• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1225-1228
• /
• 2005

Barrier ribs in the plasma display panel(PDP) function to maintain the discharge space between the glass plates as well as to prevent optical crosstalk. Patterning of barrier ribs is one of unique processes for making PDP. In this work photosensitive barrier rib pastes were prepared by incorporating binder polymer, solvent, functional monomers photoinitiator, and barrier rib powder of which surface was treated with fumed silica particles. Study on the function of materials for the barrier rib paste were undertaken. After optimization of paste formulation and photolithographic process, it was found that photolithographic patterning of barrier ribs with photosensitive barrier rib green sheet could be used in the fabrication of high resolution PDP.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04a
• /
• pp.129-132
• /
• 2000

The PDP(Plasma Display Panel) barrier rib material on the glass substrate was patterned for fabrication of the PDP cell using Nd:YAG laser(1064 nm) which can generate the second(532 nm) and forth(266 nm) harmonic wave by HGM(harmonic generation modules). At a scan speed of 20 ${\mu}m/s$ with the second harmonic wave(532 nm) of Nd:YAG laser, the etching threshold laser fluence of the PDP material was 6.5 $mJ/cm^2$ and a sample(thickness = 180 ${\mu}m$) on the glass substrate was removed clearly at a laser fluence of 19.5 $mJ/cm^2$. In order to increase the throughput of the fabrication we divided a single-beam into multi-beams by using a metal mask between the sample and the focusing lens. As a result, 10 lines of PDP cell were formed by one laser beam scanning at a scan speed of 200 ${\mu}m/s$ and a laser fluence of 2.86 $J/cm^2$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.55-58
• /
• 2004

High Xe-content PDP characteristics are discussed. A high efficacy, up to 5 lm/W for a 50% Xe in Ne gas mixture, is realized in 4-inch color PDP test panel designs with low cost stripe-type barrier rib structures, that are powder blasted in soda lime glass. Furthermore, for a high Xe-content a high luminance can be obtained with a relatively small electrode area. Therefore the inter cell gap and the driving margin can be increased in a stripe-type barrier rib structure. Finally, for a high Xe-content the panel lifetime increases, due to increasing luminance and firing voltage stability. Clearly, these findings may direct the design development for next generation PDPs towards a high Xe-content

• Journal of the Korean Ceramic Society
• /
• v.40 no.6
• /
• pp.553-559
• /
• 2003

PDP rib is one of the important parts of manufacturing process and the sintering degree of rib plays an important role to prevent some problems such as cross talk. Nowadays, the screen-printing method, which is a low price and high production, is used to make a rib. However, it is hard to judge and value the sintering ratio of sintered body itself. In this study, we measured the sintering degree by the dielectric breakdown of pores with the potentiostat. We conformed that this has similar tendency to density of sintered samples and an error being expected by open and closed pores was inspected by change of the microstructure to scanning electron microscope. This result showed that the sintering degree of PDP rib could be analyzed into the electro-chemical method.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.989-993
• /
• 2002

Barrier ribs in the color plasma display panel(PDP) function to maintain the discharge space between to glass plates as well as to prevent optical crosstalk. Patterning of barrier ribs is one of unique processes for making PDP. In this work photosensitive barrier rib pastes were prepared by incorporating binder polymer, solvent, functional monomers photoinitiator, mid barrier rib powder. Study on the function of materials for the barrier rib paste were undertaken. After optimization of paste formulation, both photolithographic and transparent soft molding method resulted in fine pattern of barrier ribs with high aspect ratio.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.73.2-73
• /
• 2000

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.184-189
• /
• 2002

This study, compared with data of PbO-base glass system is a part of new glass composition design with Bi-base composition for PDP Rib. As $Bi_2O_3-B_2O_3-ZnO$ glass composition including Bi, which have similar density value and work facility to PbO, properties of softening point, thermal expansion coefficient, chemical durability, dielectric constant, and structural changing by XPS were investigated. $Bi_2O_3-B_2O_3-ZnO$ glass system, added 50∼80 wt% $Bi_2O_3$ widely, were presented 400∼480$^{\circ}C$ softening temperature, $68{\sim}72{\times}10^{-7}/^{\circ}C$ thermal expansion coefficient and 13∼25 dielectric constant. These results were showed similar physical properties with Pb-base glass system of same composition content, application possibility as starting composition of rib material was identified through micro-control of components and physical properties. The bonding energy of $O_{1s}$ as the $Bi_2O_3$ content decreasing was increased and full width at half-maximum (FWHM) was decreased, which is caused by non-bridging oxygen increasing.

• Journal of KIEE
• /
• v.11 no.1
• /
• pp.41-45
• /
• 2001

The addressing time should be reduced by modifying cell structure and/or driving method in order to replace the dual scan system by single scan and increase the luminance in large ac plasma display panel(PDP). In this paper, the effects of the dielectric layer thickness and the barrier rib height on the addressing time of ac PDP are investigated. It is found out that the addressing time was decreased with decreasing thickness of dielectric layer on the front glass and thickness of white dielectric layer on the rear glass. The decreasing rate were 160ns/10${\mu}{\textrm}{m}$ and 270nsd/10${\mu}{\textrm}{m}$, respectively. Also in case of decreasing the height of barrier rib, addressing time was decreased at the rate of 550ns/10${\mu}m$.

• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.6
• /
• pp.176-183
• /
• 2002

Plasma Display Panel(PDP) is a type of flat panel display utilizing the light emission produced by gas discharge. Barrier Ribs of PDP separating each sub-pixel prevents optical and electrical crosstalks from adjacent sub-pixels. The mold for forming the barrier ribs has been newly researched to overcome the disadvantages of conventional manufacturing processes such as screen printing, sand-blasting and photosensitive glass methods. The mold for PDP barrier ribs have stripes of micro grooves transferring glass-material wall. In this paper , Stripes of grooves of which width 48$\mu$m, depth 124$\mu$m , pitch 274$\mu$m was acquired by machining of single crystal silicon with dicing saw blade. Maximum roughness of the bottom of the grooves was 59.6 nm Ra in grooving Si. Barrier ribs were farmed with silicone rubber mold, which is transferred from grooved Si forming hard mold. Silicone rubber mold has the elasticity, which enable to accommodate the waviness of lower glass plate of PDP. The methods assisted by the microwave and UV was adopted for reducing the forming time of glass paste.

• Journal of the Korean Ceramic Society
• /
• v.39 no.8
• /
• pp.721-727
• /
• 2002

In order to overcome trade-off among compositions, process and properties of the glasses with high PbO-base composition for PDP Rib, we studied glass crystallization and crystallization kinetics by Differential Thermal Analysis(DTA). Glass powder was obtained through melting/cooling/grinding, with 3 wt%TiO2 addition for the crystal nucleation and growth in $62PbO-19B_2O_3-10SiO_2-9(Al_2O_3-K_2O-BaO-ZnO)$(in wt%) composition glass. This powder was heat-treated for 1 to 10 h at $445^{\circ}C$ for nucleation. DTA measurements were performed to obtain the crystallization peak with $5∼25^{\circ}C/min$ heating rates. DTA crystallization peak temperature increased with increasing the heating rate and decreased with increasing the heating time. Because the Avrami parameter (n) was approximately 1, the surface crystallization occurred. The maximum nucleation time was 2 h.