• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.44 no.5
• /
• pp.72-79
• /
• 2012

In this study, to understand the aging factor and mechanism in different partitions of the beeswax-treated volumes, the duplicated beeswax-treated volume was artificially aged at $80^{\circ}C$ of temperature and 65% of relative humidity and then a physical and optical properties of an aged volumes was analyzed. Also, the degraded components of the beeswax samples isolated from different partitions of aged volumes was measured using a gas chromatography/mass spectroscopy (GC/MS). In results, the surface of beeswax-treated volume which is primarily affected by a main aging factors such as light, oxygen, moisture was more deteriorated than the inside of that volume. However, unlike inside of the book volume which was made from paper, the inside of beeswax-treated volume wax was also considerably deteriorated. The inside of the beeswax-treated volume is largely unaffected by the oxygen and humidity during aging due to the water repellency and the air permeation resistance of beeswax. Therefore, it is confirmed that aging factors and mechanisms in the inside of the volume are different from thats of the outside of the volume. This fact was also verified by the results of GC/MS analysis of an beeswax samples which was sampled from different partitions of aged volumes. As result as GC/MS analysis of the beeswax extracted from the outside of the aged volume, the low molecular compounds with a carbon length of $C_9-C_{20}$ (fatty acid, etc) were increased and the compounds with a carbon length of above $C_{34}$ (ester, etc) were also increased. But the compounds with a chain length of $C_{21}-C_{36}$ (hydrocarbon, alcohol, etc) were decreased. In case of the aged beeswax of inside, the low molecular compounds with a carbon length of $C_9-C_{20}$ (fatty acid, etc) and the compounds with a chain length of $C_{21}-C_{36}$ (hydrocarbon, alcohol, etc) were increased. While, the compounds with a carbon length of above $C_{34}$ (ester, etc) were decreased.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.2
• /
• pp.174-181
• /
• 2007

In this study, $SiO_2/poly(ethylene-co-vinyl$ alcohol)(EVOH) hybrid coating materials with gas barrier property could be produced using sol-gel method. The biaxially oriented polypropylene (BOPP) substrate with surface pretreatment was coated with the prepared hybrid sols containing various inorganic silicate component by a spin coating method. Crystallization behavior of the hybrids was investigated in terms of analysis of X-ray diffraction and cooling thermogram from DSC experiment. From the morphological observation of the $SiO_2/EVOH$ hybrid gel, it was confirmed that there existed an optimum content of inorganic silicate precursor, Tetraethylorthosilicate (TEOS), to produce hybrid materials with dense microstructure, exhibiting uniformly dispersed silica particles with average size below 100 nm. When TEOS was added at below or above the optimum content, particle clusters with large domain were observed, resulting in phase separation. This morphological result was found to be in good agreement with that of oxygen permeability of the hybrid coated films. In the case of film coated with hybrid prepared from addition of 0.01 - 0.02mol of TEOS, a remarkable improvement in barrier property could be obtained, however, with the addition of TEOS more than 0.04 mol, the barrier property was dramatically reduced because of phase separation and micro-crack formation on the film surface.

• Korean Journal of Environmental Biology
• /
• v.32 no.3
• /
• pp.216-224
• /
• 2014

Decrease in dissolved oxygen concentrations associated with temperature fluctuation is an important criteria to evaluate the mortality rate of the species. Based on this parameter, we investigated the survival rate, physiological response and histological change of warty sea squirt. It was found that the survival rate of the warty sea squirt species was 63.3% at $23^{\circ}C$ and 56.6% at $26^{\circ}C$ respectively. However, exposure of six days at $29^{\circ}C$ caused deaths among species, which indicated the 6day-$LT^{50}$ of the tested species to be $24.58^{\circ}C$ ($19.48{\sim}35.48^{\circ}C$). Further, after 11 day of exposure, the dissolved oxygen concentration has been found to decrease, with the survival rate of 20% at $4.0mg\;L^{-1}$ and deaths at $2.0mg\;L^{-1}$, thus 11day-$LC^{50}$ calculated to be $3.88mg\;L^{-1}$ ($3.29{\sim}4.57mg\;L^{-1}$). In addition, decrease in rate of oxygen consumption and excretion of ammonia was also noted at this critical water temperature and dissolve doxygen concentration. Moreover, there has been common histopathological changes were observed in warty sea squirt's gill pouch, digestive tract, and tunic as follows such as: proliferation of epithelial cells, condensation and necrosis, permeation of phagocyte and blood cell, loss of cilium and muscular fiber degeneration. Based on our study results, we suggest that these parameters can also be useful to evaluate the survival rate and physiological response in other species.

• Journal of Life Science
• /
• v.25 no.9
• /
• pp.1027-1035
• /
• 2015

A strain GP32 which produces a highly viscous extracellular polysaccharide was conducted with soil samples and identified as Pseudomonas species. The culture flask conditions for the production of extracellular polysaccharide by Pseudomonas sp. GP32 were investigated. The most suitable carbon and nitrogen source for extracellular polysaccharide production were galactose and (NH₄)₂SO₄. The optimum carbon/nitrogen ratio for the production of extracellular polysaccharide was around 50. The optimum pH and temperature for extracellular polysaccharide production was 7.5 and 32℃, respectively. In batch fermentation using a jar fermentor, the highest extracellular polysaccharide content (15.7 g/l) was obtained after 70 hr of cultivation. The extracellular polysaccharide produced by Pseudomonas sp. GP32 (designated Biopol32) was purified by ethanol precipitation, cetylpyridinium chloride (CPC) precipitation, and gel permeation chromatography. Biopol32, which has an estimated molecular weight of over 3×10⁷ datons, is a novel polysaccharide derived from sugar components consisting of galactose, glucose, gulcouronic acid and galactouronic acid in an approximate molar ratio of 1.85 : 3.24 : 1.00 : 1.42. The solution of Biopol32 showed non-Newtonian characteristics. The viscosity of Biopol32 exhibited appeared to be higher at all concentration compared to that of zooglan from Zoogloea ramigera. An analysis of the flocculating efficiency of Biopol32 in industry wastewater (food, textile, and paper wastewater) revealed chemical oxygen demand (COD) reduction rates 58.4-67.3% and suspended solid (SS) removal rates 82.6-91.3%. Based on these results, Biopol32 is a possible candidate for industrial applications such as wastewater treatment.

• Membrane Journal
• /
• v.21 no.2
• /
• pp.177-192
• /
• 2011

Hollow fiber membrane using CTA polymers were prepared by the phase separation method for the separation and purification of biogas and the hollow fiber gas separation membrane modules with the effective surface area of 0.17 $m^2$ were prepared. The pure gas permeation properties of membrane modules for methane, oxygen and carbon dioxide were measured. The permeance of $CO_2$ and $CH_4$were 0.46 GPU and 18.52 GPU, respectively, therefore, the high $CO_2$/$CH_4$ selectivity of 40.4 was obtained. The separation and purification test for 4 different simulated mixed gases were carried out after the pure gas test and the gas concentration and flux of the permeate at the various stage-cut were measured from the 1 stage, 2 stage, and 3 stage cascade of membrane modules. In the 1 stage test, the concentration of $CH_4$ increased as the increase of the stage-cut, while the $CH_4$ recovery efficiency ratio decreased. In the 2 stage test, the $CH_4$ recovery efficiency ratio increased compared to the 1 stage. The 3 stage test was employed to reduce the loss of $CH_4$ in biogas and the result showed less than 5% of $CH_4$ recovery loss.

• Journal of Korean Society of Environmental Engineers
• /
• v.37 no.3
• /
• pp.152-158
• /
• 2015

This paper investigated the membrane fouling potential at the state of passive adsorption which is no permeation with the test modules on COD (Chemical oxygen demand) loading rates, examined the recovery rate and resistance on membrane fouling by three cleaning manners of hydrophobic membrane in a bioreactor. The results showed that high COD loading led to the increase of extra-cellular polymeric substances and filtration resistance. The permeability resistance from 1st day to 63rd day was getting increased, however, the value of permeability resistance after 63th day during the operation period was almost same level at three COD loading rates, it was due that the biomass adhesion on membrane surface at the state of passive adsorption reached to the critical state. Also, the final recovery rates after three cleaning manners were 78%, 72% and 69% at the COD loading concentrations of 250 mg/L, 500 mg/L and 750 mg/L respectively, and then recovery rate by physical cleaning at Run 2 and Run 3 was decreased after 40th day, it proved that biomass cake, which is not easily removed, was formed on the membrane surface because of high COD loading rate and EPS concentration.

• Journal of Information Display
• /
• v.11 no.1
• /
• pp.8-11
• /
• 2010

In this study, a new thin films passivation technique using Zn with high electronegativity and $MgF_2$, a fluorine material with better optical transmittance than the sealing film materials that have thus far been reported was proposed. Targets with various ratios of $MgF_2$ to Zn (5:5, 4:6 and 3:7) were fabricated to control the amount of Zn in the passivation films. The Mg-Zn-F films were deposited onto the substrates and Zn was located in the gap between the lattices of $MgF_2$ without chemical metathesis in the Mg-Zn-F films. The thickness and optical transmittance of the deposited passivation films were approximately 200 nm and 80%, respectively. It was confirmed via electron dispersive spectroscopy (EDS) analysis that the Zn content of the film that was sputtered using a 4:6 ratio target was 9.84 wt%. The Zn contents of the films made from the 5:5 and 3:7 ratio targets were 2.07 and 5.01 wt%, respectively. The water vapor transmission rate (WVTR) was determined to be $38^{\circ}C$, RH 90-100%. The WVTR of the Mg-Zn-F film that was deposited with a 4:6 ratio target nearly reached the limit of the equipment, $1\times10^{-3}\;gm^2{\cdot}day$. As the Zn portion increased, the packing density also increased, and it was found that the passivation films effectively prevented the permeation by either oxygen or water vapor. To measure the characteristics of gas barrier, the film was applied to the emitting device to evaluate their lifetime. The lifetime of the applied device with passivation was increased to 25 times that of the PLED device, which was non-passivated.

• Membrane Journal
• /
• v.29 no.6
• /
• pp.362-376
• /
• 2019

In this study, hydrophilic coating characteristics of PVDF [poly(vinylidene fluoride)] hollow fiber membranes with flower type cross-section prepared by thermally induced phase separation were studied. The hollow fiber used in this study was provided from PureEnvitech Co. Ltd., and the hydrophilic coating experiment was performed with different concentration and number of coating of PEBAX 1657, 2533 and 3533 block copolymer solution using a dip coating method. The hydrophilic coated hollow fiber membrane was characterized to scanning microscope and contact angle measurements to determine the degree of hydrophilization. As a result of SEM characterization, it was confirmed that the thickness of the coating layer increased as the coating concentration increased and the number of coatings increased. Contact angle of surface of hollow fibers decreased as the concentration of the coating solution increased and the number of coatings increased. Gas permeance of oxygen gas was measured for the application of the hydrophilized hollow fiber to Membrane Areated Biofilm Reactor. As a result of gas permeation test, it was confirmed that gas permeance decreased with increasing coating concentration and number of coatings, and the more hydrophilized hollow fiber coated with PEBAX 1657 showed lower gas permeance than those coated with PEBAX 2533 and 3533.

• Membrane Journal
• /
• v.21 no.1
• /
• pp.62-71
• /
• 2011

Highly enriched oxygen is used in energy-efficient combustion due to decreased non-flammable nitrogen, while high purity nitrogen is used for explosion proof in the LNG ships and keeping the freshness of green stuffs. Membrane technology can be used in these $O_2$ and $N_2$ generation with low energy consumption. In this study, PES was used as a membrane material and 1-methyl-2-pyrollidone (NMP) and acetone were employed as a good solvent and nonsolvent addictive (swelling agent to PES), respectively. Dope solutions were prepared by changing the content of acetone (0, 6.5, 15, 25, 31.5 wt%) in 37 wt% PES solutions. Hollow fiber spinning was performed at 0~10 cm of air-gap distances for each dope solution. $O_2/N_2$ selectivity and permeability were investigated by comparing of hollow fibers coated or not by silicons. $O_2/N_2$ selectivity increased and permeance of $O_2$ and $N_2$ decreased with increasing air-gap height independently of acetone addictions. Optimized PES hollow fibers were obtained with 37/6.5/56.5 wt% PES/acetone/NMP dope solution and 10 cm air-gap, which showed 7.3 of $O_2/N_2$ selectivity and 4.3 GPU of $O_2$ permeability after silicon coating.

• Membrane Journal
• /
• v.29 no.1
• /
• pp.51-60
• /
• 2019

In order to improve gas separation properties of polymeric membranes which have been widely applied in the industry field, aluminosilicate hollow nanoparticles named as allophanes were synthesized by sol-gel method and formulated in Poly(dimethylsiloxane) (PDMS) matrix to investigate the gas separation properties of PDMS membrane. Transmission electron microscope (TEM), Energy dispersive X-ray analysis (EDX), X-ray diffractometer (XRD), Surface area and pore size analyzer (BET) and Fourier transform infrared spectrophotometer (FTIR) were carried out to characterize the synthetic allophanes. Then the PDMS mixed matrix membranes were prepared by adding different volume fraction of allophanes. To examine the effect of allophanes addition in PDMS matrix using unmodified allophane and modified ones, the gas permeation experiments were performed using oxygen, nitrogen, methane and carbon dioxide. As the volume fraction of modified allophane increased up to 4.05 Vol% the permeability of four test gases through PDMS mixed matrix membranes increased. Also, the selectivity of $O_2/N_2$ and $CO_2/CH_4$ increased with the contents of the modified allophane. Further improvement of gas separation properties of PDMS mixed matrix membranes containing higher volume percent of allophanes can be expected as long as well dispersion of allophanes in PDMS matrix can be achieved for better PDMS membranes.