• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.464-467
• /
• 1999

The undoped-InSe and Sn-doped InSe single crystals were grown by vertical Bridgman method and their properties were invesigated. The orientations and the crystallinites of these crystals were identified by X-ray diffraction(XRD), double crystal rocking curve(DCRC) and etch-pit density(EPD) measurements. From the Raman spectrum at room temperature, TO, LO modes and together with their overtones and combinations were observed. Optical properties were inves ated by PL at 12K and direct band gap of these crystals obtained from optical absorption spectrum. Compared with undo&-InSe, electrical properties of Sn-doped InSe were increased and the electrical conductivity type were n-type. But electrical properties along growth direction of crystals and radial direction of wafer showed nearly uniform distribution. The Zn diffusion mechanism in InSe could be explained by interstitial-substitutional and vacancy complex models and the activation energy of 1.15-3.01eV were needed for diffusion.fusion.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.3-4
• /
• 2002

The stainless steel sheathed MgB$_2$ tapes with Cu addition were fabricated by PIT method without heat treatment. The $J_{c}$ value of 5,600 A/ $cm^{2}$and 16,000 A/$cm^{2}$ at 4.2 K and 5 T were obtained for the $MgB_{2}$ tape and 10 vol % of Cu added $MgB_{2}$ tape respectively. The $J_{c}$-B curve shows enhancement in J$_{c}$ under magnetic field, which suggests enhancement in flux pinning property with Cu addition.n.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.11
• /
• pp.1028-1034
• /
• 1998

Bi-2223 superconductor is known as one of the candidates for practical superconducting wires. Ag-sheathed Bi-2223 superconducting wires were fabricated using the powder-in-tube(PIT) method. When the 19-filaments wire was immersed in liquid nitrogen(77K), maximum critical current density Jc of 62 A/$mm_2$ at 0T was achieved. The critical current density has been shown to depend on the mechanical properties such as tensile stress and bending strain in Ag-sheathed Bi-2223 superconducting wires. The tensile strain for Jc degradation onset was in the range of 0.12~0.3%. In the case of 19-filaments wire, the bending strain is estimated to be smaller than 0.3% for the reasonable Jc value. The observed degradation of the critical current density due to strain effect is inevitable and can be attributed to the formation of microcracks within the superconducting core.

• Tunnel and Underground Space
• /
• v.2 no.1
• /
• pp.102-115
• /
• 1992

Blasting operations associated with rock excavation work may have an environmental impact in nearby structures or human beings. With the increase of construction work in urban areas, vibration problems and complaints have also increased. In order to determine the optimum design parameters for safe blast, it is essential to understand blast mechanism, design variables involved in blast-induced damage, and their effects on the blasting results. This paper deals with the characteristics of ground vibrations, air blast and fly rock caused by blast, including the general method of establishing the vibration predictors, and damage criteria suggested by various investigators. The results of field measurements from open pit mine and tunnel construction work are discussed. Basic concepts of how to design blast parameters to control the generation of ground vibrations, air blast and fly rock are presented.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.62-69
• /
• 1995

In order to investigate the effect of TiN coating on corrosion fatigue behavior of metal, the rotary bending corrosion fatigue tests were carried out in 3% NaCl solution by using the round bar specimens of high-speed steel, SKH-9, coated with TiN by PVD method. From the experimental results, fatigue strength of TiN coating steel in air was obvious improvement as compared with that of the substrate because of the restriction of dislocation movement in near surface of the substrate by hard thin film. In 3% NaCl solution, corrosion fatigue life of TiN coating specimen in high stress level was improvement same as in air. But in low stress level, corrosion fatigue life of TiN coating one was equivalent to that without coating, due to much crack initiated from corrosion pits formed at the substrate by failure of coating layer.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2001.02a
• /
• pp.145-148
• /
• 2001

Bi-2223/Ag HTS tapes fabricated by PIT process are used to make the power transmission cable, motor, fault current limiter, transformer etc. But some problems are still remained as like bubbling, sausaging to got the high Jc. In this study. we carried out the experiment to prevent bubbling in the HTS tape. The bubbling mainly occurred when HTS tape was heat-treating. Therefore, additional vacuum annealing at 400 ~ $600^{\circ}C$and slowly ramp-up sintering method were used to decrease the bubbling. slowly ramp-up sintering was more effective to decrease the bubbling than the vacuum annealing, but Jc was also decreased after heat treatment. Optimum ramp-up sintering schedule was searched to get the high critical current and prevent bubbling at same time.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.11 s.170
• /
• pp.2096-2101
• /
• 1999

This paper presents the effect of shape of external corrosion in pipeline on failure prediction by using numerical simulation. The numerical study for the pipeline failure analysis is based on the FEM(Finite Element Method) with an elastic-plastic and large-deformation analysis. The predicted failure stress assessed for the simulated corrosion defects having different corroded shapes along the pipeline axis are compared with those by methods specified in ANSl/ASME B31G code and a modified B31G code.

• Explosives and Blasting
• /
• v.8 no.4
• /
• pp.3-22
• /
• 1990

The $\varphi{4.5}$ meters pilot tunneling work is almost done to the $\varphi{11.3}$ meters twin tunnel of NAM SAN No1. The south side pit of 400 meters is weak zone of Rock status, so client request us to allow the cautious blasting pattern for drilling on the condition of 0.2 kine vibration allowance limited for the safety of side running tunnel. The pattern of cautious blasting carried out by 6 time divided fiving on the round drilling depth of 1.20 meters(1.10) and also applied control blasting method with line drilling due to the reduction of vibration.

• Journal of Sericultural and Entomological Science
• /
• no.11
• /
• pp.55-57
• /
• 1970

There are many reports concerning to the restoring times, and the range of times are very wide. Author restored the artificial hatching silkworm eggs 1 ice pit (5$^{\circ}C$) two different method; one restored in directly after protected following different times 24 hours, 48 hours and 72 hours of room temperature (24$^{\circ}C$), another protected above suggested times and room temperature then indirectly keeping medium temperature (1$0^{\circ}C$)6 hours. It was incubated in $25^{\circ}C$ temperature after about 20 days of restoring. Pure line and hybrid silk warm eggs are no difference hatching ratio in 72 hours blocks by restoring. Especially good hatching ratio obtained by the medium temperature treatment rather than directly restoring.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2000.02a
• /
• pp.3-5
• /
• 2000

Among the various processing techniques used in HTS wire fabrication, the PIP(Powder In Tube) method is currently one of the most promising for applications on an industrial scale. In this study, we have fabricated Bi-2223/Ag superconducting tapes using the modified PIT process, where several process factors were changed and improved, ie., powder packing, drawing, rolling and heat treatment. We obtained Bi-2223 tape that have high critical current, 46 a at 77.3 K, have high critical current, 46A at 77.3 K, self field although the tape was not pressed but only rolled. The critical current of 100m class long length tape was measured 21.6A at the same criterion. Besides, the critical current of Bi-2223/Ag tape was measured applying magnetic fields with different directions at various temperatures.