• Korean Journal of Materials Research
• /
• v.21 no.7
• /
• pp.396-402
• /
• 2011

In this study, by using tin chloride solution as a raw material, a nano-sized tin oxide powder with an average particle size below 50 nm is generated by a spray pyrolysis process. The properties of the generated tin oxide powder depending on the inflow speed of the raw material solution are examined. When the inflow speed of the raw material solution is 2 ml/min, the majority of generated particles appear in the shape of independent polygons with average size above 80-100 nm, while droplet-shaped particles show an average size of approximately 30 nm. When the inflow speed is increased to 5 ml/min, the ratio of independent particles decreases, and the average particle size is approximately 80-100 nm. When the inflow speed is increased to 20 ml/min, the ratio of droplet-shaped particles increases, whereas the ratio of independent particles with average size of 80-100 nm decreases. When the inflow speed is increased to 100 ml/min, the average size of the generated particles is around 30-40 nm, and most of them maintain a droplet shape. With a rise of inflow speed from 2 ml/min to 5 ml/min, a slight increase of the XRD peak intensity and a minor decrease of specific surface area are observed. When the inflow speed is increased to 20 ml/min, the XRD peak intensity falls dramatically, although a significant rise of specific surface area is observed. When the inflow speed is increased to 100 ml/min, the XRD peak intensity further decreases, while the specific surface area increases.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.12
• /
• pp.852-856
• /
• 2014

$BaTiO_3$ nano powder can be synthesized by hydrate salt method at $120^{\circ}C$ in air. Decreasing the thickness of thick film, the nano dielectric particle is needed in electronic ceramics. However, the synthesis of $BaTiO_3$ nano particle at low temperature in air and their mechanism were not reported enough. And ultrasonic treatment can be tried because of low temperature process in air. Therefore, in this study, the $BaTiO_3$ nano powder was synthesised with the synthesis time and ultrasonic treatment at $120^{\circ}C$ in air. In the synthesis process, the effects of process were evaluated. From the experimental observation, the synthesis mechanism was proposed. The homogeneous $BaTiO_3$ particle was synthesised by KOH salt solution at $120^{\circ}C$ for 1hour. It was conformed that the ultrasonic treatment effected on the increase of synthesis rate. After cutting the salt powder using FIB, $BaTiO_3$ nano particles observed homogeneously in the cross-section of the salt particle.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.65 no.3
• /
• pp.216-218
• /
• 2016

In this study, we used not chemical and physical synthesis method but the solution plasma sputtering method in the synthesis of silver nano-particles. Synthesis of all the silver nano-particles was conducted for 1hour in 360 ml of distilled water and characteristics of changing the input voltage and frequency of the synthesised silver nano-particles by using the solution plasma sputtering method were analyzed through FE-SEM(Field Emission-Scanning Electron Microscope). We changed the input voltage from 8 kV to 10 kV in steps of 1 kV, input frequency from 20 kHz to 30 kHz in steps of 5 kHz in the solution plasma reactor with the advanced device which can control the DC voltage and frequency. We confirmed that the size of silver nano-particles were larger according to the change of the input voltage and frequency.

• Korean Journal of Materials Research
• /
• v.23 no.9
• /
• pp.489-494
• /
• 2013

In this study, by using nickel chloride solution as a raw material, a nano-sized nickel oxide powder with an average particle size below 50 nm was produced by spray pyrolysis reaction. A spray pyrolysis system was specially designed and built for this study. The influence of nozzle tip size on the properties of the produced powder was examined. When the nozzle tip size was 1 mm, the particle size distribution was more uniform than when other nozzle tip sizes were used and the average particle size of the powder was about 15 nm. When the nozzle tip size increases to 2 mm, the average particle size increases to roughly 20 nm, and the particle size distribution becomes more uneven. When the tip size increases to 3 mm, particles with an average size of 25 nm and equal to or less than 10 nm coexist and the particle size distribution becomes much more uneven. When the tip size increases to 5 mm, large particles with average size of 50 nm partially exist, mostly consisting of minute particles with average sizes in the range of 15~25 nm. When the tip size increases from 1 mm to 2 mm, the XRD peak intensities greatly increase while the specific surface area decreases. When the tip size increases to 3 mm, the XRD peak intensities decrease while the specific surface area increases. When the tip size increases to 5 mm, the XRD peak intensities increase again while the specific surface area decreases.

• Environmental Engineering Research
• /
• v.10 no.4
• /
• pp.174-180
• /
• 2005

Nano-sized iron was synthesized using borohydride reduction of $Fe^{3+}$ in aqueous solution. A wide range of synthesis conditions including varying concentrations of reagents, reagent feeding rate, and solution pH was applied in an aqueous system under anaerobic condition. The reactivity of nano-sized iron from each synthesis was evaluated by reacting the iron with TCE in batch systems. Evidence obtained from this study suggest the reactivity of iron is strongly dependent on the synthesis solution pH. The iron reactivity increased as solution pH decreased. More rapid TCE reduction was observed for iron samples synthesized from higher initial $Fe^{3+}$ concentration, which resulted in lower solution pH during the synthesis reaction. Faster feeding of $BH_4^-$ solution to the $Fe^{3+}$ solution resulted in lower synthesis solution pH and the resultant iron samples gave higher TCE reduction rate. Lowering the pH of the solution after completion of the synthesis reaction significantly increased reactivity of iron. It is presumed that the increase in the reactivity of iron synthesized at lower pH is due to less precipitation of iron (hydr)oxides or less surface passivation of iron.

• Resources Recycling
• /
• v.23 no.6
• /
• pp.22-29
• /
• 2014

Recycling process of iron should be developed for efficient recovery of neodymium (Nd), rare metal, from acid-leaching solution of Nd magnet. In this study, $FeCl_3$ solution as iron source was used for preparation of iron nano particles with the condition of various factors, such as, reductant, and surfactant. $Na_4P_2O_7$ and Polyvinylpyrrolidone (PVP) as surfactants, $NaBH_4$ as reductant, and palladium chloride ($PdCl_2$) as a nucleation seed were used. Iron powder was analyzed by using XRD, SEM for measuring shape and size. Iron nano particles were prepared at the ratio of 1:5 (Fe (III) : $NaBH_4$). Size and shape of iron particles were round-form and 50 ~ 100 nm size. Zeta-potential of iron at the 100 mg/L of $Na_4P_2O_7$ was negative value, which was good for dispersion of metal particle. When $Na_4P_2O_7$ (100 mg/L), PVP($FeCl_3:PVP$ = 1 : 4, w/w) and Pd($FeCl_3:PdCl_2$ = 1 : 0.001, w/w) were used, iron nano particles which were round-shape, well-dispersed and near 100 nm-sized range. In this condition, $FeCl_3$ solution changed with spent Nd leachate solution, and then it is possible to be made round-formed iron nano particles at pH 9 and at the reaction bath over 20 L which is not include any surfactant.

• Journal of Biomedical Engineering Research
• /
• v.28 no.1
• /
• pp.148-152
• /
• 2007

In this paper, we have synthesized $Gd_2O_3:Eu^{3+}$ nano phosphor particle using a low temperature solution-combustion method. We have investigated the structure and the luminescent characteristic as the sintering temperature and europium concentration. From XRD(X-ray diffraction) and SEM(scanning electron microscope) results, we have verified that the phosphor particle was fabricated a spherical shape with $30{\sim}40nm$ particle size. From the photoluminescence results, the strong peak exhibits at 611 um and the luminescent intensity depends on europium concentration. $Gd_2O_3:Eu$ fine phosphor particle has shown excellent luminescent efficiency at 5 wt% of europium concentration. The phosphors calcinated at $500^{\circ}C$ have possessed the x-ray peaks corresponding to the cubic phase of $Gd_2O_3$. As calcinations temperature increased to $700^{\circ}C$, the new monoclinic phase has identified except cubic patterns. From the luminescent decay time measurements, mean lifetimes were $2.3{\sim}2.6ms$ relatively higher than conventional bulk phosphors. These results indicate that $Gd_2O_3:Eu$ nano phosphor is possible for the operation at the low x-ray dose, therefore, the application as medical imaging detector.

• Korean Journal of Medicinal Crop Science
• /
• v.19 no.6
• /
• pp.464-471
• /
• 2011

Conventional Thiamine Dilauryl Sulfate (TDS) powder has a low stability. In order to solve this problem, this study was performed to improve the solubility of TDS. The process for enhance solubility of TDS was nano grinding mill and ultrasonic dispersion process. TDS paticle was manufactured to nano size through nano grinding mill process. The size of TDS nanoparticle was measured as average 220 nm by DLS. And The TDS nanoparticle in water solution manufactured through ultrasonic dispersion process. The TDS nanoparticle in water solution was showed the highest solubility with 40% ethanol. These results was increased the concentration of TDS from 200 ppm to 240 ppm in water solution. The TDS nanoparticle in water solution showed diameter of Colletotrichum gloeosporioides growth with smaller than about 1.56 cm compared to the TDS paticle in water solution at same concentration. Also, TDS nanoparticle in water solution showed growth inhibition activity as 59.2% with higher than about 10% compared to the TDS paticle water solution in same concentration. Finally, TDS nanoparticle in water solution was increased solubility through nano grinding mill and ultrasonic dispersion process. Also, the increase of concentration in TDS nanopaticle in water solution according to solubility enhancement lead to an result enhancement of antifungal activity. Consequently, we suggested that the TDS nanoparticle in water solution was more effective than TDS particle in water solution owing to the sub-cellular particle size, ability to persistence and targeting to cell membrane of Colletotrichum gloeosporioides. Furthermore we expected the applicating possibility with bio pesticide.

• Resources Recycling
• /
• v.13 no.6
• /
• pp.16-25
• /
• 2004

In this study, nano-sized indium oxide powder with the average particle size below 100 nm is prepared from the indium chloride solution by the spray pyrolysis process. The effects of the concentration of raw material solution, the nozzle tip size and the air pressure on the properties of powder were studied. As the indium concentration of the raw material solution increased from 40 g/l to 350 g/l, the average particle size of the powder gradually increased from 20 nm to 60 nm, yet the particle size distribution appeared more irregular, the intensity of a XRD peak increased and specific surface area decreased. As the nozzle tip size increased from 1 nm to 5 nm, the average particle size of the powder increased from 40 nm to 100 nm, the particle size distribution was much more irregular, the intensity of a XRD peak increased and specific surface area decreased. As the air pressure increased from 0.1 kg/cm$^2$ to 0.5 kg/cm$^2$, the average particle size of the powder varies slightly upto 90~100 nm. As the air pressure increased from 1 kg/cm$^2$ to 3 kg/cm$^2$, the average particle size decreased upto 50~60 nm, the intensity of a XRD peak decreased and the specific surface area increased.

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.4
• /
• pp.694-702
• /
• 2014

The micron-sized ITO(indium tin oxide) particles were prepared by spray pyrolysis from aqueous precursor solutions for indium, and tin and organic additives solution. Organic additives solution with citric acid(CA) and ethylene glycol(EG) were added to aqueous precursor solution for Indium and Tin. The obtained ITO particles prepared by spray pyrolysis from the aqueous solution without organic additives solution had spherical and filled morphologies whereas the obtained ITO particles with organic additives solution had more hollow and porous morphologies with increasing mole of organic additives. The micron-sized ITO particle with organic additives was changed fully to nano-sized ITO particle whereas the micron-sized ITO particle without organic additives was not changed fully to nano-sized ITO particle after post-treatment at $700^{\circ}C$ for 2 hours and wet-ball milling for 24 hours. The size of primary ITO particle by Debye-Scherrer formula and surface resistance of ITO pellet were measured.