• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.4
• /
• pp.261-265
• /
• 2011

This paper describes the fabrication and characteristics of a Au/Ni/Ti/3C-SiC Schottky diode with field plate (FP) edge termination. The Schottky contacts were annealed for 30 min at temperatures ranging from 0 to $800^{\circ}C$. At annealing temperature of $600^{\circ}C$, it showed an inhomogeneous Schottky barrier and had the best electrical characteristics. However, the annealing of $800^{\circ}C$ replaced it with ohmic behaviors because of the formation of many different types of nickel silicides. The fabricated Schottky diode had a breakdown voltage of 200 V, Schottky barrier height of 1.19 eV and worked normally even at $200^{\circ}C$.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.2
• /
• pp.59-64
• /
• 2013

In-situ annealing tests of Cu/Ni/Au/Sn-Ag/Cu micro-bump for 3D IC package were performed in an scanning electron microscope chamber at $135-170^{\circ}C$ in order to investigate the growth kinetics of intermetallic compound (IMC). The IMC growth behaviors of both $Cu_3Sn$ and $(Cu,Ni,Au)_6Sn_5$ follow linear relationship with the square root of the annealing time, which could be understood by the dominant diffusion mechanism. Two IMC phases with slightly different compositions, that is, $(Cu,Au^a)_6Sn_5$ and $(Cu,Au^b)_6Sn_5$ formed at Cu/solder interface after bonding and grew with increased annealing time. By the way, $Cu_3Sn$ and $(Cu,Au^b)_6Sn_5$ phases formed at the interfaces between $(Cu,Ni,Au)_6Sn_5$ and Ni/Sn, respectively, and both grew with increased annealing time. The activation energies for $Cu_3Sn$ and $(Cu,Ni,Au)_6Sn_5$ IMC growths during annealing were 0.69 and 0.84 eV, respectively, where Ni layer seems to serve as diffusion barrier for extensive Cu-Sn IMC formation which is expected to contribute to the improvement of electrical reliability of micro-bump.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.6
• /
• pp.408-416
• /
• 2022

In this study, the effect of Au-Sn alloy coating on reliability of electrical contacts was investigated via comparison with Au-Co alloy coating. The results show that Au-Sn alloy exhibited lower contact resistance and higher solder spreadability than those of Au-Co alloy after thermal aging. In the case of Au-Co alloy plating, the underlying Ni element diffused into Au-Co layer to form Ni oxides on surface during thermal aging, leading to increased contact resistance and decreased solder spreadability. Meanwhile, for Au-Sn alloy plating, Au-Ni-Sn metallic compound was formed at the interface between Au-Sn layer and underlying Ni layer. This compound acted as a diffusion barrier, thereby inhibiting the diffusion of Ni to Au-Sn layer during thermal aging. Consequently, Au-Sn alloy layer showed better contact reliability than that of Au-Co alloy layer.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.310-313
• /
• 2000

In this study, the Au/Ni and Au/Ni/Si/Ni layers prepared by electron beam evaporation were used to form ohmic contacts on p-type GaN. Before rapid thermal annealing, the current-voltage(I-V) characteristic of Au/Ni and Au/Ni/Si/Ni contact on p-type GaN film shows non-ohmic behavior. A Specific contact resistance as 3.4$\times$10$^{-4}$ Ω-$\textrm{cm}^2$ was obtained after 45$0^{\circ}C$-RTA. The Schottky barrier height reduction may be attributed to the presence of Ga-Ni and Ga-Au compounds, such as Ga$_4$Ni$_3$, Ga$_4$Ni$_3$, and GaAu$_2$ at the metal - semiconductor interface. The mixing behaviors of both Ni and Au have been studied by using X-ray photoelectron spectroscopy. In addition, X-ray diffraction measurements indicate that the Ni$_3$N, NiGa$_4$, Ni$_2$Si, and Ni$_3$Si$_2$ Compounds were formed at the metal-semiconductor interface.

• Journal of dental hygiene science
• /
• v.9 no.4
• /
• pp.405-412
• /
• 2009

The purpose of this study investigated the effect of Au coating on adhesion between porcelain matrix and metal substructure interface. Titanium, Ni-Cr alloy and Co-Cr alloy are well known as proper metal for the dental restorations. The success of a porcelain fused to metal (PFM) restoration depends upon the quality of the porcelain-metal bond. However, adhesion between dental alloys and porcelain is related to diffusion of oxygen during ceramic firing. The excessive oxidized layers make hard adhesion between dental alloy and ceramic. Ni-Cr and Co-Cr specimens were divided into test and a control group and Titanium specimens were divided into three test groups and a control group. Each group had 20 specimens. The adhesion characteristics of porcelain and metal with Au coating layer and without Au coating layer were observed with scanning electron microscopy(SEM). The adhesion was evaluated by a biaxial flexure test and volume fraction of adherent porcelain was determined by SEM/EDS analysis. Result of this study suggest that Au coating layer is effective barrier to diffuse oxide layer completely protect non-precious alloys from oxidation during the porcelain firing. The SEM photomicrographs of cross-section specimens showed a smooth interface between Au coating layer and metals and porcelain which suggested proper chemical bonding, and no gap, porosity were observed. The mode of failure was mainly adhesive for Ti tested specimens, but mixed failures with adhesive and cohesive were observed in Ni-Cr and Co-Cr specimens. The adhesion between non-precious metals and porcelain would not be improved by Au coating agent. However, It is suggested that the continuous study is required further investigation and development.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.412-412
• /
• 2008

ENIG(Electroless Nickel Immersion Gold)is a surface treatment method that is used most widely at fine pitch's SMT and BGA packaging process. ENIG has good diffusion barrier of Ni against solder and good wettability due to Au finish. But when the discoloration occurred on the Au finish of ENIG, some key characteristics related to the quality and reliability of PCB such as bondability, solderability and electrical flowing of packaging process could be deteriorated. In this paper, we have performed the water dip test ($88^{\circ}C$ purified water) which accelerates the galvanic corrosion of Ni diffused from the Ni-P layer. That is, the excessive oxidation of the Ni layer could result in non-wetting of the solder because the flux may not be able to remove excessive oxides. Though Au discoloration have been reported to be caused by Ni oxides in many literature, it is still open to verify and discuss The microstructures and chemical compositions have been investigated using FE-SEM, TEM, FIB, EDS and XPS. As a result, authors have found that the Au discoloration in ENIG type is severely caused by the oxidation of the Ni and the mechanism of Au discoloration can be confirmed through the experiment result of water dip test.

• Proceedings of the KIEE Conference
• /
• 2005.11a
• /
• pp.3-5
• /
• 2005

Ni/Au 쇼트키 접합의 산화를 통해 항복전압이 증가하고 누설 전류가 감소한 수평방향 GaN 쇼트키 장벽 다이오드를 제작하였다. 산화 과정 후, 턴-온 전압이 미세하게 증가하였으며 높은 애노드 전압하에서 애노드 전류가 증가하였다. 5분과 10분의 산화 과정 후, 누설 전류는 1nA 이하 수준으로 현저히 감소하였다. Edge Termination 방법으로 Floating Metal Ring을 사용하고, 산화 과정을 적용하여 제안된 GaN 쇼트키 장벽 다이오드의 항복전압은 750볼트의 큰 값을 얻을 수 있었다. 상온과 $125^{\circ}C$ 에서 제작한 GaN 쇼트키 장벽 다이오드의 역방향 회복 파형도 측정하였으며, 제작한 소자는 매우 빠른 역방향 회복 특성을 보였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.332-336
• /
• 2001

In this study, the reaction at UBM(Under Bump Metallurgy) and solder interface was investigated. The UBM employed in conventional optical packages, Au/Pt/Ti layer, were found to dissolve into molten Au-Sn eutectic solder during reflow soldering. Therefore, the reaction with different diffusion barrier layer such as Fe, Co, Ni were investigated to replace the conventional Pt layer. The reaction behavior was investigated by reflowing the solder on the pad of the metals defined by Cr layer for 1, 2, 3, 4, and 5 minutes at $330^{\circ}C$. Among the metals, Co was found to be most suitable for the diffusion barrier layer as the wettability with the solder was reasonable and the reaction rate of intermetallic formation at the interface is relatively slow.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.332-336
• /
• 2001

In this study, the reaction at UBM(Under Bump Metallurgy) and solder interface was investigated. The UBM employed in conventional optical packages, Au/Pt/Ti layer, were found to dissolve into molten Au-Sn eutectic solder during reflow soldering. Therefore, the reaction with different diffusion barrier layer such as Fe, Co, Ni were investigated to replace the conventional R layer. The reaction behavior was investigated by reflowing the solder on the pad of the metals defined by Cr layer for 1, 2, 3, 4, and 5 minutes at 330$^{\circ}C$. Among the metals, Co was found to be most suitable for the diffusion barrier layer as the wettability with the solder was reasonable and the reaction rate of intermetallic formation at the interface is relatively slow.

• Proceedings of the IEEK Conference
• /
• 2001.06b
• /
• pp.205-208
• /
• 2001

Schottky barrier diodes are fabricated on a intrinsic GaN(4${\mu}{\textrm}{m}$) epitaxial structure grown by rf plasma molecular beam epitaxy (MBE) on sapphire substrates. First, We make Ohmic electrodes (Ti/Al/Ti/Au) by evaporator. Next, we contact RuO$_2$ by dipping in the solution (RuCl$_3$.HClO$_4$), and then we deposit Ni/Au on the surface of RuO$_2$ by evaporator. We study the electrical characteristics of GaN Schottky barrier diodes made by these methods. Measurements are C-V, I-V, SEM, EDX, and XRD for the characteristics of devices. Thickness of RuO$_2$ layer depends on supplied voltage and dipping time. Device of thinner RuO$_2$ layer have a good Schottky characteristics compare with device of thicker RuO$_2$ layer