• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.110-113
• /
• 2012

Ge-S and Li-Ge-S powders were synthesized via solution-based process in order to employ chalcogenide-based solid electrolyte for use in Li secondary batteries. GeCl4 and thioacetamide in combination result in Ge-S powders of which major crystalline phase becomes GeS2 where the tetragonal and orthorhombic phases coexist after heat treatment. A chemical treatment using NaOH brings about the reduction of chlorine in the powders obtained. However, the heat treatment at 300 ℃ is more effective in minimizing the chlorine content. When lithium chloride is used as the precursor of Li ions, the LiCl powders are agglomerated with an inhomogeneous distribution. When Li2S is used, the Li-Ge-S powders are distributed more uniformly and the orthorhombic GeS2 phase dominates in the powders.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권4호
• /
• pp.404-409
• /
• 1996

The structural and electric properties of $Y_{1-x}$YbF$_{x}$Ba$_{2}$Cu$_{3}$O$_{7-y}$(x=0.0, 0.1, 0.2, 0.3, 0.4, 0.5 and 0.6) have been investigated by using XRD(X-ray diffraction), TMA(thennomechanical analysis), NMR(nuclear magnetic resonance) analysis and four probe method. $Y_{1-x}$YbF$_{x}$Ba$_{2}$Cu$_{3}$O$_{7-y}$ samples were prepared by conventional solid-state reaction method using $Y_{2}$O$_{3}$, BaCO$_{3}$, CuO and YbF$_{3}$ power. TMA and high temperature XRD results shows that orthorhombic to tetragonal phase transition occurs in the unfluorinated 1-2-3 sample while the phase change is not observed in the fluorinated 1-2-3 samples. Superconducting transition temperature(T$_{c}$) increases with increasing YbF$_{3}$ content ; T$_{c}$, of the sample reaching maximum of 102K for x=0.3, and then decreases with further increasing YbF$_{3}$ content. The structural analysis and T$_{c}$ results shows that the fluorine doping stabilize the orthorhombic phase, together with the increase in T$_{c}$.}$ c/.TEX> c/.

• Current Applied Physics
• /
• 제18권11호
• /
• pp.1289-1293
• /
• 2018

The influence of crystallization treatment on the structure, magnetic properties and magnetocaloric effect of $Gd_{71}Ni_{29}$ melt-spun ribbons has been investigated in detail. Annealing of the melt-spun samples at 610 K for 30 min, a majority phase with a $Fe_3C$-type orthorhombic structure (space group, Pnma) and a minority phase with a CrB-type orthorhombic structure (space group, Cmcm) were obtained in the amorphous matrix. The amorphous melt-spun ribbons undergo a second-order ferromagnetic to paramagnetic phase transition at 122 K. For the annealed samples, two magnetic phase transitions caused by amorphous matrix and $Gd_3Ni$ phases occur at 82 and 100 K, respectively. The maximum magnetic entropy change $(-{\Delta}S_M)^{max}$ is $9.0J/(kg{\cdot}K)$ (5T) at 122 K for the melt-spun ribbons. The values of $(-{\Delta}S_M)^{max}$ in annealed ribbons are 1.0 and $5.7J/(kg{\cdot}K)$, corresponding to the two adjacent magnetic transitions.

• 한국광물학회지
• /
• 제23권3호
• /
• pp.267-272
• /
• 2010

${\alpha}$-크리스토발라이트 구조의 $GaPO_4$에 대한 고압 x-선 회절 실험을 상온에서 8.9 GPa까지 시행하였다. 정방정계에 속하는 출발결정구조는 1 GPa 이하의 압력에서 회절피크가 분리되는 변화를 보이는데, 아마도 망상구조를 이루고 있는 사면체의 방향성이 압력에 의해 흐트러지면서 상-I'로 상변이가 유도된 것 같다. 압력을 증가시키면, 상-I'는 2 GPa와 3 GPa 사이에서 정방정계에 속하는 고압상(상-III)으로 상변이를 하고 있다. 이 결과는 최근 동일한 시료를 이용하여 얻은 고압실험결과(Ming et al., 2007)와 일치하지 않는다. 최고압력에 도달한 다음, 압력을 대기압으로 내리면 상-III이 그대로 유지되는 것으로 나타났다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.163-163
• /
• 1999

MOSFET, MESFET 그리고 MODFET는 Logic ULSIs, high speed ICs, RF MMICs 등에서 중요한 역할을 하고 있으며, 그것의 gate electrode, contact, interconnect 등의 물질로는 refractory metal을 이용한 CoSi2, MoSi2, TaSi2, PtSi2, TiSi2 등의 효과를 얻어내고 있다. 그중 TiSi2는 비저항이 가장 낮고, 열적 안정도가 좋으며 SAG process가 가능하므로 simpler alignment process, higher transconductance, lower source resistance 등의 장점을 동시에 만족시키고 있다. 최근 소자차원이 scale down 됨에 따라 TiSi2의 silicidation 과정에서 C49 TiSi2 phase(high resistivity, thermally unstable phase, larger grain size, base centered orthorhombic structure)의 출현과 그것을 제거하기 위한 노력이 큰 issue로 떠오르고 있다. 여러 연구 결과에 따르면 PAI(Pre-amorphization zimplantation), HTS(High Temperature Sputtering) process, Mo(Molybedenum) implasntation 등이 C49를 bypass시키고 C54 TiSi2 phase(lowest resistivity, thermally stable phase, smaller grain size, face centered orthorhombic structure)로의 transformation temperature를 줄일 수 있는 가장 효과적인 방법으로 제안되고 있지만, 아직 그 문제가 완전히 해결되지 않은 상태이며 C54 nucleation에 대한 physical mechanism을 밝히진 못하고 있다. 본 연구에서는 증착 시 기판온도의 변화(400~75$0^{\circ}C$)에 따라 silicon 위에 DC/RF magnetron sputtering 방식으로 Ti/Si film을 각각 제작하였다. 제작된 시료는 N2 분위기에서 30~120초 동안 500~85$0^{\circ}C$의 온도변화에 따라 RTA법으로 각각 one step annealing 하였다. 또한 Al을 cosputtering함으로써 Al impurity의 존재에 따른 영향을 동시에 고려해 보았다. 제작된 시료의 분석을 위해 phase transformation을 XRD로, microstructure를 TEM으로, surface topography는 SEM으로, surface microroughness는 AFM으로 측정하였으며 sheet resistance는 4-point probe로 측정하였다. 분석된 결과를 보면, 고온에서 제작된 박막에서의 C54 phase transformation temperature가 감소하는 것이 관측되었으며, Al impuritydmlwhswork 낮은온도에서의 C54 TiSi2 형성을 돕는다는 것을 알 수 있었다. 본 연구에서는 결론적으로, 고온에서 증착된 박막으로부터 열적으로 안정된 phase의 낮은 resistivity를 갖는 C54 TiSi2 형성을 보다 낮은 온도에서 one-step RTA를 통해 얻을 수 있다는 결과와 Al impurity가 존재함으로써 얻어지는 thermal budget의 효과, 그리고 그로부터 기대할 수 있는 여러 장점들을 보고하고자 한다.

• Transactions on Electrical and Electronic Materials
• /
• 제7권2호
• /
• pp.76-80
• /
• 2006

Well-defined orthorhombic $LiMnO_2\;and\;LiCo_{0.1}Mn_{0.9}O_2$ were synthesized by a solid-state reaction and quenching process. X-ray diffraction (XRD) results revealed that the as-synthesized powders showed an orthorhombic phase of a space group with Pmnm. The $Li/LiMnO_2\;and\;Li/LiCo_{0.1}Mn_{0.9}O_2$ cells were constituted and cycled galvanostatically in the voltage range of 2.0-4.3 V vs. $Li/Li^+$ at a current density of $0.5\;mA\;cm^{-2}$ at room temperature and $50^{\circ}C$, respectively. The results demonstrated that the highest specific capacity of $Li/LiMnO_2$ cells at room temperature and $50^{\circ}C$ was 95 and $155\;mAh\;g^{-1}$, respectively. As for $Li/LiCo_{0.1}Mn_{0.9}O_2$ cells, the highest specific capacity at room temperature and $50^{\circ}C$ was 160 and $250\;mAh\;g^{-l}$, respectively. It could be seen that the performance of $Li/LiCo_{0.1}Mn_{0.9}O_2$ cells was better than that of $Li/LiMnO_2$ cells.

• Progress in Superconductivity
• /
• 제5권2호
• /
• pp.124-127
• /
• 2004

Many of research efforts have been focused on the improvement of critical current density (Jc) of silver-sheathed Bi-2223 tapes far practical applications. In this study, the transformation of Bi-2212 phase was investigated, which was transformed to orthorhombic from tetragonal through pre-annealing during powder packing and drawing process. The relationship between hardness of Bi-2212 orthorhombic phase and workability of Bi-2223/Ag tape was investigated. Bi-2223 superconducting wires with 55 filaments were fabricated by stacking and drawing process with different heat-treatment histories. Before rolling process, round wires were pre-annealing at 76$0^{\circ}C$ and in a low oxygen partial pressure. We confirmed that pre-annealing step was to transform to Bi-2212 orthorhombic structure from Bi-2212 tetragonal structure and to reduce the formation of second phases. However the breakages were created at Ag-alloy clad during rolling for pre-annealed Bi-22231Ag tapes. Several pre-annealing scenarios were introduced to reduce the breakages during rolling process. Microstructure and critical current density of pre-annealed Bi-2223 superconducting tapes were investigated. We could achieve proper pre-annealing conditions for Ag-alloy clad Bi-2223 superconducting tapes.

• Transactions on Electrical and Electronic Materials
• /
• 제3권3호
• /
• pp.21-24
• /
• 2002

Two kinds of $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$, the sintering samples and zone melting samples, were heat-treated under pure Ar at 950$^{circ}C$. The substitution of Nd ion for Ba ion in the $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$ before and after the heat treatment was investigated by XRD. In order to confirm the effects of the heat treatment, the Tc and Jc of samples with/without the heat treatment under Ar were comparatively studied. $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$ samples were oxygenated under pure oxygen at $300^{circ}C$. From the XRD pattern it was found that the sample with x<0.4 was transferred from tetragonal phase to orthorhombic phase after the oxygenation, while the sample with x>0.4 did not show the phase transition even after a long time oxygenation. Therefore, the low oxygen partial pressure (Ar+1 % O$_2$) was used for the ambient atmosphere of the zone-melting samples, which could reduce the melting temperature and depress the substitution of Nd for Ba. After the improvement in the zone-melting process, the Jc value was increased to 2 x $10^4$A/$cm^2$ (0 T, 78 K). The particle orientation and the structure of zone-melted NdBaCuO were studied by the XRD and SEM analysis.

• 한국재료학회지
• /
• 제6권3호
• /
• pp.305-308
• /
• 1996

YxFe2-xO3(x=0.82)의 결정상 변환을 상온에서의 x선회절과 온도구간 80-541K에서의 Mossbauer 분광 방법에 의해서 연구하였다. Xtjs 회절선은 시료가 orthorhombic 결정상과 garnet 결정상이 공존하고 있으며, 공존비는 실험오차 범위내에서 garnet 구조가 orthorhombic 구조보다 우세함을 보인다. 공존상중에서 garnet 구조의 자기상 변환온도는 536$\pm$5 K로 결정하였다. Debye 모형을 이용한 Mossbauer 스펙트럼의 recoil-free fration 분석결과는 garnet 결정상내의 d자리나 a자리에 vacancy의 존재 가능성을 시사한다. 부가적으로 시료가 포함하는 각 결정상의 Debye 특성온도를 결정하였다.

• 대한전자공학회논문지
• /
• 제27권5호
• /
• pp.724-728
• /
• 1990

The X-ray diffraction pattern, electrical resistance, density and critical temperature of a series of YBa2(Cu3-xNix)O7-\ulcornersamples (0\ulcorner\ulcorner.5) were investigated with the increase of the Ni content. The samples show a principal 1.2.3-like phase with well resolved orthorhombic peaks. The final pattern of the x=0.1 sample appears to be well reacted orthorhombic YBa2(Cu,Ni)3O7-\ulcornerwith minor impurities and an appreciable amorphous fraction. From the above results, we conclude that Ni does not play an important role for the superconductivity in the Y-Ba-Cu-O system.