• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.332-340
• /
• 2023

This study investigated the effects of nanoparticles on the fracture toughness of cement mortar. Three-point bending tests, compressive tests, and slump tests were conducted on cement mortars reinforced with carbon nanotubes(CNTs), nanosilica(NS), and nano calcium carbonate(NC), respectively. Cement mortar with a water-to-cement ratio and a sand-to-cement ratio of 0.45 and 1.5, respectively, and reinforced with 0 and 2 vol.% of 19.5 mm steel fibers, respectively, was used. Reinforcement with nanoparticles partially improved the fracture toughness and compressive strength of the cement mortar. However, in the case of cement mortar reinforced with steel fibers, the reinforcement with nanoparticles was found to reduce the flowability of the mortar, adversely affecting the dispersion of steel fibers, and ultimately leading to a decrease in fracture toughness, contrary to the intended enhancement. Additional research is needed to improve the decrease in mortar fluidity caused by the reinforcement with nanoparticles.

• Journal of Adhesion and Interface
• /
• v.11 no.4
• /
• pp.174-180
• /
• 2010

The effect of carbon nanotube surface treatment on the interface and thermal conductivity of carbon nanotube-based poly(methylmethacrylate) (PMMA) composites was investigated. Coagulation and atomic-transfer radical polymerization (ATRP) was applied to modify the surface of multi-wall carbon nano-tube. The composite of ATRP method used carbon nanotube showed the higher transparency and thermal conductivities than that of the coagulation method used. In comparison to the thermal conductivity of pure PMMA, 0.21 W/mK, the ATRP carbon nanotube used PMMA/MWNT composite showed a thermal conductivity of 0.38 W/mK. The interface between carbon nanotube and PMMA was observed by scanning electron microscope and uniform dispersion of carbon nanotube was observed without any void in the PMMA matrix. It may be beneficial to transport the phonon without any scattering and it may result in a higher thermal conductivity.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.21 no.6
• /
• pp.553-563
• /
• 2010

This paper presents a tapered slot-antenna(TSA) for optimal impulse-signal transmission in ultra-wide band(UWB). The proposed TSA provides radiates in end-fire direction, which meets an impulse-radio UWB(IR-UWB) system demands(e.g., low loss, thus less error throughout the UWB band). In order to minimize the pulse distortion, we used an wideband impedance transformer and a microstrip slotline. The pulse fidelity characteristics was evaluated with finite-difference time-domain(FDTD) analysis technique and pulse fidelity correlation equation. Approximately 93.89 % pulse fidelity was obtained between the two antennas in 0.5 m range. Additionally, derived chirp Z-transform algorithm enables us to utilize the zoom-in option on the pulse signal in few nano-seconds below. Thus, it is possible to analyze the pulse signal distortion, delay or dispersion characteristics.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.74.1-74.1
• /
• 2011

탄소나노튜브는 높은 전기 전도성과 열 전도성을 가지며, 이러한 특성 때문에 21세기를 주도해 나갈 수 있는 차세대 첨단 소재로서 각광을 받고 있다. 또한 최근에는 나노공학기술의 발달로 인하여 획기적으로 높은 열전도도를 나타내는 다중벽 탄소나노튜브(Multi-walled Carbon Nanotubes, MWCNTs)의 대량 생산이 가능하게 되면서 다중벽 탄소나노튜브의 높은 열전도도 특성을 이용하여 탄소나노튜브를 기본 유체 및 기능성 유체에 안정하게 분산 시킨 후 이를 이용하고자 하는 연구가 활발히 진행되고 있으며, 탄소나노튜브를 유체에 안정하게 분산시키기 위한 방법으로는 기계적 분산법, 물리적 흡착에 의한 분산법, 화학적 개질에 의한 분산법이 있다. 따라서 본 연구에서는 이들 분산 방법과 탄소나노튜브 입자의 물성치에 따른 나노유체의 특성을 알아보기 위하여 나노유체의 열전도도와 점도 특성을 비교 분석하였다. 모든 물성치는 같지만 탄소나노튜브의 길이만 다른 두 종류의 다중벽 탄소나노튜브에 각각 계면 활성제(Sodium Dodecyl Sulfate, SDS) 100 wt%와 고분자 화합물(Polyvinyl Pyrrolidone, PVP) 300 wt%를 첨가하여 나노유체를 제조하였으며, 산화처리 된 다중벽 탄소나노튜브(Oxidized Multi-Walled Carbon Nanotubes, OMWCNTs)를 증류수에 초음파 분산하여 산화나노유체를 제조하였다. 나노유체의 열전도도는 전기 전도성 유체의 비정상 열선법(Transient Hot-wire Method)을 이용하여 측정하였고, 나노유체의 점도는 회전형 디지털 점도계를 이용하여 측정하였다. 실험 결과, 상온에서 동일 혼합비의 나노유체를 비교했을 때, 산화나노유체가 SDS 100 wt%, PVP 300 wt%를 혼합한 다른 나노유체보다 높은 열전도도 특성을 보였으며 점도 특성 또한 가장 낮은 것으로 측정되었다. 특히 상온에서 0.1vol%의 산화 CM-100 나노유체는 증류수보다 열전도도가 8.34%가 증가하였고, $10^{\circ}C$의 저온에서는 상온에서 증류수와 비교하여 측정된 열전도도 값보다 0.36%가 감소한 7.98%가 증가함을 보였다. 본 연구를 통하여 얻어진 결과는 높은 열전도도를 필요로 하는 열교환기의 작동유체나 기타 활용 분야에 대한 기초 자료로써 유용한 정보를 제공할 것이라 판단된다.

• Journal of the Korean Solar Energy Society
• /
• v.29 no.5
• /
• pp.35-44
• /
• 2009

In this study, boiling heat transfer coefficients(HTCs) and critical heat flux(CHF) are measured on a smooth square flat copper heater in a pool of pure water with and without carbon nano tubes(CNTs) dispersed at $60^{\circ}C$. Tested aqueous nanofluids are prepared using multi-walled CNTs whose volume concentrations are 0.0001, 0.001, 0.01, and 0.05%. For dispersion of CNTs, polyvinyl pyrrolidone(PVP) is used in distilled water. Pool boiling HTCs are taken from $10kW/m^2$ to critical heat flux for all nanofluids. Test results show that the pool boiling HTCs of the nanofluids are lower than those of pure water in entire nucleate boiling regime. On the other hand, critical heat flux is enhanced greatly showing up to 200% increase at volume concentration of 0.001% CNTs as compared to that of pure water. This is related to the change of surface characteristics by the deposition of CNTs. This deposition makes a thin CNT layer on the surface and the active nucleation sites of heat transfer surface are decreased due to this layer. The thin layer acts as the thermal resistance and also decreases the bubble generation rate resulting in a decrease in pool boiling HTCs. The same layer, however, maintains the nucleate boiling even at very high heat fluxes and reduces the formation of large vapor canopy at near CHF resulting in a significant increase in CHF.

• Polymer(Korea)
• /
• v.30 no.1
• /
• pp.90-94
• /
• 2006

An electrospinning process was used to fabricate poly(methyl methacrylate) (PMMA) nanofibers embedding multi-walled carbon nanotubes(MWNTs). SEM images showed that the nanofiber surface and structural morphology depended on solvent types (dimethyl formamide, chlor-form and toluene) and carbon nanotube contents (0.5 and $3.0\;wt\%$). Nano-fiber alignments could be controlled by adjusting the electrodes configuration at collector sites. Relationship between carbon nanotube and PMMA nanofiber was studied with radius of gyration of polymer chain and carbon nanotube sizes. As the carbon nanotube content ratio increased, the number of bead increased.

• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.869-878
• /
• 2001

Alumina $(Al_2O_3)$ green bodies were fabricated by gel-casting using three kinds of alumina with different particle size (mean particle size: 4.6 $\mu\textrm{m}$, 0.32 $\mu\textrm{m}$, 10nm). The effects of particle size on gel-casting process and green microstructure were investigated. The optimum dispersion conditions using ammonium salt (D-3019) as dispersant were 0.2 wt% (4.63 $\mu\textrm{m}$), 0.5 wt% (0.32 $\mu\textrm{m}$), and 5.0 wt% (10 nm), in high solid loading. The optimum solid loading of each starting material for gel-casting was obtained as 59 vol% (4.63 $\mu\textrm{m}$), 57 vol% (0.32 $\mu\textrm{m}$), 15 vol% (10 nm), depending on particle size, indicating that nano-size particle (10 nm) represent lower solid loading as high specific surface area than those of other two starting materials. The drying at ambient conditions (humidity; $\thickapprox$90%) was performed more than 48hrs to enable ejection of the part from the mold and then at $120^{\circ}C$ for 2hrs in an air oven, showing no crack and flaw in the dried green bodies. The pore size and distribution of the gelcast green bodies showed the significant decrease with decreasing particle size. Green microstructure was dependent on the pore size and distribution due to the particle size, and on the deairing step. The green density maximum obtained was 58.9% (4.63 $\mu\textrm{m}$), 60% (0.32 $\mu\textrm{m}$), 47% (10 nm) theoretical density (TD), and the deairing step applied before gel-casting did not affect green density.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.39 no.2
• /
• pp.247-256
• /
• 2015

This study prepared fabric-heating elements of carbon nanofiber composite to characterize morphologies and electrical properties. Carbon nanofiber composite was prepared with 15wt% PVDF-HFP/acetone solution, and 0, 1, 2, 4, 8, and 16wt% carbon nanofiber. Dispersion of solution was conducted with stirring for a week, sonification for 24 hours, and storage for a month, until coating. Carbon nanofiber composite coated fabrics were prepared by knife-edge coating on nylon fabrics with a thickness of 0.1mm. The morphologies of carbon nanofiber composite coated fabrics were measured by FE-SEM. Surface resistance was determined by KS K0555 and worksurface tester. A heating-pad clamping device connected to a variable AC/DC power supply was used for the electric heating characteristics of the samples and multi-layer fabrics. An infrared camera applied voltages to samples while maintaining a certain distance from fabric surfaces. The results of morphologies indicated that the CNF content increased specifically to the visibility and presence of carbon nanofiber. The surface resistance test results revealed that an increased CNF content improved the performance of coated fabrics. The results of electric heating properties, surface temperatures and current of 16wt% carbon nanofiber composite coated fabrics were $80^{\circ}C$ and 0.35A in the application of a 20V current. Carbon nanofiber composite coated fabrics have excellent electrical characteristics as fabric-heating elements.

• Macromolecular Research
• /
• v.17 no.9
• /
• pp.688-696
• /
• 2009

In this study, a new class of polyurethane (PU) nanofibers containing silver (Ag) nanoparticles (NPs) was synthesized by electrospinning. A simple method that did not depending on additional foreign chemicals was used to self synthesize the silver NPs in/on PU nanofibers. The synthesis of silver NPs was carried out by exploiting the reduction ability of N,N-dimethylformamide (DMF), which is used mainly to decompose silver nitrate to silver NPs. Typically, a sol-gel consisting of $AgNO_3$/PU was electrospun and aged for one week. Silver NPs were created in/on PU nanofibers. SEM confirmed the well oriented nanofibers and good dispersion of pure silver NPs. TEM indicated that the Ag NPs were 5 to 20 nm in diameter. XRD demonstrated the good crystalline features of silver metal. The mechanical properties of the nanofiber mats showed improvement with increasing silver NPs content. The fixedness of the silver NPs obtained on PU nanofibers was examined by harsh successive washing of the as-prepared mats using a large amount of water. The results confirmed the good stability of the synthesized nanofiber mats. Two model organisms, E. coli and S. typhimurium, were used to check the antimicrobial influence of these nanofiber mats. Subsequently, antimicrobial tests indicated that the prepared nanofibers have a high bactericidal effect. Accordingly, these results highlight the potential use of these nanofiber mats as antimicrobial agents.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.545-549
• /
• 2006

Blends of poly(acrylic acid- co-maleic acid) (PAM) with poly (vinyl alcohol) (PVA) were pre -pared in distilled water PVA/PAM/saponite (PVA/PAM/SPT) nanocomposite films were prepared with various clay contents by using the solution intercalation method. The variations of the dispersion, morphology, and thermo-mechanical properties of the nanocomposites with clay content in the range 0 to 9 wt% were examined. Up to 3 wt% clay loading, the clay particles were homogeneously dispersed in the PVA/PAM blends. However, some agglomerated structures form in the polymer matrix above a clay content of 7 wt%. The thermal stability of the hybrids was increased linearly with increasing the clay loading up to 9 wt%. The maximum strength and modulus were obtained at a clay content of 7 wt%. Thus, the addition of small amounts of clay to the PVA/PAM blends produced PVA/PAM nano-composites with improved the thermo-mechanical properties.