• The Journal of the Korea Contents Association
• /
• v.22 no.3
• /
• pp.586-592
• /
• 2022

In this study cerium nano particles(CNPs) with 0-4.0 wt% was incorporated to the conventional dental pit and fissure sealant(ConciseTM) to produce new pit and fissure sealant the physical properties and cytotoxicity. The physical properties were measured for polymerizing depth the degree of water absorption and solubility. The cytotoxicity of cell viability was analyzed by MTT assay using immortalized human oral keratinocyte(IHOK). As a result of this preceding study the polymerizing depth was decreased by the increasing of the amount of CNPs. The solubility degree of the sealant added CNPs with 2.0 wt% showed was the lower and the water absorption showed no significantly difference with the control groups(p>0.05). The cytotoxicity test results showed high survival rates in all experimental groups. Therefore, pit and fissure sealant by the addition of CNPs excellent cell viability be produced without weaken the physical property of the cell viability fissure sealant containing CNPs does not weaken physical properties and has no cytotoxic effects biocompatibility. Considering its properties effect of CNPs, further studies are required for distribution technology application.

• Composites Research
• /
• v.31 no.4
• /
• pp.171-176
• /
• 2018

We proposed new and easy fabrication method of micro-nano hierarchical structures for synthetic dry adhesives and conducted feasibility tests of alignment characteristics of nano-materials in the microstructures by capillary effect. Candidates of fabrication conditions were selected based on the degree of cure and viscosity of mixtures of multiwall carbon nanotubes (MWCNTs) and polydimethylsiloxane (PDMS), which were measured with respect to the fabrication conditions. Scanning electron microscopy images of cross sections of MWCNT-PDMS microstructures were analyzed. MWCNT alignment in microstructures was better when fabrication temperature and degree of cure at fabricating start were lower, but areal density of MWCNTs was little affected by fabrication conditions.

• Journal of Powder Materials
• /
• v.14 no.1 s.60
• /
• pp.13-18
• /
• 2007

The mother Ni-W (1-5 wt.%) alloy billets for coated conductor substrate were fabricated by powder metallurgy process. The tensile test results for the sintered Ni-W rods showed the increase of mechanical strength and decrease of ductility with increasing W content due to the solid solution hardening. All the fracture surfaces of the tested specimens showed the typical ductile fracture mode of dimple rupture due to the local necking. The Ni-W alloy billets were made into tape by cold rolling. After the appropriate heat treatment for recrystallization, the brass texture formed by the cold rolling was converted to the complete cube texture. The in-plane and out of plane texture of the tapes estimated by x-ray pole figure were smaller than 9 degree and 7 degree, respectively. The effect of the W addition on the texture development seems not to be significant.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.87-90
• /
• 2005

This paper presents an evaluation of the effect of titanium dioxide nanoparticles in sulfonated poly(ether ether ketone) (SPEEK) with sulfonation degree of 57%. A series of inorganic-organic hybrid membranes were prepared with a systematic variation of titanium dioxide nanoparticles content. Their water uptake, methanol permeability and proton conductivity as a function of temperature were investigated. The results obtained show that the inorganic oxide network decreases the proton conductivity and water swelling. It is also found that increase in inorganic oxide content leads to decrease of methanol permeability. In terms of morphology, membranes are homogeneous and exhibit a good adhesion between inorganic domains and the polymer matrix. The properties of the composite membranes are compared with standard nafion membrane.

• KSBB Journal
• /
• v.27 no.1
• /
• pp.45-50
• /
• 2012

In this paper, we investigated the effect of nanostructure on the cell behaviors such as adhesion and growth rate. Nanoporous structures with various diameters (30, 40, 45, 50, 60 nm) and 500 nm of the depth were fabricated using the anodizing method. The water contact angle of the surface consisting of nanopores with 30 nm diameter was 40 degree and those were 60~70 degree in cases of nanopores with over 40 nm diameter. Hela cells were cultivated on various nanoporous structure surface to investigate the cell behavior on nanostructure. As a result, Hela cells preferred 30 nm diameter nanoporous surface that has lower water contact angle. This result was confirmed by protein adsorption experiment and scanning electron microscope investigation.

• Proceedings of the SCSK Conference
• /
• 2003.09a
• /
• pp.178-191
• /
• 2003

OMC is essentialiy necessary compound in sun goods as organic UV protecting products. But the skin-trouble problem is raising because of skin penetration of OMC. In this study, non-capsulated pure OMC was compared with Organic-Inorganic-Nano-hybrid OMC for skin penetration force and SPF degree. Organic- Inorganic Nano-Hybrid OMC is OMC trapped in the pore of the mesoporous silica synthesized by the sol-gel method after OMC is nanoemulsified in the system of the hydrogenated Lecithin/ Ethanol/caprylic/capric triglyceride/OMC/water. OMC- nano- emulsion was obtained by a microfluidizing process at 1000bar and then micelle size in the nanoemulsion solution is 100-200nm range. Mesoporous silica nano-hybrid OMC was prepared by the process; surfactant was added in dissolved OMC-Nanoemulsion, then the rod Micelle was formed. OMC-nanoemulsion was capsulated in this rod Micelle and then silica precursor was added in the OMC-nanoemulsion solution. Through the hydrolysis reaction of the silica precursor, mesoporous silica concluding OMC-Nanocapsulation was obtained. The nano-hybrid surface of this OMC-Nanoemulsion-Inorganic system was treated with polyalkyl-silane compound. OMC-Mesoporous silica Nano-hybrids coated with polyalkyl-silane compound show the higher sun protecting factor (SPF Analyzer: INDEX 10-15) than pure OMC and could reduce a skin penetration of OMC. The physico-chemical properties of these nano-hybrids measured on the SPF index, partical size, strcture, specific surface area, pore size, morphology, UV absorption, rate of the OMC dissolution using SPF Analyzer, Laser light scattering system, XRD, BET, SEM, chroma Meter, HPLC, Image analyzer, microfluidizer, UV/VIS. spectrometer.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.1
• /
• pp.42-50
• /
• 2006

Co-Fe-Al-O nano-granular thin films with high electrical resistivity, fabricated by radio frequency magnetron sputtering under an $Ar+O_2$ atmosphere, are found to show good soft magnetic properties in the GHz frequency range. The real part value of the relative permeability is 260 at low frequencies and this value is maintained up to the GHz frequency range. A non-integrated type noise filter on a coplanar waveguide transmission line is demonstrated by using the Co-Fe-Al-O nano-granular thin film with the dimensions of $4\;mm(l){\times}4\;mm(w){\times}0.1\;{\mu}m(t)$. The insertion loss is very low being less than 0.3 dB and this low value is maintained up to 2 GHz. At a ferromagnetic resonance frequency of 3.3 GHz, the degree of noise suppression is measured to be 3 dB. This level of noise attenuation is small for real applications, but there is much room for further improvement by increasing the magnetic volume and integrating the magnetic thin film into the CPW transmission line.

• Journal of ILASS-Korea
• /
• v.17 no.4
• /
• pp.185-191
• /
• 2012

Particulate matters (PM) that is generated by most diesel engine is regulated by the mass concentration measured by the conventional method it had been. Recently, Europe PMP (Particle Measurement Program) decided to start the regulation of vehicle's nano-sized particle number (PN) from the year of 2011 because of nano-particle's higher degree of harm to the human body. So firstly, the standard level of PN emission is introduced in the Euro 5/6 emissions regulation with a limit of $6{\times}10^{11}$ per km for light duty vehicle. Also KPMP(Korea Particle Measurement Program) was organized to copy quickly international technical trend. In this paper, it was investigated the nano-sized PN measurement characteristics for different particle generators between spray type and soot type. And the difference ratio between particle generators, the characteristic of PN concentration, counting efficiency and linearity was analyzed. Then, we make conclusions as followed. When particle diameter is increased, counting efficiency of two generators is decreased. Also Secondary calibration method is more higher 3% than Primary calibration method. Finally, SOF which is included in soot particles is not totally removed so it have great influence on test result of counting efficiency and linearity.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.270-270
• /
• 2016

We fabricated an organic-inorganic nano laminated encapsulation layer using molecular layer deposition (MLD) combined with atomic layer deposition (ALD). The $Al_2O_3$ inorganic layers as an effective single encapsulation layer were deposited at 80 degree C using ALD with alternating surface-saturation reactions of TMA and $H_2O$. A self-assembled organic layers (SAOLs) were fabricated at the same temperature using MLD. MLD and ALD deposition process were performed in the same reaction chamber. The prepared SAOL-$Al_2O_3$ organic-inorganic nano laminate films exhibited good mechanical stability and excellent encapsulation property. The measurement of water vapor transmission rate (WVTR) was performed with Ca test. We controlled thickness-ratio of organic and inorganic layer, and specific ratio showed a lowest WVTR value. Also this encapsulation layer contained very few pin-holes or defects which were linked in whole area by defect test. To apply into real OLEDs panels, we controlled a film stress from tensile to compressive and flexibility defined as an elastic modulus with organic-inorganic ratio. It has shown that OLEDs panel encapsulated with nano laminate layer exhibits better properties than single layer encapsulated in acceleration conditions. These results indicate that the organic-inorganic nano laminate thin films have high potential for flexible display applications.

• Journal of Sensor Science and Technology
• /
• v.25 no.3
• /
• pp.208-212
• /
• 2016

In this work, a loop sensor for Arc-Flash detections has been developed in order to trip a circuit breaker within 2.5 ms after an Arc-Flash event. For an efficient capturing of the flash light, plastic optical fibers, where light attenuations are larger than those in silica-based ones, with different diameters and surface conditions were utilized. The performance was comparatively analyzed with those of a point sensor and a commercialized product. The point sensor module was designed for hemisphere-like capturings of Arc-Flashes larger than 3 kA at 2 meters from the sensor. On the other hand, the loop sensor allowed 360-degree-detections around the fiber axis and the measurement range was dependent on the length of the fiber connected to the sensor module. The trip-level-dependent brightness measurement results showed that the fabricated point sensor and loop sensor satisfied a brightness condition, 10~40 klux, and the responses of the system to Arc-Flashes were completed within 2.5 ms.