• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.217-223
• /
• 1993

Thin films of the Au/Cr, Au/Ni/Cr and Au/Pd/Cr systems were deposited on alumina substrates at ambient temperature and $250^{\circ}C$ in a high-vacuum resistance heating evaporator and annealed at $300^{\circ}C$, $450^{\circ}C$ and $600^{\circ}C$ for 1 hour in air, respectively. The film thicknesses of Au, Ni(or pd), and Cr were $1000{\AA}$, $300{\AA}$, and $50{\AA}$, respectively. The substrate temperature during deposition and the post-deposition annealing temperature affected the sheet resistance of thin-films due to the inter-diffusion of each layer. As a result of Auger depth profile analysis, in the Au/Cr system Cr already diffused out to Au surface during deposition at the substrate temperature of $250^{\circ}C$ and Au distribution changed after heat treatment. In the Au/Ni/Cr and Au/Pd/Cr systems, diffusion phenomena of Ni and Pd were found and especially Ni (approximately 45 at.%) diffused out to Au surface and oxidized.

• Journal of the Korean Ceramic Society
• /
• v.13 no.3
• /
• pp.55-62
• /
• 1976

순수한 닉켈과 금 박막을 (III)규소 단 결정위에 진공 증착시켰다. Ni/Au/Si나 Au/Ni/Si시료를 진공중에서 약 55$0^{\circ}C$로 가열하였을 때 육방정 혹은 변형된 육방정의 미소 결정들이 규소 기질위에 형성되었다. 이들 미소 결정들의 형성과정 및 조성은 X-선 회절법, scanning electron microscopy 및 scanning Auger microprobe 법을 사용하여 결정하였다. 이들 미소 결정은 NiSi2임이 확인되었다. Ni/Au/Si 시료에서는 Au-Si 공융점(37$0^{\circ}C$) 이상으로 온도가 증가됨에 따라 닉켈과 규소가 Au-Si 공융체 속으로 이동한 후 반응하여 NiSi2를 형성하였다. Au/Ni/Si 시료에 있어서의 Au-Si 공융체 형성은 닉켈 박막에 있는 바늘구멍형의 표면 결함과 관련 지을 수 있겠다. 금이 닉켈 박막의 grain boundary를 통하여 Ni/Si 계면으로 확산되어 그 계면을 습윤시킨 다음 Au-Si 공융체를 형성하였다. 이런 Au-Si 공용체는 닉켈과 규소 원자에 대한 높은 확산 매질로서 작용하여 NiSi2 형성을 촉진시켰다. 표면에 평행한 (III)규소면 위의 NiSi2 미소 결정은 유사한 육방정으로 나타났으며, 경사진 미소결정은 부등변 사변형과 유사하였다. Auger 스펙트럼 및 Ni, Au 및 Si에 대한 내층조성(indepth Composition Profiles)은 NiSi2 미소 결정이 Au-Si 공융체의 matrix에 미소 부분으로 나타났음을 보여주었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.3 s.32
• /
• pp.47-53
• /
• 2004

Eutectic Au-20Sn(compositions are all in weight percent unless specified otherwise) solder alloys were soldered on the Ni substrate with various time and temperature. The composition, phase identification and morphology of intermetallic compounds(IMC) at the interface were examined using Scanning Electron Microscopy(SEM). There were two types of IMCs, $(Au,Ni)_3Sn_2$ and $(Au,Ni)_3Sn$ at the interface. The transition in morphology of $(Au,Ni)_3Sn_2$ has been observed at $300{\~}400^{\circ}C$. The morphology transition of $(Au,Ni)_3Sn_2$ is due to the decrease of enthalpy of formation of $(Au,Ni)_3Sn_2$ phase and has been explained well by Jackson's parameter with temperature. Because the number of diffusion channel is different at each soldering temperature, IMC thickness is nearly same at all temperature.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.4
• /
• pp.296-300
• /
• 2017

NiO nanofibers with Au nanoparticles were synthesized by sol-gel and electrospinning techniques, in which the reduction process by ultraviolet exposure is included for the growth of Au nanoparticles in the electrospinning solution. FE-SEM(Field Emission Scanning Electron Microscopy), TEM(Transmission Electron Microscopy) revealed that the synthesized nanofibers had the diameter of approximately 200 nm. X-ray diffraction showed the successful formation of Au-decorated NiO nanofibers. Gas sensing tests of Au-decorated NiO nanofibers were performed using reducing gases of CO, and $C_6H_6$, $C_7H_8$, $C_2H_5OH$. Compared to as-synthesized NiO nanofibers, the response of Au-loaded NiO nanofibers to CO gas was found to be about 3.4 times increased. On the other hand, the response increases were only 1.1-1.3 times for $C_6H_6$, $C_7H_8$, and $C_2H_5OH$.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.2
• /
• pp.59-64
• /
• 2013

In-situ annealing tests of Cu/Ni/Au/Sn-Ag/Cu micro-bump for 3D IC package were performed in an scanning electron microscope chamber at $135-170^{\circ}C$ in order to investigate the growth kinetics of intermetallic compound (IMC). The IMC growth behaviors of both $Cu_3Sn$ and $(Cu,Ni,Au)_6Sn_5$ follow linear relationship with the square root of the annealing time, which could be understood by the dominant diffusion mechanism. Two IMC phases with slightly different compositions, that is, $(Cu,Au^a)_6Sn_5$ and $(Cu,Au^b)_6Sn_5$ formed at Cu/solder interface after bonding and grew with increased annealing time. By the way, $Cu_3Sn$ and $(Cu,Au^b)_6Sn_5$ phases formed at the interfaces between $(Cu,Ni,Au)_6Sn_5$ and Ni/Sn, respectively, and both grew with increased annealing time. The activation energies for $Cu_3Sn$ and $(Cu,Ni,Au)_6Sn_5$ IMC growths during annealing were 0.69 and 0.84 eV, respectively, where Ni layer seems to serve as diffusion barrier for extensive Cu-Sn IMC formation which is expected to contribute to the improvement of electrical reliability of micro-bump.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.2 s.35
• /
• pp.95-103
• /
• 2005

The interfacial reaction between 42Sn-58Bi solder (in wt.$\%$ unless specified otherwise) and electroless Ni-P/immersion Au has been investigated before and after thermal aging, with a focus on formation and growth of an intermetallic compound (IMC) layer, consumption of under bump metallurgy (UBM), and bump shear strength. The immersion Au layer with thicknesses of 0 (bare Ni), 0.1, and $1{\mu}m$ was plated on the $5{\mu}m$ thick electroless Ni-P ($14{\~}15 at.\%$P) layer. Then, the 42Sn-58Bi solder balls were fabricated on three different UBM structures by screen-printing and pre-reflow. The $Ni_3Sn_4$ layer (IMC1) was formed at the joint interface after pre-reflow for all the three UBM structures. On aging at $125^{\circ}C$, a quaternary phase (IMC2) was observed above the $Ni_3Sn_4$ layer in the Au-containing UBM structures, which was identified as $Sn_{77}Ni{15}Bi_6Au_2$ (in at.$\%$). The thick $Sn_{77}Ni{15}Bi_6Au_2$ layer deteriorated the integrity of the solder joint and the shear strength of the solder bump was decreased by about $40\%$ compared with non-aged joints.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.6
• /
• pp.408-416
• /
• 2022

In this study, the effect of Au-Sn alloy coating on reliability of electrical contacts was investigated via comparison with Au-Co alloy coating. The results show that Au-Sn alloy exhibited lower contact resistance and higher solder spreadability than those of Au-Co alloy after thermal aging. In the case of Au-Co alloy plating, the underlying Ni element diffused into Au-Co layer to form Ni oxides on surface during thermal aging, leading to increased contact resistance and decreased solder spreadability. Meanwhile, for Au-Sn alloy plating, Au-Ni-Sn metallic compound was formed at the interface between Au-Sn layer and underlying Ni layer. This compound acted as a diffusion barrier, thereby inhibiting the diffusion of Ni to Au-Sn layer during thermal aging. Consequently, Au-Sn alloy layer showed better contact reliability than that of Au-Co alloy layer.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.6
• /
• pp.235-241
• /
• 2013

In this study, the effects of alloying elements and thermal aging on the contact resistance of electroplated gold alloy layers were investigated by surface analysis using X-ray photoelectron spectroscopy (XPS). The contact resistance of Au-Ag alloy was lower than that of Au-Ni or Au-Co alloy after thermal aging. The XPS results show that nickel and oxygen present as nickel oxides such as NiO and $Ni_2O_3$ on the surface of gold layers after thermal aging. The increase in the contact resistance after thermal aging is attributable to the nickel oxide layer formed on the surface of the gold layers. The content of nickel diffused from the underlayer during the thermal aging was high in the order of Au-Co, Au-Ni and Au-Ag alloy because the area of grain boundary was large in the order of Au-Ag, Au-Ni and Au-Co alloy.

• ETRI Journal
• /
• v.24 no.5
• /
• pp.349-359
• /
• 2002

With Ni/Au and Pd/Au metal schemes and low temperature processing, we formed low resistance stable Ohmic contacts to p-type GaN. Our investigation was preceded by conventional cleaning, followed by treatment in boiling $HNO_3$:HCl (1:3). Metallization was by thermally evaporating 30 nm Ni/15 nm Au or 25 nm Pd/15 nm Au. After heat treatment in $O_2$ + $N_2$ at various temperatures, the contacts were subsequently cooled in liquid nitrogen. Cryogenic cooling following heat treatment at $600^{\circ}C$ decreased the specific contact resistance from $9.84{\times}10^{-4}$ ${\Omega}cm^2$ to $2.65{\times}10^{-4}$ ${\Omega}cm^2$ for the Ni/Au contacts, while this increased it from $1.80{\times}10^{-4}$ ${\Omega}cm^2$ to $3.34{\times}10^{-4}$ ${\Omega}cm^2$ for the Pd/Au contacts. The Ni/Au contacts showed slightly higher specific contact resistance than the Pd/Au contacts, although they were more stable than the Pd contacts. X-ray photoelectron spectroscopy depth profiling showed the Ni contacts to be NiO followed by Au at the interface for the Ni/Au contacts, whereas the Pd/Au contacts exhibited a Pd:Au solid solution. The contacts quenched in liquid nitrogen following sintering were much more uniform under atomic force microscopy examination and gave a 3 times lower contact resistance with the Ni/Au design. Current-voltage-temperature analysis revealed that conduction was predominantly by thermionic field emission.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.4
• /
• pp.1-9
• /
• 2002

The metallurgical reaction properties between the pad consisted of 0.5 $\mu\textrm{m}$Au/5 $\mu\textrm{m}$Ni/Cu layers on a conventional ball grid array (BGA) substrate and In-15 (wt.%)Pb-5Ag solder ball were characterized during the reflow process and solid aging. During the reflow process of 1 to 5 minutes, it was observed that thin $AuIn_2$ or Ni-In intermetallic layer was formed at the interface of solder/pad. The dissolution rate of the Au layer into the molten solder was about $2\times 10^{-3}$ $\mu\textrm{m}$/sec which is remarkably low in comparison with a eutectic Sn-37Pb solder. After solid aging treatment for 500 hrs at $130^{\circ}C$, the thickness of $Ni_{28}In_{72}$ intermetallic layer was increased to about 3 $\mu\textrm{m}$ in all the conditions nevertheless the initial reflow time was different. These result show that In atoms in the solder alloy were diffused through the $AuIn_2$ phase to react with underlaying Ni layer during solid aging treatment. From the microstructural observation and shear tests, the reaction properties between In-15Pb-5Ag alloy and Au/Ni surface finish were analyzed not to trigger Au-embrittlement in the solder joints unlike Sn-37Pb composition.