• KEPCO Journal on Electric Power and Energy
• /
• 제6권4호
• /
• pp.461-466
• /
• 2020

There are many application fields of electrical energy storage such as load shifting, integration with renewables, frequency or voltage supports, and so on. Especially, the frequency regulation is needed to stabilize the electric power system, and there have to be more than 1 GW as power reserve in Korea. Ni-rich layered oxide cathode materials have been investigated as a cathode material for Li-ion batteries because of their higher discharge capacity and lower cost than lithium cobalt oxide. Nonetheless, most of them have been investigated using small coin cells, and therefore, there is a limit to understand the deterioration mode of Ni-rich layered oxides in commercial high energy Li-ion batteries. In this paper, the pouch-type 20 Ah-scale Li-ion full cells are fabricated using Ni-rich layered oxides as a cathode and graphite as an anode. Above all, two test conditions for the application of frequency regulation were established in order to examine the performances of cells. Then, the electrochemical performances of two types of Ni-rich layered oxides are compared, and the long-term performance and degradation mode of the cell using cathode material with high nickel contents among them were investigated in the frequency regulation conditions.

• Journal of Industrial and Engineering Chemistry
• /
• 제68권
• /
• pp.180-186
• /
• 2018

We report the discovery of Li-rich $Li_{1+x}[(Ni_{0.225}Co_{0.15}Mn_{0.625})_{1-y}V_y]O_2$ as a cathode material for rechargeable lithium-ion batteries in which a small amount of tetravalent vanadium ($V^{4+}$) is selectively and completely incorporated into the manganese sites in the lattice structure. The unwanted oxidation of vanadium to form a $V_2O_5-like$ secondary phase during high-temperature crystallization is prevented by uniformly dispersing the vanadium ions in coprecipitated $[(Ni_{0.225}Co_{0.15}Mn_{0.625})_{1-y}V_y](OH)_2$ particles. Upon doping with $V^{4+}$ ions, the initial discharge capacity (>$275mA\;h\;g^{-1}$), capacity retention, and voltage decay characteristics of the Li-rich layered oxides are improved significantly in comparison with those of the conventional undoped counterpart.

• 한국재료학회지
• /
• 제28권5호
• /
• pp.273-278
• /
• 2018

Lithium-ion batteries have been considered the most important devices to power mobile or small-sized devices due to their high energy density. $LixCoO_2$ has been studied as a cathode material for the Li-ion battery. However, the limitation of its capacity impedes the development of high capacity cathode materials with Ni, Mn, etc. in them. The substitution of Mn and Ni for Co leads to the formation of solid solution phase $LiNi_xMn_yCo_{1-x-y}O_2$ (NMC, both x and y < 1), which shows better battery performance than unsubstituted $LiCoO_2$. However, despite a high discharge capacity in the Ni-rich compound (Ni > 0.8 in the metal site), poor cycle retention capability still remains to be overcome. In this study, aiming to improve the stability of the physical and chemical bonding, we investigate the stabilization effect of Ca in the Ni-rich layered compound $Li(Ni_{0.83}Co_{0.12}Mn_{0.05})O_2$, and then Ca is added to the modified secondary particles to lower the degree of cationic mixing of the final particles. For the optimization of the final grains added with Ca, the Ca content (x = 0, 2.5, 5.0, 10.0 at.%) versus Li is analyzed.

• 공업화학
• /
• 제31권1호
• /
• pp.97-102
• /
• 2020

최근 리튬이차전지 양극 소재의 다양한 열화 메커니즘들이 밝혀지면서 이것을 제어하여 새로운 전기화학적 특성을 구현하고 기존 소재의 한계점을 극복하고자 하는 연구결과들이 많이 보고되고 있다. 특히, 리튬과잉산화물은 250 mA h g^-1 이상의 고 용량 차세대 리튬이차전지 양극 물질로 주목받고 있으나, 충방전 과정 중에 소재 특유의 원자 구조 열화로 인해 활용이 제한되고 있다. 본 연구는 0.4Li₂MnO₃_0.6LiNi_1/3Co_1/3Mn_1/3O₂ 리튬과잉소재의 충방전 과정 중에서 겪는 원자 구조 변화 과정을 분석하여 소재의 열화 과정을 밝히고 이를 개선하기 위한 연구 방향을 제시하고자 한다. 이를 위해, 원자 단위의 분해능을 갖는 전자투과현미경을 활용하여 충방전 중 원자 구조의 변화 과정을 분석하고 이러한 구조 변화가 소재의 전기화학적 특성에 어떠한 영향을 미치는지 밝히고자 하였다. 충전 과정 중에 발생한 다량의 리튬 빈자리로 인해 구조 불안정성이 일어났고, 이로 인해 전이 금속이 리튬 빈 자리로 이동하면서 구조 열화가 확인되었다. 결과적으로 이러한 구조 변이는 리튬과잉소재의 가장 큰 문제점인 방전 전압 강하 특성을 야기한다는 것을 알아내었다.

• Corrosion Science and Technology
• /
• 제14권3호
• /
• pp.113-119
• /
• 2015

Alloy 82/182 weld metals had been extensively used in joining the components of the PWR primary system. Unfortunately, there have been a number of incidents of cracking caused by PWSCC in Alloy 82/182 welds during the operation of PWR worldwide. To mitigate PWSCC, optimization of water-chemistry conditions, especially dissolved hydrogen (DH) and Zn contents, is considered as the most promising and effective remedial method. In this study, the PWSCC behaviours of Alloy 182 weld were investigated in simulated PWR environments with various DH content. Both in-situ and ex-situ oxide characterizations as well as PWSCC initiation tests were performed. The results showed that PWSCC crack initiation time was shortest in PWR water (DH: 30cc/kg). Also, high stress reduced crack initiation time. Oxide layer showed multi-layered structures consisted of the outer needle-like Ni-rich oxide layer, Fe-rich crystalline oxide, and inner Cr-rich inner oxide layers, which was not altered by the level of applied stress. To analyse the multi-layer structure of oxides, EIS measurement were fitted into an equivalent circuit model. Further analyses including TEM and EDS are underway to verify appropriateness of the equivalent circuit model.

• Journal of Electrochemical Science and Technology
• /
• 제13권2호
• /
• pp.269-278
• /
• 2022

Utilization of high-voltage electrolyte additive(s) at a small fraction is a cost-effective strategy for a good solid electrolyte interphase (SEI) formation and performance improvement of a lithium-rich layered oxide-based high-energy lithium-ion cell by avoiding the occurrence of metal-dissolution that is one of the failure modes. To mitigate metal-dissolution, we explored fluorinated dual-additives of fluoroethylene carbonate (FEC) and di(2,2,2-trifluoroethyl)carbonate (DFDEC) for building-up of a good SEI in a 4.7 V full-cell that consists of high-capacity silicon-graphite composite (15 wt% Si/C/CF/C-graphite) anode and Li_1.13Mn_0.463Ni_0.203Co_0.203O₂ (LMNC) cathode. The full-cell including optimum fractions of dual-additives shows increased capacity to 228 mAhg^-1 at 0.2C and improved performance from the one in the base electrolyte. Surface analysis results find that the SEI stabilization of LMNC cathode induced by dual-additives leads to a suppression of soluble Mn²⁺-O formation at cathode surface, mitigating metal-dissolution event and crack formation as well as structural degradation. The SEI and structure of Si/C/CF/C-graphite anode is also stabilized by the effects of dual-additives, contributing to performance improvement. The data give insight into a basic understanding of cathode-electrolyte and anode-electrolyte interfacial processes and cathode-anode interaction that are critical factors affecting full-cell performance.

• 한국재료학회지
• /
• 제30권11호
• /
• pp.636-640
• /
• 2020

Due to the serious air pollution problem, interest in eco-friendly vehicles is increasing. Solving the problem of pollution will necessitate the securing of high energy storage technology for batteries, the driving force of eco-friendly vehicles. The reason for the continuing interest in the transition metal oxide LiMO₂ as a cathode material with a layered structure is that lithium ions reveal high mobility in two-dimensional space. Therefore, it is important to investigate the effective intercalation and deintercalation pathways of Li⁺, which affect battery capacity, to understand the internal structure of the cathode particle and its effect on the electrochemical performance. In this study, for the cathode material, high nickel Ni_0.8Co_0.1Mn_0.1(OH)₂ precursor is synthesized by controlling the ammonia concentration. Thereafter, the shape of the primary particles of the precursor is investigated through SEM analysis; X-ray diffraction analysis is also performed. The electrochemical properties of LiNi_0.8Co_0.1Mn_0.1O₂ are evaluated after heat treatment.