• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.2 s.35
• /
• pp.155-159
• /
• 2005

In this report, Polymer light emitting diodes (PLEDs) with an ITO/PEDOT:PSS/MEH-PPV/Al structure were prepared by spin coating method on the glass substrate patterned ITO (indium tin oxide), using PEDOT:PSS(poly(3,4=ethylenedioxythiophene):poly(styrene sulfolnate)) as the hole transfer material and MEH-PPV(poly(2-methoxy-5-(2-ethyhexoxy)-1,4-phenylenvinylene)) having a different concentration (0.1, 0.3, 0.5, 0.7, 0.9, 1.5 wt$\%$) as the emitting material. The electrical and optical properties of the prepared PLED samples were investigated. The good electrical and optical properties were observed for the PLED samples with a MEH-PPV concentration ranging from 0.5 to $0.9 wt\%$. However, the current and luminance values for PLED sample with $1.5 wt\%$ of MEH-PPV decreased greatly. The maximum luminance and light efficiency for the PLEDs with concentration of $0.5 wt\%$ MEH-PPV were $409 cd/m^2$ and 4.90 Im/W at 9 V, respectively. The emission spectrums were found to be $560{\~}585 nm$ in wavelength showing orange color.

• Polymer(Korea)
• /
• v.37 no.6
• /
• pp.736-743
• /
• 2013

Novel carbazole based copolymers were synthesized by Suzuki coupling polymerization. (Diphenylene)vinylene and n-octyl was introduced to carbazole as pendants for reducing band gap and improving solubility, respectively. Thermal, photoluminescence and electro-luminescence of copolymers were studied for applying the emitting layer of polymer light emitting diode (PLED). Maximum UV-vis absorption and photoluminescence (PL) emission wavelength of copolymers showed 333~340 nm and 409~464 nm in solution state, respectively. The relative quantum yield using 9,10-diphenylanthracene as a reference was 25.8%. These copolymers exhibited high thermal stability ($T_d$ = $350^{\circ}C$) and good film forming ability. Good luminance was obtained at voltages lower than 8 V and the onset voltage was observed at 4.0 V.

• Journal of the Semiconductor & Display Technology
• /
• v.7 no.2
• /
• pp.49-53
• /
• 2008

The yellow base polymer light emitting diodes(PLEDs) with double emission and hole blocking layers were prepared to improve the light efficiency. ITO(indium tin oxide) and PEDOT : PSS[poly(3,4-ethylenedioxythiophene) : poly(styrene sulfolnate)] were used as cathode and hole transport materials. The PFO[poly(9,9-dioctylfluorene)] and MEH-PPV[poly(2-methoxy-5(2-ethylhe xoxy)-1,4-phenylenevinyle)] were used as the light emitting host and guest materials, respectively. TPBI[Tpbi1,3,5-tris(N-phenylbenzimidazol-2-yl)benzene] was used as hole blocking layer. To investigate the optimization of device structure, we prepared four kinds of PLED devices with different structures such as single emission layer(PFO : MEH-PPV), two double emission layer(PFO/PFO : MEH-PPV, PFO : MEH-PPV/PFO) and double emission layer with hole blocking layer(PFO/PFO : MEH-PPV/TPBI). The electrical and optical properties of prepared devices were compared. The prepared PLED showed yellow emission color with CIE color coordinates of x = 0.48, y = 0.48 at the applied voltage of 14V. The maximum luminance and current density were found to be about 3920 cd/$m^2$ and 130 mA/$cm^2$ at 14V, respectively for the PLED device with the structure of ITO/PEDOT : PSS/PFO/PFO : MEH-PPV/TPBI/LiF/Al.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.35-38
• /
• 2003

Polymer light emitting diode (PLED) with an ITO/MEH-PPV/Al structure were prepared by spin coating method on the ITO (indium tin oxide)/glass substrates, using poly(2-methoxy-5-(2-ethylhexoxy)-1,4-phenylenevinylene (MEH-PPV) as the light emitting material. The dependence of heat treatment on the electrical and optical properties for the prepared PLED samples were investigated. The luminance decreased greatly from 630 cd/$\m^2$ to 280 cd/$\m^2$ at 10V input voltage as the heating temperature increased from $65^{\circ}C$ to $170^{\circ}C$. In addition, the luminance efficiency was found to be about 2 lm/W for the sample heat treated at $65^{\circ}C$. These results may be related to the interface roughness and/or the formation of an insulation layer, which is caused by the reaction between electrode and MEH-PPV organic luminescent film layer.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2003.07a
• /
• pp.153-156
• /
• 2003

Thermal annealing of a polymer light-emitting diode (PLED) is shown to result in a remarkable improvement in the long-term stability of the device. The best half-life is obtained at an annealing temperature above the $T_g$ of emitting polymer. It is shown that the annealing of the emitting polymer layer results in a more than an order of magnitude increase in the half-life in spite of a decrease in the efficiency of the device as the annealing temperature increases.$^1$

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.2
• /
• pp.23-28
• /
• 2008

To improve the external quantum efficiency by means of the optimization of the polymer light emitting diodes(PLEDs) structure, the PLED with ITO/PEDOT:PSS/(PFO)/PFO:MEH-PPV/LiF/Al structure were fabricated and investigated the electrical and optical properties for the prepared devices. ITO(indium tin oxide) and PEDOT:PSS [poly (3,4-ethylenedioxythiophene): poly(styrene sulfolnate)] were used as transparent anode film and hole transport materials, respectively. PFO[poly(9,9-dioctylfluorene)] and MEHPPV[poly(2-methoxy-5(2-ethylhe xoxy)-1,4-phenylenevinyle)] were used as the light emitting host and dopant materials. The doping concentration of MEH-PPV was 9wt% with thickness of about $400{\AA}$. We investigated the dependence of the PFO thickness ranging from $200{\AA}$ to $300{\AA}$ on the electrical, optical properties of PLEDs. Among prepared PLED devices with different PFO thicknesses, the highest value of the luminance was obtained for the PLED device with $250{\AA}$ in thickness. As a result, the current density and luminance ware found to be about $400mA/cm^2$ and $1500cd/m^2$ at 13V, respectively. In addition, the luminance and current efficiency of PLED device with double emitting layer (PFO/PFO:MEH-PPV) were improved about 3 times compared with the one with single emitting layer (PFO:MEH-PPV).

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.3
• /
• pp.124-129
• /
• 2015

Organic electronics are the domain in which the components and circuits are made of organic materials. This new electronics help to realize electronic and optoelectronic devices on flexible substrates. In recent years, organic materials have replaced conventional semiconductors in many electronic components such as, organic light-emitting diodes (OLEDs), organic field-effect transistors (OFETs) and organic photovoltaic (OPVs). It is well known that organic light emitting diodes (OLEDs) have many advantages in comparison with inorganic light-emitting diodes LEDs. These advantages include the low price of manufacturing, large area of electroluminescent display, uniform emission and lower the requirement for power. The aim of this paper is to model polymer LEDs and OLEDs made with small molecules for studying the electrical and optical characteristics. The purpose of this modeling process is, to obtain information about the running of OLEDs, as well as, the injection and charge transport mechanisms. The first simulation structure used in this paper is a mono layer device; typically consisting of the poly (2-methoxy-5(2'-ethyl) hexoxy-phenylenevinylene) (MEH-PPV) polymer sandwiched between an anode with a high work function, usually an indium tin oxide (ITO) substrate, and a cathode with a relatively low work function, such as Al. Electrons will then be injected from the cathode and recombine with electron holes injected from the anode, emitting light. In the second structure, we replaced MEH-PPV by tris (8-hydroxyquinolinato) aluminum (Alq₃). This simulation uses, the Poole-Frenkel -like mobility model and the Langevin bimolecular recombination model as the transport and recombination mechanism. These models are enabled in ATLAS- SILVACO. To optimize OLED performance, we propose to change some parameters in this device, such as doping concentration, thickness and electrode materials.

• Proceedings of the KAIS Fall Conference
• /
• 2008.05a
• /
• pp.184-185
• /
• 2008

본 연구에서는 ITO/PEDOT:PSS//PFO:MEH-PPV/LiF/Al 구조를 갖는 고분자 유기발광다이오드를 제작하여 발광 도펀트인 MEH-PPV의 농도에 따른 황색 PLED 소자의 전기 광학적 특성에 대하여 조사하였다. MEH-PPV의 농도를 각각 6, 7, 8, 9, 10 wt% 로 변화시켜 소자를 평가한 결과 9 wt%의 농도에서 가장 우수한 전기 및 광학적 특성을 보였으며, 16 V의 인가전압에서 약 630 cd/$m^2$의 휘도 특성과 256 mA/$cm^2$의 전류밀도 특성이 관찰되었다. 또한 10 wt%의 소자에서는 오히려 낮은 광학적 특성이 관찰되어 9 wt%에서 도펀트의 농도가 포화됨이 관찰되었고, 제작된 소자의 색좌표 (CIE coordiante)는 모든 소자에서 (x, y = 0,49, 0.49)로 거의 동일하게 나타났다.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.4
• /
• pp.79-83
• /
• 2011

White phosphorescence polymer light emitting diodes (WPhPLEDs) with a glass/ITO/PEDOT:PSS/PFO:$Ir(ppy)_3$:MDMO-PPV/TPBI/LiF/Al structure were fabricated to investigate the effects of $Ir(ppy)_3$ doping concentrations on the optical and electrical properties of the devices. PFO, $Ir(ppy)_3$ and MDMO-PPV conjugated polymers as host and guest materials in the emission layer were spin coated at various concentrations of $Ir(ppy)_3$ ranging from 0.0 to 20.0 vol.%. As the concentration of $Ir(ppy)_3$ increased from 5.0 to 20.0 vol.%, the luminance and current efficiency values of the devices decreased clearly, which are attributable to the quenching effect at a high doping concentration. The maximum luminance and current density were 2850 $cd/m^2$ and 741 $mA/cm^2$, respectively for a WPhPLED with an $Ir(ppy)_3$ concentration of 5.0 vol.%. The CIE color coordinates were about x=0.33 and y=0.34 at 11V, showing a good white color.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1511-1514
• /
• 2009

Organic light emitting layer in OLED device was formed by gravure printing process in this work. Organic surface coated by gravure printing typically showed relatively bad uniformity. Thickness and roughness control was characterized by applying various mixed solvents in this work. Poly (N-vinyl carbazole) (PVK) and fact-tris(2-phenylpyridine)iridium($Ir(ppy)_3$) are host dopant system materials. PVK was used as a host and Ir(ppy)3 as green-emitting dopant. To luminance efficiency of the plasma treatment on etched ITO glass and then PEDOT:PSS spin coated. The device layer structure of OLED devices is as follow Glass/ITO/PEDOT:PSS/PVK+Ir(ppy)3-Active layer /LiF/Al. It was printed by gravure printing technology for polymer light emitting diode (PLED). To control the thickness multi-printing technique was applied. As the number of the printing was increased the thickness enhancement was increased. To control the roughness of organic layer film, thermal annealing process was applied. The annealing temperature was varied from room temperature, $40^{\circ}C$, $80^{\circ}C$, to $120^{\circ}C$.