• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.3
• /
• pp.43-50
• /
• 2014

By the trends of electronic package to be smaller, thinner and more integrative, the reliability of interconnection between Si chip and printed circuit board is required. This paper reports on a study of high speed shear energy of Sn-4.0wt%Ag-0.5wt%Cu (SAC405) solder joints with different the thicknesses of electroless Ni-P deposit. A high speed shear testing of solder joints was conducted to find a relationship between the thickness of Ni-P deposit and the brittle fracture in electroless Ni-P deposit/SAC405 solder. A focused ion beam (FIB) was used to polish the cross sections to reveal details of the microstructure of the fractured pad surface with and without $HNO_3$ vapor treatment. The high speed shear energy of SAC405 solder joint with $1{\mu}m$ Ni-P deposit was found to be lower without $HNO_3$ vapor, compared to those of over $3{\mu}m$ Ni-P deposit. This could be due to the edge of solder resist in $1{\mu}m$ Ni-P deposit, which provides a fracture location for the weakened shear energy of solder joints and brittle fracture in high speed shear test. With $HNO_3$ vapor, the brittle fracture mode in high speed shear test decreased with increasing the thickness of Ni-P deposit. Then the roughness (Ra) of Ni-P deposits decreased with increasing its thickness. Thus, this gives the evidence that the decrease in roughness of Ni-P deposit for Eelectroless Ni/ Electroless Pd/ Immersion Au (ENEPIG) surface play a critical role for improving the robustness of SAC405 solder joint.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.4
• /
• pp.197-201
• /
• 2018

Dynamic nano-indentation method was applied to characterize thin electroformed Ni-P layers. The Ni-P layers were produced in a sulphamic acid bath at $50^{\circ}C$ in $0.02A/cm^2$ for 10-60 minutes. The chemical analyses by XRD and EDX showed that the Ni-P layers were very fine grains with mainly $Ni_3P$ with Ni. The surface roughness determined by atomic force microscopy increased with thickness, which was relative to the surface morphology. The nano-hardness and the stiffness of the thin Ni-P layers with thickness of 1.9, 6.2 and $7.5{\mu}m$ were 5.52, 6.52 and 6.77 [GPa] and 56.7, 76.2 and 108.0 [${\mu}N/nm$], respectively. The elastic modulus of the Ni-P layer increased with thickness such as 37.29, 54.50 and 78.76 [GPa], respectively. The surface roughness of the electroplated Ni-P layers with diverse thickness was 8.66, 18.56 and 35.22 [nm], respectively. The enhanced nano-mechanical properties were related to mainly residual stress of the Ni-P layers.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.6
• /
• pp.315-323
• /
• 2021

In general, surface treatments of electroless Ni-P coating are extensively applied in the industry due to their excellent properties for considerable wear resistance, hardness, corrosion resistance. This study aims to determine the effect of ultrasonic conditions on the morphology, alumina content, roughness, hardness, and corrosion resistance of electroless Ni-P-Al₂O₃ composite coatings. The characteristics were analyzed by Energy-dispersive X-ray spectroscopy (EDX), x-ray diffractions (XRD), and atomic force microscopy (AFM), etc. In this study, the effect of ultrasonic condition uniformly distributed alumina within Ni-P solution resulting in a smoother surface, lower surface roughness. Furthermore, the corrosion resistance behavior of the coating was analyzed using tafel polarization curves in a 3.5 wt.% NaCl solution at 25 ℃. Under ultrasonic, Al₂O₃ content in Ni-P composite solution increased from 0.5 to 5.0 g/L, Al₂O₃ content at 3.0 g/L was showed a significantly enhanced corrosion resistance. These results suggested that ultrasonic condition was an effective method to improve the properties of the composite coating.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.6
• /
• pp.437-443
• /
• 2003

The effects of additive(grain refiner, GR) on process efficiency of the Ni-Fe-P alloy electrodeposition and the material properties of the deposit were investigated. Electrochemical properties of the deposits were investigated using polarization and electrochemical impedance techniques, and the material properties of the deposits were characterized through inductively coupled plasma(ICP), spiral contractometer, XRD, SEM and TEM. When the additive was added into the electrodeposition bath, current efficiency, Ni content and corrosion resistance of the deposit increased, whereas residual stress, surface roughness and grain size of the deposit decreased.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.1
• /
• pp.32-38
• /
• 2007

Ni coating layers were formed using a newly developed electroless Ni plating solution. The properties of Ni coating layer such as internal stress, hardness, surface roughness, crystallinity, solderability and surface morphology were investigated using various tools. Results revealed that internal stress decreased with plating time and reached $40N/mm^2$ at 20 minutes of the plating time. Hardness increased with increasing P content and thickness. Surface roughness of the pad decreased with Ni and Ni/Au plating. Crystallinity decreased with increasing P content. Solderability based on wettability decreased with Ni and Ni/Au plating. Based on surface morphology, it is expected that Ni coating layer formed using a newly developed electroless Ni plating solution is lower than that formed using a commercial electroless Ni plating solution in possibility of black pad occurrence.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.3
• /
• pp.51-56
• /
• 2014

The reliability of solder joint is significantly affected by the property of surface finish. This paper reports on a study of high speed shear energy and failure mode for Sn-4.0wt%Ag-0.5wt%Cu (SAC405) solder joints with the time of Pd activation. The nodule size of electroless Ni-P deposit increased with increasing the time of Pd activation. The roughness (Ra) of electroless Ni-P deposit decreased with increasing the time of Pd activation. Then, with $HNO_3$ vapor, the quasi-brittle and brittle mode of SAC405 solder joint decreased with increasing the time of Pd activation. This results indicate that the increase in the Pd activation time for Electroless Ni/ Electroless Pd/ Immersion Au (ENEPIG) surface finish play a critical role for improving the robustness of SAC405 solder joint.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.1
• /
• pp.65-72
• /
• 2011

Purpose: The purpose of this study was to evaluate the level of electro-chemical corrosion and surface roughness change for the cases of Ti abutment connected to restoration made of base metal alloys. Materials and methods: It was hypothesized that Ni-Cr alloys in different compositions possess different corrosion resistances, and thus the specimens ($13{\times}13{\times}1.5\;mm$) in this study were fabricated with 3 different types of metal alloys, commonly used for metal ceramic restorations. The electrochemical characteristics were evaluated with potentiostat (Parstat 2273A) and the level of surface roughness change was observed with surface roughness tester. Paired t-test was used to compare mean average surface roughness (Ra) changes of each specimen group. Results: All specimens made of nickel-chromium based alloys, average surface roughness was increased significantly (P < .05). Among them, the Ni-Cr-Be alloy ($0.016{\pm}.007\;{\mu}m$) had the largest change of roughness followed by Ni-Cr ($0.012{\pm}.003\;{\mu}m$) and Ni-Cr-Ti ($0.012{\pm}.002\;{\mu}m$) alloy. There was no significant changes in surface roughness between each metal alloys after corrosion. Conclusion: In the case of galvanic couples of Ti in contact with all specimens made of nickel-chromium based alloys, average surface roughness was increased.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.2
• /
• pp.178-190
• /
• 2000

The purpose of this study was to evaluate the surface roughness of Ni-Cr-Be alloy($Verabond^{(R)}$, Aalba Dent Inc., USA) according to electrolyte concentration and etching time. Total of 150 metal specimens ($12{\times}10{\times}1.5mm$) composed of 5 polisded specimens, 5 sandblasted specimens, 140 etched specimens were prepared. Etched groups were divided into 28 groups by the $HClO_4$ concentrations(10, 30, 50, 70%) and etching times(15, 30, 60, 120, 180, 240, 300 seconds). The mean surface roughness(Ra) and the etching depth were measured with Optical 3-dimensional surface roughness measuring machine(Accura 1500M, Intek Engineering Co., Korea) and observed under SEM. The results obtaind were as follows: 1. Surface roughness(Ra) and etching depth were affected by the order of etching time, electrolyte concentration, and their interaction(P<0.05). 2. Surface roughness(Ra) and etching depth were increased with etching time in 10%, 30% electrolyte concentrations, but they had no significant difference with etching time in 70% (P<0.05). 3. Surface roughness(Ra) and etching depth decreased in the order of 30, 10, 50, 70% electrolyte concentrations from 120 seconds etching time(P<0.05). 4. The remarkable morphologic changes in etched surface were observed along the grain boundaries in 15, 30 seconds of 10%, 30% concentrations and the morphologic changes could be denoted in the grains themselves as well as along the boundaries with the lapse of time. Even though the noticeable morphologic changes also took place in etched surface with 50% concentration, the degree of changes were less than that of changes with 10%, 30%. However, there were little morphologic changes with 70% concentration regardless of etching time. 5. Surface roughness(Ra) of sandblasting group with $50{\mu}m\;Al_2O_3$ had no significant difference with 30%-30 seconds etched group(P<0.05).

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.1
• /
• pp.1-19
• /
• 2003

The surface of metals should be as smooth as possible for optimum comfort, oral hygiene, low plaque retention, and resistance to corrosion. In this study five specimens of each precious metal(type III gold alloy, ceramic gold alloy, and Ag-Pd alloy) were divided into five groups according to finishing and polishing procedures : group 1(sandblaster), group 2(group 1+stone), group 3(group 2+brown rubber), group 4(group 3+green rubber), and group 5(group 4+rouge). Six specimens of each non-precious metal(Co-Cr alloy, Ni-Cr alloy, and Co-Cr-Ti alloy) were divided into six groups: group 1(sandblaster), group 2(group 1+hard stone), group 3(group 2+electrolytic polisher), group 4(group 3+brown hard rubber point), group 5(group 4+green hard rubber point), and group 6(group 5+rouge). Considering factors affecting the rate of abrasion, the same dentist applied each finishing and polishing procedure. In addition, the surface roughness of enamel, resin, and porcelain was evaluated. The effect of finishing and polishing procedures on surface roughness of precious and non-precious metals, enamel, resin, and porcelain was evaluated by means of Atomic Force Microscope(AutoProbe CP. Park Scientific Instruments, U.S.A.) that can image the three dimensional surface profile and measure average surface roughness values of each sample at the same time. The obtained results were as follows : 1. According to finishing and polishing procedures, the surface roughness of type III gold alloy, ceramic gold alloy, and Ag-Pd alloy was decreased in the order of group 1, 2, 3, 4, and 5 (P<0.01). 2. According to finishing and polishing procedures. the surface roughness of Co-Cr alloy, Ni-Cr alloy, and Co-Cr-Ti alloy was decreased in the order of group 1, 2, 3, 4, 5, and 6 (p<0.01). 3. There was not statistically significant difference in the surface roughness among three metals of precious metals in group 1 but was significant difference in group 2, 3, 4, and 5 (P<0.05). 4. There was not statistically significant difference in the surface roughness among three metals of non-precious metals in all groups. 5. When the surface roughness of the smoothest surface of each metal, enamel. porcelain, and resin was compared, porcelain was the smoothest and the surface roughness was decreased in the order of Ni-Cr alloy. Co-Cr alloy. Co-Cr-Ti alloy, resin. Ag-Pd alloy, ceramic gold alloy type III gold alloy, and enamel (P<0.01). The results of this study indicate that the finishing and polishing procedures should be carried out in a logical, systematic sequence of steps and the harder non-precious metals may be less resistance to abrasion than are the softer precious metals.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.205-205
• /
• 2009

As a p-type semiconductor NiO is potential material which can be used in many application including QD-LED. NiO films were deposited on glass substrates using rf-sputtering method. The properties of resistivity, surface roughness, etc in the NiO films were investigated at different sputtering parameters. The resistivity of $l.88{\times}10^{-2}{\sim}3.71{\times}10^{-2}{\Omega}cm$ with sputtering power(80~200 watts) and change was very low. The sputtering pressure at 3~60 mTorr resulted in rather broad change ofresistivity of $0.58{\times}10^{-2}{\sim}4.67{\Omega}cm$. The oxygen content in sputtering gas was found to be very effective to control the resistivity from $2.01{\times}10^{-2}$ to $1.22{\times}10^2{\Omega}cm$ with 100~2.5% $O_2$ in Ar gas. In addition, the surface roughness showed the RMS values of 0.6~1.1 nm and the dependence on sputtering parameters was weak.