• 한국분말재료학회지
• /
• 제27권5호
• /
• pp.414-419
• /
• 2020

In the present study, we investigated the austenite stability of a sintered Fe-based nanocrystalline alloy. The volume fraction of austenite was measured based on the X-ray diffraction data of sintered Fe-based nanocrystalline alloys, which were prepared by high-energy ball milling and spark plasma sintering. The sintered alloy samples showed a higher volume fraction of austenite at room temperature as compared to the equilibrium volume fraction of austenite obtained using thermodynamic calculations, which resulted from the nanosized crystalline structure of the sintered alloy. It was proved that the austenite stability of the sintered Fe-based alloy increased with a rise in the amount of austenite stabilizing elements such as Mn, Ni, and C; however, it increased more effectively with a decrease in the actual grain size. Furthermore, we proposed a new equation to predict the martensite starting temperature for sintered Fe-based alloys.

• 한국분말재료학회지
• /
• 제23권6호
• /
• pp.409-413
• /
• 2016

Electrical wire explosion in liquid media is a promising method for producing metallic nanopowders. It is possible to obtain high-purity metallic nanoparticles and uniform-sized nanopowder with excellent dispersion stability using this electrical wire explosion method. In this study, Ni-Fe alloy nanopowders with core-shell structures are fabricated via the electrical explosion of Ni-Fe alloy wires 0.1 mm in diameter and 20 mm in length in de-ionized water. The size and shape of the powders are investigated by field-emission scanning electron microscopy, transmission electron microscopy, and laser particle size analysis. Phase analysis and grain size determination are conducted by X-ray diffraction. The result indicate that a core-shell structured Ni-Fe nanopowder is synthesized with an average particle size of approximately 28 nm, and nanosized Ni core particles are encapsulated by an Fe nanolayer.

• 한국분말재료학회지
• /
• 제23권6호
• /
• pp.442-446
• /
• 2016

The sol-gel method is the simplest method for synthesizing monodispersed silica particles. The purpose of this study is to synthesize uniform, monodisperse spherical silica nanoparticles using tetraethylorthosilicate (TEOS) as the silica precursor, ethanol, and deionized water in the presence of ammonia as a catalyst. The reaction time and temperature and the concentration of the reactants are controlled to investigate the effect of the reaction parameters on the size of the synthesized particles. The size and morphology of the obtained silica particles are investigated using transmission electron microscopy and particle size analysis. The results show that monodispersed silica particles over a size range of 54-504 nm are successfully synthesized by the sol-gel method without using any additional process. The nanosized silica particles can be synthesized at higher TEOS/$H_2O$ ratios, lower ammonia concentrations, and especially, higher reaction temperatures.

• 한국분말재료학회지
• /
• 제26권3호
• /
• pp.220-224
• /
• 2019

The aluminum (Al)/copper oxide (CuO) complex is known as the most promising material for thermite reactions, releasing a high heat and pressure through ignition or thermal heating. To improve the reaction rate and wettability for handling safety, nanosized primary particles are applied on Al/CuO composite for energetic materials in explosives or propellants. Herein, graphene oxide (GO) is adopted for the Al/CuO composites as the functional supporting materials, preventing a phase-separation between solvent and composites, leading to a significantly enhanced reactivity. The characterizations of Al/CuO decorated on GO(Al/CuO/GO) are performed through scanning electron microscopy, transmission electron microscopy, and energy dispersive X-ray spectroscopy mapping analysis. Moreover, the functional bridging between Al/CuO and GO is suggested by identifying the chemical bonding with GO in X-ray photoelectron spectroscopy analysis. The reactivity of Al/CuO/GO composites is evaluated by comparing the maximum pressure and rate of the pressure increase of Al/CuO and Al/CuO/GO. The composites with a specific concentration of GO (10 wt%) demonstrate a well-dispersed mixture in hexane solution without phase separation.

• 대한금속재료학회지
• /
• 제48권1호
• /
• pp.57-61
• /
• 2010

Nanosized surface structures of Cu powders were investigated at the atomic scale by field-emission transmission electron microscope techniques. The nanoscale surface oxide layer on the Cu powder was analyzed to be the $CU_2O$ phase by electron diffraction pattern and electron energy-loss spectroscopy. In addition, it was found from high-resolution transmission electron microscopy study that there are formed no surface oxide layers on the surface of alkanethiol coated Cu powders.

• 한국세라믹학회지
• /
• 제39권6호
• /
• pp.604-609
• /
• 2002

분자 단위의 균일한 조성을 가지는 $BaCeO_3$ 나노 분말을 Pechini법에 기초한 citrate 공정을 통하여 합성하였다. 금속 이온의 chelating제로서 citric acid를, 반응 촉매로서는 ethylen glycol을 각각 사용하여 고분자 전구체를 형성시켰고, 이를 기반으로 $900^{\circ}C$의 온도에서 4시간동안 열처리하여 약 100nm의 균일한 크기와 형상을 가진, 사방정 구조의 단일상 $BaCeO_3$ 분말을 합성하는데 성공하였다. 잔존하는 미량의 $CO_3^{2-}$는 $1100^{\circ}C$ 이상의 온도에서 완전히 분해되었고, 이 때 평균 입도 는 약 2배 증가하였으나 매우 균일한 분포를 나타내었다.

• 한국재료학회지
• /
• 제12권12호
• /
• pp.930-934
• /
• 2002

Nanosized $WO_3$ powders were synthesized by the sol-precipitation process using $WCl_{6}$ as the starting material, ethanol as a solvent and $NH_4$OH solution as a precipitant, followed by a washing-drying treatment and calcination. The effects on the powder crystallinity and microstructure of calcination temperature were investigated with XRD and FE-SEM. The $WO_3$ powders calcined at $500^{\circ}C$ and $700^{\circ}C$ showed good crystallinity and their mean particle size was 30nm and 70nm, respectively. These powders were used for the preparation of pastes which were printed as thick films on alumina substrates with comb-type Pt electrodes. The particle size strongly influenced the $NO_2$ gas sensing property of the thick films. A significant reduction in the $NO_2$ sensitivity was observed for the film prepared from larger particle size, having thus a larger grain size. For the film having a smaller grain size, on the other hand, the higher $NO_2$ sensitivity was observed and the sensitivity increased with $NO_2$ concentration.

• 한국재료학회지
• /
• 제21권10호
• /
• pp.568-572
• /
• 2011

The preparation of $Y_2O_3$-doped $ZrO_2$ nanoparticles in Igepal CO-520/cyclohexane reverse micelle solutions is studied here. In this work, we synthesized nanosized $Y_2O_3$-doped $ZrO_2$ powders in a reverse micelle process using aqueous ammonia as the precipitant. In this way, a hydroxide precursor was obtained from nitrate solutions dispersed in the nanosized aqueous domains of a microemulsion consisting of cyclohexane as the oil phase, with poly (oxyethylene) nonylphenylether (Igepal CO-520) as the non-ionic surfactant. The synthesized and calcined powders were characterized by thermogravimetrydifferential thermal analysis (TGA-DTA), X-ray diffraction analysis (XRD) and transmission electron microscopy (TEM). The crystallite size was found to nearly identical with an increase in the water-to-surfactant (R) molar ratio. A FTIR analysis was carried to monitor the elimination of residual oil and surfactant phases from the microemulsion-derived precursor and the calcined powder. The average particle size and distribution of the synthesized $Y_2O_3$-doped $ZrO_2$ were below 5 nm and narrow, respectively. The TG-DTA analysis showed that the phase of the $Y_2O_3$-doped $ZrO_2$ nanoparticles changes from the monoclinic phase to the tetragonal phase at temperatures close to $530^{\circ}C$. The phase of the synthesized $Y_2O_3$-doped $ZrO_2$ when heated to $600^{\circ}C$ was tetragonal $ZrO_2$.

• 세라미스트
• /
• 제22권3호
• /
• pp.256-268
• /
• 2019

Ceramic nano pigments have attracted much interest owing to recent demand for nontoxic, heavy metal-free pigments. In general, ceramic pigments must possess thermal stability at high temperature, however nanosized powder easily undergoes aggregation at high temperature, and its color turns. serveral groups have focused on to minimize agglomeration and oxidation, a core-shell structure with a silica coating is suggested. In this review, we introduce the reported the trend of nano-ceramic powders and we summarized method improve color and physical properties throuth morphology control and ceramic coating technology.

• Nuclear Engineering and Technology
• /
• 제44권1호
• /
• pp.9-20
• /
• 2012

A brief review on the thermal plasma synthesis of nano-sized powders is presented according to the application materials, such as, metals, ceramics, glasses, carbonaceous materials and other functional composites, such as, supported metal catalyst and core-shell structured nano materials. As widely adopted plasma sources available for thermal plasma synthesis of nanosized powders, three kinds of plasma torches, such as transferred and non-transferred DC and RF plasma torches, are introduced with the main features of each torch system. In the basis of the described torch features and the properties of suggested materials, application results including synthesis mechanism are reviewed in this paper.