This study investigates microstructural characteristics of alkali-activated cements incorporating slag and fly ash. Samples were prepared with four fly ash:slag ratios, i.e., 100:0, 90:10, 70:30 and 50:50, and they were synthesized by using an alkali activator. Microstructural characteristics of the alkali-activated cements were determined by XRD, TGA, SEM, N2 gas adsorption/desorption methods, and compressive strength test. The results showed that properties of alkali-activated fly ash/slag were significantly affected by slag contents. Alkali-activated fly ash/slag with slag content of 30-50% showed higher compressive strength than ordinary Portland cement paste. An increase in slag content resulted in a denser microstructure, which composed of amorphous gel, therefore contributed to strength development of the material.

• Structural Engineering and Mechanics
• /
• 제52권1호
• /
• pp.97-113
• /
• 2014

In the present work appropriate concrete material models have been proposed to predict drying shrinkage and specific creep of High-performance concrete (HPC) using Artificial Neural Network (ANN). The ANN models are trained, tested and validated using 106 different experimental measured set of data collected from different literatures. The developed models consist of 12 input parameters which include quantities of ingredients namely ordinary Portland cement, fly ash, silica fume, ground granulated blast-furnace slag, water, and other aggregate to cement ratio, volume to surface area ratio, compressive strength at age of loading, relative humidity, age of drying commencement and age of concrete. The Feed-forward backpropagation networks with Levenberg-Marquardt training function are chosen for proposed ANN models and same implemented on MATLAB platform. The results shows that the proposed ANN models are more rational as well as computationally more efficient to predict time-dependent properties of drying shrinkage and specific creep of HPC with high level accuracy.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.433-438
• /
• 2000

The purpose of this study is to examine the resistance of water-permeable concretes to freezing and thawing action. The water-permeable concretes with cement-aggregate ratio of 1:5.5(by weight) and two kinds of admixture content [SP : superplasticizer(0, 1.0%), HPAE : high performance air entraining agent(0.5, 1%)] used OPC(ordinary portland cement) as binder were prepared, and then tested for relative dynamic modulus of elasiticity, mass change, length change and durablity factor. It's been concluded from the test results that the superior relative dynamic modulus of elasiticity and durability factor of water-permeable concretes were obtained at superplaciticizer 1.0% after 300 cycles. The water-permeable concretes used superplasiticizer 1.0% having relative durability factor of 88% after 300 cycles.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.497-502
• /
• 2000

This study was performed to change the latex content for properties of freezing-thawing resistance. When styrene-butadiene latex is added to portland cement, aggregate and water, a concrete with the color, consistency and workability of ordinary conventional concrete results, but with 20% to 35% less water. When cured, the concrete consists of hydrated cement and aggregate interconnected by a film of latex particles. In general, increasing the amount of latex will produce concrete with increased tensile and flexural strength and lower modulus of elasticity. Air entrainment has been used in conventional concrete for the past 50 years to impart freeze-thaw resistance. Latex modified concrete does not need additional air entrainment for freeze-thaw resistance provided adequate cure occurs.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.639-642
• /
• 2005

Main components of metakaolin(MK) were $SiO_2\;and\;Al_2O_3$. and specific surface was 2.2 times larger than that of ordinary portland cement(OPC). MK indicated the fine particle and fiber texture. Flow value of mortar with MK was decreased linearly each $13\%$ as the replacement ratio of MK was increased each $5\%$. Compressive strength of mortar with MK was increased more than that of mortar with OPC by 3days. Compressive strength of mortar with $10\%$ MK was about 83MPa at 28 days. When MK was replaced with $10\%$ of cement volume, flexural strength and modulus of elasticity of mortar was indicated the maximum value at 28 days.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.711-714
• /
• 2005

This paper focused on development of geopolymer for wood wool ceramic board. Geopolymer can substitude ordinary portland cement and its accelerator of wood wool cement board as inorganic polymer. In this study, what we would obtain geopolymer's properties such as initial setting time(KS L 5108), flow(KS L 5102) and compressive strength of 3days aged(KS L 5105), was less than 1 hour, more than $110\%$, more than 40Mpa. Geopolymer have three essential materials called filler, hardener and geopolymer liquor. So, We applied filler by quartz, hardener by blast furnace slag powder, metakaoline and fly ash, geopolymer liquor by NaOH, KOH and sodium silicate solution. As result of this experiment, what we could obtain best fitted geopolymer's properties such as initial setting time, flow and compressive strength of 3days aged, was 45min, $116\%$ and 43.6Mpa. This result can be applicable to commercial wood wool ceramic board.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.621-624
• /
• 2008

This study deal with the effects of ground granulated blast furnace slag (SG) and silica fume (SF) on the mechanical characteristics of pavement concrete made with ordinary portland cement and regulated set cement. Compressive and flexural strengths as well as unit weight of concretes were monitored. From a result of the study, it was found that the SG was effective for development of flexural strength of concretes, but not for development of compressive strength. However, it must be noted that the present study is limited only to the data by the age of 28 days. More data at long-term age should be accumulated for reliability.

• 한국세라믹학회지
• /
• 제31권7호
• /
• pp.745-752
• /
• 1994

A polymer reinforced grouts using ordinary portland cement mortar and water soluble polymer{polyvinyl alcohol(PVA), styrene-butadiene rubbre(SBR), etylene-vinyl acetate copolymer(EVA)} were made. The mechanical properties of the hardened specimens were investigated through the observation of the microstructure and application of fracture mechanics. When the PVA, SBR and EVA was added with 1.5 wt% to the grouts, the compressive strength were about 54 MPa, 63 MPa and 68 MPa respectively, and the flexural strength was about 11 MPa, 12.8 MPa, and 13.6 MPa respectively, and Young's modulus was about 3.8 GPa, 4.4 GPa and 4.6 GPa respectively, and critical stress intensity was about 0.73 MNm-1.5, 0.85 MNm-1.5 and 0.9 MNm-1.5 respectively. It can be considered that the strength improvement of polymer mortar grouts may be due to the removal of macropores and the increase of various fracture toughness effects, such as grain bridging, frictional interlocking and polymer bridging.

• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2001년도 The 6th International Symposium of East Asian Resources Recycling Technology
• /
• pp.581-585
• /
• 2001

Alinite-Calciumchloroaluminate system clinker was synthesized from solid state waste. The raw materials were municipal incineration ash, sewage sludge, limestone and clay. ecocement was prepared by the mixing of synthesized clinker and optimum amount of gypsum and its hydrolysis characteristic was investigated. X-ray diffraction, conduction calorimeter and reflecting microscope were used to analyze structural and physical properties. The main phase of clinker were alinite, calcium chloroaluminate. $C_2$S, $C_3$S. From the results of hardening time, hydration reactivity of synthesized all samples was faster than that of ordinary portland cement.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.248-249
• /
• 2017

Red mud is an industrial by-product produced during the manufacturing aluminum hydroxide (Al(OH)₃) and aluminum oxide(Al₂O₃) from Bauxite ores. In Korea, approximately 2tons of red mud in a sludge form with 40~60% moisture content is produced when 1 ton of Al₂O₃ is produced through the Bayer process. An annual production of approximately 20tons are produced by company K, which is responsible for most of the domestic production. Therefore, in order to utilize Red Mud in the construction industry, this study evaluated the pore characteristics of ordinary portland cement mortar according to the red mud replacement ratio.