도, 고탄성을 갖는 섬유의 제조가 가능한 소재이다[1]. PVA섬유의 제조는 용매를 이용한 습식방사 및 겔방사로 섬유를 제조한다. (중략)