• Journal of the Korean institute of surface engineering
• /
• v.36 no.1
• /
• pp.34-41
• /
• 2003

Effects of additives and plating conditions of high speed electroplating were investigated. The Sn content in electrodeposit was highly decreased with increasing current density from $10A/dm^2$ to $50A/dm^2$, and the current efficiency on the cathode was decreased. The carbon content in the electrodeposit was decreased with increasing current density from $10A/dm^2$ to $30A/dm^2$, however the carbon content was highly increased in the range of $40A/dm^2$$∼50A/dm^2$. The formation of tetravalent tin and stannic oxide sludge was prevented by the addition of gallic acid in the bath. The changing of Sn content in the electrodeposit is caused by the addition of gallic acid.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.1
• /
• pp.3-11
• /
• 1994

Cyclic hot corrosion studies have been carried out on(82~94) wt. % Fe-(5, 10, 15) wt. % Cr alloys con-taining either (1, 3)wt. % of Si or Pt as minor alloying elements in molten salts of($Na_2SO_4$+NaCl) between 820 and $920^{\circ}C$. Si or Pt decreased corrosion rate with the most pronounced effect being observed for alloys having 15wt. %Cr. Especially, as Si or Pt contents are increased from 1 to 3 wt. %, improved corrosion resistance was obtained. The beneficial effect of Si addition is due to the presence of the Si-rich second phase along the grain boundaries as well as the formation of the protective $SiO_2$layer between substrates and oxide scale. The Pt addition also increased the corrosion resistance by enhancing the formation ($Cr_2O_3$+layers and by increasing the adherence of the oxide scale.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.05a
• /
• pp.83-83
• /
• 1998

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.30.1-30
• /
• 2003

• Proceedings of the Korean Nuclear Society Conference
• /
• 2003.05a
• /
• pp.233.2-233.2
• /
• 2003

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.4
• /
• pp.156-161
• /
• 2020

Recently, as there has been growing demand for aesthetic quality in structural materials, the development of excellent color cement concrete having good coloration properties has become a requirement. This study is designed to analyze the basic physical properties of mortar and the properties of keeping the coloration under an ultraviolet ray accelerated weathering test environment according to changes in the mixing ratio between carbon black and iron oxide used as colorants. The test results show that the use of carbon black and iron oxide reduces the initial flow by 6.3~17.2 % and the air content by 3.5~31.5 % but increases the unit volume weight by 3.4~5.5 %, compared to ordinary Portland cement (OPC). In addition, the study shows that the addition of iron oxide increases the self drying shrinkage. So, caution needs to be taken on the workability of the concrete. The brightness value L^⁎ represented by black showed the most excellent black colour when carbon black 3 % and iron oxide 5 % are added. According to UV accelerated weatherproof test, the brightness value L^⁎ was found to increase in all experiment specimens by 4.28~11.97 %, and the color change by UV was found to be higher for the case where carbon black colorant was not used. Therefore, in terms of color revelation characteristics, the case using carbon black 3 % and iron oxide 5 % was found to show the best black color.

• Applied Chemistry for Engineering
• /
• v.26 no.3
• /
• pp.331-335
• /
• 2015

We prepared films by a bar-coating of various graphene oxide (GO) pastes by varying pH with amine compounds. The thermal treatment of films at $150^{\circ}C$ and measurement of surface resistances exhibited that the pH variation does not significantly affect the surface resistance. We, however, found that the addition of amines reduced the surface resistance by approximately 10 times and N,N-dimethylethanolamine (DMEA) showed the most significant effect among all amines investigated. XPS studies demonstrated that the addition of DMEA accelerated the reduction reaction of GO, and finally enhanced the electrical properties of GO films.

• Biomolecules & Therapeutics
• /
• v.12 no.4
• /
• pp.209-214
• /
• 2004

Lead has long been considered as a toxic environmental pollutant that severely damages the central nervous system. In various neurogenerative diseases, actrocytes become activated by proinflammatory cytokines. In the present study, we investigated whether lead (Pb$^{2+}$) affects inducible nitric oxide synthase (iNOS) expression in activated glial cells. Rat primary glial cells were stimulated with lipopolysaccharide (LPS, 1 ${\mu}$g/ml) plus IFN$_{\gamma}$(100 U/ml). Pre-treatment of Pb$^{2+}$ increased nitric oxide (NO) production in LPS/IFN$_{\gamma}$-stimulated glial cells. Lead itself, however, suppressed the basal production of NO in control glial cells. Addition of the iNOS inhibitors L-NAME (1 mM) and L-NNA (800 ${\mu}$M) prevented the Pb$^{2+}$-induced increase in NO production. Western blot analysis showed that pre-treatment of Pb$^{2+}$ augmented LPS/IFN$_{\gamma}$-induced increase in iNOS immunoreactivity, which was well correlated with the increased NO production. In addition, pre-treatment of Pb$^{2+}$ synergistically increased the iNOS mRNA expression induced by LPS and IFN${\gamma}$. The present results indicate that lead intoxication adversely affect brain function by potentiating iNOS expression and NO production in activated glial cells observed in various neurodegenerative diseases.

• Journal of Powder Materials
• /
• v.22 no.4
• /
• pp.271-277
• /
• 2015

As wrought stainless steel, sintered stainless steel (STS) has excellent high-temperature anti-corrosion even at high temperature of $800^{\circ}C$ and exhibit corrosion resistance in air. The oxidation behavior and oxidation mechanism of the sintered 316L stainless was reported at the high temperature in our previous study. In this study, the effects of additives on high-temperature corrosion resistances were investigated above $800^{\circ}C$ at the various oxides ($SiO_2$, $Al_2O_3$, MgO and $Y_2O_3$) added STS respectively as an oxidation inhibitor. The morphology of the oxide layers were observed by SEM and the oxides phase and composition were confirmed by XRD and EDX. As a result, the weight of STS 316L sintered body increased sharply at $1000^{\circ}C$ and the relative density of specimen decreased as metallic oxide addition increased. Compared with STS 316L sintered parts, weight change ratio corresponding to different oxidation time at $900^{\circ}C$ and $1000^{\circ}C$, decreased gradually with the addition of metallic oxide. The best corrosion resistance properties of STS could be improved in case of using $Y_2O_3$. The oxidation rate was diminished dramatically by suppression the peeling on oxide layers at $Y_2O_3$ added sintered stainless steel.

• Applied Chemistry for Engineering
• /
• v.24 no.6
• /
• pp.599-604
• /
• 2013

In this study, Ti added Mn-Cu mixed oxide catalysts were prepared by a co-precipitation method and used for the low temperature (< $200^{\circ}C$) selective catalytic reduction (SCR) of NOx with $NH_3$. Physicochemical properties of these catalysts were characterized by BET, XRD, XPS, and TPD. Mn-Cu mixed oxide catalysts were found to be amorphous with a large surface and they showed high SCR activity. Experimental results showed that the addition of $TiO_2$ to Mn-Cu oxide enhanced the SCR activity and $N_2$ selectivity. Ti addition led to the chemically adsorbed oxygen species that promoted the oxidation of NO to $NO_2$ and increased the number of $NH_3$ adsorbed-sites such as $Mn^{3+}$.