• 한국세라믹학회지
• /
• 제37권2호
• /
• pp.164-167
• /
• 2000

Flue gases in the iron foundry consist of 15~20% CO2 as an air pollution gas whose emission should be mitigated in order to protect the environment. In the present study, ultrafine powders of NixZn1-xFe2O4 as a potential catalyst for the CO2 decomposition were prepared by the coprecipitation methods. Oxygen deficient ferrites (MeFe2O4-$\delta$) can decompose CO2 as C and O2 at a low temperature of about 30$0^{\circ}C$. The XRD result of synthesized ferrites showed the spinel structure of ferrites and ICP-AES and EDS quantitative analyses showed the composition similar with initial molar ratios of the mixed solution prior to reaction. The BET surface area of the (Ni, Zn)-ferrites was about 77~89.5$m^2$/g and their particle size was observed about 10~20 nm. The CO2 decomposition efficiency of the oxygen deficient (Nix, Zn1-x)-ferrites was the highest at x=0.3, and the ternary (Ni, Zn)-ferrites was better than that of binary Ni-ferrites.

• 한국세라믹학회지
• /
• 제40권2호
• /
• pp.146-152
• /
• 2003

지구온난화의 주요 원인인 $CO_2$를 분해시키기 위하여 Ni-Zn 페라이트와 Mn-Zn 페라이트 코어 제조시 대량으로 배출되는 페라이트 폐기물을 이용하였다. 폐기물 페라이트와 페라이트 코어 완제품인 Ni-Zn 페라이트와 Mn-Zn 페라이트는 5% $H_2$/Ar과의 환원반응에서 14~16wt%가 환원되었다. 환원된 페라이트를 이용한 $CO_2$분해 반응에서는 세 종류의 페라이트 모두 약 11wt%에 해당하는 $CO_2$를 분해하였다. 이 반응에서 $CO_2$는 환원된 페라이트 중 Fe와 FeO치 산화에 의해 분해되었으며. 폐기물 페라이트의 경우 $CO_2$분해 반응 후 스피넬 결정상을 형성하였다. 대량으로 버려지는 폐기물 페라이트를 이용하여 저비용으로 $CO_2$분해가 가능한 폐기물 활용기술을 개발하였다.

• 한국자기학회지
• /
• 제7권1호
• /
• pp.19-24
• /
• 1997

적층형 chip inductor 소재인 NiCuZn ferrite의 제조 공정 조건 및 조성을 선정하였다. NiCuZn ferrite의 NiO 함량이 증가할 수록 저온 소결에 필요한 Fe$_{2}$O$_{3}$ 결핍량은 점차 증가하였고, NiO 함량과 Co$_{3}$O$_{4}$ 첨가량을 변화하여 투자율을 12 ~ 562 범위에서 제어할 수 있었다. NiCuZn ferrite의 투자율이 562에서 60으로 변화함에 따라서 Q$_{max}$ 주파수는 3 MHz에서 50 MHz 범위로 제어할 수 있었다. 이때 Q$_{max}$ 주파수(Y)와 투자율(X)은 log Y = 4.2-1.4 log X의 상관관계를 나타내었다.

• 한국재료학회지
• /
• 제10권3호
• /
• pp.223-226
• /
• 2000

산소 결핍 페라이트 (oxygen deficient ferrites, ODF) $MeFe_2O_{4-\delta}$는 약 $300^{\circ}C$의 낮은 온도에서 $CO_2$를 C와 $O_2$로 분해한다. 본 연구에서는 $(Ni_x,\;Zn_{1-x}Fe_2_4$ 초미세 페라이트 분말을 수열합성법으로 제조하여 $CO_2$ 분해특성을 살펴보았다. 제조된 페라이트는 XRD 분석 결과, 페라이트의 전형적인 스피넬 구조를 보여주고 있으며, ICP-AES, EDS 정량분석에 의하여 초기 혼합 조성비와 거의 동일한 조성비로 합성되었음을 알 수 있었다. 제조된 (Ni, Zn)-ferrites 분말의 BET 비표면적은 약 $110\textrm{mg}^2$/g$ 이상의 큰 값으로 나타났으며, 입자크기는 약 5~10nm로 매우 작았다. 산소결핍 페라이트 $(Ni_x,\;Zn_{1-x})Fe_2O_{4-{$\delta}}$의 $CO_2$ 분해 효율은 조성에 따라 큰 차이를 보이지 않았으며 3원계 (Ni, Zn)-ferrite가 Ni-ferrite보다 더 높았다.

• 한국재료학회지
• /
• 제11권10호
• /
• pp.846-850
• /
• 2001

In the present study, nano-size powders of ternary ferrites, $Ni_{0.5}Zn_{0.5}Fe_2O_4$, as the potential catalysts of $CO_2$decomposition, were prepared by the wet processing of hydrothermal synthesis and coprecipitation method, and the catalyzing effects of impregnation of the noble metals, Pt and Pd, onto $Ni_{0.5}Zn_{0.5}Fe_2O_4$for the $CO_2$decomposition were investigated. XRD results of the synthesized ferrites showed a typical spinel structure of ferrite and the particle size was very small as about 6~10 nm. BET surface area of the ternary ferrites was not affected by the impregnation of Pt and Pd. The reactivity of the $CO_2$decomposition to carbon was improved by the impregnation of the noble metals of Pd and Pt. The effect of Pd-impregnation on the $CO_2$decomposition rate was higher than Pt-impregnation.

• 한국자기학회지
• /
• 제6권6호
• /
• pp.382-387
• /
• 1996

본 연구에서는 ${(Ni_{x}Cu_{0.2}Zn_{0.8-x}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$의 Ni 함량(x)과 $Co_{3}O_{4}$ 첨가량에 따른 복소투자율 변화에 관하여 검토하였다. Ni 함량 x=0.6 이상에서는 매우 좁은 투자율 허수항($\mu$") 피이크가 형성됨으로서 다른 조성에 비해 손실이 적음을 알 수 있었고 공명주파수($f_{\mu"max}$)는 Ni 함량의 변화와 비례하여 현저하게 증가하였다. $Fe_{2}O_{3}$ 결핍량(w)이 많을 수록 $\mu$" 값은 낮았으나, $Fe_{2}O_{3}$ 결핍량(w)의 변화가 공명주파수에는 큰 영향을 미치지 않는 경향을 나타내었다. NiCuZn 페라이트 조성에 대하여 $Co_{3}O_{4}$를 첨가한 경우는 첨가량이 많아짐에 따라 초기투자율이 감소하여 $f_{\mu"max}$ 값은 증가하였으나, 전체적인 손실의 정도를 제어하는데에는 Ni 함량을 변화시키는 것이 더 효과적임을 알 수 있었다.

• 한국분말재료학회지
• /
• 제21권6호
• /
• pp.429-433
• /
• 2014

This study investigated the magnetic properties and frequency dispersion of complex permeability of Ni-Zn-Co ferrites used for magnetic shielding in near field communication (NFC) system. The sintered specimens of $(Ni_{0.7}Zn_{0.3})_{1-x}Co_xFe_2O_4$ composition were prepared by the conventional ceramic processing. The coercive force and saturation magnetization were measured by vibrating sample magnetometer. The complex permeability was measured by RF impedance analyzer in the range of 1 MHz~1.8 GHz. The coercive force increased and saturation magnetization decreased with increasing the Co substitution. The real and imaginary parts of complex permeability decreased and the resonance frequency increased with Co substitution, which was attributed to the increase in crystal anisotropy field and reduction in saturation magnetization. The effect of Co substitution could be found in reducing the magnetic loss to nearly zero at the operating frequency of NFC (13.56 MHz).

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.31.1-31
• /
• 2000

• Journal of Magnetics
• /
• 제21권1호
• /
• pp.40-45
• /
• 2016

Nickel substituted nano-sized ferrite powders, $Co_{1-x}Ni_xFe_2O_4$, $Mn_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ($0.0{\leq}x{\leq}0.2$), were fabricated using a sol-gel method, and their crystallographic and magnetic properties were subsequently compared. The lattice constants decreased as quantity of nickel substitution increased, while the particle size decreased in $Co_{1-x}Ni_xFe_2O_4$ ferrite but increased for the $Mn_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ferrites. For the $Co_{1-x}Ni_xFe_2O_4$ and $Mn_{1-x}Ni_xFe_2O_4$ ($0.0{\leq}x{\leq}0.2$) ferrite powders, the $M{\ddot{o}}ssbauer$ spectra could be fitted as the superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the $Fe^{3+}$ ions. However, the $M{\ddot{o}}ssbauer$ spectrum of $Mn_{0.8}Zn_{0.1}Ni_{0.1}Fe_2O_4$ consisted of two Zeeman sextets and one single quadrupole doublet due to the ferrimagnetic and paramagnetic behavior. The area ratio of the $M{\ddot{o}}ssbauer$ spectra could be used to determine the cation distribution equation, and we also explain the variation in the $M{\ddot{o}}ssbauer$ parameters by using this cation distribution equation, the superexchange interaction and the particle size. The saturation magnetization decreased in the $Co_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ferrites but increased in the $Mn_{1-x}Ni_xFe_2O_4$ ferrite with nickel substitution. The coercivity decreased in the $Co_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ferrites but increased in the $Mn_{1-x}Ni_xFe_2O_4$ ferrite with nickel substitution. These variations could thus be explained by using the site distribution equations, particle sizes and spin magnetic moments of the substituted ions.

• 한국자기학회지
• /
• 제5권1호
• /
• pp.15-20
• /
• 1995

연자성재료인 Mn-Zn 페라이트에 미량의 첨가물로 CaO(0.1 mol%), NiO(0.0~6.0 mol%) 그리고 CoO(0.0~0.8 mol%) 첨가하여 20 종류의 시료를 공침법으로 제조하여, 첨가물의 첨가량에 따른 Mn-Zn 페라이트의 자기적 성질을 연구하였다. NiO, CoO의 첨가량이 증가함에 따라 초기투자율은 감소하고, 반면 Curie 온도는 증가하였다. 보자력$(H_{c})$, 포화자화$(B_{s})$ 및 자기이력손실$(W_{h})$은 NiO의 첨가량이 증가함에 따라 증가하는 것으로 나타났다.