• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.120-125
• /
• 2007

The microstructure, mechanical properties and melting range of Ni-Cr-Mo based alloys were investigated to develop Be-free Ni-Cr-Mo base dental alloys for Porcelain-Fused-to-Metal Firing(PFM). All as-cast alloys showed dendritic structure. Rockwell hardness of 20Cr7Mo was increased with addition of Si and Ti. On the contrary, it was decreased with addition of Co. The duplex alloying elemental addition such as 3Co + xTi, 2Si + xCo and 2Si + xTi to 20Cr7Mo resulted in much increase of hardness. Rockwell hardness and compressive strength for 20Cr3CoSiTi or 17Cr6CoSiTi alloy that add Si-Ti had similar values compared to the commercial alloys. Melting range for 20Cr3CoSiTi and 17Cr6CoSiTi alloy that add Si-Ti showed similar or lower than commercial alloys. In conclusion, 20Cr3CoSiTi and 17Cr6CoSiTi alloys can be applied for commercial use.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.8
• /
• pp.714-719
• /
• 2005

NiCr thin film was deposited by DC magnetron sputtering on $A;_2O_3$/Si substrate with NiCr (80:20) alloy target. NiCr thin films were annealed at $300^{\circ}C,\;400^{\circ}C,\;500^{\circ}C,\;600^{\circ}C,\;and\;700^{\circ}C$ for 6 hr in $H_2$ after annealing at $500^{\circ}C$ for 6hr in air atmosphere, respectively. To analyze NiCr thin film properties, the changes of its micro structure were Investigated through field emission scanning electron microscope (FESEM). X-ray photoelectron spectroscopy (XPS) was used to analyze a surface of NiCr thin film. Resistance of NiCr thin film was measured by 4-point probe technique. The generated heats were measured by infrared thermometer through the application of DC voltage (5 V/l2 V). NiCr thin film treated by gradational double annealing process had uniform and small grains. Maximum temperature generated heat by NiCr micro heater was $173^{\circ}C$. We expect that our results will be a useful reference in the realization of NiCr micro heater.

• Journal of the Korean Ceramic Society
• /
• v.37 no.9
• /
• pp.839-846
• /
• 2000

통전활성 소결법을 이용하여 단상의 세라믹스(PSZ) 및 금속(NiCrAlY)과 PSZ/NiCrAlY 복합체를 각 소결온도에서 제조하였으며, 이에 대한 특성평가는 개량형 소형펀치 시험법을 이용하여 수행하였다. 복합체의 밀도 및 경도에 미치는 소결온도의 영향은 NiCrAlY의 부피분율 증가에 따라 감소되었으며, 중간조성에서의 밀도 및 경도는 연속적인 변화를 나타내었다. 파괴인성의 변화에서는 60vol%-NiCrAlY 이상의 조성에서 급격한 증가를 나타내었으며, 짧은 소결시간 및 빠른 승온속도 등 통전활성 소결법의 장점에 의해 단상의 PSZ에서도 10 MPa.m$^{1}$2/ 의 높은 파괴인성 값을 얻을 수 있었다. PSZ/NiCrAlY 복합체에서의 특성은 소결온도와 NiCrAlY의 부피분율에 의해 지배적으로 영향을 받았으며, 단상의 PSZ은 전형적인 취성거동을 나타내었고 80vol%-NiCrAlY 까지의 복합체에서는 부분적인 취성 및 소성거동을 함께 나타내었다. 각 소결체에서 최고의 특성을 나타내고 소결온도는 단상의 PSZ 경우인 140$0^{\circ}C$에서부터 단상의 NiCrAlY 경우인 120$0^{\circ}C$까지 최대 20$0^{\circ}C$의 차이를 나타내었으며, PSZ과 NiCrAlY의 조성비에 따라서 연속적인 변화를 보였다.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.3
• /
• pp.129-136
• /
• 2006

The high velocity oxy-fuel sprayed coatings of 38Ni-23Co-20Cr-11Al-3Y-5Ta, 25Ni-34Co-20Cr-11Al-3Y-2Re and 32Ni-34.5Co-22Cr-11Al-0.5Ir (in wt%) were oxidized at 1000 and $1100^{\circ}C$ in air in order to find the alloying effect of Ta, Re and Ir on the oxidation properties of the NiCoCrAlY-base coatings. The primary phase of the coatings was $Ni_3Al$. The oxides formed on the coatings consisted primarily of ${\alpha}-Al_2O_3$, together with some $CoCr_2O_4,\;CoAl_2O_4$, and $Al_5Y_3O_{12}$. Tantalum oxidized to $Ta_2O_5$ and $Ta_2O_{22}$. However, no oxides of Re and Ir were detected by XRD owing to their thermodynamic inertness and/or their small amount.

• Journal of the Korean Magnetics Society
• /
• v.4 no.1
• /
• pp.20-24
• /
• 1994

The read/write characteristics of CoCr/NiFe double layered media are strongly affected by the magnetic properties of NiFe magnetic soft layer as well as those of CoCr recording layer. Modification of the permalloy layer by NiFe/Ge multilayer scheme resulted in the higher recording sensitivity and the higher reproduced voltage of CoCr/NiFe medium and this is attributed to the higher permeability of the back layer and high perpendicular anisotropy of the CoCr recording layer. Although higher permeability of back layer results in higher recording sensitivity, the increment of the reproduced voltage was not remarkable, which can be confirmed in the FEM numerical analysis. On the contrary, peak shift characteristics of the CoCr/NiFe medium with the NiFe multi back layer was deteriorated compared to that of the CoCr/NiFe medium with NiFe single back layer. Insertion of ferromagnetic thin CoZrNb intermediate layer between CoCr and NiFe layer was effective to ensure large reproduced voltage and low peak shift. These recoridng characteristics were also discussed in connection with microstructural characteristics.

• Korean Journal of Materials Research
• /
• v.13 no.10
• /
• pp.640-644
• /
• 2003

NiCr thin films were fabricated by rf magnetron sputtering for applying to both the top electrode and absorption layer on Pb(Zr, Ti)O$_3$(PZT) thin films for infrared sensors. The rms roughness and resistivity of NiCr films prepared with Ni power of 80 W and Cr power of 50 W showed the most stable oxidation resistance after annealing at $600^{\circ}C$ for 5 min in oxygen ambient. The rms roughness and resistivity of NiCr films annealed at $V^{\circ}C$ in oxygen ambient were about 2$0\AA$ and $70 \mu$Ω-cm, respectively. As-deposited Ni/PZT/Pt and NiCr (Ni 80 W, Cr 50 W)/PZT/Pt structures showed well saturated hysteresis loops. However, in case of the samples annealed at $500^{\circ}C$ in oxygen ambient, only NiCr/PZT/Pt showed saturated loops having a remanent polarization of 20$\mu$C/$\textrm{cm}^2$. Ultra-thin NiCr films showed a possibility as a top electrode for infrared sensors.

• 한국전기화학회:학술대회논문집
• /
• 2004.04a
• /
• pp.32-32
• /
• 2004

• Korean Journal of Soil Science and Fertilizer
• /
• v.11 no.2
• /
• pp.119-126
• /
• 1979

Rice seeds, suweon 264, were germinated under 5 levels of toxic heavy metals, Cd(0, 0.05, 0.5, 5, 20ppm), Cu(0, 0.05, 0.5, 5, 20, ppm), Cr(0, 0.5, 1, 5, 10ppm), Ni(0, 0.5, 1, 5, 10ppm), Co(0, 0.5, 1, 5, 10ppm), Zn(0, 0.5, 5, 20, 40, ppm), Pb(0, 0.5, 5, 20, 40ppm) and Mn(0, 1, 10, 25, 50, ppm) in culture solution, and then grown with supplying culture solution contained respective concentrations. Germination and growth response to the toxic heavy metals were studied. Results obtained are as follows : 1) The germination injury of rice seeds by excess concentration of toxic heave metal in culture solution occured in Cd and Cu; below 0.05 ppm, Ni; below 0.5 ppm, Mn; below 1.0 ppm, Co and Cr; 0.5-1.0 ppm, and 0.5-5 ppm, Zn and Pb. Thereby, in the order of degrees of the elements toxicity to germination, they were arranged as follows : Cd>Cu>Ni>Co>Cr>Mn>Zn$$\geq_-$$Pb. 2) Toxic heavy metal concentrations in culture solution, which result in decreasing dry weight due to the injury of excess concentration of treated elements, were Cd: below 0.05 ppm, Ni, Cr and Co; below 0.5 ppm, Cu and Zn; 0.5-5 ppm, Pb; 5-20 ppm and Mn; 10-25 ppm. The order was Ni>Cd>Cr>Co>Cu$$\geq_-$$Zn>Pb>Mn. 3) The critical contents of Cd, Ni, Pb, Cu, Zn, Mn, and Co in dry matter, Which result in decreasing dry weight, were considered to be 0.05-15.5, 1.50-25.0, 24.0-28.0, 26.5-62.5, 470-645.0, 231.0-500.0 and below 15.0 ppm, respectively. 4) The contents of Cr, Co, Cd, Pb, Ni, Cu and Zn in dry matter by 0.5 ppm treatment concentration of each heavy metals was trace, 15.0, 17.5, 24.0, 25.0, 84.5 and 470.0 ppm, respectively. Thereby, in the order of each element to uptaked by rice seedlings, they were arranged as follow; Zn>Cu>Ni>Pb>Cd>Co>Cr. 5) The hazardous concentrations of root activity by toxic heavy metals in culture solution were Cd; below 0.05, Cu; 0.05-0.5, Cr; below 0.5, Ni; 0.5-1.0, Co; 0.5-1.0, Zn; above 0.5, Pb; 0.5-5.0 and Mn; 1.0-10.0 ppm. The hazardous degree of root activity by toxic heave metals was in the order of Cd>Cu>Cr>Zn>Ni>Co>Pb>Mn.

• Applied Microscopy
• /
• v.45 no.1
• /
• pp.32-36
• /
• 2015

The microstructural features of FeCoCrNi, FeCoCrNiAl and FeCoCrNiSix (x=0, 5, 10, 15, 20) alloys have been investigated in the present study. The microstructure of FeCoCrNi alloy changes dramatically with equiatomic addition of Al. The fcc irregular shaped grain structure in the as-cast FeCoCrNi alloy changes into the bcc interconnected structure with phase separation of Al-Ni rich and Cr-Fe rich phases in the as-cast FeCoCrNiAl alloy. The microstructure of FeCoCrNi alloy changes with the addition of Si. With increasing the amount of Si, the fcc structure of the grains is maintained, but new phase containing higher amount of Si forms at the grain boundary. As the amount of Si increases, the fraction the Si-rich grain boundary phase increases.

• Journal of Powder Materials
• /
• v.13 no.3 s.56
• /
• pp.178-186
• /
• 2006

The effect of use of $H_2O$ as PCA(process control agent) to prevent the carbon contamination during mechanical alloying process and the precipitation behavior in Ni-20Cr-20Fe-5Nb bulk alloy after aging were investigated. NbC and $Cr_2O_3$ were formed during mechanical alloying and consolidation processes in the Ni-20Cr-20Fe-5Nb alloy in which methanol($CH_3OH$) was added as PCA. Formation of NbC in this alloy decreased the amount of Nb dissolved in the Ni matrix. The use of $H_2O$ as PCA in Ni-20Cr-20Fe-5Nb alloy prevented the formation of NbC and increased the hardness. The increase of hardness in this alloy was attributed to the increased amount of Nb dissolved in the Ni matrix. After aging treatment for 20 hours at $600^{\circ}C\;and\;720^{\circ}C$ of Ni-20Cr-20Fe-5Nb bulk alloy in which $H_2O$ added as PCA, ${\gamma}"$$(Ni_3Nb,\;tetragonal)\;and\;{\delta}\;(Ni_3Nb,\;orthorhombic)$ precipitates were formed, respectively. The precipitation temperatures of ${\gamma}"$ and ${\delta}$ in this bulk alloy were lower than those in commercial IN 718 alloy. It seemed that the lower precipitation temperatures for ${\gamma}"$ and ${\delta}$ in this bulk alloy than in commercial IN 718 alloy were due to severe plastic deformation during mechanical alloying.