• Journal of the korean academy of Pediatric Dentistry
• /
• v.25 no.1
• /
• pp.234-248
• /
• 1998

The purpose of this study was to compare the fracture and shear bonding strength of resin-modified glass ionomer cements with composite resin and conventional glass ionomer cement Three kinds of restorative materials including a composite resin (Z 100), a conventional glass ionomer cement(Fuji II), and resin- modified glass ionomer cements(Fuji II LC, Vitremer, Dyract and Compoglass) were investigated in this study. For measurement of fracture and shear bonding strength, disk samples of the materials were prepared and cylindrical samples of the materials were bonded the flat enamel and dentin surfaces according to manufactuer's instructions. All specimen were determinated by using an Instron testing machine with a crosshead speed of 1 mm/min. Then, each treated enamel and dentin surface was observed by SEM. The following results were obtained. 1. The bi-axial flexural strength of Z 100 was highest, and Fuji n LC, Vitremer, Dyract and Compoglass were significantly higher than Fuji n (P<0.05). 2. The shear bonding strength of Z 100 on the enamel and dentin surface was higher than other experimental groups except Fuji II LC(P<0.05). Fuji II LC was significantly higher than Fuji II (P<0.05), but in the case of Vitremer, Dyract and Compoglass were similar to Fuji II (P>0.05). 3. The shear bonding strength of Z 100 and Fuji II LC on the enamel surface were highly increased as compared with dentin surface (P<0.05), but in the case of Fuji II, Vitremer, Dyract and Compoglass were not different between enamel and dentin(P>0.05). 4. In the Z 100 and Fuji II LC, obvious etched enamel surface and exposed dentinal tubules according to remove of smear layer and smear plug were observed.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.4
• /
• pp.503-509
• /
• 2019

The demand for smaller, faster, and multi-functional mobile devices in increasing at a rapidly increasing rate. In response to these trends, Stacked Chip Scale Package (SCSP) is used widely in the assembly industry. A film type adhesive called die attach film (DAF) is used widely for bonding chips in SCSP. The DAF requires high flowability at high die attachment temperatures for bonding chips on organic substrates, where the DAF needs to feel the gap depth, or for bonding the same sized dies, where the DAF needs to penetrate bonding wires. In this study, the mixture design of experiment (DOE) was performed for three raw materials to obtain the optimized DAF recipe for low elastic modulus at high temperature. Three components are acrylic polymer (SG-P3) and two solid epoxy resins (YD011 and YDCN500-1P) with different softening points. According to the DOE results, the elastic modulus at high temperature was influenced greatly by SG-P3. The elastic modulus at $100^{\circ}C$ decreased from 1.0 MPa to 0.2 MPa as the amount of SG-P3 was decreased by 20%. In contrast, the elastic modulus at room temperature was dominated by YD011, an epoxy with a higher softening point. The optimized DAF recipe showed approximately 98.4% pickup performance when a UV dicing tape was used. A DAF crack that occurred in curing was effectively suppressed through optimization of the cure accelerator amount and two-step cure schedule. The imizadole type accelerator showed better performance than the amine type accelerator.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.3
• /
• pp.389-396
• /
• 2002

The purpose of this study was to compare the microtensile bonding strength of chemomechanically excavated dentin($Carisolv^{TM}$) to conventional caries removal(bur). The following adhesive systems were used; AB: All-Bond 2(3M, USA), PB: Prime & Bond 2.1(Dentsply, DE), AQ: AQ Bond(sun medical, Japan). 42 human molars with occlusal caries were assigned to 6 groups. Sequential caries removal was controlled with laser fluorescence. Each group was devided as follows; group A, B, C were $Carisolv^{TM}$ applied, group D,E,F were bur used. In group A and D, AB was used as a dentin adhesive. group B,E and group C,F was AQ and AQ was used each. The cavity was filled with composite resin(Z-100). The specimens were sectioned vertically into multiple serial 0.7 mm thick slabs. And then those slabs were sectioned into rectangular parts under 0.7 mm width. Finally 0.7-1.0 mm a right hexahedron shape stick become. Microtensile bonding test was carried out with testing apparatus at cross-head speed of $0.5\;mm/min^{-1}$ and fractured surfaces were observed with scanning electron microscope(JSM-6400, Jeol, Japan). The obtained results were summarized as follows ; 1. In the group of caries removal with $Carisolv^{TM}$, micro-tensile bonding strength decreased to $75.8{\sim}80$ percent of bur used group. 2. In the group of caries removal with $Carisolv^{TM}$, decreased degree of micro-tensile bonding strength is not so different in 3 kinds of dentin adhesives(p<0.05). 3. In the group of caries removal with $Carisolv^{TM}$, microtensile bonding strength of AB, PB, AQ was 32.6MPa(2.4), 30.1Mpa (1.8), 21.2Mpa(1.9). 4. In the group of caries removal with Bur and $Carisolv^{TM}$, microtensile bonding strength of AQ was significantly lower than that of AB and PB(p<0.01).

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.5
• /
• pp.658-671
• /
• 1999

The major influencing factors on the strength of all-ceramic crowns are types of dental ceramics, fabrication techniques, methods of abutment preparation and cementation modes of all-ceramic restorations. Zinc phosphate cement and glass-ionomer cement were used as an early lot-ing media for all-ceramic crowns. Recently many studies have reported that resin cements have more advantages in increasing the fracture strength of restorations comparing with zincphosphate cement and glass-ionomer cement. The purpose of this study is to investigate the effect of etching, silane treatment, sandblasting and dentin bonding agents on fracture strengths of dental ceramics. 40 flat dentin specimens and 40 ceramic discs of 1.5mm thickness and 8mm diameter were fabricated, and divided into 4 groups according to surface treatments. Surface treatments before cementation were as follows Group I : (ceramic) : HF etching - silane treatment - application of bonding resin (dentin) : application of dentin bonding agent Group II : (ceramic) : sandblasting - application of bonding resin (dentin) : application of dentin bonding agent Group III : (ceramic) : application of bonding resin (dentin) : application of dentin bonding agent Group IV : (ceramic) : HF etching - silane treatment - application of bonding resin (dentin) : no dentin bonding procedure Dentin specimens and ceramic discs were cemented with dual cure resin cement, and went through thermocycling. Compressive stress es were loaded on the centers of ceramic discs with Instron test-ing machine, and fracture strengths resistance for catastrophic fracture were measured The results were as follows. 1. The group I showed the highest fracture resistance. The next was group II And group III, IV followed. 2. There was a significant difference in the mean value of fracture strengths between group I and group III (p<0.05), but no significant differences between group I and group II, and group II and group III (p>0.05). 3. There was a significant difference in the mean value of fracture strengths between group I and group IV (p<0.05).

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.2
• /
• pp.129-146
• /
• 2000

An increasing demand for esthetic restorations has led to the development of new ceramic systems. In-Ceram, a glass-infiltrated alumina ceramic has three to few times greater flexural strength than other ceramic glass material. Because of its high strength, In-Ceram has been suggested as inlay, crown, laminate veneer and core material for resin bonded fixed partial dentures. This clinical application requires a stable resin bond to In-Ceram core. The purpose of this study was to evaluate the shear bond strength between In-Ceram core and resin cements according to various surface treatments and storage conditions. The surface of each In-Ceram core sample was subjected to one of the following treatments and then bonded to Panavia 21 or Variolink II resin cement. ; (1) sandblasting with $110{\mu}m$ aluminum oxide powder, (2) sandblasting and silanization, (3) sandblasting and Siloc treatment, (4) sandblasting and Targis link application. Each of eight bonding groups was tested in shear bond strengths after the following storage times and thermocycling. ; A) 24 hours storage in distilled water at $37^{\circ}C$, B) 5 weeks storage in distilled water at $37^{\circ}C$ C) 5 weeks storage in distilled water at $37^{\circ}C$ and thermocycled 2,000 thormocycling for every 10 days(totally 10,000 thermocycting) in $5^{\circ}C-55^{\circ}C$ bath. The bond failure modes were observed with scanning electron microscope(SEM). The results were as fellows : 1 The shear bond strengths of sandblasting group were significantly lesser than the other groups after 24 hours water storage. No significant difference of bonding strengths was found between storage time conditions(24 hours and 5 weeks). The shear bond strengths showed a tendency to decrease in Variolink II bonding groups and to increase in Panavia 21 bonding groups. 3. After thermocycling, the shear bond strengths of all groups were significantly decreased(p<0.01) and Targis link group exhibited significantly greater strengths than the other groups(p<0.05). 4. Panavia 21 bonding groups exhibited significantly greater bonding strengths in sandblasting group(p<0.01) and silane group(p<0.05) than Variolink II bonding groups. 5. In observation of bond failure modes, Targis link group showed cohesive failure in resin part and silane group and Siloc group showed complex failure and sandblasting group showed adhesive failure between In-Ceram and resin.

• Journal of the Korean Chemical Society
• /
• v.54 no.3
• /
• pp.275-282
• /
• 2010

2-Fluorocyclopropanemethanol and 2-chlorocyclopropanemethanol have been studied with MP2 and B3LYP methods with 6-311++G(d,p) basis set. The optimized structures show several stable conformers. The most stable conformer show the possibility of intramolecular hydrogen bonding, but the distance between $H{\cdots}F$, or $H{\cdots}Cl$ is longer than van der Waals radii and it may not be strong covalent bonding. Rather the second stable conformer has optimum structure for intramolecular hydrogen bonding but the energy of the conformer is 5 ~ 7 kJ higher than the most stable conformer. When the methanol group and the F or Cl atom have opposite direction, the conformers are less stable than the most stable conformer.

• Journal of Powder Materials
• /
• v.8 no.4
• /
• pp.258-267
• /
• 2001

In this work, the conventional transient liquid phase(TLP) bonding was modified. An attempt was made of using a liquid phase sintered alloy, which will be a liquid phase coexisting with a solid phase at the bonding temperature, as an interlayer for bonding metals. With an aim of revealing the fundamental features of this modified TLP bonding, the kinetics concerned with the growth of solid particles and the isothermal solidification process in Fe-1.16wt%B and Fe-4.5wt%P interlayers for the bonding pure iron, as well as the morphological change of the solid particle, were investigated.

• Journal of Technologic Dentistry
• /
• v.33 no.1
• /
• pp.25-35
• /
• 2011

Purpose: There are some advantages of the acrylic resin denture base ; appropriate strength, volume safety, simple processing apparatus, and low cost. But, it have a weakness for fracture by intense pressure or shock. However, the repairs for resin denture base are possible using various materials and techniques. There is a few studies in repairs for resin denture base, but not clinical researches. And there is no studies in absorbed saliva into the region of fracture and bond strength. This study is to observe re-bond strength of resin denture base after repairing under saliva absorption. Methods: The samples were made of heat curing resin and the rectangular parallelepiped specimens which were 50mm long, 10mm wide and 3mm high. The four different groups immersed in the artificial saliva for 2 weeks were prepared, 1) no repaired control samples, 2) immediately repaired samples, 3) repaired samples after 1 day dry, and 4) repaired samples after 3 days dry. The prepared samples were repaired by two different curing materials, self curing resin and heat curing resin method. Each groups composed of 10 specimens were experimented with the three point bending tests for bonding strength measuring Results: There were under condition absorbed in the artificial saliva and repaired by self curing resin method, repaired specimens after 1 day and 3 days dry groups had higher values of bonding strengths than control group, and bonding strengths of immediately repaired samples were similar to those of control samples (p<0.05). There were under condition immersed in the artificial saliva and repaired by heat curing resin method, immediately repaired samples showed similar values to bonding strengths of control groups, and repaired samples after 1 day and 3 days dry groups were lower than those of control group (p>0.05). Conclusion: In this study, the repairs for resin denture base were remarkably high values of bonding strengths than those of the past, and showed that have stable bonding strengths independent of saliva absorption of denture base, so present repairs for resin denture base can be performed, regardless of saliva conditions.

• Journal of Technologic Dentistry
• /
• v.8 no.1
• /
• pp.23-29
• /
• 1986

One of the primary advantage of acrylic resin teeth is their ability to bond chemically to the denture base resins. But, occasionally, failure have been observed in which acrylic resin teeth break lose from the denture, indicating that chemical bonding does not always occur. The most probable explanation for this type of failure was the presence of a trace of wax remaining as a residue on the surfaces of the teeth after the boiling-out procedure which adgered to the tooth surface and prevented bonding. The purpose of this stdy was preparing the specimens of denture base resin with acrylic resin teeth that four treatment method to ridge lap portion of the tooth and investigated bond between the teeth and denture base resin with tensile strength. Compared results of tensile strength on test specimens were as follows: 1. The mean of strength among the four test groups showed the difference was significant enough(P 0.01). The order of its strength mean was methylene chloride treatment group, detergent solution treatment group, kerosene-ether treatment grgoup, boiling water only group. 2. In compared results between the wax eliminating method groups, there were significant difference between the boiling water only group and other groups(P 0.01), no significant difference were found in the wax eliminating method groups except boiling water only group(P 0.05).

• Restorative Dentistry and Endodontics
• /
• v.20 no.2
• /
• pp.699-720
• /
• 1995

This study was conducted to evaluate the effect of benzalkonium chloride solution as a wetting agent instead of water on dentin bonding with NTG-GMA/BPDM system (All-bond 2, Bisco.) and DSDM system (Aelitebond, Bisco.). Benzalkonium chloride solution is a chemical disinfectant widely used in medical and dental clinics for preoperative preparation of skin and mucosa due to its strong effect of cationic surface active detergent. Eighty freshly extracted bovine lower incisor were grinded labially to expose flat dentin surface, and then were acid-etched with 10 % phosphoric acid for 15 second, water-rinsed, and dried for 10 second with air syringe. The specimens were randomly divided into 8 groups of 10 teeth. The specimens of control group were remoistured with water and the specimens of experimental groups were remoistured with 0.1 %, 0.5 %, and 1.0 % benzalkonium chloride solution respectively. And then, the Aelitefil composite resin was bonded to the pretreated surface of the specimens by use of All-bond 2 dentin bonding system or Aelitebond dentin bonding system in equal number of the specimens. The bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured, the mode of failure was observed, the fractured dentin surface were examined under scanning electron microscopy, and FT-IR spectroscopy was taken for the purpose of investigating the changes of the dentin surface pretreated with benzal konium chloride solution followed by each primer of the dentin bonding systems. The results were as follows : In the group of bonding with NTG-GMA/BPDM dentin bonding agent(All-bond 2), higher tensile bond strength was only seen in the experimental group remoistured with 0.1 % benzal konium chloride solution than that in water-remoistured control group(p<0.05). In the group of bonding with DSDM dentin bonding agent (Aelitebond), no significant differences were seen between the control and each one of the experimental group(p<0.05). Higher tensile bond strength were seen in NTG-GMAIBPDM dentin bonding agent group than in DSDM dentin bonding agent group regardless of remoistur ization with benzal konium chloride solution. On the examination of failure mode, cohesive and mixed failure were predominantly seen in the group of bonding with NTG-GMAIBPDM dentin bonding agent, while adhesive failure was predominantly seen in the group of bonding with DSDM dentin bonding agent. On SEM examination of fractured surfaces, no differences of findings of primed dentin surface between the groups with and without remoisturization with benzal konium chloride solution. FT-IR spectroscopy taken from the control and the experimental group reve::.led that some higher absorbance derived from the primers binding to dentin surface was seen at the group pretreated with 0.1 % benzal konium chloride solution than at the control group of remoisturizing with water.