• Journal of Adhesion and Interface
• /
• v.18 no.1
• /
• pp.25-32
• /
• 2017

For application to display module junction process, the silk screen printing based on UV curable acrylic pressure sensitive adhesive(PSA) with silica nano-particles and the rheological properties were studied to investigate the effect on printability and adhesion. The monomers for PSA were based on 2-ethylhexyl acrylate(2-EHA) and acrylic acid(AA) 93:7, butyl acylate(BA), 2-hydroxyethyl acrylate(2-HEA) and tetrahydrofurfuryl acrylate(THFA) were added. Additionally, hydrophobic and hydrophilic nano-particles AEROSIL R974 and AEROSIL 200 were added, respectively. When the ratio of nano-particle was used above 4 or 7 phr, G' and ${\eta}^*$ were increased significantly. When the ratio of AEROSIL 200 was used above 7 phr, the penetration property was decreased during the silk screen printing. We found that the adhesion was decreased with increasing the nano-particle content, and it was decreased in the case of the hydrophilic nano-particle AEROSIL 200.

• Journal of Adhesion and Interface
• /
• v.14 no.2
• /
• pp.88-94
• /
• 2013

Because of recent requirement for environmentally-friendly adhesive, water and/or alkali soluble pressure sensitive adhesives are being developed and produced. Our research laboratory newly developed the test method for measuring the water and alkali solubility of the adhesives. Also, we made the test method published both in KS and ISO. In this research, the test of measuring the water and/or alkali solubility of the test adhesive samples as a function of time at various temperatures was carried out using the proposed test method. The results showed this proposed test method made stable output data for the change of solubility as a function of time in the proper range of temperature.

• Journal of Adhesion and Interface
• /
• v.9 no.1
• /
• pp.22-27
• /
• 2008

The effect of functional monomers on the acrylic pressure sensitive adhesive (PSA) property was measured. Design of experiments in order to optimal peel adhesion was applied and commercial program (MINITAB) was used. Analysis was used to mixture design (special cubic model) in response surface methodology. Optimal monomer compositions was construed by 2-EHA (0.8861), EA (0.0639), MAA (0.03) and AAm (0.02). The estimated regression equation was as follows : $$y=54.8816x_1+80.7067x_2-44.4700x_3-99.0288x_1x_2+60.7706x_1x_3-441.030x_2x_3+974.341x_1x_2x_3$$.

• Polymer(Korea)
• /
• v.32 no.4
• /
• pp.313-321
• /
• 2008

Acrylic pressure sensitive adhesive(PSA) was prepared by UV radiation curing and the peel energy and physical properties of PSA were investigated. The increase of amount of acrylic acid leads to improve the peel energy, associated with the substrate having smooth surface and high layer thickness. The high peel energy is obtained when the direction of irregularity in substrate is horizontal with the peeling direction. This is attributed to the increase of resistance to peeling in spite of decrease of wetting and the result corresponds to our supposition.

• Journal of Pharmaceutical Investigation
• /
• v.29 no.4
• /
• pp.343-348
• /
• 1999

The purpose of this study is to prepare the controlled release adhesive patch containing naproxen. Pressuresensitive adhesive (PSA)-type patch was fabricated by casting of polyisobutylene (PIE.) and mineral oil in toluene. Membrane-controlled release (MCR)-type patch was prepared by the attachment of the controlled release membrane on the PSAtype patch. The membrane was mainly composed of Eudragit, polyethylene glycol(PEG) and glycerin. The drug release profile and skin permeation test with various patches were evaluated in vitro. The release of naproxen from PIE-based PSAtype patch with various loading doses fitted Higuchi's diffusion equation. However, the permeation of naproxen through hairless mouse skin from PSA-type patch followed zero-order kinetics. In MCR-type patch, thickness of controlled release membrane affected on the drug release rate highly. In the composition of membrane, the release rate was decreased as the ratio of Eudragit increased. The drug release from the MCR-type patch followed zero order kinetics. The permeation of naproxen through hairless mouse skin from MCR-type patch showed lag time for the intial release period and didn't fit the zero-order kinetics

• Journal of Adhesion and Interface
• /
• v.10 no.1
• /
• pp.1-10
• /
• 2009

The waterborne acrylic pressure-sensitive adhesive in the basis of butylacylate (BA) and 2-Ethylhexylacrylate (2-EHA) was synthesized and the methyl methacrylate (MMA) have been used to give the rigidity perfroamce. The polymreric latex was synthesized using butyl acrylate (BA), 2-ethylhexyl acrylate (EHA), methyl methacrylate (MMA) and each 1, 2, 3% of various functional monomers. The dimethyl-2-imidazlidon acrylate and 2-acrylamido-2-methyl-1-propanesulfonate was used in order to increase the wetting properties of acrylic emulsion. To study of properties of functional monomer, The polymreric latex was synthesized various functional monomers each 1, 2, 3%. The 2-acrylamido-2-methyl-1-propanesulfonate showed the best properties. Latex with acrylic acid and dimethyl-2-imidazlidon acrylate had good peel strength, holding power, but it showed that they didn't separate from adhered cleanly by weak cohesion strength. The adhesion performance was increased by increasing amount of 2-acrylamido-2-methyl-1-propanesulfonate however latexes with upper 7% 2-acrylamido-2-methyl-1-propanesulfonate showed that the properties of PSA decreased.

• Journal of Adhesion and Interface
• /
• v.5 no.4
• /
• pp.1-8
• /
• 2004

UV-curable pressure sensitive adhesives were prepared by blending acrylic copolymer, copolymerized with butyl acrylate, acrylic acid and methyl methacrylate by solution polymerization, and trimethylolpropane triacrylate. The PSAs were evaluated by adhesion strength with varying UV dose, and also glass transition temperature ($T_g$) of PSAs were measured. When exposed on UV irradiation, the PSAs showed the decreased adhesion strength and increased $T_g$. And following UV irradiation, the PSAs did not leave any residue on wafer after peel off PSA.

• Journal of Convergence for Information Technology
• /
• v.7 no.4
• /
• pp.75-81
• /
• 2017

The design trend of information technology is quickly changed with the times. The design trend of information display is a bezel-less display, recently. The bezel-less display or edge-less display is a new trend of mobile phone display. In this study, the shading tape was manufactured for assembling process of touch panel display with the high screen-to-body ratio so-called bezel-less display. The shading tape was fabricated on PET film with the UV curable acrylic pressure sensitive adhesive(PSA) by roll-to-roll process. The UV curable PSA was synthesized with the eco-friendly toluene-less manufacturing method. The adhesive power of manufactured shading tape was investigated by motorized tensile testing machine. The thixotropic, maintaining property of cutting shape, was characterized by field emission scanning electron microscope. As results, the shading tape exhibits high adhesive power and good thixotropic performance suitable for assembly process of touch panel display. The functional shading tape will be expected to improve productivity of assembly process of touch panel display.

• Applied Chemistry for Engineering
• /
• v.28 no.5
• /
• pp.539-546
• /
• 2017

In this study, an outstanding anion exchange chemical filter was prepared for acidic gas removal. Commercial anion exchange resin was attached to polyurethane (PU) foam by using different types of pressure sensitive adhesive (PSA). The water and chemical resistance and also adhesive elongation were investigated. Also, the behavior of HCl and HF adsorption was evaluated as functions of the initial concentration and flow rate. ATE-701, AT-4000C and HCA-1000 showed 900, 1,500% and 2,400% of the elongation, respectively. It was confirmed that the desorption ratio of HCA-1000 was less than 6% and had excellent durability in water and chemical resistance tests. The adsorption occurred faster as the concentration and flow rate of HCl and HF increased. But 100% adsorption equilibrium occurred after 110 minutes, regardless of the concentration and flow rate. In addition, SEM morphology showed that the adhesive was uniformly dispersed, while the porous structure of the ion exchange resin was maintained, and the chemical filter exhibited excellent durability for the adsorption/desorption process.

• Journal of Adhesion and Interface
• /
• v.8 no.2
• /
• pp.15-21
• /
• 2007

To prepare a natural rubber-based pressure-sensitive adhesive (PSA) for protection film of opto- functionalized sheet, natural rubber (NR) was blended with a DCPD type tackifier and three types of aliphatic hydrocarbon resins, respectively. Also, to supply low cohesion strength of NR, in the fixed ratio of tackifier, synthetic rubber, styrene-isoprene-styrene (SIS) block copolymer was blended with NR as a function of SIS contents. PSA performance of prepared PSAs was evaluated using probe tack and peel strength. Probe tack of NR/tackifier blends was increased with increasing tackifier contents, and showed maximum peak. In addition, probe tack of NR/tackifier blends slightly increased with increasing softening point of aliphatic hydrocarbon resins. Their peel strength increased up to 50 wt% of tackifier contents, but in the over contents of tackifier, they showed stick-slip failure mode. Finally, probe tack of NR/SIS/tackifier blends showed the maximum values at 20~40 wt% of tackifier contents, but at 20 wt% of tackifier contents, they showed fibrillation. For this reason, peel strength showed maximum values at 40 wt% of tackifier contents.