• Korean Chemical Engineering Research
• /
• v.47 no.2
• /
• pp.203-207
• /
• 2009

In the NCAs(non-conductive adhesive) for adhesion of Micro Electro Mechanical System(MEMS), there are some problems such as delamination and cracking, because of the differences of CTE(coefficients of thermal expansion) between NCAs and substrates. Addition of inorganic particle or flexibilizer have been performed to solve those problems. In this study, to improve the flexibility of epoxy adhesive, epoxy/siloxane composites were prepared by adding 1, 3, or 5 phr of amino modified siloxane(AMS). Glass transition temperatures(Tg), moduli and CTE of those composites were measured to confirm effects of siloxane on thermal/mechanical properties of siloxane/epoxy-composites. Tg of AMS/epoxy-composites decreased from $134^{\circ}C$ to $122^{\circ}C$ with increasing AMS contents and moduli decreased from 2,425 MPa to 2,143 MPa with increasing AMS contents. But CTE of AMS/epoxy-composites increased from $67ppm/^{\circ}C$ to $71ppm/^{\circ}C$ with increasing AMS contents. In short, the addition of siloxane is effective for enhancing the flexibility of epoxy but leads to the decrease of Tg.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.29 no.2
• /
• pp.1-13
• /
• 2011

The recent spotlight on electronic touch-screen display, a rapid breakthrough in the information society is evolving. Touch panel input device such as a keyboard or mouse without the use of, the on-screen character or a specific location or object on the person's hand touches a particular feature to identify the location of a panel is to be handled. The touch screen on the touch panel is used in the Ag paste is used mostly for low-curable paste. The thermal-curing paste according to the drying process of thermal energy consumption and improve the working environment of organic solvents have problems. In this study, Ag paste used in the non-thermal curing friendly and cost-effective UV curable paste was prepared. Current commercially available thermal-curable binder, was used instead of the flow characteristics of UV-curable oligomers and monomers with functional groups to give a single conductive Ag paste with the addition of a pattern could be formed. Ag paste as a result, thermal-curing adhesive, hardness, resistance and excellent reproduction of fine patterns and was available with screen printing environmentally friendly could see its potential as a patterning technology.

• Applied Chemistry for Engineering
• /
• v.22 no.1
• /
• pp.104-108
• /
• 2011

In the non-conductive adhesives (NCAs) for adhesion of micro electro mechanical system (MEMS), there are some problems such as delamination and cracking resulting from the large differences of coefficients of thermal expansion (CTE) between NCAs and substrates. So, the addition of inorganic particles such as silica and nano clay to the CTEs composit have been applied to reduce the CTEs of the adhesives. Additions of the flexibilizers such as siloxanes have also been performed to improve the flexibility of epoxy composite. Amino modified siloxane (AMSs) were used to improve compatibility between epoxy and siloxane. In this study, glass transition temperatures (Tg) and moduli of those composites were measured to confirm the effects of AMS with two different equivalents on thermal/mechanical properties of AMS/epoxy composites. Tg of KF-8010/epoxy composites decreased from 148 to $122^{\circ}C$ and those of X-22-161A/epoxy composites decreased from 148 to $121^{\circ}C$. Moduli of KF-8010/epoxy composites decreased from 2648 to 2143 MPa by adding KF-8010 and moduli of X-22-161A/epoxy composites decreased from 2648 to 2014 MPa. In short, using long Si-O chain AMS leads to a greater decrease in moduli. However, haven't showed significant differences in Tg's.