• 한국염색가공학회지
• /
• 제27권1호
• /
• pp.35-49
• /
• 2015

This paper investigated optimum process conditions of coating yarn for awning fabric. For this purpose, the simulation for processability and yarn quality using SPSS statistics package was carried out, and PP/TPO and PET/PVC coating yarns specimens were made with variation of extruder temperature and feed speed of core yarn on the yarn coating machine for examining simulation result. It was revealed that optimum coating conditions of PP/TPO 1000d coating yarn were extruder temperature $150^{\circ}C$, and core yarn feed speed 400~500m/min. Mechanical property and thermal shrinkage of PP/TPO coating yarn made at this conditions were best and core evenness rates of these coating yarns by yarn compression tester were also superior, which was certified by SEM photograph. In addition, these experimental results were coincided with simulation results. It was found that, in PET/PVC coating yarn, yarn physical properties between 1500d and 1200d coated yarns were not shown any difference, and core evenness rates of these coating yarns were superior. It revealed and concluded that these simulated coating conditions are applicable to production field.

• 열처리공학회지
• /
• 제20권4호
• /
• pp.195-202
• /
• 2007

Corrosion resistance and torque of M10 bolt coated with Magni 565 were investigated. Corrosion protection mechanism were also studied with the microstructure of coating film. The bolts with the optimum conditions showed around $10{\mu}m$ layer thickness, a great corrosion resistance in salt spray test and a proper torque in torque/tension test. But torque coefficient k increased with the number of bolting and clamping force of M10 bolt showed significantly lower than that of specified value 28.3kN. It was thought that the repeated bolting made the coating film peel off and powdery. The sample coated with optimum coating conditions showed more higher polarization resistance and corrosion potential than the specimens of top and base coat only. The base coating film was composed of lamellar zinc flakes, which provides a large sacrificial cathodic protection. Meanwhile, the top coating film was composed of organic aluminium pigments layer, which provides barrier protection to the corrosion circumstances.

• Journal of Welding and Joining
• /
• 제15권1호
• /
• pp.125-134
• /
• 1997

This study was conducted by L9 orthogonal array to obtain optimum spray parameters for This study was conducted by L9 orthogonal array to obtain optimum spray parameters for $Cr_3C_2 - 7wt%$(80wt%Ni-20wt%Cr) coating powder. The factors were hydrogen flow rate, oxygen flow rate, gun-to-work distance, powder feed rate. And evaluation methods for the coating were surface roughness, oxygen concentration, micro-hardness, pore size and distribution, low angle ($30^{\circ}$) erosion rate, and microstructure of coating. The optimum HVOF spray conditions were proved as follows : hydroen flow rate ; 681 SLPM, oxygen flow rate ; 215 SLPM $H^2/O^2 ratio= 3.16), gun-to-work distance ; 22cm, powder feed rate; 25g/min. The hardness (Hv300) was 1147 and the erosion rate ($30^{\circ}$degree) was $3.16\times10^{-4}$g/g. It is believed that the optimized spray conditions can be improved the wear-resistance and anti-erosion characteristics of the coating.

• 한국표면공학회지
• /
• 제22권1호
• /
• pp.26-42
• /
• 1989

It has between investigated that the optimum spaying conditions, such as, spraying distance, fusing temperature and fusing time, ect, in a Ni-cr base self fluxing alloy sprayed on the mild steel substrate by oxygen-acetylenc flame spraying. Sprayed specimens on various conditions were fuused in a vacuum furnace and the results were as follows. The optimum spraying condition for excellent coating layer are obtained under spraying distances, fusing temperature and fusing and time ; 180~240mm,1050~110$0^{\circ}C$and 15~30min, respectively. The adhesive strength and surface hurface hardness of the as sprayed specimens were very low by mechanical bonding becaus of the diffusion layer during process. The carbides and borides and formed in the sprayed coating layer and densification of the layer was resulted from the elimination of pores and oxides. The hardness of sprayed coating layer, particularly in the high temperature, was superior to ordinary tool steels.

• 한국식품조리과학회지
• /
• 제19권5호
• /
• pp.571-580
• /
• 2003

The purpose of this study was to assess the optimum coating ratio for rice, using various ratios of mulberry leaves extract, 1.0, 1.5, and 2.0%, and to determine the optimum ratio of added water, in proportion to the total weight of mulberry rice. The moisture content of the soaked rice, and the optimum water uptake rate, moisture content of the cooked rice, as well as its blue and color values, mechanical characteristics, internal structure and sensory evaluation, were analyzed. The statistical data analyses were completed using the SAS program. The results are summarized as follows: The moisture content of mulberry rice was less than that of raw rice. The average optimum water uptake of the soaked mulberry rice at the different water temperatures, 10, 20 and 30, was 20% of the total weight of the raw mulberry rice. As for the results of the sensory evaluation,; 140% water, in proportion to the total weight of raw mulberry rice, was judged to be the optimum. The average moisture content of the cooked mulberry rice was 45∼50%, but there was no significant difference in the various coating ratios. The blue value of the cooked mulberry rice awas highest on the first day of cooking. The L- and a-values decreased with increasing coating ratio, but the b-value increased under the same conditions. As for the mechanical characteristics,; the adhesiveness, hardness and springiness decreased during 2 days of storage. The internal structure of the mulberry rice, observed by SEM, showed a close structure on increasing the coating ratios of mulberry leaves extracts. It was concluded that the optimum coating ratio of mulberry rice and ratio of added water for cooking wereas 1.5 and 140%, respectively, in proportion to the total weight of raw mulberry rice.

• Journal of Welding and Joining
• /
• 제16권5호
• /
• pp.86-92
• /
• 1998

High speed wire seam weldability of tin coated thin gage sheet steels was investigated. Thickness and coating weight ranges of the test materials were 0.21~0.35mm and 1.1/1.1~2.8/11.2g/$m^2$, respectively. Test results indicated that the surface roughness value, Rz decreased as increasing the coating weight. The Rz was thought to be one of the important factors to influence the optimum welding condition range, $\triangle$Q. The $\triangle$Q showed close relationship with welding conditions such as welding pressure and travel speed. Higher welding pressure widened the $\triangle$Q while higher travel speed reduced the $\triangle$Q value. Results also demonstrated that tin coating weight should be optimized based on the weldability or the serviceability after welding. At th HAZ of sheet materials with thinner coating layer, tin depleted zone was produced since molten film of the coating material on the base metal agglomerated by the surface tension, which could result in reducing the corrosion resistance of the HAZ in the service environment.

• 한국축산식품학회지
• /
• 제38권3호
• /
• pp.636-652
• /
• 2018

The study aims to determine the optimum sterilization rate and water activity of Chinese traditional smoke-cured bacon product (Larou) in the preservation with natural coating solution. With the response surface methodology (RSM), we analyzed 3 factors of processing conditions (the concentration of lysozyme, concentration of sodium alginate, and concentration of chitosan) and 2 response factors (sterilization rate and water activity). Sterilization rate and water activity of Larou were largely affected by the concentration of lysozyme, concentration of sodium alginate, and concentration of chitosan. The final optimum concentrations of lysozyme, sodium alginate, and chitosan were 0.09, 1.40, and 1.60% and realized the high sterilization rate. Water activity of sliced Larou was significantly correlated with the sterilization rate. Low-field nuclear magnetic resonance analysis verified the optimum processing conditions. The coating resulted in 99.69% rate of reducing bacteria after 30-day storage. The data of the total number of colony, peroxidation value, moisture content, pH, and sensory evaluation provided the theoretical basis for extending the shelf life of Chinese traditional smoke-cured bacon product (Larou) with natural coating solution.

• KSTLE International Journal
• /
• 제3권1호
• /
• pp.17-22
• /
• 2002

Roughing of tool steel in its hardened state represents a real challenge in the die and meld industry and process improvement depends on research of tool material, coating technique, and lubrication. However, roughing of hardened steels generates extreme heat and without coolant flooding, tool material cannot withstand the high temperature without choosing the right tools with proper coating. This research conducted milling tests using coated ball end mills to study effects of cutting conditions and geometric parameters of ball end mills on the machinability of hardened tool steel. KP4 steel and STD 11 heat treated steels were used in the dry cutting as the workpiece and TiAIN coated ball end mills with side relief angle of 12$^{\circ}$ was utilized in the cutting tests. Cutting forces, tool wear, and surface roughness were measured in the cutting tests. Results from the experiments showed that 85 m/min of cutting speed and 0.32 mm/rev of feed rate were optimum conditions for better surface finish during rough cutting and 0.26mm/rev with the same cutting speed are optimum conditions in the finish cutting.

• Journal of Biosystems Engineering
• /
• 제26권2호
• /
• pp.177-188
• /
• 2001

This research was carried out to examine the optimum design conditions of a vertical small-scale milling machine where the rough rice is processed directly into the white rice in one pass. Effects of the main spindle speed, feed screw pitch and ceramic coating length of the roller on various milling characteristics such as white rice processing capacity, electric energy consumption, rice temperature increase, broken rice ratio, moisture reduction, outlet force and crack ratio increase were studied. The results are as follows. 1. The maximum white rice processing capacity and the lowest crack ratio increase, were obtained from a machine with specification: main spindle speed of 970rpm having a feed screw pitch of 19㎜. 2. The minimum electric energy consumption was obtained with the main spindle speeds of 900 and 970rpm respectively having a feed screw pitch of 19㎜. 3. The rice temperature was increased as the feed screw pitch decreased and the main spindle speed increased. 4. Broken rice ratio was relatively low with the range of 0.8∼1.3%. 5. Moisture content loss was with the range of 0.05∼0.4%. 6. The highest outlet force was 0.72kg$\_$f/ with 900rpm of the main spindle speed and 19㎜ of the feed screw pitch and the lowest outlet force was 0.18∼0.34kg$\_$f/ with 970rpm of the main spindle speed and 16㎜ of the feed screw pitch. 7. The optimum design conditions for the vertical small-scale milling machine were obtained at 970rpm of the main spindle speed, 19㎜ of the feed screw pitch and 20㎜ of the ceramics coating length.

• 한국표면공학회지
• /
• 제35권1호
• /
• pp.53-63
• /
• 2002

Ni coating was carried out by pulse plating at room temperature. So, experimental conditions for Ni-coating were based on Watt's bath, and new additives(propionic acid) were introduced in the Watt's bath electrolyte as $H_3$$BO_3$ alternatives. By adding propionic acid, coating layer demonstrated a good adhesion and uniformity without special pre-treatment of the 316L stainless steel at room temperature. With a decrease of amount of propionic acid and applied average current density, cathode current efficiency increased. Also, edge effect was decreased with decreasing a peak current and increasing a pulse frequency in the same bath condition. It was found that the optimum condition for Ni coating was a current density of 10~20mA/$\textrm{cm}^2$ at below 500 mA peak current in the $5m\ell/\ell$ propionic acid solution.