• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.12
• /
• pp.878-881
• /
• 2013

In this study, we have fabricated the dye sensitized solar cell (DSSC) composed by a transparent conductive oxide (TCO), a nanocrystalline semiconductor film usually $TiO_2$, a sensitizer adsorbed on the surface of the semiconductor, an electrolyte containing a redox mediator and a counter electrode. The $TiO_2$ nanopowder was prepared by sol-gel methode. The HCl (hydrochloric acid) and TBAOH (Tetrabutyl amonium hydroxide) was added for improving the catalyst and distributed properties of $TiO_2$ nanopowder. Ammonium hydroixde was added in order to control the morphology and size of $TiO_2$ nano crystal. A $TiO_2$ paste for working electrode was prepared with the addition of HPC (hydroxypropyl cellulos) used as a binder of which volume was controled as 1.3, 1.5, 1.7, and 2.0%. The measured I-V curves of assembled DSSC showed that the cell with 1.7% HPC binder had the best efficiency of 6.79%.

• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.6-13
• /
• 2004

The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of Alloy 600(UNS N06600) was evaluated in 10% sodium hydroxide solution at $315^{\circ}C$. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours with and without inhibitors such as titanium oxide, titanium boride and cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in no inhibitor solution. It was found that the changes of the active-passive transition potentials and the film compositions were related to the resistance to stress corrosion cracking in high temperature caustic solution.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.171.2-171.2
• /
• 2015

Nowadays, trivalent rare-earth ($RE^{3+}$) ions activated metal oxides have been proved to be excellent host materials due to their various applications. Facile wet-chemical technique have been considered as the best synthetic route due its intensive interest in the preparation of nanostructures. Europium ion doped lanthanum hydroxide ($La(OH)_3:Eu^{3+}$) phosphors were synthesized by the facile wet chemical method using the hexamethylenetetramine (HMTA) as a mediated surfactant. The thermal behavior for the $La(OH)_3:Eu^{3+}$ phosphors was investigated by thermogravimetric and differential thermal analysis method. The morphological studies were measured by scanning electron microscope and transmission electron microscope measurements, indicating three-dimensional (3D) flower-like $La(OH)_3:Eu^{3+}$ nanorod bundles. After subsequent annealing process, the lanthanum oxide ($La_2O_3:Eu^{3+}$) phosphor exhibited similar kind of morphology. The synthesized $La(OH)_3:Eu^{3+}$ and $La_2O_3:Eu^{3+}$ samples were characterized by X-ray powder diffraction and Fourier transform infrared spectroscopy. Furthermore, photoluminescence and cathodoluminescence properties were studied in details.

• International Journal of Industrial Entomology and Biomaterials
• /
• v.13 no.1
• /
• pp.45-50
• /
• 2006

Papers were prepared from cut cocoons and mulberry branches, which are byproducts from sericulture industry. The long filament of silk should be cut into appropriate length in order to prepare paper and this was achieved by chemical method. By a mixture of sodium hydroxide and sodium carbonate solution, the silk filaments were cut into short fibers (less than 1 mm in length). Since the short silk fibers (sSf) could not bind each other by itself, starch and poly(ethylene oxide)(PEO) were added as a bonding agent. When starch and PEO were used in a ratio of 3:7, the silk papers had optimum mechanical properties for paper. Fibers from the skin of mulberry branches (MBF) were added to sSf to enhance the mechanical properties of pure silk paper. Bleaching of MBF was performed with a mixture of hydrogen peroxide and sodium silicate. The mechanical properties were greatly enhanced and the optimum blend ratio of MBF and sSf were 7:3. The mulberry/silk paper has good absorption property against formaldehyde, and therefore, the paper could be applied as a wall paper for preventing the sick house syndrome.

• Korean Journal of Materials Research
• /
• v.15 no.5
• /
• pp.348-352
• /
• 2005

Gallium oxyhydroxide (GaOOH) powders were heat-treated in a flowing ammonia gas to form GaN, and the reaction kinetics of the oxide to nitride was quantitatively determined by X-ray diffraction analysis. GaOOH turned into intermediate mixed phases of $\alpha-\;and\;\beta-Ga_2O_3$, and then single phase of GaN. The reaction time for full conversion $(t_c)$ decreased as the temperature increased. There were two-types of rapid reaction processes with the reaction temperature in the initial stage of nitridation at below $t_c$, and a relatively slow processes followed over $t_c$ does not depends on temperatures. The nitridation process was found to be limited by the rate of an interfacial reaction with the reaction order n value of 1 at $800^{\circ}C$ and by the diffusion-limited reaction with the n of 2 at above $1000^{\circ}C$, respectively, at below $t_c$. The activation energy for the reaction was calculated to be 1.84 eV in the temperature of below $830^{\circ}C$, and decreased to 0.38 eV above $830^{\circ}C$. From the comparative analysis of data, it strongly suggest the rate-controlling step changed from chemical reaction to mass transport above $830^{\circ}C$.

• Journal of Adhesion and Interface
• /
• v.4 no.2
• /
• pp.1-9
• /
• 2003

Epoxy-amine liquid prepolymers are extensively applied onto metallic substrates and cured to obtain painted materials or bonded joint structures. Overall performances of such systems depend on the created interphase between the organic layer and the substrate. When epoxy-amine liquid mixtures are applied onto more or less hydrated metallic oxide layer, concomitant amine chemical sorption and hydroxide dissolution appear lending to the chelate formation. As soon as the chelate concentration is higher than the solubility product, these species crystallize as sharp needles. Moreover, intrinsic and thermal residual stresses are developed within painted or bonded systems. When residual stresses are higher than the organic layer/substrate adhesion, buckling, blistering, debonding may occur leading to a catastrophic drop of system performances. Practical adhesion can be evaluated with either ultimate parameters (Fmax or Dmax) or the critical strain energy release rate, using the three point flexure test (ISO 14679-1997). We observe that, for the same system, the ultimate load decreases while residual stresses increase when the liquid/solid time increases. Ultimate loads and residual stresses depend on the metallic surface treatment. For these systems, the critical strain energy release rate which takes into account the residual stress profile and the Young's modulus gradient remains quite constant whatever the metallic surface treatment was. These variations will be discussed and correlate to the formation mechanisms of the interphase.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.111-113
• /
• 2011

This study investigated about how much the limestone's volume was changed as time passed while maintaining a certain level of moisture condition in the limestone material for concrete under high temperature. The result is summarized as follows: It was appeared that the limestone material under high temperature emitted some CO₂ resulting from the decarboxylation, so that as the heating temperature was increased, the limestone's length change rate was decreased. In the leave time change after heating the stone, the both conditions of 50% and 100% made the limestone create Ca(OH)₂ using some H₂O. So it was appeared that as time passed, the limestone's length change rate first increased because of its volume expansion, but the rate was reduced after the limestone material was crumbled.

• Journal of the Korean Society for Precision Engineering
• /
• v.32 no.1
• /
• pp.69-74
• /
• 2015

Cadmium telluride (CdTe) is being developed for thin film of the X-Ray detector recently. But a rough surface of the CdTe should be improved for resolution and signal speed. This paper shows the study on the improvement of surface roughness and removal rate by applying Chemical Mechanical Polishing. The conventional potassium hydroxide (KOH) based colloidal silica slurry could not realize a mirror surface without physical defects, resulting in low material removal rate and many scratches on surface. In order to enhance chemical reaction such as form oxidized layer on the surface of cadmium telluride, we used hydrogen peroxide ($H_2O_2$) as an oxidizer. Consequently, in case of 3 wt% concentration of hydrogen peroxide, the highest MRR (938 nm/min) and the lowest surface roughness ($R_{p-v}=10.69nm$, $R_a=0.8nm$) could be obtained. EDS was also used to confirm the generated oxide of cadmium telluride surface.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.1
• /
• pp.194-198
• /
• 2012

In this work, we studied the microstructural changes of ITO during the annealing process. ITO nanoparticles were prepared by the sol-gel method using indium tin hydroxide as the precursor. The prepared sample was investigated using TEM, powder XRD, XPS, DRIFT, and 2D correlation analysis. The O 1s XPS spectra suggested that the microstructural changes during the annealing process are closely correlated with the oxygen sites of the ITO nanoparticles. The temperature-dependent in situ DRIFT spectra suggested that In-OH in the terminal sites is firstly decomposed and, then, Sn-O-Sn is produced in the ITO nanoparticles during the thermal annealing process. Based on the 2D correlation analysis, we deduced the following sequence of events: 1483 (due to In-OH bending mode) ${\rightarrow}$ 2268, 2164 (due to In-OH stretching mode) ${\rightarrow}$ 1546 (due to overtones of Sn-O-Sn modes) ${\rightarrow}$ 1412 (due to overtones of Sn-O-Sn modes) $cm^{-1}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.87-88
• /
• 2006

It is needed several large reservoirs and long time in order to remove suspended solid like steel fines and iron oxide at steel making factory. If removing rate of suspended solid in rolling coolant is improved, the productivity of working process can be increased and the area of reservoir can be reduced. Pre-treatment to add extra magnetization of suspended solid was studied Iron hydroxide and electrolytic dissociation were used for pretreatment. High gradient magnetic separation (HGMS) system was used for removing of magnetized suspended solid. Removing ratio showed over than 99% in the coolant containing magnetic fines. Magnetic properties of suspended solid were investigated after mixed with Al2(SO2)3 and organic flocculant by using electrochemical treatment.