• Transactions on Electrical and Electronic Materials
• /
• v.3 no.2
• /
• pp.24-27
• /
• 2002

The NdBaCuO superconductor samples were zone-melted in low oxygen partial pressure (1%O$_2$+99%Ar). The zone-melting temperature was decreased about 12$0^{\circ}C$ film 1,06$0^{\circ}C$, the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during: the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased and, therefore, the substitution of Nd for Ba was occurred. The superconductivity of zone-melted Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{y}$ prepared under low oxygen partial pressure was distinctively improved.d.d.d.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.91-94
• /
• 2002

The conditions of zone-melting method such as a sample travel speed in a furnace, content of Nd422, control of melting temperature, and heat-treatment with/without Ar gas for $NdBa_{2}Cu_{3}O_{7-\delta}$ superconductor was optimized, As a results, a $NdBa_{2}Cu_{3}O_{7-\delta}$ sample with a surface area of $25mm^{2}$ showed a good superconducting properties when its travel speed was 6 mm/h, The improvement of superconductivity added with 10~20 wt% of Nd422 phase increasing pinning effect was also shown. The critical current density, $J_{c}$ was remarkable affected by the condition of heat-treatment temperature of $NdBa_{2}Cu_{3}O_{7-\delta}$superconductor with/without Ar ambient gas.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% $O_{2}+ 99% Ar$ ). The Zone-melting temperature was decreased about $120^{\circ}C$ from $1060^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase ($BaCuO_{2}$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted $Nd_{1+x}Ba_{2-x}Cu_{3}O_{y}$ prepared under low oxygen partial pressure was distinctively improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% O$_2$+99% Ar). The Zone-melting temperature was decreased about 120$^{\circ}C$ from 1060$^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted Nd$\sub$1+x/Ba$\sub$2-x/Cu$_3$O$\sub$y/ prepared under low oxygen partial pressure was distinctively improved.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.21-25
• /
• 2002

The effect of Ca-doping on the superconducting properties of Nd-Ba-Cu-O bulk superconductors, fabricated by the oxygen-controlled melt growth process, has been systematically investigated. Various c-axis textured bulk samples were grown using precursors with the nominal compositions of $Nd_{1.8-x}Ca_{x]Ba_{2.4}Cu_{3.4}O_{y}$ (x= 0.00, 0.02, 0.05, 0.10, 0.15) in a reduced oxygen atmosphere of 1%O$_2$ in Ar. Magnetization measurements revealed that the critical temperatures(Tc) were almost linearly depressed from 95K to 86K with increasing the Ca dopant from x : 0.0 to 0.15, respectively, and thus critical current densities(Jc) at 77K and for H//c-axis of specimens were gradually degraded with increasing x. Compositional analyses revealed that although the amounts of the Ca dopant both in $NdBa_2Cu_2O_y(Nd123) and Nd_4Ba_2Cu_2O_{10}(Nd422)$,/TEX> were increased with increasing x, only less than half of the initial Ca compositions were detected in melt-grown Ca-doped Nd-Ba-Cu-O bulk crystals. The supression of Tc is attributed to an increased Nd substitution for the Ba site in the Nd123 superconducting matrix with increasing the amount of the Ca dopant.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.6-8
• /
• 2004

The NdBaCuO superconductor samples were zone-melted in low oxygen partial pressure (1 % $O_2$＋99%Ar). The zone-melting temperature was decreased about 12$0^{\circ}C$ from 1, 06$0^{\circ}C$, the zone-melting temperature in air. Thus the loss of liquid phase (BaCu $O_2$and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased and, therefore, the substitution of Nd for Ba was occurred. The superconductivity of zone-melted N $d_{1＋x}$B $a_{2－x}$C $u_3$ $O_{y}$prepared under low oxygen partial pressure was distinctively improved.d.d.d.

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.133-138
• /
• 2009

The $Nd_{1+x}Ba_{2-x}Cu_3O_{7-{\delta}}$(Nd123) superconductor exhibits high performance in high magnetic field and high temperature. We have studied phase stability for Nd123 under reduced oxygen partial pressure and various heat-treatment conditions. The main phase is Nd123 and some samples contain small amounts of Nd422 depending on the temperature and oxygen partial pressure. The decomposition temperature decreases with decreasing oxygen partial pressure from $1052^{\circ}C(P(O_2)$=150 Torr) to about $845^{\circ}C(P(O_2)$=0.1 Torr). The liquidus line was steeper temperature with decreasing oxygen partial pressure. In same condition of oxygen partial pressure, the region of stable Nd123 phase was formed at slightly higher temperature than the region of stable YBCO phase.

• Journal of Powder Materials
• /
• v.18 no.5
• /
• pp.417-422
• /
• 2011

Hydrophobic nanodiamond (ND) were dispersed in engine oil (Helix Oil, Shell co.) as an additives to improve tribology properties. In this study, nanodiamond prepared by an explosive method was used. Tribology properties of both pure Helix oil and engine oil containing ND additive were evaluated. The rotating disks were made of Gray Cast Iron (240 Hv) and SKD11 (710 Hv). Surface topographies of the disks' wear tracks and friction coefficient were compared. The results show that nanodiamond-dispersed lubricants are capable of reducing these metals' wear loss. The friction coefficient is strongly affected to the hardness of wear track.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.346-350
• /
• 2002

The effect of Ca-doping on the superconducting properties of Nd-Ba-Cu-O bulk superconductors, fabricated by the oxygen-controlled melt growth process, has been systematically investigated. Various c-axis textured bulk samples were grown using precursors with the nominal compositions of N $d_{1.8-x}$C $a_{x}$B $a_{2.4}$C $u_{3.4}$ $O_{y}$ (x = 0.00, 0.02, 0.05, 0.10, 0.15) in a reduced oxygen atmosphere of 1% $O_2$ in Ar. Magnetization measurements revealed that the critical temperatures( $T_{c}$) were almost linearly depressed from 95K to 86K with increasing the Ca dopant from x = 0.0 to 0.15, respectively, and thus critical current densities( $J_{c}$) at 77K and for H//c-axis of specimens were gradually degraded with increasing x. Compositional analyses revealed that although the amounts of the Ca dopant both in NdB $a_2$C $u_3$ $O_{y}$(Nd123) and N $d_4$B $a_2$C $u_2$ $O_{10}$(Nd422) were increased with increasing x, only less than half of the initial Ca compositions were detected in melt-grown Ca-doped Nd-Ba-Cu-O bulk crystals. The supression of $T_{c}$ is attributed to an increased Nd substitution for the Ba site in the Nd123 superconducting matrix with increasing the amount of the Ca dopant.t.opant.t.t.t.t.t.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.913-916
• /
• 2001

From 1994 the cooperation between NEU of China and MJU of South Korea for study of ReBaCuO (Re=Rare earth elements) superconductors has been carried out. The progress has been got in following projects. Critical current density ($J_c$) of YBaCuO superconductor prepared by Melting Textured Growth (MTG) was improved. In the preparation of textured YBaCuO, 20 wt.% of YBaCuO 211 phase was added, which would be climactic for the microcracks in the textured YBaCuO. The effects of the 211 phase and Ag content on the superconductivity were studied and discussed in detail. The improved $J_c$ value was reached to 8$\times$10^4 A/cm^2 (77K,0T). Single phase $YbBa_{2}Cu_{3}O_{x}$ superconductor was sintered by the traditional powder metallurgical method, and its reaction process was studied. In recent years, NdBaCuO superconductor is being performed. The behavior of $Nd_{4}Ba_{2}Cu_{2}O_{10}$(Nd422 phase) and the solid solubility, x in the superconductor $Nd_{1+x}Ba_{2-x}Cu_{3}O_{y}$ by the heat treatment in the low oxygen partial pressure (1%) or Ar at $950{\circ}C$ were investigated. The zone-melting process was used to make oriented NdBaCuO superconductor in order to increase the critical current density.