• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.6
• /
• pp.663-668
• /
• 2017

SOFC anode fabricated core-shell using machano-fusion method using core with submicron size Ni, nano size YSZ for shell. Using prepared core-shell, depending on the thickness of the shell, we studied how the characteristics of sintering and SOFC cell change by sintering the anode. The Ni-YSZ core-shell has a Ni core of 0.5 to $1.2{\mu}m$ over 2 to 7 YSZ of 15 to 20 nm is, and as the high speed mixing time increases, the YSZ number increases and the shell thickness becomes uniform increased. When the fuel electrode is manufactured with core-shell, it has superior sintering property, has grain of uniform size compared with the one synthesized by general mixing, the falling path is short, the conductors (electrons and ions) connection is excellent, the electrical conductivity has become excellent. The thicker the shell, the lower the electrical conductivity. When the thickness of shell ranged from 46 to 139 nm and 61 to 81 nm, the performance was the highest and the ASR was the smallest.

• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.357-361
• /
• 2014

An Ni-Fe/YSZ core-shell structured anode for uniform microstructure and catalytic activity was synthesized. Flat tubular segmented-in-series solid oxide fuel cell-stacks were prepared by decalcomania method using synthesized anode powder. The Ni-Fe/YSZ core-shell anode exhibited better electrical conductivity than a commercially available Ni-YSZ cermet anode. Also power output increased by 1.3 times with a higher open circuit voltage. These results can be attributed to the uniformly distributed Ni particles in the YSZ framework. The impedance spectra of a Ni-Fe/YSZ core-shell anode showed comparable reduced ohmic resistance similar to those of the commercially available Ni-YSZ cermet anodes.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.103.1-103.1
• /
• 2011

고체 산화물 연료전지(SOFC)는 크게 음극(anode), 양극(cathode), 전해질(electrolyte)로 구성되 있으며 연결자를 통해 직렬 또는 병렬로 연결된 형태로 발전장치 등에 활용되고 있다. 이중 연료의 산화반응을 담당하고 있는 연료전지의 음극으로 지금까지 Cobalt, Platinum, Palladium 등의 전이금속 또는 귀금속들이 사용되었지만 현재는 Nickel 또는 Nickel을 함유한 물질들 특히, Ni-YSZ 복합체가 주로 사용되고 있다. Ni-YSZ 복합체는 가격과 성능 등 여러가지 면에서 SOFC의 음극으로 사용하기에 가장 적합한 물질인데 특히 전지의 지지체 역할과 동시에 전극으로서의 역할도 병행해야하는 음극 지지형 SOFC의 경우 Ni-YSZ 복합체의 효용성을 더욱 커지게 된다. 본 연구에서는 SOFC의 음극물질로 가장 널리 쓰이고 있는 Ni-YSZ 복합체를 core shell 형태로 만들어 전도 path를 효율적으로 하고 그 특성을 최적화하기 위한 미세구조 및 소결 거동, 전기적 특성을 평가하였다.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.1
• /
• pp.40-46
• /
• 2017

We reviewed the electrical properties of SOFC anode manufactured using spherical Ni and nano YSZ powder. When core-shell is fabricated by using submicron Ni as core and nano-sized YSZ as shell for SOFC anode, the electrical conductivity of the $0.2{\mu}m$ Ni-YSZ core-shell was 3 times higher than that of $1.0{\mu}m$ NiO or $1.0{\mu}m$ Ni-YSZ. Hydrogen selectivity was similar at $800^{\circ}C$, but hydrogen selectivity and methane conversion rate under $750^{\circ}C$ was 10~25% higher, Power density was more than 2 times, ASR was about 1/3, when exposed to $H_2$ atmosphere at $750^{\circ}C$ for a long time, Ni particles did not have any growth or cut off conduction path.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.31.2-31.2
• /
• 2011

We studied a method of manufacturing an anode to restrict contraction in reducing NiO/YSZ by uniformly mixing. In order to mix Ni and YSZ, a sub-micron Ni core surface was coated at high-speed by a mixture of nano-sized YSZ and a spherical core-shell was subsequently formed. The micron-sized core-shell anode powder was then heat treated at $400{\sim}1,450^{\circ}C$ in an air atmosphere and Ni was extruded and synthesized in nano-size. Subsequently, when the nano-sized mixture of the anode was heat treated and maintained at a temperature of $1,450^{\circ}C$, the anode was manufactured, where Ni and YSZ were uniformly distributed with the nano-structure. According to the nano-sized anode powder synthesis process, Ni particles were oxidized at $400{\sim}500^{\circ}C$ and became spherical by surface tension. In the case of the spherical core Ni powder, the heat treatment temperature rose to $1,250^{\circ}C$ and then a gap between the internal and external pressures occurred due to thermal and tensile stresses. A crack subsequently appeared on the surface, and the heat treatment temperature was increased continuously to increase the pressure gap and then the core Ni extruded as a nano-sized powder, Ni and YSZ uniformly distributed. It was found that the anode of 50~200 nm with a consistent structure obtained in this study has electric conductivity that is approximately 3 times larger than that of a commercial anode.

• Journal of the Korean Ceramic Society
• /
• v.43 no.12 s.295
• /
• pp.781-787
• /
• 2006

NiO-coated YSZ powder was prepared using heterogeneous precipitation of Ni hydroxides on YSZ particle surface and high energy milling. The powders were characterized by TG/DTA, XRD, XPS, and SEM. Amorphous Ni precipitate completely decomposed into NiO at $500^{\circ}C$ and the growth of NiO crystallites was constrained by the core particles. Nanocrystalline NiO-coated YSZ core-shell structure powder could be obtained after calcination at $800^{\circ}C$ for 2 h. A core-shell powder compact, due to high sinterability, showed a near theoretical density at $1350^{\circ}C$. After reduction at $900^{\circ}C$, interpenetrating Ni-YSZ microstructure with very uniformly distributed fine Ni and YSZ grains and pores was observed. In contrast, the mechanically mixed oxide sample showed less uniform distribution of pores and larger discontinuous We particles as compared with the core-shell samples.