• Journal of the Korean Society for Aviation and Aeronautics
• /
• v.20 no.1
• /
• pp.103-111
• /
• 2012

This study reviews several fracture models for predicting the residual strength of notched composite laminates. Representative experimental results on the residual strength of composite laminates containing a notch subjected to static uniaxial tensile loading have been collected from open literature. And notched strength data for T300/5208 are analyzed. The various parameters associated with the fracture models have been determined for laminates. Notched strength data sets are compared with fracture models and the applicability of the different fracture models in predicting the notched strength of composite laminates is discussed. And static tests have been performed on 2.0mm depth notched specimen. And the test results are compared with analysis models.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.11
• /
• pp.1965-1971
• /
• 1997

The relaxation of stress concentration in notched members can be very significant in the improvement of notched strength and fatigue life. This paper investigated the relationship of stress concentration factor, and notched strength and fatigue life. The stress concentration factors were analyzed by FEM. Uniaxial tensile and fatigue tests were carried on plain woven composite specimens which have a main hole and two defence holes. From experimental results, the notched strength and the fatigue limit increased up to about 50% and 30% respectively due to the reduction in stress concentration. The fatigue lives predicted by Juvinall's approach were underestimated than test results and this trends were remarkable as nothed strength increased. This is because of the underestimation of a coefficient. A in S-N curve (.sigma.$_{ar}$ =A $N_{f}$ $^{B}$). Therefore, considering notched strength the coefficient A was modified. The fatigue lives by this process were agreed well with the experimental results.sults.

• Aerospace Engineering and Technology
• /
• v.7 no.2
• /
• pp.21-26
• /
• 2008

This study reviews several fracture models for predicting the notched strength of composite laminates. Representative experimental results on the notched strength of composite laminates containing a large notch subjected to static uniaxial tensile loading have been collected from open literature. Notched strength data for T300/5208 are analyzed. and the various parameters associated with the fracture models have been determined for laminates. Notched strength data sets are compared with fracture models and the applicability of the different fracture models in predicting the notched strength of composite laminates is discussed.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.7
• /
• pp.1285-1293
• /
• 1992

The fracture behavior of glass/epoxy plain woven composite plates containing circular holes is experimentally investigated to examine the effects of hole size and specimen width on notched tensile strength. It is shown in this paper that the characteristic length according to the point stress criterion depends on the hole size and specimen width. For predicting the notched tensile strength, a modified failure criterion is developed. An excellent agreement is found between the experimental results and the analytical prediction of modified failure criterion. The notched strength and the characteristic length have an increase and decrease relations. When the unstable fracture occured, the critical crack length equivalent for the damage zone size at the edge of hole is about twice the characteristic length. The critical energy release rate G$_{c}$ is independent of hole size(0.03 .leq. 2R/W .leq. 0.5) under the same specimen width. However G$_{c}$ increases with an increase in specimen width which can be explained by stress relaxation due to the notch insensitivity.ity.

• Steel and Composite Structures
• /
• v.25 no.6
• /
• pp.685-692
• /
• 2017

In this study, the effect of various adhesively bonded composite patches on mechanical properties of notched Al-Mg alloy plates was analyzed. For this purpose firstly, the un-notched and notched specimens were fabricated from 5086 Al-Mg alloys which have been used in armor-plated military vehicles. The surface notches as a flaw were machined with circular cutting tool to form notch aspect ratio a/c=0.15 and notch-to-thickness ratios a/t=0.5 in the radial direction on the test specimens. Then, various composite patches which reinforced by glass, carbon and Kevlar fibers were bonded adhesively at elliptically surface notches. Finally, experimental measurements conducted by applying tensile static loading. The experimental results showed that repairing with composite patches with order of carbon, glass and Kevlar fibers have remarkable effect on tensile strength of the notched plate. Also the finite element models were developed using Abaqus/Explicit code to predict the tensile strength and elongation of unrepaired notched specimen and specimen repaired by carbon fiber composite patch. The comparison between numerical and experimental results showed good agreement between them and proved the accuracy of numerical modeling.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.850-856
• /
• 1998

The dynaamic fatigue behavior of alumina ceramics was observed at room temperature using four-point bending method. Dynamic fatigue fracture strength was observed as function of down speed and notch length. The crack growth exponent of the specimens was calculated from the fracture strength and lifetime in dynamic fatigue test. After loading the stresses in the range of 0% to 105% compared with the average in-ert strength the value of residual fracture strength was measured for unnotched and 0.5mm notched speci-mens at the 0.001 and 0.0005 mm/min down speed respectively. After the 95% stress of the average inert strength was applied repeatedly the value of rsidual fracture strength was measured for 0.5mm notched specimens at the 0.001 and 0.0005 mm/min down speed respectively. The material constant A was found to be almost the same and not to depend on the loading mode or the down speed for unnotched and notched specimen. The value of fracture strength with time calculated from the constants n and A was in good agreement with the measured value.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.2 s.32
• /
• pp.41-50
• /
• 1999

As for the properties on both the aluminum and the CFRP which are used to make A17075/CFRP multi-layered hybrid composites, CRALL(carbon reinforced aluminum laminate). In the CRALL specimen for rule of mixture, we were analyzed notched strength by finite element method. The results obtained from FEM analysis are as follows; In the unnotch CRALL specimen, the stresses CFRP, epoxy, Al 7075 obtained by finite element method strength solution for A/C0001, when strain is 0.28%, are 1400MPa, 38MPa, 411MPa. respectively and for A/C9991, when strain 0.48%, are 392MPa, 26MPa and 321Mpa, respectively. the solpe of the stress-strain curve by FEM increases in keeping with the hole size and the yield strain decrease to 36% and 55% for A/C9993 and A/C9991 respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.3
• /
• pp.51-62
• /
• 1999

The objective of this research is to develop paper sludge reinforced thermoplastic composites which incorporate the advantages of each component materials. The effects of paper sludge content(0, 10, 20, 30, 40----), mesh size(20~40, 60~80, less than 100mesh), and coupling agent(Epolene E-43 and Epolene G-3003) on the mechanical properties of paper sludge-polypropylene composites were investigated. Composite density increased with an increase in the paper sludge content. When paper sludge is incorporated into a polypropylene matrix, the flexural properties of the composite increase significantly with an increase in the paper sludge mixing ratio. Especially, flexural modulus was improved with increasing paper sludge content. The flexural strength of composites was improved, but flexural modulus reduced somewhat with decreasing paper sludge particle size. The flexural properties of paper sludge-polypropylene composites were improved by using coupling agents to enhance the bonding between reinforcing filler and matrix. Use of the epolene E-43 and G-3003 resulted in considerable improvement in the flexural strength over control specimens. The flexural strength of the G-3003 composite system is higher than that of the E-43 system. Generally, izod notched impact strength of paper sludge-polypropylene composite decreased slightly, whereas izod unnotched impact strength decreased significantly with increasing paper sludge contents. There was no effects of paper sludge particle size on impact strength of paper sludge-polypropylene composites. And izod unnotched impact strength of epolene E-43 composite system sharply decreased but that of G-3003 composite system was no tendency with increasing additive content.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.4 s.175
• /
• pp.1055-1064
• /
• 2000

First, various specimen geometries, namely, coupon type, waisted type and dog-bone type, were examined to determine appropriate fatigue specimen of thermoplastic composite material AS4/PEEK and the n, fatigue strength of smooth and notched specimens of AS4/PEEK [-45/0/+45/90]2s was investigated. Fatigue tests were performed under load controlled condition at a stress ratio of 0. 1 at a frequency of 5Hz. Stiffness degradation of specimens with fatigue cycling was monitored using an automated unloading compliance technique. The waisted type specimen is found appropriate for smooth fatigue specimen geometry of AS4/PEEK. As for the effect of stress concentration, it is found that fatigue strength is higher for a 2mm-diameter hole notched specimen than a 5mm-diameter one. Fatigue notch factor decreases with the increase of fatigue life. These results are far different from the trend of fatigue strength of metallic materials. The stiffness variation of smooth specimen was only 4% at maximum until final fracture. On the other hand, the stiffness of hole notched specimen was reduced by 45% at maximum. Notched fatigue strength was compared between thermoplastic composite AS4/PEEK and thermosetting composite Graphite/Epoxy. In long-life fatigue (>104), the AS4/PEEK composite shows superior fatigue strength, but in short-life fatigue, the fatigue strength of the Graphite/Epoxy composite is nearly equal or somewhat higher than that of the AS4/PEEK composite.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1818-1823
• /
• 2007

In this paper, notched bar tensile tests of Inconel 617 were performed at room ($20^{\circ}C$) and elevated ($800^{\circ}C$) temperature. Finite element analyses are also performed. It is found that, at the room temperature, smooth bar tensile test results could be used to simulate notched bar tensile tests. However, at the elevated temperature, notched bar tensile test results can not be simulated from smooth bar tensile test results. Metallurgical examination reveals that strength weakening results from many cavities over the specimens for smooth bar test at the elevated temperature. "True" tensile properties at the elevated temperature is found using FE simulations. It also suggests that cautious should be taken to determine tensile properties of Inconel 617 at elevated temperatures using smooth bar tests.