• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1086-1091
• /
• 1999

$K^+-{\beta}/{\beta}"-Al_2O_3$ in the ternary system $K_2O-MgO-Al_2O_3$ was directly synthesized by solid state reaction. The phase formation and phase relation were carefully investigated in relation to starting composition, calcining temperature and time, and dispersion medium. The optimal synthetic condition was also examined for the formation of ${\beta}"-Al_2O_3$ phase with a maximum fraction. As a composition range, the mole ratio of $K_2O$ to $Al_2O_3$ was changed from 1:5 to 1:6.2 and the amount of MgO used as a stabilizer was varied from 4.2 wt % to 6.3 wt %. The calcining temperature was selected between $1000^{\circ}C$ and $1500^{\circ}C$. At $1000^{\circ}C$, the ${\beta}/{\beta}"-Al_2O_3$ phases began to form resulted from the combining of ${\alpha}-Al_2O_3$ and $KAlO_2$ and increased with temperature rising. All of ${\alpha}-Al_2O_3$ phase disappeared to be homogenized to the ${\beta}/{\beta}"-Al_2O_3$ phase at $1200^{\circ}C$. Near the temperature at $1300^{\circ}C$, the fraction of ${\beta}"-Al_2O_3$ phase showed a maximum value with the composition of $K_{1.67}Mg_{0.67}Al_{10.33}O_{17}$. At temperatures above $1300^{\circ}C$, the fraction of ${\beta}"-Al_2O_3$ phase decreased gradually owing to $K_2O$ loss caused by a high potassium vapor pressure, and the appropriate calcining time was about 5 hours. Acetone was more effective than distilled water as a dispersion medium for milling and mixing.

• Journal of the Korean Vacuum Society
• /
• v.19 no.4
• /
• pp.307-313
• /
• 2010

One-dimensional cubic phase silicon carbide nanowires (${\beta}$-SiC NWs) were efficiently synthesized by thermal chemical vapor deposition (TCVD) with mixtures containing Si powders and nickel chloride hexahydrate $(NiCl_2{\cdot}6H_2O)$ in an alumina boat with a carbon source of methane $(CH_4)$ gas. SEM images are shown that the growth temperature (T) of $1,300^{\circ}C$ is not enough to synthesize the SiC NWs owing to insufficient thermal energy for melting down a Si powder and decomposing the methane gas. However, the SiC NWs could be synthesized at T>$1,300^{\circ}C$ and the most efficient temperature for growth of SiC NWs is T=$1,400^{\circ}C$. The synthesized SiC NWs have the diameter with an average range between 50~150 nm. Raman spectra clearly revealed that the synthesized SiC NWs are forming of a cubic phase (${\beta}$-SiC). Two distinct peaks at 795 and $970 cm^{-1}$ in Raman spectra of the synthesized SiC NWs at T=$1,400^{\circ}C$ represent the TO and LO mode of the bulk ${\beta}$-SiC, respectively. XRD spectra are also supported to the Raman spectra resulting in the strongest (111) peaks at $2{\Theta}=35.7^{\circ}$, which is the (111) plane peak position of 3C-SiC. Moreover, the gas flow rate of 300 sccm for methane is the optimal condition for synthesis of a large amount of ${\beta}$-SiC NW without producing the amorphous carbon structure shown at a high methane flow rate of 800 sccm. TEM images are shown two kinds of the synthesized ${\beta}$-SiC NWs structures. One is shown the defect-free ${\beta}$-SiC NWs with a (111) interplane distance of 0.25 nm, and the other is the stacking-faulted ${\beta}$-SiC NWs. Also, TEM images exhibited that two distinct SiC NWs are uniformly covered with $SiO_2$ layer with a thickness of less 2 nm.

• KSBB Journal
• /
• v.23 no.6
• /
• pp.513-518
• /
• 2008

This paper described the extraction/purification of $\beta$-carotene from recombinant E.coli and evaluation of anti-wrinkle activity of purified $\beta$-carotene. No significant differences in extraction yields were observed when hexane or isobutyl acetate was used. However, extraction from wet-cell cake resulted in 2-fold higher amount of $\beta$-carotene than that from dry cells. Disruption of 5 g-wet cells by ultrasonic homogenizer, acetone dehydration, extraction with isobutyl acetate resulted in 36 mg of $\beta$-carotene corresponding to 61.2% of recovery. The formation and separation of $\beta$-carotene crystal improved the purity. 633 mg of $\beta$-carotene crystal with 93% purity was obtained from 223 g/L of wet-cell cake harvested from 2.5-L fed-batch culture broth. The cultures of normal human primary fibroblast were performed to investigate the effect of $\beta$-carotene on cytotoxicity as MTT assay and anti-wrinkle activity as collagen synthesis assays. $1.7{\mu}M$ of $\beta$-carotene was found to be optimal concentration at which 1.4-fold higher amount of collagen was synthesized than that in absence of $\beta$-carotene. This indicates that highly purified $\beta$-carotene can be obtained from recombinant E.coli by applying simple method with less toxic solvent and can be used in functional cosmetics as anti-wrinkle agent.