• Journal of the Korean Magnetics Society
• /
• v.20 no.2
• /
• pp.41-44
• /
• 2010

The Cu thickness dependence of magnetic sensitivity for the NiFe/Cu/NiFe/IrMn spin valve multilayer was investigated. The magnetic properties measured by minor MR curves for the Ta(5 nm)/NiFe(8 nm)/Cu(3.5 nm)/NiFe(4 nm)/IrMn(8 nm)/Ta(2.5 nm) multilayer is MR = 1.46 %, MS = 2.0 %/Oe, $H_c\;=\;2.6\;Oe$, and $H_{int}\;=\;0.1\;Oe$. The magnetic sensitivities of GMR-SV devices with ten different widths and a same length of $4.45\;{\mu}m$ by fabricated by photo lithography decreased from 0.3 %/Oe to 0.06%/Oe as from a width of $10\;{\mu}m$ to $1\;{\mu}m$.

• Journal of the Korean Magnetics Society
• /
• v.20 no.2
• /
• pp.35-40
• /
• 2010

The GMR-SV (giant magnetoresistance-spin valve) device depending on the micro patterned features according to two easy directions of longitudinal and transversal axes has been studied. The GMR-SV multilayer structure was Ta(5 nm)/NiFe(8 nm)/Cu(2.3 nm)/NiFe(4 nm)/IrMn(8 nm)/Ta(2.5 nm). The applied anisotropy direction of the GMR-SV thin film was performed under the magnitude of 300 Oe using by permanent magnet during the deposition. The size of micro patterned device was a $1\;{\times}\;18\;{\mu}m^2$ after the photo lithography process. In the aspects of the shape magnetic anisotropy effect, there are two conditions of fabrication for GMR-SV device. Firstly, the direction of sensing current was perpendicular to the magnetic easy axis of the pinned NiFe/IrMn bilayer with the transversal direction of device. Secondly, the direction of shape magnetic anisotropy was same to the magnetic easy axis of the free NiFe layer with the longitudinal direction of device.

• Journal of the Korean Magnetics Society
• /
• v.23 no.3
• /
• pp.98-103
• /
• 2013

The magnetic easy axis of the ferromagnetic layer for the dual-type GMR-SV (giant magnetoresistance-spin valve) having NiFe/Cu/NiFe/IrMn/NiFe/Cu/NiFe multuilayer structure controlled by the post annealing treatment. The magnetoresistive curves of a dual-type IrMn based GMR-SV depending on the direction of the magnetic easy axis of the free and the pinned layers are measured by the different angles for the applied fields. By investigating the switching process of magnetization for an arbitrary measuring direction, the optimum annealing temperature having a steady and isotropy magnetic sensitivity of 2.0 %/Oe was $105^{\circ}C$. This result suggests that the in-plane orthogonal magnetization for the dual-type GMR-SV film can be used by a high sensitive biosensor.

• Journal of the Korean Magnetics Society
• /
• v.12 no.2
• /
• pp.64-67
• /
• 2002

IrMn pinned spin valve (SV) films with stacks of Ta/NiFe/IrMn/CoFe/Cu/CoFe/NiFe/Ta were prepared by dc sputtering onto thermally oxidized Si (111) substrates at room temperature under a magnetic field of about 100 Oe. The annealing cycle number and temperature dependence of exchange coupling field (H$_{ex}$), magnetoresistance (MR) ratio, and coercivity (H$_{c}$) were investigated. By optimizing the process of deposition and post thermal annealing condition, we obtained the IrMn based SV films with MR ratio of 3.6%, H$_{ex}$ of 1180 Oe for the pinned layer. The H$_{ex}$ is stabilized after the second annealing cycle and it is thought that this SV reveals high thermal stability. The H$_{ex}$ maintained its strength of 600 Oe in operation up to 24$0^{\circ}C$ and decreased monotonically to zero at 27$0^{\circ}C$.

• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.156-161
• /
• 2007

To develop array magnetic sensors, specular-type giant magnetoresistive- spin valve (GMR-SV) film of Glass/Ta(5)MiFe(7)/IrMn(10)NiFe(5)/$O_2$/CoFe(5)/Cu(2.6)/CoFe(5)/$O_2$/NiFe(7)/Ta(5)(nm) was deposited by using a high-vacuum sputtering system. One of 15 way sensors in the area of $8{\times}8mm^2$ was Patterned a size of $20{\times}80{\mu}m^2$ in multilayer sample by Photo-lithography. All of 15 sensors with Cu electrodes were measured a uniform magnetic properties by 2-probe method. The highest magnetic sensitivity of MR and output voltage measured nearby an external magnetic field of 5 Oe were MS = 0.5%/Oe and ${\triangle}$V= 3.0 mV, respectively. An easy-axis of top-free layers of $CoFe/O_2/NiFe$ with shape anisotropy was perpendicular to one of bottom-pinned layers $IrMn/NiFe/O_2/CoFe$. When the sensing current increased from 1 mA to 10 mA, the output working voltage uniformly increased and the magnetic sensitivity was almost stable to use the nano-magnetic devices with good sensitive properties.

• Journal of the Korean Magnetics Society
• /
• v.17 no.1
• /
• pp.22-25
• /
• 2007

In this research, magnetic properties of spin valve structures using IrMn layers as antiferromagnetic were studied depending on the thickness of the pinned layer. The spin valve structure was Si substrate/$SiO_2(2,000\;{\AA})/Mo(17\;{\AA})NiFe(21\;{\AA})/CoFe(28\;{\AA})/Cu(22\;{\AA})/CoFe(18\;{\AA})/IrMn(t\;{\AA})/Ta(25\;{\AA})$. Also, Mo film was deposited on Si substrates and the thermal annealing effect was analyzed. The resistivity of the Mo film was increased as an annealing temperature was increased up to $600^{\circ}C$. The variations of MR ratio were related with magnetic exchange coupling field of the spin valve structures for various IrMn pinned layer thickness up to 130 ${\AA}$. MR ratio and $H_{ex}$ of spin valves was about 9.05% and 277.5 Oe when the thickness of the IrMn pinned layer was $32.5\;{\AA}(t=32.5\;{\AA})$. It was increased to 9.65% and 337.5 Oe for $t=65\;{\AA}$. For $t=97.5\;{\AA}$, the MR ratio and Hex decreased to 8.2% and 285 Oe, and further decrease was observed up to $t=130\;{\AA}$.

• Journal of the Korean Magnetics Society
• /
• v.23 no.6
• /
• pp.193-199
• /
• 2013

The regional distribution of magnetic isotropy depending on the post annealing condition for the dual-type structure GMR-SV (giant magnetoresistance-spin valve) of NiFe/Cu/NiFe/IrMn/NiFe/Cu/NiFe multilayer was investigated. The rotation of in-plane ferromagnetic layer induced by controlment of the post annealing temperature inside of the vacuum chamber. The magnetoresistive curves of a dual-type IrMn based GMR-SV depending on the direction of the magnetization easy axis of the free layer and the pinned layer are measured by between $0^{\circ}$ and $360^{\circ}$ angles for the applied fields. The optimum annealing temperature having a steady and isotropy magnetic sensitivity of 1.52 %/Oe was $107^{\circ}C$ in the rotational section of $0{\sim}90^{\circ}$. By investigating the switching process of magnetization for an arbitrary measuring direction, the in-plane orthogonal magnetization for the dual-type GMR-SV multilayer can be used by a high sensitive biosensor for detection of magnetized micro-beads.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.5
• /
• pp.421-426
• /
• 2008

The magnetic bio-sensor used the PHR (planar hall resistance) effect generated by the free layer in spin-valve giant magnetoresistance structure of Ta/NiFe/CoFe/Cu/NiFe/IrMn/Ta. The PHR element with micrometer size was fabricated through the photolithograph and dry etching process. The PHR signal with magnetic field was measured under the conditions of with and without single magnetic bead. A single magnetic bead of diameter $2.8\;{\mu}m$ was successfully detected using the PHR sensor. Therefore, the high resolution PHR sensor can be applied to bio-sensor application utilizing the output voltage variation of the PHR signals in the presence and absence of a single magnetic bead.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.240-244
• /
• 2006

In this paper, magnetic properties and annealing behavior of spin valve structures using Mo(MoN) layers as underlayers were studied varying the thickness of the underlayers. The spin valve structure was consisted of Si substrate/$SiO_2(2,000{\AA})/Mo(MoN)(t{\AA})/NiFe(21\;{\AA})/CoFe(28\;{\AA})/Cu(22\;{\AA})/CoFe(18\;{\AA})/IrMn(65\;{\AA})/Ta(25\;{\AA})$. Also, MoN films were deposited on Si substrates and their thermal annealing behavior was analyzed. The resistivity of the MoN film increased as the $N_2$ gas flow rate was increased. After annealing at $600^{\circ}C$, XRD results did not show peaks of silicides. XPS results indicated MoN film deposited with 5 sccm of $N_2$ gas flow rate was more stable than the film deposited with 1 sccm of $N_2$ gas flow rate. The variations of MR ratio and magnetic exchange coupling fold were small for the spin valve structures using Mo(MoN) underlayers up to thickness of45 ${\AA}$. MR ratio of spin valves using MoN underlayers deposited with various $N_2$ gas flow rate was about 7.0% at RT and increased to about 7.5% after annealing at $220^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased to about 3.5%. Variation of $N_2$ gas flow rate up to 5 sccm did not change the MR ratio and $H_{ex}$ appreciably.

• Journal of Magnetics
• /
• v.5 no.3
• /
• pp.90-98
• /
• 2000

The change in the magnetic properties of a spin-valve multilayer with the structure IrMn (9 m)/CoFe (4 nm)/Cu (2.6 nm)/CoFe (2 nm)/NiEe (6 nm) is investigated as a function of the size and the aspect ratio. At a fixed aspect ratio (the length/width ratio) of 2, the magnetostatic interactions begin to affect the magnetic properties substantially at a spin-valve length of 5 $\mum$, and, at a length of 1 $\mum$, they become even more dominant. In the case of a fixed multilayer size (2.4 $\mum$) which is indicated by the sum of the length and the width, magnetization change occurs by continuous spin-reversal and M-H loops are characterized by no or very small hysteresis at aspect ratios smaller than unity, At aspect ratios greater than unity, magnetization change occurs by spin-flip resulting in squared hysteresis loops. A very large changes in the coercivity and the bias field is observed, and these results are explained by two separate contributions to the total magnetostatic interactions: the coercivity by the self-demagnetizing field and the bias field by the interlayer magnetostatic interaction field.